CN108893061A - A kind of weather-proof dual-component silicane modified polyether seal glue and preparation method thereof - Google Patents

A kind of weather-proof dual-component silicane modified polyether seal glue and preparation method thereof Download PDF

Info

Publication number
CN108893061A
CN108893061A CN201810765519.7A CN201810765519A CN108893061A CN 108893061 A CN108893061 A CN 108893061A CN 201810765519 A CN201810765519 A CN 201810765519A CN 108893061 A CN108893061 A CN 108893061A
Authority
CN
China
Prior art keywords
component
modified polyether
weather
seal glue
plasticizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810765519.7A
Other languages
Chinese (zh)
Inventor
陈霞
朱勇
黄本卫
方贵坜
陆初典
李仁才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Debenshi Sealing Material Co Ltd
Original Assignee
Guangxi Debenshi Sealing Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Debenshi Sealing Material Co Ltd filed Critical Guangxi Debenshi Sealing Material Co Ltd
Priority to CN201810765519.7A priority Critical patent/CN108893061A/en
Publication of CN108893061A publication Critical patent/CN108893061A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of weather-proof dual-component silicane modified polyether seal glue and preparation method thereof, the sealant includes that mass ratio is 10:1 component A and B component mixes;The component A includes the raw material of following mass percent:Silane modified polyether resin 20-35%, plasticizer 10-25%, nanometer calcium carbonate 40-60%, titanium dioxide 1-3%, hollow resin 1-3%, composite light stabilizer 0.5-1.5%, light-cured resin 0.5-1.5% and coupling agent 0.5-1.5%;The B component includes the raw material of following mass percent:Nanometer calcium carbonate 35-65%, plasticizer 30-60% and catalyst 1-10%.Sealant prepared by the present invention has excellent water resistance, elastic recovery rate, weather resistance, mechanical property, quick solidifying and low modulus etc., can be widely applied to the bonding and sealing of all kinds of construction materials.

Description

A kind of weather-proof dual-component silicane modified polyether seal glue and preparation method thereof
Technical field
The present invention relates to sealant technical field, specifically a kind of weather-proof dual-component silicane modified polyether seal glue and its Preparation method.
Background technique
With the fast development of modern industry, atmospheric ozone layer is by the serious broken of widely used fluorochlorohydrocarbon substance It is bad, so that the amount of ultraviolet irradiation for shining directly into earth surface increasingly increases, and the increase of amount of ultraviolet irradiation and shortwave, It can not only cause damages to human skin, also will cause the destruction of intramolecule structure, molecular chain rupture destroys polymer material. Glass curtain wall accounting is continuously increased in modern high-rise building, and the refraction of glass curtain wall and reflection effect exacerbate ultraviolet aging Destruction.The fields such as automobile, building propose increasingly harsher requirement to the durability of high molecule sealing materials, especially It is higher to requirements such as the photooxidation stability of sealing material, thermo-oxidative stabilities.
Recently as the promotion energetically of national environmental protection policy, prefabrication has become the weight of Building Trade in China Want one of developing direction and the main path of construction industry transition and upgrade.Assembled architecture is by pre-constructed unit in assemble in site Made of build, large number of deep wide seam, these depths can be generated after assembled architecture outer wall hanging plate or Exterior Wall Components splicing The formation of wide seam not only expands the application field of sealing material, while proposing more to the deep cure rate of sealing material High requirement.Sealing material is divided into one-component sealing material and bi-component sealing material according to product packaging.One-component product makes With convenient, but solidify the moisture relied primarily in air, is affected by the external environment significant, solidifies from outward appearance to inner essence, deep cure is slow, And curing depth is limited, is not suitable for the waterproof sealing of deep wide seam.It is aqueous using itself institute when bi-component sealing material solidifies Point, glue-line outwardly and inwardly solidifies simultaneously, and solidification rate is fast, can be widely applied to the neck such as building, automobile, locomotive, electronic apparatus Domain.
Silicone, polyurethane, silane modified polyether glue and polysulfide sealant are global four big most important sealant materials.State Interior silicone adhesive and polysulfide sealant mechanical property and in terms of it is suitable with same kind of products at abroad, but weatherability is poor, Xanthochromia, dusting, cracking phenomena easily has occurred in service phase in colloid, pollutes bonding substrates, does great damage to building beauty. Polyurethane sealant has good mechanical property, is widely used in multiple fields, but the weather resistance of product is poor.Silane The main chain of modified polyether molecule is the macromolecular polyethers of methoxy silane sealing end, is formed after solidification using-Si-O-Si- as skeleton Three-dimensional space network structure has the good weather resistance of silicone sealant and anti-deformational displacement ability, and has polyurethane The good caking property of sealant, paintability and low pollution.The silane of silane modified polyether seal glue especially bi-component changes Property polyether seal glue in Japanese architecture sealant market occupy leading position, also occupy the market part of significant proportion in states such as America and Europes Volume.In China, the research and development and application of silane modified polyether seal glue are started late, and are still in the marketing stage at present.
As 105219337 A of Chinese patent CN discloses a kind of dual-component silicane modified polyether sealing material and its preparation Method.Used light stabilizer is UV-P, UV-9,326,327,328,531,540,622,744,770,788 of BASF One of or more than one mixture.The above light stabilizer is the stabilizer of more common low molecular weight, inevitably There are volatile, easy to migrate and the disadvantages of intolerant to extraction, especially liquid stabilisers of low molecular weight diffuse to bonding after precipitation Substrate is even penetrated into interface.
In conclusion a kind of good weatherability how is researched and developed, the fast dual-component silicane modified polyether sealing of deep cure rate Glue is fluid sealant for construction field technical staff's urgent problem to be solved.
The disclosure of background above technology contents is only used for auxiliary and understands inventive concept and technical solution of the invention, not The prior art for necessarily belonging to present patent application shows above content in the applying date of present patent application in no tangible proof In the case where having disclosed, above-mentioned background technique should not be taken to the novelty and creativeness of evaluation the application.
Summary of the invention
Object of the present invention is to overcome the deficiencies of existing technologies, a kind of weather-proof dual-component silicane modified polyether seal glue is provided And preparation method thereof.The advantages that sealant prepared by the present invention has good weatherability, and adhesive property is good, quick solidifying and low modulus, It can be widely applied to the bonding and sealing of all kinds of construction materials.
In order to achieve the goal above, the present invention is to be achieved through the following technical solutions:
A kind of weather-proof dual-component silicane modified polyether seal glue, including mass ratio are 10:1 component A and B component is mixed It closes;The component A includes the raw material of following mass percent:Silane modified polyether resin 20-35%, plasticizer 10- 25%, nanometer calcium carbonate 40-60%, titanium dioxide 1-3%, hollow resin 1-3%, composite light stabilizer 0.5-1.5%, photocuring Resin 0.5-1.5% and coupling agent 0.5-1.5%;The B component includes the raw material of following mass fraction ratio:Nanometer calcium carbonate 35-65%, plasticizer 30-60% and catalyst 1-10%.
Further, the silane modified polyether resin be methoxy group silane modified polyether S810, SAX510 and One of SAX520 or numerous compositions, molecular weight 10000-25000.Above-mentioned model silane-modified resin is by Japan The production of KANEKA company.
Further, the plasticizer is phthalic ester plasticizer or/and polyethers plasticizer.Neighbour's benzene two Formate ester plasticizer such as diisooctyl phthalate DIDP, diisononyl phthalate DINP, hexamethylene -1,2- diformazan Sour dinonyl DINCH etc..The polyethers plasticizer be polyether polyol N220 and
Polyether polyol N330.The polyether polyol is that main chain contains ehter bond, and end group or side group contain no less than 2 hydroxyls The polymer of base, molecular weight 1500-3500.
Further, it is 18-25m that the nanometer calcium carbonate, which is through the BET specific surface area that stearic acid surface is handled,2/ The hydrophobic nano calcium carbonate of g.
Further, the titanium dioxide crystal structure is rutile-type.
Further, the hollow resin is high-performance hollow glass micropearl (HGS), new by mine institute of Ma'an Mountain of Sinosteel Corporation The production of material Science and Technology Ltd..
Further, the compound stabilizer is 1 by mass ratio:1 low molecule quality stabilizer and aggretion type macromolecule Quality compound stabilizer forms;The low molecule quality stabilizer is UV-360 (benzotriazole UV absorbers), aggretion type High molecule mass stabilizer is 1,2,3,4- butanetetra-carboxylic acid four (1,2,2,6,6- pentamethyl -4- piperidyl) esters, model ADK STAB LA-52 is a kind of N- methylation HALS (hindered amine light stabilizer), structural formula such as following formula:
Further, the coupling agent is dodecyl methyl dimethoxysilane HD109,3- aminopropyl trimethoxy Silane (KH540), γ-aminopropyl triethoxysilane (KH550) or γ-glycidyl ether oxygen propyl trimethoxy silicane Or numerous compositions one of (KH560).
Further, the light-cured resin is trimethylolpropane trimethacrylate.
Further, the catalyst is one of dibutyl tin dilaurate, chelating tin (U-220H) or a variety of groups It closes.
The preparation method of weather-proof dual-component silicane modified polyether seal glue of the present invention, includes the following steps:
(1) prepared by component A:Each raw material is weighed according to aforementioned proportion, by silane modified polyether resin, plasticizer, nano-sized carbon Sour calcium, titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, and material is warming up to 80-100 DEG C, 1.5-2.5h is stirred under 0.090 ± 0.005MPa vacuum degree, obtains mixed material;Material to be mixed is cooled to 45 DEG C hereinafter, being added Light-cured resin and coupling agent, stir 20-30min, and cooling discharge packaging obtains component A product;
(2) prepared by B component:Each raw material is weighed according to aforementioned proportion, nanometer calcium carbonate, plasticizer and catalyst are added high In fast dispersion machine, temperature is controlled at 30-40 DEG C, 0.5-1h is stirred under 0.090 ± 0.005MPa vacuum degree, and discharging packaging obtains To B component product;
(3) by component A and B component product according to 10:1 ratio is uniformly mixed modified to get dual-component silicane of the present invention Polyether seal glue.
Compared with prior art, it advantages of the present invention and has the beneficial effect that:
1, sealant prepared by the present invention have excellent water resistance, elastic recovery rate, weather resistance, mechanical property, Quick solidifying and low modulus etc., constituent is relatively simple, low in cost, and preparation process simple possible, production cost is low, have compared with Good economic benefit and social benefit, can be widely applied to the bonding and sealing of all kinds of construction materials.
2, the stabilizer that uses of the present invention by low molecule quality stabilizer and aggretion type high molecule mass compound stabilizer and At aggretion type light stabilizer is that polymer electrolyte UV absorbers and sealant matrix resin compatibility are good, is also had good Resistance to extraction and resistance to migration, additive amount is few, can be formed and be acted synergistically with small molecule ultraviolet absorbing agent, protection effect is good, can have Improve the weatherability of system in effect ground.
3, the thixotropy of sealant reaction system of the present invention is good, reduces the use of thixotropic agent during the preparation process, is made Nanometer calcium carbonate hygroscopicity is small, and base-material mixed process is easily dehydrated, and ensure that system stability.
4, coupling agent used in the present invention is improving infiltration of the organic matter to filler due to having flexible hydrophobicity long-chain Property aspect there is unique advantage, while can effectively improve the water resistance and elastic recovery rate of sealant, while can be effective Raising sealant stability and adhesive property.
Specific embodiment
Invention is further described in detail With reference to embodiment.It is emphasized that following the description is only It is merely exemplary, the range and its application being not intended to be limiting of the invention.
Embodiment 1
The present embodiment dual-component silicane modified polyether seal glue according to quality is 10 by component A and B component:1 mixing and At wherein component A and B component are prepared by the raw material of following mass percent:
The preparation method of sealant, includes the following steps:
(1) prepared by component A:Each raw material is weighed according to aforementioned proportion, by silane modified polyether resin, plasticizer, nano-sized carbon Sour calcium, titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, and material is warming up to 85 DEG C, 0.090 ± 2.5h is stirred under 0.005MPa vacuum degree, obtains mixed material;Material to be mixed be cooled to 45 DEG C hereinafter, be added light-cured resin and Coupling agent, stirs 30min, and cooling discharge packaging obtains component A product;
(2) prepared by B component:Each raw material is weighed according to aforementioned proportion, nanometer calcium carbonate, plasticizer and catalyst are added high In fast dispersion machine, temperature is controlled at 35-40 DEG C, 1h is stirred under 0.090 ± 0.005MPa vacuum degree, and discharging packaging obtains B group Part product;
(3) by component A and B component product according to 10:1 ratio is uniformly mixed modified to get dual-component silicane of the present invention Polyether seal glue.
Embodiment 2
The present embodiment dual-component silicane modified polyether seal glue according to quality is 10 by component A and B component:1 mixing and At wherein component A and B component are prepared by the raw material of following mass percent:
The preparation method of sealant, includes the following steps:
(1) prepared by component A:Each raw material is weighed according to aforementioned proportion, by silane modified polyether resin, plasticizer, nano-sized carbon Sour calcium, titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, and material is warming up to 90 DEG C, 0.090 ± 2h is stirred under 0.005MPa vacuum degree, obtains mixed material;Material to be mixed is cooled to 45 DEG C hereinafter, light-cured resin and idol is added Join agent, stir 15min, cooling discharge packaging obtains component A product;
(2) prepared by B component:Each raw material is weighed according to aforementioned proportion, nanometer calcium carbonate, plasticizer and catalyst are added high In fast dispersion machine, temperature is controlled at 35-40 DEG C, 1h is stirred under 0.090 ± 0.005MPa vacuum degree, and discharging packaging obtains B group Part product;
(3) by component A and B component product according to 10:1 ratio is uniformly mixed modified to get dual-component silicane of the present invention Polyether seal glue.
Embodiment 3
The present embodiment dual-component silicane modified polyether seal glue according to quality is 10 by component A and B component:1 mixing and At wherein component A and B component are prepared by the raw material of following mass percent:
The preparation method of sealant, includes the following steps:
(1) prepared by component A:Each raw material is weighed according to aforementioned proportion, by silane modified polyether resin, plasticizer, nano-sized carbon Sour calcium, titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, material are warming up to 100 DEG C, 0.090 1.5h is stirred under ± 0.005MPa vacuum degree, obtains mixed material;Material to be mixed is cooled to 45 DEG C hereinafter, light-cured resin is added And coupling agent, 30min is stirred, cooling discharge packaging obtains component A product;
(2) prepared by B component:Each raw material is weighed according to aforementioned proportion, nanometer calcium carbonate, plasticizer and catalyst are added high In fast dispersion machine, temperature is controlled at 30-35 DEG C, 0.5h is stirred under 0.090 ± 0.005MPa vacuum degree, and discharging packaging obtains B Component product;
(3) by component A and B component product according to 10:1 ratio is uniformly mixed modified to get dual-component silicane of the present invention Polyether seal glue.
Embodiment 4
The present embodiment dual-component silicane modified polyether seal glue according to quality is 10 by component A and B component:1 mixing and At wherein component A and B component are prepared by the raw material of following mass percent:
The preparation method of sealant, includes the following steps:
(1) prepared by component A:Each raw material is weighed according to aforementioned proportion, by silane modified polyether resin, plasticizer, nano-sized carbon Sour calcium, titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, and material is warming up to 80 DEG C, 0.090 ± 2.5h is stirred under 0.005MPa vacuum degree, obtains mixed material;Material to be mixed be cooled to 45 DEG C hereinafter, be added light-cured resin and Coupling agent, stirs 20min, and cooling discharge packaging obtains component A product;
(2) prepared by B component:Each raw material is weighed according to aforementioned proportion, nanometer calcium carbonate, plasticizer and catalyst are added high In fast dispersion machine, temperature is controlled at 30-35 DEG C hereinafter, stirring 0.5h under 0.090 ± 0.005MPa vacuum degree, discharging is packed, Obtain B component product;
(3) by component A and B component product according to 10:1 ratio is uniformly mixed modified to get dual-component silicane of the present invention Polyether seal glue.
Embodiment 5
The present embodiment dual-component silicane modified polyether seal glue according to quality is 10 by component A and B component:1 mixing and At wherein component A and B component are prepared by the raw material of following mass percent:
The preparation method of sealant, includes the following steps:
(1) prepared by component A:Each raw material is weighed according to aforementioned proportion, by silane modified polyether resin, plasticizer, nano-sized carbon Sour calcium, titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, and material is warming up to 90 DEG C, 0.090 ± 2.5h is stirred under 0.005MPa vacuum degree, obtains mixed material;Material to be mixed be cooled to 45 DEG C hereinafter, be added light-cured resin and Coupling agent, stirs 25min, and cooling discharge packaging obtains component A product;
(2) prepared by B component:Each raw material is weighed according to aforementioned proportion, nanometer calcium carbonate, plasticizer and catalyst are added high In fast dispersion machine, temperature is controlled at 35-40 DEG C hereinafter, stirring 1h under 0.090 ± 0.005MPa vacuum degree, discharging packaging obtains To B component product;
(3) by component A and B component product according to 10:1 ratio is uniformly mixed modified to get dual-component silicane of the present invention Polyether seal glue.
The obtained sealant of embodiment 1-5 is tested for the property, test result is as shown in table 1.Tensile strength presses GB/ T528-2009 standard, elongation at break press GB/T528-2009 standard, and weather resistance refers to ASTMC1184 and JCT 485- 2007《Building window elastic sealant》It is tested.Anti-yellowing property:Sealant is immediately placed into after sebific duct extrusion sizing material 120 DEG C of baking ovens, 24 hours non-yellowing.Weather resistance:Film after solidifying 7 days is put into ultraviolet (UV) aging test chamber, every A period of time observation appearance, with adhesive sticker sticker face, observe surface whether xanthochromia, cracking or dusting;Thixotropy:By double groups Silane modified polyether seal glue is divided to be extruded into long 70mm, the rectangle adhesive tape of wide 10mm, high 5mm are beaten on the vertical plane, it places for 24 hours, Test the displacement of adhesive tape.
Table 1:Sealant the performance test results of the embodiment of the present invention
It is learnt from above-mentioned test result, compared with commercially available production piece, weather-proof dual-component silicane prepared by the present invention is modified poly- Ether sealant not only has good thixotropy good and higher tensile strength and elongation, also has excellent weatherability.
The above content is combine it is specific/further detailed description of the invention for preferred embodiment, cannot Assert that specific implementation of the invention is only limited to these instructions.General technical staff of the technical field of the invention is come It says, without departing from the inventive concept of the premise, some replacements or modifications can also be made to the embodiment that these have been described, And these substitutions or variant are regarded as belonging to the scope of protection of the present invention.

Claims (10)

1. a kind of weather-proof dual-component silicane modified polyether seal glue, it is characterised in that:It is 10 including mass ratio:1 component A and B component mixes;The component A includes the raw material of following mass percent:Silane modified polyether resin 20-35%, plasticizer 10-25%, nanometer calcium carbonate 40-60%, titanium dioxide 1-3%, hollow resin 1-3%, composite light stabilizer 0.5-1.5%, photocuring tree Rouge 0.5-1.5% and coupling agent 0.5-1.5%;The B component includes the raw material of following mass percent:Nanometer calcium carbonate 35- 65%, plasticizer 30-60% and catalyst 1-10%.
2. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:It is described silane-modified Polyether resin is one of silane modified polyether S810, SAX510 and SAX520 or numerous compositions of methoxy group, Molecular weight is 10000-25000.
3. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:The plasticizer is Phthalic ester plasticizer or/and polyethers plasticizer.
4. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:The hollow resin For hollow glass micropearl.
5. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:The stable composition Agent is formed by low molecule quality stabilizer and aggretion type high molecule mass compound stabilizer;The low molecule quality stabilizer is UV-360, aggretion type high molecule mass stabilizer are 1,2,3,4- butanetetra-carboxylic acids four (1,2,2,6,6- pentamethyl -4- piperidyl) Ester.
6. weather-proof dual-component silicane modified polyether seal glue according to claim 5, it is characterised in that:The low molecule matter The mass ratio for measuring stabilizer and aggretion type high molecule mass stabilizer is 1:1.
7. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:The coupling agent is Dodecyl methyl dimethoxysilane, 3- TSL 8330, γ-aminopropyl triethoxysilane or γ- One of glycidyl ether oxygen propyl trimethoxy silicane or multiple combinations.
8. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:The photocuring tree Rouge is trimethylolpropane trimethacrylate.
9. weather-proof dual-component silicane modified polyether seal glue according to claim 1, it is characterised in that:The catalyst is One of dibutyl tin dilaurate, chelating tin or multiple combinations.
10. the preparation method of weather-proof dual-component silicane modified polyether seal glue, feature as described in claim any one of 1-9 It is, includes the following steps:
(1)Component A preparation:Weigh each raw material according to aforementioned proportion, by silane modified polyether resin, plasticizer, nanometer calcium carbonate, Titanium dioxide, hollow resin and composite light stabilizer are added in high speed disperser, and material is warming up to 80-100 DEG C, 0.090 ± 1.5-2.5h is stirred under 0.005MPa vacuum degree, obtains mixed material;Material to be mixed is cooled to 45 DEG C hereinafter, photocuring tree is added Rouge and coupling agent, stir 20-30min, and cooling discharge packaging obtains component A product;
(2)B component preparation:Each raw material is weighed according to aforementioned proportion, high speed point is added in nanometer calcium carbonate, plasticizer and catalyst It dissipates in machine, controls temperature at 30-40 DEG C, 0.5-1h is stirred under 0.090 ± 0.005MPa vacuum degree, discharging packaging obtains B group Part product;
(3)By component A and B component product according to 10:1 ratio is uniformly mixed to get dual-component silicane modified polyether of the present invention Sealant.
CN201810765519.7A 2018-07-12 2018-07-12 A kind of weather-proof dual-component silicane modified polyether seal glue and preparation method thereof Pending CN108893061A (en)