CN108909089A - A kind of novel oil resistant fire-proof plate - Google Patents
A kind of novel oil resistant fire-proof plate Download PDFInfo
- Publication number
- CN108909089A CN108909089A CN201810584699.9A CN201810584699A CN108909089A CN 108909089 A CN108909089 A CN 108909089A CN 201810584699 A CN201810584699 A CN 201810584699A CN 108909089 A CN108909089 A CN 108909089A
- Authority
- CN
- China
- Prior art keywords
- parts
- plate
- oil resistant
- fire
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of novel oil resistant fire-proof plates, including：Backing material plate, plate core layer, resistance to oil reservoir, the plate core upper layer and lower layer are coated with fibre resin fireproof coating layer, and the resistance to oil reservoir is glass cellulose, and the fireproof coating layer constituent is as follows according to mass fraction meter：5-8 parts of aluminium borate, 2-4 parts of C2O3,4-6 parts of sodium hydroxide, 3-5 parts of polyphosphate, 7-10 parts of fertile soil, 6-9 parts of ammonium nitrate, 10-12 parts of conch meal, 2-4 parts of promotor, it is to be bonded as one by alkyd resin fiber and the mixing of modified polycarbonate fiber with fire prevention adhesive that the plate core layer aluminium alloy material, which is the fibre resin,.By the above-mentioned means, the present invention can effectively improve the advantages of oil resistivity and stability of fire-proof plate.
Description
Technical field
The present invention relates to a kind of construction material, in particular to a kind of novel oil resistant fire-proof plate.
Background technique
As the improvement of people's living standards, requirement of the modern metropolitan cities people for house household is higher and higher, for plate
Whether having an impact the higher and higher of concern to the physical and mental health of people, the requirement to oil resistant plate is also higher and higher, normal architectural,
The fire-proof plate that household uses is to heat-resisting, and oil resistant has certain requirement, and existing fire-proof plate does not often reach requirement, so to resistance to
Oiliness is high and stable fire-proof plate demand more highlights.
Summary of the invention
The invention mainly solves the technical problem of providing a kind of novel oil resistant fire-proof plates, can effectively improve fire-proof plate
The advantages of oil resistivity and stability.
In order to solve the above technical problems, one technical scheme adopted by the invention is that：A kind of novel oil resistant fire-proof plate is provided,
Including：Backing material plate, plate core layer, resistance to oil reservoir, the plate core upper layer and lower layer are coated with fibre resin fireproof coating layer, the resistance to oil reservoir
For glass cellulose, the fireproof coating layer constituent is as follows according to mass fraction meter：5-8 parts of aluminium borate, C2O3 2-4
Part, 4-6 parts of sodium hydroxide, 3-5 parts of polyphosphate, 7-10 parts of fertile soil, 6-9 parts of ammonium nitrate, 10-12 parts of conch meal, promotor
2-4 parts, it is by alkyd resin fiber and modified polycarbonate fiber that the plate core layer aluminium alloy material, which is the fibre resin,
Mixing is bonded as one with fire prevention adhesive.
In a preferred embodiment of the present invention, the backing material plate is cross section cuboid.
In a preferred embodiment of the present invention, the fireproof coating layer is with a thickness of 0.3-0.5mm.
In a preferred embodiment of the present invention, the plate core layer is including composition proportion：Zinc accounts for the 52% of content, and aluminium accounts for
The 48% of content.
In a preferred embodiment of the present invention, the fibre resin includes that composition proportion is：Alkyd resin fiber 67%,
Modified polycarbonate fiber 33%.
In a preferred embodiment of the present invention, the fire prevention adhesive is methyl silicone rubber.
The beneficial effects of the invention are as follows：A kind of novel oil resistant fire-proof plate of the present invention, can effectively improve the oil resistant of fire-proof plate
The advantages of property and stability.
Specific embodiment
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
The embodiment of the present invention includes：
Embodiment 1：
A kind of novel oil resistant fire-proof plate, including：Backing material plate, plate core layer, resistance to oil reservoir, the plate core upper layer and lower layer are coated with fiber tree
Rouge fireproof coating layer, the resistance to oil reservoir are glass cellulose, and the fireproof coating layer constituent is as follows according to mass fraction meter：Boron
5 parts of sour aluminium, 2 parts of C2O3,4 parts of sodium hydroxide, 3 parts of polyphosphate, 7 parts of fertile soil, 6 parts of ammonium nitrate, 10 parts of conch meal,
2 parts of promotor, it is by alkyd resin fiber and modified polycarbonate that the plate core layer aluminium alloy material, which is the fibre resin,
Fiber mixing is bonded as one with fire prevention adhesive；The backing material plate is cross section cuboid；The fireproof coating layer with a thickness of
0.3mm；The plate core layer is including composition proportion：Zinc accounts for the 52% of content, and aluminium accounts for the 48% of content；The fibre resin includes into
Distribution ratio is：Alkyd resin fiber 67%, modified polycarbonate fiber 33%；The fire prevention adhesive is methyl silicone rubber.
Embodiment 2：
A kind of novel oil resistant fire-proof plate, including：Backing material plate, plate core layer, resistance to oil reservoir, the plate core upper layer and lower layer are coated with fiber tree
Rouge fireproof coating layer, the resistance to oil reservoir are glass cellulose, and the fireproof coating layer constituent is as follows according to mass fraction meter：Boron
8 parts of sour aluminium, 4 parts of C2O3,6 parts of sodium hydroxide, 5 parts of polyphosphate, 10 parts of fertile soil, 9 parts of ammonium nitrate, conch meal 12
Part, 4 parts of promotor, the plate core layer aluminium alloy material are by alkyd resin fiber and modified poly- carbon for the fibre resin
The mixing of acid esters fiber is bonded as one with fire prevention adhesive；The backing material plate is cross section cuboid；The fireproof coating thickness
Degree is 0.5mm；The plate core layer is including composition proportion：Zinc accounts for the 52% of content, and aluminium accounts for the 48% of content；The fibre resin packet
Including composition proportion is：Alkyd resin fiber 67%, modified polycarbonate fiber 33%；The fire prevention adhesive is methyl silicone rubber.
Embodiment 3：
A kind of novel oil resistant fire-proof plate, including：Backing material plate, plate core layer, resistance to oil reservoir, the plate core upper layer and lower layer are coated with fiber tree
Rouge fireproof coating layer, the resistance to oil reservoir are glass cellulose, and the fireproof coating layer constituent is as follows according to mass fraction meter：Boron
6 parts of sour aluminium, 3 parts of C2O3,5 parts of sodium hydroxide, 4 parts of polyphosphate, 8 parts of fertile soil, 7 parts of ammonium nitrate, 11 parts of conch meal,
3 parts of promotor, it is by alkyd resin fiber and modified polycarbonate that the plate core layer aluminium alloy material, which is the fibre resin,
Fiber mixing is bonded as one with fire prevention adhesive；The backing material plate is cross section cuboid；The fireproof coating layer with a thickness of
0.4mm；The plate core layer is including composition proportion：Zinc accounts for the 52% of content, and aluminium accounts for the 48% of content；The fibre resin includes into
Distribution ratio is：Alkyd resin fiber 67%, modified polycarbonate fiber 33%；The fire prevention adhesive is methyl silicone rubber.
It is different from the prior art, a kind of novel oil resistant fire-proof plate of the present invention coats fibre resin using plate core upper layer and lower layer
Fireproof coating layer, the advantages of oil resistivity and stability of fire-proof plate can be effectively improved.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (6)
1. a kind of novel oil resistant fire-proof plate, which is characterized in that including：Backing material plate, plate core layer, resistance to oil reservoir, the plate core upper and lower two
Layer re-coating fibre resin fireproof coating layer, the resistance to oil reservoir is glass cellulose, and the fireproof coating layer constituent is according to matter
It is as follows to measure number meter：5-8 parts of aluminium borate, 2-4 parts of C2O3,4-6 parts of sodium hydroxide, 3-5 parts of polyphosphate, fertile soil 7-
10 parts, 6-9 parts of ammonium nitrate, 10-12 parts of conch meal, 2-4 parts of promotor, the plate core layer aluminium alloy material are the fiber
Resin is to be bonded as one by alkyd resin fiber and the mixing of modified polycarbonate fiber with fire prevention adhesive.
2. novel oil resistant fire-proof plate according to claim 1, which is characterized in that the backing material plate is cross section cuboid.
3. novel oil resistant fire-proof plate according to claim 1, which is characterized in that the fireproof coating layer is with a thickness of 0.3-
0.5mm。
4. novel oil resistant fire-proof plate according to claim 1, which is characterized in that the plate core layer is including composition proportion：
Zinc accounts for the 52% of content, and aluminium accounts for the 48% of content.
5. novel oil resistant fire-proof plate according to claim 1, which is characterized in that the fibre resin includes composition proportion
For：Alkyd resin fiber 67%, modified polycarbonate fiber 33%.
6. novel oil resistant fire-proof plate according to claim 1, which is characterized in that the fire prevention adhesive is methyl silicon rubber
Glue.