CN108892975A - Preparation method of weather-resistant heavy calcium carbonate - Google Patents
Preparation method of weather-resistant heavy calcium carbonate Download PDFInfo
- Publication number
- CN108892975A CN108892975A CN201810877898.9A CN201810877898A CN108892975A CN 108892975 A CN108892975 A CN 108892975A CN 201810877898 A CN201810877898 A CN 201810877898A CN 108892975 A CN108892975 A CN 108892975A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- weather
- preparation
- powdered whiting
- coarse powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of weather-resistant heavy calcium carbonate, which comprises the steps of adding limestone into a grinder, grinding the limestone into particles with the particle size of less than or equal to 0.25mm to obtain calcium carbonate coarse powder; adding calcium carbonate coarse powder, water, PMA and a first surface modifier into a grinding machine, and grinding by a wet method to obtain calcium carbonate slurry; the first surface modifier consists of polyethylene glycol distearate and polyoxypropylene polyoxyethylene glycerol ether; and conveying the calcium carbonate slurry to a high-speed stirrer, adding a second surface modifier consisting of N-phenyl maleimide, sodium abietic acid diethanol amide ether carboxylate and octaaminophenyl polyhedral oligomeric silsesquioxane, stirring at a high speed, uniformly mixing, dehydrating and drying to obtain the weather-resistant heavy calcium carbonate. The heavy calcium carbonate obtained by surface modification by the method has good dispersibility, hydrophilic and oleophilic properties, thixotropy and processing fluidity, also has good chemical stability, weather resistance and heat resistance, and can be widely applied to industries such as building materials, coatings, rubber, sealants, printing ink and the like.
Description
Technical field
The present invention relates to calcium carbonate modified technical field, the preparation method of specifically a kind of weather-proof powdered whiting.
Background technique
Calcium carbonate is a kind of important inorganic chemical product, is widely used in rubber, plastics, papermaking, coating, oil
In the industry such as ink, medicine, cosmetics, food.But since calcium carbonate particle partial size is smaller, the atomicity on surface is more, then table
Face can be higher, and suction-operated is stronger, mutually reunites between each particle;Followed by calcium carbonate is as a kind of inorganic filler, particle table
Face is hydrophilic and oleophobic, with the compatibility of organic polymer it is poor, easily formed aggregation, cause high polymer internal flaw, mechanical property become
Difference.In order to improve the filling capacity of calcium carbonate, it is necessary to carry out surface to calcium carbonate using effective technique and surface modifying method
It is modified.At present in calcium carbonate modified method, the surface treating agent mainly selected is usually fatty acid or its salt, although system
Dispersibility and processing fluidity make moderate progress, but effect is unobvious.
Since the weatherability of powdered whiting is poor, applies in the industry productions such as building materials, coating, rubber, encounter low temperature
Or calcium carbonate is easy to happen xanthochromia or coacervation occurs etc. under hot conditions.Therefore, research has good dispersion, excellent weather-proof
The good calcium carbonate of property, stability is the demand of today's society.
Summary of the invention
The present invention provides a kind of preparation of weather-proof powdered whiting for defect existing for existing powdered whiting performance
Method.The method of the present invention carries out one-time surface by using polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether
It is modified, it not only can be improved the dispersibility, compatibility and processing fluidity of calcium carbonate, then with N-phenylmaleimide, rosin
The compounding surface treating agent of sour diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition carries out secondary change
Property, improve the thixotropy, stability and weatherability of calcium carbonate.
In order to achieve the goal above, the invention is realized by the following technical scheme:
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:Calcium carbonate coarse powder, water, PMA and first surface modifying agent are added into grinder, by wet grinding, obtain calcium carbonate slurry
Material;The first surface modifying agent is made of polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether;
S3:Calcium carbonate slurry is delivered to high-speed mixer, is added by N-phenylmaleimide, rosin acid diglycollic amide
The second surface modifying agent of ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, high-speed stirred are uniformly mixed, dehydration,
Drying is to get weather-proof powdered whiting.
Further, the calcium carbonate coarse powder, water, PMA weight ratio be 100:300-500:5-10.
Further, the additional amount of the first surface modifying agent is the 1.5-3% of calcium carbonate coarse powder weight.
Further, polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerol in the first surface modifying agent
The weight ratio of ether is 2-4:1.
Further, the additional amount of the second surface modifying agent is the 1-2% of calcium carbonate coarse powder weight.
Further, the N-phenylmaleimide, rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cages
The mass ratio of shape silsesquioxane is 1:2-3:0.5-1.5.
Further, the wet grinding is to grind 1-2h in the case where revolving speed is 1000-1500r/min.
Further, the partial size of the calcium carbonate slurry is 500-1000 mesh.
Further, the drying be temperature be at 80-120 DEG C it is dry.
The present invention is to realize above scheme based on following technical principle:
This method first uses polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether to carry out a modification, by
Hydroxyl, Long carbon chain fatty acid, carboxyl, carbonyl in polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether etc.
Group, it is wet-process modified in be also equipped with PMA use, the dispersibility and processing fluidity of calcium carbonate, and each group not only can be improved
It is mutually wound in network structure, improves the compatibility of calcium carbonate particle and organic polymer, improves the thixotropic property of filling system.
Two are carried out with N-phenylmaleimide, rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes again
Secondary modification can introduce the groups such as maleic anhydride, silicon oxygen bond, phenyl ring, amide on calcium carbonate particle surface, can be improved carbon
Chemical stability, weatherability and the heat resistance of sour calcium.
Compared with prior art, it advantages of the present invention and has the beneficial effect that:
1, the modified obtained powdered whiting in this method surface not only have good dispersibility, hydrophilic and oleophilic performance, thixotropy,
Processing fluidity also has good chemical stability, weatherability and heat resistance, in building materials, coating, rubber, sealant, ink
Etc. industries be widely used.
2, the modified obtained calcium carbonate-filled sealant of the present invention, not only has good compatibility with inorganic organic substrate
And dispersibility, improve the adhering performance and mechanical property of sealant, moreover it is possible to make sealant that there is excellent color inhibition, weatherability etc.
Performance.
3, the method for the present invention simple process, high production efficiency, production cost are low, consume energy low advantage, industry easy to accomplish
Metaplasia produces.
Specific embodiment
Invention is further described in detail With reference to embodiment, but limits the scope of the invention and its answer
With.
Embodiment 1
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:400:6 ratio adds to grinder, and weight ratio is added
It is 3:The first surface modifying agent of 1 polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether composition, the first table
The additional amount of surface treatment agent is the 2% of calcium carbonate coarse powder weight, grinds 1.5h in the case where revolving speed is 1000r/min, obtaining partial size is 700
Purpose calcium carbonate slurry;
S3:Calcium carbonate slurry is delivered to high-speed mixer, adding by weight ratio is 1:2:1 N-phenylmaleimide,
The second surface modifying agent of rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, described the
The additional amount of two surface modifiers is the 1.6% of calcium carbonate coarse powder weight, and high-speed stirred is uniformly mixed, dehydration, in 100 DEG C of dryings,
Up to weather-proof powdered whiting.
Embodiment 2
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:350:7 ratio adds to grinder, and weight ratio is added
It is 2:The first surface modifying agent of 1 polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether composition, the first table
The additional amount of surface treatment agent is the 2.4% of calcium carbonate coarse powder weight, grinds 2h in the case where revolving speed is 1200r/min, obtaining partial size is 1000
Purpose calcium carbonate slurry;
S3:Calcium carbonate slurry is delivered to high-speed mixer, adding by weight ratio is 1:2.5:1.5 N- benzyl maleimide
The second surface modifying agent of amine, rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, institute
The additional amount for stating second surface modifying agent is the 1.5% of calcium carbonate coarse powder weight, and high-speed stirred is uniformly mixed, dehydration, dry at 80 DEG C
It is dry to get weather-proof powdered whiting.
Embodiment 3
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:500:8 ratio adds to grinder, and weight ratio is added
It is 4:The first surface modifying agent of 1 polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether composition, the first table
The additional amount of surface treatment agent is the 3% of calcium carbonate coarse powder weight, grinds 1.5h in the case where revolving speed is 1500r/min, obtaining partial size is 830
Purpose calcium carbonate slurry;
S3:Calcium carbonate slurry is delivered to high-speed mixer, adding by weight ratio is 1:2:1 N-phenylmaleimide,
The second surface modifying agent of rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, described the
The additional amount of two surface modifiers is the 2% of calcium carbonate coarse powder weight, and high-speed stirred is uniformly mixed, dehydration, in 90 DEG C of dryings, i.e.,
Obtain weather-proof powdered whiting.
Embodiment 4
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:300:6 ratio adds to grinder, and weight ratio is added
It is 2:The first surface modifying agent of 1 polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether composition, the first table
The additional amount of surface treatment agent is the 1.5% of calcium carbonate coarse powder weight, grinds 1h in the case where revolving speed is 1200r/min, obtaining partial size is 600
Purpose calcium carbonate slurry;
S3:Calcium carbonate slurry is delivered to high-speed mixer, adding by weight ratio is 1:2.5:0.5 N- benzyl maleimide
The second surface modifying agent of amine, rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, institute
The additional amount for stating second surface modifying agent is the 2% of calcium carbonate coarse powder weight, and high-speed stirred is uniformly mixed, dehydration, dry at 100 DEG C
It is dry to get weather-proof powdered whiting.
Embodiment 5
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:400:8 ratio adds to grinder, and weight ratio is added
It is 3:The first surface modifying agent of 1 polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether composition, the first table
The additional amount of surface treatment agent is the 2% of calcium carbonate coarse powder weight, grinds 1.5h in the case where revolving speed is 1200r/min, obtaining partial size is 500
Purpose calcium carbonate slurry;
S3:Calcium carbonate slurry is delivered to high-speed mixer, adding by weight ratio is 1:2:0.5 N- benzyl maleimide
The second surface modifying agent of amine, rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, institute
The additional amount for stating second surface modifying agent is the 1.8% of calcium carbonate coarse powder weight, and high-speed stirred is uniformly mixed, dehydration, at 120 DEG C
Drying is to get weather-proof powdered whiting.
Embodiment 6
A kind of preparation method of weather-proof powdered whiting, includes the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:500:7 ratio adds to grinder, and weight ratio is added
It is 2:The first surface modifying agent of 1 polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether composition, the first table
The additional amount of surface treatment agent is the 3% of calcium carbonate coarse powder weight, grinds 1.5h in the case where revolving speed is 1500r/min, obtaining partial size is 700
Purpose calcium carbonate slurry;
S3:Calcium carbonate slurry is delivered to high-speed mixer, adding by weight ratio is 1:3:1 N-phenylmaleimide,
The second surface modifying agent of rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, described the
The additional amount of two surface modifiers is the 1.5% of calcium carbonate coarse powder weight, and high-speed stirred is uniformly mixed, dehydration, in 120 DEG C of dryings,
Up to weather-proof powdered whiting.
Comparative example
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:By calcium carbonate coarse powder, water, PMA according to weight ratio be 100:500:7 ratio adds to grinder, and calcium carbonate is added
4.5% odium stearate of coarse powder weight grinds 1.5h in the case where revolving speed is 1500r/min, obtains the calcium carbonate that partial size is 700 mesh and starches
Material;
S3:It is dry to get powdered whiting at 120 DEG C by calcium carbonate slurry through being dehydrated.
Powdered whiting products application prepared by 1-6 of the embodiment of the present invention and comparative example sealant filler, it is described
Sealant is made of the raw material of following parts by weight:80 parts of organic hydroxylic silicone, 20 parts of organic methyl silicone, dimethicone
10 parts, 60 parts of powdered whiting, 5 parts of fumed silica, 1.5 parts of crosslinking agent, 0.5 part of acid dibutyl tin and silane are even
2 parts of agent of connection, and sealant is conventionally made.Resulting sealant is conventionally measured to the stretching of sealant
Intensity, elongation at break, color inhibition and weather resistance, test result are as shown in table 1.Tensile strength is marked by GB/T528-2009
Standard, elongation at break press GB/T528-2009 standard, and weather resistance refers to ASTMC1184 and JCT 485-2007《Building window
Use elastic sealant》It is tested.Anti-yellowing property:After sealant squeezes out sizing material from sebific duct, it is immediately placed into 120 DEG C of baking ovens, 24
Hour is non-yellowing.Weather resistance:Film after solidifying 7 days is put into ultraviolet (UV) aging test chamber, is seen at regular intervals
Examine appearance, with adhesive sticker sticker face, observe surface whether xanthochromia, cracking or dusting.
Table 1:Powdered whiting of the present invention applies the performance test results in sealant
Product | Tensile strength(MPa) | Elongation at break (%) | Anti-yellowing property | Weatherability |
Embodiment 1 | 0.97 | 576 | Nothing | It is unchanged |
Embodiment 2 | 0.86 | 481 | Nothing | It is unchanged |
Embodiment 3 | 0.93 | 563 | Nothing | It is unchanged |
Embodiment 4 | 0.76 | 431 | Nothing | It is unchanged |
Embodiment 5 | 0.85 | 539 | Nothing | It is unchanged |
Embodiment 6 | 0.90 | 497 | Nothing | It is unchanged |
Comparative example | 0.68 | 327 | Surface jaundice | It turns to be yellow and cracks |
It learns from the above, the modified powdered whiting of the present invention and the product modified by odium stearate, filling with sealant
There is good tensile strength and elongation at break afterwards, and color inhibition and weatherability are more excellent.
The above content is combine it is specific/further detailed description of the invention for preferred embodiment, cannot
Assert that specific implementation of the invention is only limited to these instructions.General technical staff of the technical field of the invention is come
It says, without departing from the inventive concept of the premise, some replacements or modifications can also be made to the embodiment that these have been described,
And these substitutions or variant are regarded as belonging to the scope of protection of the present invention.
Claims (9)
1. a kind of preparation method of weather-proof powdered whiting, it is characterised in that:Include the following steps:
S1:Pulverizer is added in lime stone, is crushed to partial size≤0.25mm, obtains calcium carbonate coarse powder;
S2:Calcium carbonate coarse powder, water, PMA and first surface modifying agent are added into grinder, by wet grinding, obtain calcium carbonate slurry
Material;The first surface modifying agent is made of polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether;
S3:Calcium carbonate slurry is delivered to high-speed mixer, is added by N-phenylmaleimide, rosin acid diglycollic amide
The second surface modifying agent of ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes composition, high-speed stirred are uniformly mixed, dehydration,
Drying is to get weather-proof powdered whiting.
2. the preparation method of weather-proof powdered whiting according to claim 1, it is characterised in that:The calcium carbonate coarse powder,
Water, PMA weight ratio be 100:300-500:5-10.
3. the preparation method of weather-proof powdered whiting according to claim 1, it is characterised in that:The first surface is modified
The additional amount of agent is the 1.5-3% of calcium carbonate coarse powder weight.
4. the preparation method of weather-proof powdered whiting according to claim 3, it is characterised in that:The first surface is modified
The weight ratio of polyethylene glycol stearate diester and polyoxyethylene polyoxypropylene glycerin ether is 2-4 in agent:1.
5. the preparation method of weather-proof powdered whiting according to claim 1, it is characterised in that:The second surface is modified
The additional amount of agent is the 1-2% of calcium carbonate coarse powder weight.
6. the preparation method of weather-proof powdered whiting according to claim 5, it is characterised in that:N- phenyl Malaysia acyl
The mass ratio of imines, rosin acid diglycollic amide ether carboxylic acid sodium and eight aminophenyl cagelike silsesquioxanes is 1:2-3:0.5-
1.5。
7. the preparation method of weather-proof powdered whiting according to claim 1, it is characterised in that:The wet grinding be
Revolving speed is to grind 1-2h under 1000-1500r/min.
8. the preparation method of weather-proof powdered whiting according to claim 1, it is characterised in that:The calcium carbonate slurry
Partial size is 500-1000 mesh.
9. the preparation method of weather-proof powdered whiting according to claim 1, it is characterised in that:The drying is in temperature
It is dry at 80-120 DEG C.