CN108908569A - A kind of fire resisting bamboo matter building material making process - Google Patents

A kind of fire resisting bamboo matter building material making process Download PDF

Info

Publication number
CN108908569A
CN108908569A CN201810416282.1A CN201810416282A CN108908569A CN 108908569 A CN108908569 A CN 108908569A CN 201810416282 A CN201810416282 A CN 201810416282A CN 108908569 A CN108908569 A CN 108908569A
Authority
CN
China
Prior art keywords
bamboo
plate
fire resisting
thick stick
building material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810416282.1A
Other languages
Chinese (zh)
Inventor
王玉环
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanan Chuangpei Electronic Technology Co Ltd
Original Assignee
Nanan Chuangpei Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanan Chuangpei Electronic Technology Co Ltd filed Critical Nanan Chuangpei Electronic Technology Co Ltd
Priority to CN201810416282.1A priority Critical patent/CN108908569A/en
Publication of CN108908569A publication Critical patent/CN108908569A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of fire resisting bamboo matter building material making process, include the following steps：Step 1, workshop selection；Step 2, material selection；Step 3, bamboo wood and coating processing；Step 4, plate processing；Step 5：It is laid with.The present invention passes through in traffic convenience, there is the place at abundant water source to build workshop, traffic convenience is convenient to transport bamboo material, quickly the plate of fire resisting is dispersed into the market, water resource abundant increases the production of aqueous fire-proof coating, thick stick bamboo, which is chosen, as construction material itself has good fire resisting effect, facilitate extra process required for reduction processing bamboo, bamboo fibre content it is high have gas permeability, instant water absorption, the characteristics such as stronger wearability and good dyeability, common bamboo is selected to need to guarantee the water content inside bamboo often, it can crack after bamboo is dry, abrasion, floor and the good using effect of wallboard guarantee can not built.

Description

A kind of fire resisting bamboo matter building material making process
Technical field
The present invention relates to building material technical field, in particular to a kind of fire resisting bamboo matter building material making process.
Background technique
Bamboo, You Mingzhu.Various in style, it is one point gramineous that perennial gramineous bamboo department linoleic plant, stem, which is wooden, Branch, in tropical and subtropical region, is distributed on East Asia, Southeast Asia and the Indian Ocean and Pacific Islands and most concentrates, there are many type, have It is short like grass, some high such as big tree, growth is rapid.
On building materials are selected, usually portion is carried out using, bamboo for most product manufacturing in living in the room, In use, needing to guarantee the fire resisting effect of material inside room, inflammable situation is avoided.
Therefore, it is necessary to solve the above problems to invent a kind of fire resisting bamboo matter building material making process.
Summary of the invention
The purpose of the present invention is to provide a kind of fire resisting bamboo matter building material making process, need to carry out bamboo clappers before daub Soaked processing increases the aqueous effect of bamboo clappers, then coats in painting, increases the fire resisting effect of bamboo clappers, and aqueous fireproof coating is matched Bamboo clappers surface is applied to than after, partition bamboo clappers itself is contacted with external environment, increases the service life of bamboo clappers, bamboo clappers cooperation processing When, increase the toughness and use scope of bamboo clappers in the way of superposition, it is convenient to carry out a variety of different cuttings using upper in plate Mode, to solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides the following technical solutions：A kind of fire resisting bamboo matter building material making process, including with Lower step：
Step 1, workshop selection：Traffic convenience is chosen, has the plate manufacturing building at abundant water source, thus to bamboo building material It is manufactured；
Step 2, material selection：Choose the healthy thick stick bamboo that growth period is 2-3, the high 7-13m of thick stick bamboo, the thick 3-8 ㎝ of diameter, thick stick Bamboo will connect root and dig, and slightly trim, and be placed on interior and dry in the shade, and the time of drying in the shade is 30-40 days, and fire resistance is extremely strong；
Step 3, bamboo wood and coating processing：By thick stick bamboo cutting at length be 0.8-1.2m, width be 4-6 ㎝, thickness 0.2- The plate of 0.4 ㎝, using water 30wt%-37wt%, dispersing agent 0.1wt%-0.2wt%, ammonium polyphosphate 23wt%-25wt%, Pentaerythrite 11wt%-13wt%, melamine 11wt%-13wt%, titanium dioxide 3wt%-5wt%, acrylate and vinyl acetate emulsion 13wt%- 15wt%, hydroxyethyl cellulose 1wt%-2wt% and defoaming agent 0.1wt%-0.2wt% match aqueous fire-proof coating, Then the coating material by proportion after good is on plate；
Step 4, plate processing：The thickness and length of the plate according to needed for building construction, so that plate is overlapped, The plate quantity of superposition is 3-10 block, is then polished in the plate of superposition, chamfered；
Step 5 is laid with：The plate processed is laid on floor, or is utilized wooden inside plate manufacture room Product.
Preferably, thick stick bamboo bamboo fibre content is 58wt%-66wt% in the step 2, bamboo fibre content is high With characteristics such as gas permeability, instant water absorption, stronger wearability and good dyeabilities, thick stick bamboo itself has good fire resisting Effect.
Preferably, when smearing fireproof coating, the dosage of fireproof coating is generally 350~500g/ in the step 3 ㎡。
Preferably, the plate quantity of superposition is 3-10 block in the step 4, facilitate the thickness of adjustment bamboo clappers.
Preferably, bamboo clappers laying is to take over laying one by one in the step 5, facilitate the whole of adjustment bamboo clappers Neat effect.
Technical effect and advantage of the invention：
1, for the present invention by having the place at abundant water source to build workshop in traffic convenience, traffic convenience is convenient to bamboo material Material is transported, and is quickly dispersed into the plate of fire resisting in the market, and water resource abundant increases the production of aqueous fire-proof coating, choosing It takes thick stick bamboo that there is good fire resisting effect as construction material itself, facilitates extra process required for reduction processing bamboo, bamboo Fiber content it is high there are the characteristics such as gas permeability, instant water absorption, stronger wearability and good dyeability, select common Bamboo needs to guarantee often to crack after the water content inside bamboo, bamboo are dry, wears, and can not build floor and wallboard guarantor Demonstrate,prove good using effect；
2, for the present invention by smearing refractory material on bamboo clappers surface, aqueous fireproof coating is applied to bamboo clappers surface after matching, Partition bamboo clappers itself is contacted with external environment, is increased the service life of bamboo clappers and is increased in the way of superposition when bamboo clappers cooperation is handled Add the toughness and use scope of bamboo clappers, it is convenient to carry out a variety of different cutting methods using upper in plate.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described, Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all Belong to the scope of protection of the invention.
Below with reference to embodiment, the present invention is further described.
Embodiment 1
A kind of fire resisting bamboo matter building material making process, includes the following steps：
Step 1, workshop selection：Traffic convenience is chosen, has the plate manufacturing building at abundant water source, thus to bamboo building material It is manufactured, traffic convenience is convenient to transport bamboo material, is quickly dispersed into the plate of fire resisting in the market, water abundant The production of resource increase aqueous fire-proof coating；
Step 2, material selection：The healthy thick stick bamboo that growth period is 2 years, the high 7m of thick stick bamboo, thick 3 ㎝ of diameter are chosen, thick stick bamboo will connect root It digs, slightly trims, be placed on interior and dry in the shade, the time of drying in the shade is 30 days, and fire resistance is extremely strong, and thick stick bamboo bamboo fibre content is 58wt%, Bamboo fibre content it is high there is the characteristics such as gas permeability, instant water absorption, stronger wearability and good dyeability, thick stick bamboo itself With good fire resisting effect；
Step 3, bamboo wood and coating processing：By thick stick bamboo cutting at length be 0.8m, width be 4 ㎝, the plate of 0.2 ㎝ of thickness Material utilizes water 30wt%wt%, dispersing agent 0.1wt%, ammonium polyphosphate 23wt%, pentaerythrite 11wt%, melamine 11wt%, titanium dioxide 3wt%, acrylate and vinyl acetate emulsion 13wt%, hydroxyethyl cellulose 1wt% and defoaming agent 0.1wt% are to water-based fireproof Coating is matched, and then the coating material by proportion after good is on plate, when smearing fireproof coating, the dosage one of fireproof coating As be 350g/ ㎡；
Step 4, plate processing：The thickness and length of the plate according to needed for building construction, so that plate is overlapped, The plate quantity of superposition is 3 pieces, is then polished in the plate of superposition, chamfered when processing to bamboo board, needs Use gluing, cutting machine, alignment jig and tape measure etc. handling implement；
Step 5 is laid with：The plate processed is laid on floor, or is utilized wooden inside plate manufacture room Product, bamboo clappers laying is to take over laying one by one, facilitates the neat effect of adjustment bamboo clappers.
Embodiment 2
A kind of fire resisting bamboo matter building material making process, includes the following steps：
Step 1, workshop selection：Traffic convenience is chosen, has the plate manufacturing building at abundant water source, thus to bamboo building material It is manufactured, traffic convenience is convenient to transport bamboo material, is quickly dispersed into the plate of fire resisting in the market, water abundant The production of resource increase aqueous fire-proof coating；
Step 2, material selection：The healthy thick stick bamboo that growth period is 3 years, the high 13m of thick stick bamboo, thick 8 ㎝ of diameter are chosen, thick stick bamboo will connect Root is dug, and is slightly trimmed, and is placed on interior and is dried in the shade, and the time of drying in the shade is 40 days, and fire resistance is extremely strong, and thick stick bamboo bamboo fibre content is 66wt%, bamboo fibre content it is high there are the characteristics such as gas permeability, instant water absorption, stronger wearability and good dyeability, Thick stick bamboo itself has good fire resisting effect；
Step 3, bamboo wood and coating processing：By thick stick bamboo cutting at length be 1.2m, width be 6 ㎝, the plate of 0.4 ㎝ of thickness Material utilizes water 37wt%, dispersing agent 0.2wt%, ammonium polyphosphate 25wt%, pentaerythrite 13wt%, melamine 13wt%, titanium White powder 5wt%, acrylate and vinyl acetate emulsion 15wt%, hydroxyethyl cellulose 2wt% and defoaming agent 0.2wt% match aqueous fire-proof coating Than then the coating material by proportion after good is on plate, and when smearing fireproof coating, the dosage of fireproof coating is generally 500g/ ㎡；
Step 4, plate processing：The thickness and length of the plate according to needed for building construction, so that plate is overlapped, The plate quantity of superposition is 10 pieces, is then polished in the plate of superposition, chamfered, when processing to bamboo board, is needed Use gluing, cutting machine, alignment jig and tape measure etc. handling implement；
Step 5 is laid with：The plate processed is laid on floor, or is utilized wooden inside plate manufacture room Product, bamboo clappers laying is to take over laying one by one, facilitates the neat effect of adjustment bamboo clappers.
Embodiment 3
A kind of fire resisting bamboo matter building material making process, includes the following steps：
Step 1, workshop selection：Traffic convenience is chosen, has the plate manufacturing building at abundant water source, thus to bamboo building material It is manufactured, traffic convenience is convenient to transport bamboo material, is quickly dispersed into the plate of fire resisting in the market, water abundant The production of resource increase aqueous fire-proof coating；
Step 2, material selection：The healthy thick stick bamboo that growth period is 2.5 years, the high 10m of thick stick bamboo, thick 6 ㎝ of diameter are chosen, thick stick bamboo is wanted Even root is dug, and is slightly trimmed, is placed on interior and dries in the shade, and the time of drying in the shade is 35 days, and fire resistance is extremely strong, and thick stick bamboo bamboo fibre content is 62wt%, bamboo fibre content it is high there are the characteristics such as gas permeability, instant water absorption, stronger wearability and good dyeability, Thick stick bamboo itself has good fire resisting effect；
Step 3, bamboo wood and coating processing：By thick stick bamboo cutting at length be 1m, width be 5 ㎝, the plate of 0.3 ㎝ of thickness, Utilize water 34wt%, dispersing agent 0.15wt%, ammonium polyphosphate 24wt%, pentaerythrite 12wt%, melamine 12wt%, titanium white Powder 4wt%, acrylate and vinyl acetate emulsion 14wt%, hydroxyethyl cellulose 1.5wt% and defoaming agent 0.15wt% carry out aqueous fire-proof coating Proportion, then the coating material by proportion after good is on plate, and when smearing fireproof coating, the dosage of fireproof coating is generally 425g/㎡；
Step 4, plate processing：The thickness and length of the plate according to needed for building construction, so that plate is overlapped, The plate quantity of superposition is 7 pieces, is then polished in the plate of superposition, chamfered when processing to bamboo board, needs Use gluing, cutting machine, alignment jig and tape measure etc. handling implement；
Step 5 is laid with：The plate processed is laid on floor, or is utilized wooden inside plate manufacture room Product, bamboo clappers laying is to take over laying one by one, facilitates the neat effect of adjustment bamboo clappers.
Table is obtained according to embodiment 1-3 data：
Working principle of the present invention：There is good fire resisting effect by choosing thick stick bamboo as construction material itself, conveniently subtract Extra process required for small processing bamboo, bamboo fibre content it is high have gas permeability, instant water absorption, stronger wearability and The characteristics such as good dyeability select common bamboo to need to guarantee often to hold after the water content inside bamboo, bamboo are dry It splits, wears, floor and the good using effect of wallboard guarantee can not built, be applied to bamboo clappers table after aqueous fireproof coating proportion Face, partition bamboo clappers itself contact with external environment, increase the service life of bamboo clappers, need to carry out bamboo clappers before daub soaked Processing, increases the aqueous effect of bamboo clappers, then coats in painting, when bamboo clappers cooperation is handled, increases bamboo clappers in the way of superposition Toughness and use scope, it is convenient to carry out a variety of different cutting methods using upper in plate.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features, All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention Within protection scope.

Claims (5)

1. a kind of fire resisting bamboo matter building material making process, which is characterized in that include the following steps：
Step 1, workshop selection：Traffic convenience is chosen, there is the plate manufacturing building at abundant water source, to be carried out to bamboo building material Manufacture；
Step 2, material selection：The healthy thick stick bamboo that growth period is 2-3, the high 7-13m of thick stick bamboo, the thick 3-8 ㎝ of diameter are chosen, thick stick bamboo is wanted Even root is dug, and is slightly trimmed, is placed on interior and dries in the shade, and the time of drying in the shade is 30-40 days, and fire resistance is extremely strong；
Step 3, bamboo wood and coating processing：By thick stick bamboo cutting at length be 0.8-1.2m, width be 4-6 ㎝, thickness 0.2-0.4 The plate of ㎝ utilizes water 30wt%-37wt%, dispersing agent 0.1wt%-0.2wt%, ammonium polyphosphate 23wt%-25wt%, season penta Tetrol 11wt%-13wt%, melamine 11wt%-13wt%, titanium dioxide 3wt%-5wt%, acrylate and vinyl acetate emulsion 13wt%- 15wt%, hydroxyethyl cellulose 1wt%-2wt% and defoaming agent 0.1wt%-0.2wt% match aqueous fire-proof coating, Then the coating material by proportion after good is on plate；
Step 4, plate processing：The thickness and length of the plate according to needed for building construction, to be overlapped to plate, then It polishes in the plate of superposition, chamfered；
Step 5 is laid with：The plate processed is laid on floor, or utilizes the wooden production inside plate manufacture room Product.
2. a kind of fire resisting bamboo matter building material making process according to claim 1, it is characterised in that：In the step 2, thick stick Bamboo bamboo fibre content be 58wt%-66wt%, bamboo fibre content it is high have gas permeability, instant water absorption, stronger wearability There is good fire resisting effect with characteristics, thick stick bamboos itself such as good dyeabilities.
3. a kind of fire resisting bamboo matter building material making process according to claim 1, it is characterised in that：In the step 3, apply When smearing fireproof coating, the dosage of fireproof coating is generally 350~500g/ ㎡.
4. a kind of fire resisting bamboo matter building material making process according to claim 1, it is characterised in that：In the step 4, fold The plate quantity added is 3-10 block, facilitates the thickness of adjustment bamboo clappers.
5. a kind of fire resisting bamboo matter building material making process according to claim 1, it is characterised in that：In the step 5, bamboo Plate laying is to take over laying one by one, facilitates the neat effect of adjustment bamboo clappers.
CN201810416282.1A 2018-05-03 2018-05-03 A kind of fire resisting bamboo matter building material making process Pending CN108908569A (en)