CN108914168A - A kind of sheet metal surface treatment process - Google Patents
A kind of sheet metal surface treatment process Download PDFInfo
- Publication number
- CN108914168A CN108914168A CN201810861874.4A CN201810861874A CN108914168A CN 108914168 A CN108914168 A CN 108914168A CN 201810861874 A CN201810861874 A CN 201810861874A CN 108914168 A CN108914168 A CN 108914168A
- Authority
- CN
- China
- Prior art keywords
- sheet metal
- zinc
- treatment
- processing
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sheet metal treatment process, carry out surface impurity clearing process to sheet metal first, and the surface impurity clearing process specifically comprises the following steps:Surface clean, acidleach processing, blasting treatment, drying process;After the completion of surface impurity removes work, surface coating process is carried out, the surface coating process includes the following steps:Zinc-plated, chemical polishing, Passivation Treatment, drying and processing.Sheet metal surface treatment process provided by the invention carries out specially treated to sheet metal first before zinc-plated processing, removes surface impurity, and carry out blasting treatment, improves sheet metal surface characteristic;Chemical polishing and Passivation Treatment have been carried out after zinc-plated, are made subsequent zinc coat that there is maximum adhesive force in sheet metal surface, are improved the quality of coating.
Description
Technical field
The present invention relates to a kind of sheet metal surface treatment process, belong to sheet metal processing technique field.
Background technique
The metal material is pure metal and its alloy on ordinary meaning, is the basic material for constituting modern civilization society
One of.And common metal material the problems such as will appear aging, corrosion when using in the natural environment, and then seriously affect it and make
With characteristic, it is therefore desirable to carry out the surface treatment such as anti-corrosion.Zinc-plated is a kind of common process of surface treatment, electrogalvanizing sheet metal
Also it is widely used in household electrical appliances, automobile and the field of building materials.But there are still deficiencies for existing galvanizing technique, lead to zinc coat
Softer, processability is poor.
Summary of the invention
Purpose:In order to overcome the deficiencies in the prior art, the present invention provides a kind of sheet metal surface treatment process.
Technical solution:In order to solve the above technical problems, the technical solution adopted by the present invention is:
A kind of sheet metal surface treatment process carries out surface impurity clearing process, the surface impurity to sheet metal first
Clearing process specifically comprises the following steps,
S1.1, surface clean:Sheet metal is first put into chemical degreasing liquid to and is carried out 10 ~ 15min of ultrasonic treatment, is then taken out
It is rinsed, is finally stood spare after draining surface moisture with clear water;
S1.2, acidleach processing:By step S1.1, treated that sheet metal is put into 8 ~ 13min of immersion treatment in acid solution, then takes
It is rinsed, is stood spare after draining surface moisture with clear water out;
S1.3, blasting treatment:By step S1.2, treated that sheet metal is put into sandblasting instrument carries out blasting treatment, during which
The pressure for controlling sandblasting is 0.5 ~ 0.55MPa, is after the completion taken out sheet metal spare;
S1.4 is dried:Sheet metal successively Jing Guo above three step process is put into drying box, place is dried
It manages, is taken out after 1 ~ 2h;
After the completion of surface impurity removes work, surface coating process is carried out, the surface coating process includes the following steps,
S2.1, it is zinc-plated:Carry out zinc-plated processing will be put it into electroplating bath by the sheet metal of above-mentioned steps S1.1 to S1.4 processing,
It is washed three times after the completion;Wherein, plating solution formula is in electroplating bath:Sodium hydroxide 110g/L, zinc oxide 10g/L, alkalinity
Zinc-plating additive 5ml/L, in alkaline zinc plating additive, brightener concentration 5ml/L, auxiliary additive concentration is 5ml/L;
S2.2, chemical polishing:Mobile at least 5 in the nitric acid liquid for being 3% by step S2.1 treated sheet metal is put into concentration
Second;It then takes out and cleans in the sink at least twice;
S2.3, Passivation Treatment:By step S2.2 treated sheet metal is put into passivator solution 15 ~ 25min of immersion, then
Taking-up is rinsed with clear water;
S2.4, drying and processing:Metal plate after Passivation Treatment is rinsed with clear water again, is then placed in drying box at drying
It manages, is taken out after 1 ~ 2h.
Preferably, chemical degreasing liquid described in step S1.1 is acetone.
Preferably, acid solution described in step S1.2 is 15% nitric acid solution.
Preferably, the granular size that blast media is controlled when blasting treatment described in step S1.3 is 0.6 ~ 0.75mm,
Spray angle and workpiece surface are in 90 °, and nozzle is 100 ~ 105mm at a distance from workpiece surface.
Preferably, in step S2.1, controlling the current density in electroplating bath is 2A/dm2, ambient operation, electroplating time is extremely
Few 10min.
Preferably, the passivator that Passivation Treatment described in step S2.3 uses includes following component:2 parts of phosphoric acid, 1 portion of dye yam
Slag extract, 1.2 parts of dodecyl sodium sulfates, 2.3 parts of vinyltrimethoxysilanes, 0.9 part of trimethyl bromination
Ammonium, 8.2 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids, 1.2 parts of succinic acid alkyl ester sulfonate sodium, 0.7 part of sodium chlorate, 38 parts of deionized waters.
Preferably, step S1.4, the temperature of drying box described in S2.4 is controlled at 80 ~ 85 DEG C.
Beneficial effect:Sheet metal surface treatment process provided by the invention, before zinc-plated processing first to sheet metal into
Row specially treated removes surface impurity, and carries out blasting treatment, improves sheet metal surface characteristic;Chemistry has been carried out after zinc-plated
Polishing and Passivation Treatment make subsequent zinc coat have maximum adhesive force in sheet metal surface, improve the quality of coating.
Specific embodiment
Below with reference to embodiment, the present invention will be further explained.
Embodiment
A kind of sheet metal surface treatment process carries out surface impurity clearing process, the surface to sheet metal first
Impurity clearing process specifically comprises the following steps:
S1.1, surface clean:Sheet metal is first put into chemical degreasing liquid to and is carried out 10 ~ 15min of ultrasonic treatment, is then taken out
It is rinsed, is finally stood spare after draining surface moisture with clear water;
The chemical degreasing liquid is acetone.
S1.2, acidleach processing:By step S1.1, treated that sheet metal is put into 8 ~ 13min of immersion treatment in acid solution, so
Taking-up is rinsed with clear water afterwards, is stood spare after draining surface moisture;
The acid solution is 15% nitric acid solution.
S1.3, blasting treatment:By step S1.2, treated that sheet metal is put into sandblasting instrument carries out blasting treatment,
The pressure that period controls sandblasting is 0.5 ~ 0.55MPa, is after the completion taken out sheet metal spare;
The granular size of control blast media is 0.6 ~ 0.75mm when the described blasting treatment, and spray angle is in workpiece surface
90 °, nozzle is 100 ~ 105mm at a distance from workpiece surface.
S1.4 is dried:Sheet metal successively Jing Guo above three step process is put into drying box and is done
Dry processing is taken out after 1 ~ 2h;The temperature of drying box is controlled at 80 ~ 85 DEG C.
After the completion of surface impurity removes work, surface coating process is carried out, the surface coating process includes the following steps:
S2.1, it is zinc-plated:Carry out zinc-plated processing will be put it into electroplating bath by the sheet metal of above-mentioned steps S1.1 to S1.4 processing,
It is washed three times after the completion;Wherein, plating solution formula is in electroplating bath:Sodium hydroxide 110g/L, zinc oxide 10g/L, alkalinity
Zinc-plating additive 5ml/L, in alkaline zinc plating additive, brightener concentration 5ml/L, auxiliary additive concentration is 5ml/L;
In electroplating process, controlling the current density in electroplating bath is 2A/dm2, ambient operation, electroplating time at least 10min.
S2.2, chemical polishing:It is moved in the nitric acid liquid for being 3% by step S2.1 treated sheet metal is put into concentration
It is 5 seconds few;It then takes out and cleans in the sink at least twice.
S2.3, Passivation Treatment:By step S2.2 treated sheet metal is put into passivator solution 15 ~ 25min of immersion,
It then takes out and is rinsed with clear water;
Passivator used in Passivation Treatment includes following component:2 parts of phosphoric acid, 1 part of dye yam slag extract, 1.2 parts of dodecyl sodium sulfonates
Sodium, 2.3 parts of vinyltrimethoxysilanes, 0.9 part of dodecyl trimethyl ammonium bromide, 8.2 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids, 1.2
Part succinic acid alkyl ester sulfonate sodium, 0.7 part of sodium chlorate, 38 parts of deionized waters.
S2.4, drying and processing:Metal plate after Passivation Treatment is rinsed with clear water again, is then placed in drying in drying box
It handles, is taken out after 1 ~ 2h;The temperature of drying box is controlled at 80 ~ 85 DEG C.
By above-mentioned removal of impurities, coating process processing, can be formed in sheet metal surface has the quality of maximum adhesion power
Different zinc coat.
The above is only a preferred embodiment of the present invention, it should be pointed out that:For the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (7)
1. a kind of sheet metal surface treatment process, it is characterised in that:Surface impurity clearing process is carried out to sheet metal first,
The surface impurity clearing process specifically comprises the following steps,
S1.1, surface clean:Sheet metal is first put into chemical degreasing liquid to and is carried out 10 ~ 15min of ultrasonic treatment, is then taken out
It is rinsed, is finally stood spare after draining surface moisture with clear water;
S1.2, acidleach processing:By step S1.1, treated that sheet metal is put into 8 ~ 13min of immersion treatment in acid solution, then takes
It is rinsed, is stood spare after draining surface moisture with clear water out;
S1.3, blasting treatment:By step S1.2, treated that sheet metal is put into sandblasting instrument carries out blasting treatment, during which
The pressure for controlling sandblasting is 0.5 ~ 0.55MPa, is after the completion taken out sheet metal spare;
S1.4 is dried:Sheet metal successively Jing Guo above three step process is put into drying box, place is dried
It manages, is taken out after 1 ~ 2h;
After the completion of surface impurity removes work, surface coating process is carried out, the surface coating process includes the following steps,
S2.1, it is zinc-plated:Carry out zinc-plated processing will be put it into electroplating bath by the sheet metal of above-mentioned steps S1.1 to S1.4 processing,
It is washed three times after the completion;Wherein, plating solution formula is in electroplating bath:Sodium hydroxide 110g/L, zinc oxide 10g/L, alkalinity
Zinc-plating additive 5ml/L, in alkaline zinc plating additive, brightener concentration 5ml/L, auxiliary additive concentration is 5ml/L;
S2.2, chemical polishing:Mobile at least 5 in the nitric acid liquid for being 3% by step S2.1 treated sheet metal is put into concentration
Second;It then takes out and cleans in the sink at least twice;
S2.3, Passivation Treatment:By step S2.2 treated sheet metal is put into passivator solution 15 ~ 25min of immersion, then
Taking-up is rinsed with clear water;
S2.4, drying and processing:Metal plate after Passivation Treatment is rinsed with clear water again, is then placed in drying box at drying
It manages, is taken out after 1 ~ 2h.
2. sheet metal surface treatment process according to claim 1, it is characterised in that:Chemistry described in step S1.1
Degreasing fluid is acetone.
3. sheet metal surface treatment process according to claim 1, it is characterised in that:Acid solution described in step S1.2
For 15% nitric acid solution.
4. sheet metal surface treatment process according to claim 1, it is characterised in that:Sandblasting described in step S1.3
The granular size that blast media is controlled when processing is 0.6 ~ 0.75mm, and spray angle and workpiece surface are in 90 °, nozzle and workpiece table
The distance in face is 100 ~ 105mm.
5. sheet metal surface treatment process according to claim 1, it is characterised in that:In step S2.1, control plating
Current density in slot is 2A/dm2, ambient operation, electroplating time at least 10min.
6. sheet metal surface treatment process according to claim 1, it is characterised in that:In the step S2.3 at passivation
Managing passivator used includes following component:2 parts of phosphoric acid, 1 part of dye yam slag extract, 1.2 parts of dodecyl sodium sulfates, 2.3 parts of second
Alkenyl trimethoxy silane, 0.9 part of dodecyl trimethyl ammonium bromide, 8.2 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids, 1.2 parts of succinic acid alkane
Base ester sodium sulfonate, 0.7 part of sodium chlorate, 38 parts of deionized waters.
7. sheet metal surface treatment process according to claim 1, it is characterised in that:Step S1.4, described in S2.4
Drying box temperature control at 80 ~ 85 DEG C.