CN108914627A - A kind of chain tooth and zipper with translucent effect - Google Patents
A kind of chain tooth and zipper with translucent effect Download PDFInfo
- Publication number
- CN108914627A CN108914627A CN201810915531.1A CN201810915531A CN108914627A CN 108914627 A CN108914627 A CN 108914627A CN 201810915531 A CN201810915531 A CN 201810915531A CN 108914627 A CN108914627 A CN 108914627A
- Authority
- CN
- China
- Prior art keywords
- owf
- translucent
- monofilament
- zipper
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the preparation method and zipper of a kind of chain tooth with translucent effect, method includes by after polyethylene terephthalate slice dehumidifying, and melting extrusion, cooling and drawing and setting obtains transparent monofilament；Monofilament is dyed in dye bath, dyeing is contaminated by 40~60 DEG C of beginnings, and 20~60min is kept the temperature after being warming up to 125~135 DEG C, is washed after cooling, the translucent monofilament dyed；Dye bath includes 0.001~6%owf of disperse dyes；0.001~3g/L of 0.05~3g/L of pH adjusting agent and levelling agent；By the translucent monofilament heated die of dyeing, obtained continuous U-shaped element chain combination obtains the chain tooth with translucent effect.Chain tooth and strap combine to obtain the zipper with translucent effect, possess unique visual sense, promote the class of zipper；Zipper also has preferable Washing, PERSPIRATION COLOR FASTNESS and fastness to rubbing, at 4 grades or more.
Description
Technical field
The invention belongs to zipper technology field more particularly to a kind of chain tooths and zipper with translucent effect.
Background technique
Auxiliary material on clothes combines fashion trend instantly, the zipper based on special visual effect class product also increasingly by
Client welcomes, wherein a kind of effect of the salad chain as nearest prevalence is hit, it is deep to be pursued.
However more common zipper is that white zipper code dress carries out dyeing again and is made into the market, the cloth of this zipper
Band, chain tooth, suture are all a kind of unified colors, give cheap sense, do not meet the need of currently popular individual requirement
It wants.
Summary of the invention
In view of this, the purpose of the present invention is to provide a kind of chain tooth and zipper with translucent effect, the chain tooth are done
At zipper there is translucent effect, promote zipper class, and meet color fastness requirement.
The present invention provides a kind of preparation methods of chain tooth with translucent effect, include the following steps：
After polyethylene terephthalate slice dehumidifying, melting extrusion, cooling and drawing and setting obtains transparent monofilament；
Monofilament to be dyed in dye bath, dyeing is contaminated by 40~60 DEG C of beginning, heat preservation 20 after being warming up to 125~135 DEG C~
60min is washed after cooling, the translucent monofilament dyed；
The dye bath includes 0.001~6%owf of disperse dyes；0.05~3g/L of pH adjusting agent and levelling agent 0.001~
3g/L；
By the translucent monofilament heated die of dyeing, continuous U-shaped element chain is obtained, combination obtains the chain with translucent effect
Tooth.
Preferably, the levelling agent is selected from neopelex and/or polyethylene glycol monooleate.
Preferably, the bath raio when dyeing is 1:6~1:20.
Preferably, the temperature of the dehumidifying is 140~170 DEG C, and the time of dehumidifying is 5~7h.
Preferably, the temperature of the melting extrusion is 280~300 DEG C, and the pressure of melting extrusion is 7.5~8.5MPa；It draws
The temperature for stretching sizing is 170~250 DEG C.
Preferably, dye bath includes 0.5~1g/L of 0.02~0.42%owf of disperse dyes and levelling agent.
Preferably, the dye bath includes scattered fluorescent yellow 0.05%owf, disperses color indigo plant 0.15%owf, glacial acetic acid 0.2g/L
With levelling agent 0.5g/L；
Or including scattered fluorescent yellow 0.23%owf, dispersion fluorescence red 0.19%owf, glacial acetic acid 0.2g/L and levelling agent 1g/
L；
Or including disperse violet 0.06%owf, disperse brilliant blue 0.15%owf, glacial acetic acid 0.2g/L and levelling agent 0.5g/L.
Preferably, 125~135 DEG C are warming up to 1~2 DEG C/min.
The present invention provides a kind of zippers, including have translucent effect made from preparation method described in above-mentioned technical proposal
Chain tooth.
The present invention provides a kind of preparation methods of chain tooth with translucent effect, include the following steps：It will be poly- to benzene
After the slice dehumidifying of dioctyl phthalate second diester, melting extrusion, cooling and drawing and setting obtains transparent monofilament；Monofilament is contaminated in dye bath
Color, dyeing are contaminated by 40~60 DEG C of beginnings, and 20~60min is kept the temperature after being warming up to 125~135 DEG C, is washed after cooling, half dyed
Transparent monofilament；The dye bath includes 0.001~6%owf of disperse dyes；0.05~3g/L of pH adjusting agent and levelling agent 0.001
~3g/L；By the translucent monofilament heated die of dyeing, continuous U-shaped element chain is obtained, combination obtains the chain with translucent effect
Tooth.The present invention is raw material by using polyethylene terephthalate slice, in the dye bath of special formulation and under specified conditions
Dyeing, obtains the chain tooth with translucent effect.Chain tooth and strap combine to obtain the zipper with translucent effect, possess uniqueness
Visual sense, promote the class of zipper；Zipper also has preferable Washing, PERSPIRATION COLOR FASTNESS and fastness to rubbing.Experiment
The result shows that：The Washing of zipper with translucent effect is at 4 grades or more, and PERSPIRATION COLOR FASTNESS is more than 4 ranks, antifriction
Rubbing fastness is more than 4 ranks.
Detailed description of the invention
Fig. 1 is the apparent visual effect picture of zipper prepared by the embodiment of the present invention 1；
Fig. 2 is the apparent visual effect picture of zipper prepared by the embodiment of the present invention 2；
Fig. 3 is the apparent visual effect picture of zipper prepared by the embodiment of the present invention 3.
Specific embodiment
The present invention provides a kind of preparation methods of chain tooth with translucent effect, include the following steps：
After polyethylene terephthalate slice dehumidifying, melting extrusion, cooling and drawing and setting obtains transparent monofilament；
Monofilament to be dyed in dye bath, dyeing is contaminated by 40~60 DEG C of beginning, heat preservation 20 after being warming up to 125~135 DEG C~
60min is washed after cooling, the translucent monofilament dyed；
The dye bath includes 0.001~6%owf of disperse dyes；0.05~3g/L of pH adjusting agent and levelling agent 0.001~
3g/L；
By the translucent monofilament heated die of dyeing, continuous U-shaped element chain is obtained, combination obtains the chain with translucent effect
Tooth.
It is raw material by using polyethylene terephthalate slice, contaminates in the dye bath of special formulation and under specified conditions
Color obtains the chain tooth with translucent effect.Chain tooth and strap combine to obtain the zipper with translucent effect, possess unique
Visual sense promotes the class of zipper；Zipper also has preferable Washing, PERSPIRATION COLOR FASTNESS and fastness to rubbing.
By after polyethylene terephthalate slice dehumidifying, melting extrusion, cooling and drawing and setting obtains transparent the present invention
Monofilament.In the present invention, the temperature of polyethylene terephthalate slice dehumidifying is preferably 140~170 DEG C, dehumidifying when
Between preferably 5~7h.
Present invention preferably employs monofilament extrusion equipments to carry out melting extrusion；The temperature of the melting extrusion is preferably 280~
300 DEG C, the pressure of melting extrusion is preferably 7.5~8.5MPa.Monofilament after extrusion is cooling preferably at 60~80 DEG C, and preferably
Drawing and setting is carried out at 170~250 DEG C, obtains transparent monofilament.
After obtaining transparent monofilament, the present invention dyes the transparent monofilament in dye bath, and dyeing is contaminated by 40~60 DEG C of beginnings, rises
Temperature is washed, the translucent monofilament dyed to 20~60min of heat preservation after 125~135 DEG C after cooling.The present invention preferably with 1~
2 DEG C/min is warming up to 125~135 DEG C.In the present invention, the dye bath includes 0.001~6%owf of disperse dyes；PH value is adjusted
0.001~3g/L of 0.05~3g/L of agent and levelling agent.In the present invention, the levelling agent is preferably selected from neopelex
And/or polyethylene glycol monooleate；The pH adjusting agent is preferably selected from Acetic acid-sodium acetate buffer or acetic acid；The pH value
The pH value of dye bath is preferably adjusted to 4~6 by regulator.The disperse dyes carry out the selection of different dyes according to client's needs；
The disperse dyes preferably include one of fluorescein, fluorescein, pink, purple, gorgeous blue, color blue and bright red or a variety of.
In the present invention, the dye bath preferably includes 0.5~1g/L of 0.02~0.42%owf of disperse dyes and levelling agent.
In a particular embodiment, the dye bath includes scattered fluorescent yellow 0.05%owf, disperses color indigo plant 0.15%owf, glacial acetic acid 0.2g/L
With levelling agent 0.5g/L；
Or including scattered fluorescent yellow 0.23%owf, dispersion fluorescence red 0.19%owf, glacial acetic acid 0.2g/L and levelling agent 1g/
L；
Or including disperse violet 0.06%owf, disperse brilliant blue 0.15%owf, glacial acetic acid 0.2g/L and levelling agent 0.5g/L.
In the present invention, the dye bath when dyeing is than preferably 1:6~1：20；More preferably 1:10~1:15.
If chain tooth surface has the dyestuff of attachment when dyeing, the present invention is carried out preferably after cooling using piece alkali and sodium hydrosulfite
Reduction cleaning；It is washed again after reduction cleaning, the translucent monofilament dyed.
After the translucent monofilament dyed, the present invention is by the translucent monofilament heated die of the dyeing, obtained company
Continuous U-shaped element chain combination, obtains the chain tooth with translucent effect.Specifically, the present invention preferably twines the translucent monofilament of dyeing
It is around on center bar, temperature is heated to 100~180 DEG C, is formed by the screw extruding of two spirals, forms the element of continuous U-shaped
Chain.Two plain chains obtain continuous U-shaped element chain by combination；Two continuous U-shaped element chains are combined, chain tooth is obtained.
The present invention provides a kind of zippers, including have translucent effect made from preparation method described in above-mentioned technical proposal
Chain tooth.The present invention preferably sutures chain tooth and two straps to obtain zipper.
The present invention makes drawing obtained by the dyeing to polyethylene terephthalate monofilament progress special formulation and technique
Chain has translucent special surface effect.
In order to further illustrate the present invention, below with reference to embodiment to provided by the invention a kind of with translucent effect
The preparation method and zipper of chain tooth are described in detail, but they cannot be interpreted as limiting the scope of the present invention.
Embodiment 1
Put polyethylene terephthalate slice into dry barrel, the continuous drying 7h at 150 DEG C；
By above-mentioned steps obtain by it is dry thoroughly after, stretch, then be formed at 230 DEG C, obtain transparent at 170 DEG C
Monofilament；
Transparent monofilament obtained above is wound on stain kit, send to dyeing process and is dyed；What dyeing used
Dye bath includes scattered fluorescent yellow 0.05% (owf), disperses color indigo plant 0.15% (owf), glacial acetic acid 0.2g/L, levelling agent 0.5g/L；
Bath raio is 1:10.Acetic acid, levelling agent, dyestuff are sequentially added in dye vat, after mixing evenly, are contaminated in 40 DEG C of beginnings, with 2 DEG C/min liter
Temperature is washed, the translucent monofilament dyed in 130 DEG C of heat preservation 20min after cooling；
The translucent monofilament dyed is wound on center bar, is heated to 160 DEG C, passes through the screw extruding of two spirals
Molding, forms the plain chain of continuous U-shaped；Two plain chains obtain translucent chain tooth by combination；
Above-mentioned translucent chain tooth and two straps are combined with suture by automatic sewing machine, drawn
Chain.
It is the apparent visual effect picture of zipper prepared by the embodiment of the present invention 1 referring to Fig. 1, Fig. 1；Drawing prepared by embodiment 1
Chain has translucent effect, possesses unique visual sense, improves the class of zipper.
Washing, PERSPIRATION COLOR FASTNESS and the fastness to rubbing of zipper prepared by embodiment 1 are at 4 grades or more.
Embodiment 2
Put polyethylene terephthalate slice into dry barrel, the continuous drying 7h at 150 DEG C；
By above-mentioned steps obtain by it is dry thoroughly after, stretch, then be formed at 230 DEG C, obtain transparent at 170 DEG C
Monofilament；
Transparent monofilament obtained above is wound on stain kit, send to dyeing process and is dyed；What dyeing used
Dye bath includes scattered fluorescent yellow 0.23% (owf), dispersion fluorescence red 0.19% (owf), glacial acetic acid 0.2g/L, levelling agent 1.0g/
L；Bath raio is 1:12.Acetic acid, levelling agent, dyestuff are sequentially added in dye vat, after mixing evenly, are contaminated in 60 DEG C of beginnings, with 2 DEG C/min
Heating, in 130 DEG C of heat preservation 30min, is washed, the translucent monofilament dyed after cooling；
The translucent monofilament dyed is wound on center bar, is heated to 160 DEG C, passes through the screw extruding of two spirals
Molding, forms the plain chain of continuous U-shaped；Two plain chains obtain translucent chain tooth by combination；
Above-mentioned translucent chain tooth and two straps are combined with suture by automatic sewing machine, drawn
Chain.
Referring to fig. 2, Fig. 2 is the apparent visual effect picture of zipper prepared by the embodiment of the present invention 2；Drawing prepared by embodiment 2
Chain has translucent effect, possesses unique visual sense, improves the class of zipper.
Washing, PERSPIRATION COLOR FASTNESS and the fastness to rubbing of zipper prepared by embodiment 2 are at 4 grades or more.
Embodiment 3
Put polyethylene terephthalate slice into dry barrel, the continuous drying 7h at 160 DEG C；
By above-mentioned steps obtain by it is dry thoroughly after, stretch, then be formed at 230 DEG C, obtain transparent at 170 DEG C
Monofilament；
Transparent monofilament obtained above is wound on stain kit, send to dyeing process and is dyed；What dyeing used
Dye bath includes disperse violet 0.06% (owf), disperse brilliant blue 0.15% (owf), glacial acetic acid 0.2g/L, levelling agent 0.5g/L；Bath raio
It is 1:15.Acetic acid, levelling agent, dyestuff are sequentially added in dye vat, after mixing evenly, are contaminated in 60 DEG C of beginnings, are heated up with 2 DEG C/min,
In 130 DEG C of heat preservation 20min, piece alkali and sodium hydrosulfite reduction cleaning are used after cooling, then washed, the translucent list dyed
Silk；
The translucent monofilament dyed is wound on center bar, is heated to 160 DEG C, passes through the screw extruding of two spirals
Molding, forms the plain chain of continuous U-shaped；Two plain chains obtain translucent chain tooth by combination；
Above-mentioned translucent chain tooth and two straps are combined with suture by automatic sewing machine, drawn
Chain.
It is the apparent visual effect picture of zipper prepared by the embodiment of the present invention 3 referring to Fig. 3, Fig. 3；Drawing prepared by embodiment 2
Chain has translucent effect, possesses unique visual sense, improves the class of zipper.
Washing, PERSPIRATION COLOR FASTNESS and the fastness to rubbing of zipper prepared by embodiment 3 are at 4 grades or more.
As seen from the above embodiment, the present invention provides a kind of preparation methods of chain tooth with translucent effect, including
Following steps：After polyethylene terephthalate slice dehumidifying, melting extrusion, cooling and drawing and setting obtains transparent monofilament；
Monofilament is dyed in dye bath, dyeing is contaminated by 40~60 DEG C of beginnings, 20~60min is kept the temperature after being warming up to 125~135 DEG C, after cooling
Washing, the translucent monofilament dyed；The dye bath includes 0.001~6%owf of disperse dyes；PH adjusting agent 0.05~
0.001~3g/L of 3g/L and levelling agent；By the translucent monofilament heated die of dyeing, continuous U-shaped element chain is obtained, combination is had
There is the chain tooth of translucent effect.The present invention is raw material by using polyethylene terephthalate slice, in the dye of special formulation
Bath neutralizes to be dyed under specified conditions, obtains the chain tooth with translucent effect.Chain tooth and strap, which combine to obtain, has semi-transparent obvious results
The zipper of fruit possesses unique visual sense, promotes the class of zipper；Zipper also has preferable Washing, PERSPIRATION COLOR FASTNESS
And fastness to rubbing.The experimental results showed that：For the Washing of zipper with translucent effect at 4 grades or more, sweat stain color is firm
Degree is more than 4 ranks, and fastness to rubbing is more than 4 ranks.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (9)
1. a kind of preparation method of the chain tooth with translucent effect, includes the following steps：
After polyethylene terephthalate slice dehumidifying, melting extrusion, cooling and drawing and setting obtains transparent monofilament；
The transparent monofilament to be dyed in dye bath, dyeing is contaminated by 40~60 DEG C of beginning, heat preservation 20 after being warming up to 125~135 DEG C~
60min is washed after cooling, the translucent monofilament dyed；
The dye bath includes 0.001~6%owf of disperse dyes；0.001~3g/ of 0.05~3g/L of pH adjusting agent and levelling agent
L；
By the translucent monofilament heated die of dyeing, obtained continuous U-shaped element chain combination obtains the chain with translucent effect
Tooth.
2. preparation method according to claim 1, which is characterized in that the levelling agent is selected from neopelex
And/or polyethylene glycol monooleate.
3. preparation method according to claim 1, which is characterized in that the bath raio when dyeing is 1:6~1:20.
4. preparation method according to claim 1, which is characterized in that the temperature of the dehumidifying is 140~170 DEG C, dehumidifying
Time be 5~7h.
5. preparation method according to claim 1, which is characterized in that the temperature of the melting extrusion is 280~300 DEG C,
The pressure of melting extrusion is 7.5~8.5MPa；The temperature of drawing and setting is 170~250 DEG C.
6. preparation method according to claim 1, which is characterized in that dye bath includes 0.02~0.42%owf of disperse dyes
With 0.5~1g/L of levelling agent.
7. preparation method according to claim 1, which is characterized in that the dye bath includes scattered fluorescent yellow 0.05%owf,
Disperse color indigo plant 0.15%owf, glacial acetic acid 0.2g/L and levelling agent 0.5g/L；
Or including scattered fluorescent yellow 0.23%owf, dispersion fluorescence red 0.19%owf, glacial acetic acid 0.2g/L and levelling agent 1g/L；
Or including disperse violet 0.06%owf, disperse brilliant blue 0.15%owf, glacial acetic acid 0.2g/L and levelling agent 0.5g/L.
8. preparation method according to claim 1, which is characterized in that be warming up to 125~135 DEG C with 1~2 DEG C/min.
9. a kind of zipper, including the chain tooth with translucent effect made from any one of claim 1~8 preparation method.