CN108907903A - A kind of electromechanical equipment processing of surface polishing - Google Patents
A kind of electromechanical equipment processing of surface polishing Download PDFInfo
- Publication number
- CN108907903A CN108907903A CN201810778401.8A CN201810778401A CN108907903A CN 108907903 A CN108907903 A CN 108907903A CN 201810778401 A CN201810778401 A CN 201810778401A CN 108907903 A CN108907903 A CN 108907903A
- Authority
- CN
- China
- Prior art keywords
- electromechanical equipment
- polishing
- equipment surface
- acid solution
- equipment processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electromechanical equipment processing of surface polishing, specifically comprise the following steps:Degreaser is sprayed to electromechanical equipment surface, is rinsed well after spraying 10-15min with clear water, then drying unit is used to toast 50-70min with 60-80 DEG C of temperature;Acid solution is sprayed to electromechanical equipment surface again, sprays and rinses 2-3min with lye after 5-6min, then rinsed well with clear water;Then it is pasted onto electromechanical equipment surface to using the blotting paper immersed with polishing fluid, the stickup time is 1-2h;Eventually by polishing machine is used, electromechanical equipment surface is mechanically polished, the mechanical polishing time is 5-10min, through the above way, the present invention can be realized three reburnishings to electromechanical equipment surface, greatly improve the polishing effect on electromechanical equipment surface, and maintenance protection is good.
Description
Technical field
The present invention relates to a kind of electromechanical equipments to maintain technology, in particular to a kind of electromechanical equipment processing of surface polishing.
Background technique
With the continuous improvement of people's living standards, people are more and more to the demand of electromechanical equipment in daily life,
Indispensable electronic product in for people's lives is had become from the vehicles to various household electrical appliance, computer, printer etc., first
Into electromechanical equipment can not only greatly improve labor productivity, reduce labor intensity, but also production environment can be improved, and machine
For electric equipment after long-term use, surface will appear more spot, clast or even the trace of damage, not only influence its beauty,
And will cause the big problem of electromechanical equipment maintenance difficulty, thus the service life of electromechanical equipment.
Summary of the invention
The invention mainly solves the technical problem of providing a kind of electromechanical equipment processing of surface polishing, can be realized to machine
Three reburnishings on electric equipment surface, greatly improve the polishing effect on electromechanical equipment surface, and maintenance protection is good.
In order to solve the above technical problems, one technical scheme adopted by the invention is that:A kind of electromechanical equipment surface is provided
Polishing process specifically comprises the following steps:
S1:Pretreatment:Degreaser is sprayed to electromechanical equipment surface, is rinsed well after spraying 10-15min with clear water, then using baking
Equipment for drying toasts 50-70min with 60-80 DEG C of temperature;
S2:Chemical polishing:To electromechanical equipment surface sprinkling acid solution, 2-3min is rinsed with lye after sprinkling 5-6min, then use
Clear water is rinsed well;
S3:Impregnate polishing:Electromechanical equipment surface is pasted onto using the blotting paper immersed with polishing fluid, the stickup time is 1-2h;
S4:Mechanical polishing:By using polishing machine, electromechanical equipment surface is mechanically polished, the mechanical polishing time is 5-
10min。
In a preferred embodiment of the present invention, the acid solution is sulfuric acid solution.
In a preferred embodiment of the present invention, the sulfuric acid solution concentration is 0.8-1.0 mol/L.
In a preferred embodiment of the present invention, the lye is sodium carbonate liquor, sodium chloride solution or sodium hydroxide
Any one or more mixing in solution.
In a preferred embodiment of the present invention, in impregnating polishing, each seamless unoccupied place of blotting paper is completely covered on electromechanics
Equipment surface.
In a preferred embodiment of the present invention, protective liquid should be also coated after mechanical polishing.
The beneficial effects of the invention are as follows:A kind of electromechanical equipment processing of surface polishing of the present invention, by successively using chemistry
Polishing, the three reburnishing means for impregnating polishing and mechanical polishing, not only increase the overall aesthetics of electromechanical equipment, Er Qieneng
Enough effects improved to electromechanical equipment surface polishing are conducive to the later period protection and maintenance of electromechanical equipment, in addition, polishing impregnating
It is middle using blotting paper absorb polishing fluid by the way of come to electromechanical equipment surface carry out adherent polishing, enable in polishing fluid
Polishing ingredient can closely stick on electromechanical equipment surface, further increase polishing effect.
Specific embodiment
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
Embodiment 1:
A kind of electromechanical equipment processing of surface polishing, electromechanical equipment processing of surface polishing specifically comprise the following steps:
S1:Pretreatment:Degreaser is sprayed to electromechanical equipment surface, is rinsed well after spraying 10min with clear water, then using drying dress
It sets and 70min is toasted with 60 DEG C of temperature;
S2:Chemical polishing:To electromechanical equipment surface sprinkling acid solution, 3min is rinsed with lye after sprinkling 5min, then use clear water
It rinses well, wherein the acid solution uses concentration for 0.8 mol/L sulfuric acid solution;
S3:Impregnate polishing:Electromechanical equipment surface is pasted onto using the blotting paper immersed with polishing fluid, the stickup time is 2h;
S4:Mechanical polishing:By using polishing machine, electromechanical equipment surface is mechanically polished, the mechanical polishing time is 5min.
Embodiment 2:
A kind of electromechanical equipment processing of surface polishing, electromechanical equipment processing of surface polishing specifically comprise the following steps:
S1:Pretreatment:Degreaser is sprayed to electromechanical equipment surface, is rinsed well after spraying 15min with clear water, then using drying dress
It sets and 50min is toasted with 80 DEG C of temperature;
S2:Chemical polishing:To electromechanical equipment surface sprinkling acid solution, 2min is rinsed with lye after sprinkling 6min, then use clear water
It rinses well, wherein the acid solution uses concentration for 1.0 mol/L sulfuric acid solutions;
S3:Impregnate polishing:Electromechanical equipment surface is pasted onto using the blotting paper immersed with polishing fluid, the stickup time is 1h;
S4:Mechanical polishing:By using polishing machine, electromechanical equipment surface is mechanically polished, mechanical polishing the time be
10min。
Embodiment 3:
A kind of electromechanical equipment processing of surface polishing, electromechanical equipment processing of surface polishing specifically comprise the following steps:
S1:Pretreatment:Degreaser is sprayed to electromechanical equipment surface, is rinsed well after spraying 12.5min with clear water, then using drying
Device toasts 60min with 70 DEG C of temperature;
S2:Chemical polishing:To electromechanical equipment surface sprinkling acid solution, 2.5min is rinsed with lye after sprinkling 5.5min, then use
Clear water is rinsed well, wherein the acid solution uses concentration for 0.9 mol/L sulfuric acid solution;
S3:Impregnate polishing:Electromechanical equipment surface is pasted onto using the blotting paper immersed with polishing fluid, the stickup time is 1.5h;
S4:Mechanical polishing:By using polishing machine, electromechanical equipment surface is mechanically polished, mechanical polishing the time be
7.5min。
It further illustrates, the lye is any one in sodium carbonate liquor, sodium chloride solution or sodium hydroxide solution
Kind or a variety of mixing, can neutralize the acid solution used in chemical polishing, in case acid solution exists too long and damages electromechanical
Equipment.
It further illustrates, in impregnating polishing, each seamless unoccupied place of blotting paper is completely covered on electromechanical equipment surface, Neng Goubao
Card electromechanical equipment surface can be adhesive with blotting paper completely, be further ensured that immersion quality of finish.
Further illustrate, protective liquid should be also coated after mechanical polishing, for the protection to electromechanical equipment, prevents
After only polishing, there is phenomena such as aoxidizing, burn into gets rusty in electromechanical equipment surface.
It is different from the prior art, a kind of electromechanical equipment processing of surface polishing of the present invention, on the one hand, pass through successively useization
Optical polishing, the three reburnishing means for impregnating polishing and mechanical polishing, not only increase the overall aesthetics of electromechanical equipment, and
It can be improved the effect to electromechanical equipment surface polishing, on the other hand the later period protection and maintenance for being conducive to electromechanical equipment are being soaked
Adherent polishing is carried out to electromechanical equipment surface in such a way that blotting paper absorbs polishing fluid in bubble polishing, enables to polish
Polishing ingredient in liquid can closely stick on electromechanical equipment surface, further increase polishing effect.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of electromechanical equipment processing of surface polishing, which is characterized in that specifically comprise the following steps:
S1:Pretreatment:Degreaser is sprayed to electromechanical equipment surface, is rinsed well after spraying 10-15min with clear water, then using baking
Equipment for drying toasts 50-70min with 60-80 DEG C of temperature;
S2:Chemical polishing:To electromechanical equipment surface sprinkling acid solution, 2-3min is rinsed with lye after sprinkling 5-6min, then use
Clear water is rinsed well;
S3:Impregnate polishing:Electromechanical equipment surface is pasted onto using the blotting paper immersed with polishing fluid, the stickup time is 1-2h;
S4:Mechanical polishing:By using polishing machine, electromechanical equipment surface is mechanically polished, the mechanical polishing time is 5-
10min。
2. electromechanical equipment processing of surface polishing according to claim 1, which is characterized in that the acid solution is sulfuric acid
Solution.
3. electromechanical equipment processing of surface polishing according to claim 2, which is characterized in that the sulfuric acid solution concentration is
0.8-1.0 mol/L.
4. electromechanical equipment processing of surface polishing according to claim 1, which is characterized in that the lye is that sodium carbonate is molten
Any one or more mixing in liquid, sodium chloride solution or sodium hydroxide solution.
5. electromechanical equipment processing of surface polishing according to claim 1, which is characterized in that each to inhale in impregnating polishing
Water paper is seamless, and unoccupied place is completely covered on electromechanical equipment surface.
6. electromechanical equipment processing of surface polishing according to claim 1, which is characterized in that after mechanical polishing also
Protective liquid should be coated.