CN106590062A - Preparation method of composite titanium dioxide pigment with wollastonite coated with titanium dioxide - Google Patents
Preparation method of composite titanium dioxide pigment with wollastonite coated with titanium dioxide Download PDFInfo
- Publication number
- CN106590062A CN106590062A CN201611108140.6A CN201611108140A CN106590062A CN 106590062 A CN106590062 A CN 106590062A CN 201611108140 A CN201611108140 A CN 201611108140A CN 106590062 A CN106590062 A CN 106590062A
- Authority
- CN
- China
- Prior art keywords
- titanium dioxide
- wollastonite
- composite
- consumption
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of composite titanium dioxide pigment with wollastonite coated with titanium dioxide. The preparation method includes following steps: (1), performing surface pretreatment on wollastonite, and wetting titanium dioxide for surface pretreatment; (2), adding wollastonite powder and titanium dioxide into a high-speed stirrer, and mixing sufficiently; (3), utilizing a wet-type grinder for grinding, and performing envelope treatment on the wollastonite powder and titanium dioxide after being mixed; (4), using a plate-and-frame filter press to filter-press ground paste, and subjecting an obtained filter cake to water washing; (5), drying; (6), crushing. By the preparation method, whiteness is improved without lowering using effects like covering power of titanium dioxide, using cost can be lowered substantially, and sedimentation in the previous process of solely using wollastonite to replace titanium dioxide is avoided.
Description
Technical field
The present invention relates to chemical field, more specifically to a kind of titanium dioxide peplos covering method.
Background technology
Presently disclosed composite titanium dioxide production technology is mainly coated with triple superphosphate, fine particle calcium carbonate etc. as core, Application No.
The patent of CN89108819.9 discloses a kind of method of use wollastonite composite titanium dioxide, its mainly by TiO2, CaSiO3, ZnO,
AL2O3 and silane coupler are constituted, and above-mentioned raw materials is simply mixed and be uniformly composite titanium dioxide, and production technology is simple and crude, cladding
Not exclusively, using effect is poor, high cost.
The content of the invention
In order to solve that existing composite titanium dioxide is present it is above-mentioned the problems such as, the invention provides a kind of titanium white cladding wollastonite
Composite titanium dioxide pigment manufacture method.
The technical scheme that adopted for achieving the above object of the present invention is:A kind of titanium white coats the composite titanium dioxide of wollastonite
The manufacture method of pigment, comprises the following steps:
(1), the wollastonite for meeting predetermined particle diameter carried out into surface preparation, ready titanium dioxide moistening is carried out into surface and is located in advance
Reason;
(2), wollastonite in powder and titanium dioxide added in homogenizer, be sufficiently mixed, homogenizer mixing speed is
50-300rpm, heating-up temperature is 20-90 DEG C, and the response time is 8-60min;
(3), using controlling wet-type finishing machine grind, while carrying out peplos process to mixed wollastonite in powder and titanium dioxide:Using super
Thin wollastonite particle is core, adds dispersant and coloring agent, and peplos, milling time 2- are carried out as covering with titanium dioxide
50min;
(4), to grind slurry filter press filter pressing, the filter cake for obtaining is washed;
(5), drying;
(6)It is broken.
The step(1)In, wollastonite carry out inorganic agent used by surface preparation for silane coupling agent by quality percentage
Number meter, consumption is 0-3%;It is silane coupling agent that titanium dioxide moistening carries out inorganic agent used by surface preparation, by weight percent
Meter consumption is 0-3%.
The step(3)In the mean diameter of ultra-fine wollastonite be 2-90 μm, ultra-fine wollastonite by mass percentage
Consumption is 20-69%.
The step(3)In, it is 20-80% that titanium dioxide consumption used is coated by mass percentage.
The step(3)In, coloring agent is chemical method Zinc Oxide, and by mass percentage consumption is 3-19%;Dispersant is molten
Liquid is sodium hexameta phosphate, and by mass percentage consumption is 0.5-8%.
The step(3)In, titanium white powder content is 200-600g/L in titanium dioxide and wollastonite in powder slurry;Titanium dioxide and silicon
Wollastonite in powder content is 200-600g/L in limestone flour slurry.
The manufacture method of the composite titanium dioxide pigment of the titanium white cladding wollastonite of the present invention, is not reducing titanium dioxide covering power
Simultaneously and in the case of improving whiteness, use cost can be greatly reduced, while silicon is used alone before avoiding etc. using effect
Lime stone point substitutes the sedimentation phenomenon produced during titanium dioxide.
Specific embodiment
The manufacture method of the composite titanium dioxide pigment of the titanium white cladding wollastonite of the present invention, comprises the following steps:
(1), the wollastonite for meeting predetermined particle diameter carried out into surface preparation, ready titanium dioxide moistening is carried out into surface and is located in advance
Reason, wollastonite carry out inorganic agent used by surface preparation for silane coupling agent by mass percentage, consumption is 0-3%;Titanium white
It is silane coupling agent that powder moistening carries out inorganic agent used by surface preparation, and by mass percentage consumption is 0-3%;
(2), wollastonite in powder and titanium dioxide added in homogenizer, be sufficiently mixed, wollastonite, the skill of titanium dioxide mixing
Art condition is:Homogenizer mixing speed is 50-300rpm, and heating-up temperature is 20-90 DEG C, and the response time is 8-60min;
(3), using controlling wet-type finishing machine grind, while carrying out peplos process to mixed wollastonite in powder and titanium dioxide:Using super
Thin wollastonite particle is core, adds dispersant and coloring agent, and peplos, wollastonite base material peplos are carried out as covering with titanium dioxide
Technical conditions be milling time 2-50min, the mean diameter of ultra-fine wollastonite is 2-90 μm, by mass percentage ultra-fine silicon
Lime stone consumption is 20-69%, and it is 20-80% that titanium dioxide consumption used is coated by mass percentage, and coloring agent is chemical method oxygen
Change zinc, by mass percentage consumption is 3-19%;Dispersant solution is sodium hexameta phosphate, and by mass percentage consumption is
Titanium white powder content is 200-600g/L in 0.5-8%, titanium dioxide and wollastonite in powder slurry;Silicon in titanium dioxide and wollastonite in powder slurry
Lime stone powder content is 200-600g/L;
(4), to grind slurry filter press filter pressing, the filter cake for obtaining is washed;
(5), drying;
(6)It is broken, that is, obtain composite titanium dioxide.
When wet grinding is carried out to titanium dioxide and wollastonite slurry, by the titanium dioxide, wollastonite slurry and dispersant
Mixing is ground simultaneously, can be prevented effectively from titanium dioxide and wollastonite slurry and flocculation caking phenomenon is produced in pulping process.
Can with titanium dioxide be profit effectively that wollastonite carries out peplos process using this method, obtain the composite titanium dioxide of excellent performance.
The present invention is described by embodiment, and those skilled in the art know, in the spirit without departing from the present invention
In the case of scope, various changes or equivalence replacement can be carried out to these features and embodiment.In addition, in the religion of the present invention
Lead down, these features and embodiment can be modified to adapt to the essence of particular situation and material without departing from the present invention
God and scope.Therefore, the present invention is not limited to the particular embodiment disclosed, and falls with claims hereof
In the range of embodiment belong to protection scope of the present invention.
Claims (6)
1. a kind of titanium white coats the manufacture method of the composite titanium dioxide pigment of wollastonite, it is characterised in that:Comprise the following steps:
(1), the wollastonite for meeting predetermined particle diameter carried out into surface preparation, ready titanium dioxide moistening is carried out into surface and is located in advance
Reason;
(2), wollastonite in powder and titanium dioxide added in homogenizer, be sufficiently mixed, homogenizer mixing speed is
50-300rpm, heating-up temperature is 20-90 DEG C, and the response time is 8-60min;
(3), using controlling wet-type finishing machine grind, while carrying out peplos process to mixed wollastonite in powder and titanium dioxide:Using super
Thin wollastonite particle is core, adds dispersant and coloring agent, and peplos, milling time 2- are carried out as covering with titanium dioxide
50min;
(4), to grind slurry filter press filter pressing, the filter cake for obtaining is washed;
(5), drying;
(6)It is broken.
2. a kind of titanium white according to claim 1 coats the manufacture method of the composite titanium dioxide pigment of wollastonite, its feature
It is:The step(1)In, wollastonite carry out inorganic agent used by surface preparation for silane coupling agent by weight percent
Meter, consumption is 0-3%;It is silane coupling agent that titanium dioxide moistening carries out inorganic agent used by surface preparation, by mass percentage
Consumption is 0-3%.
3. a kind of titanium white according to claim 1 coats the manufacture method of the composite titanium dioxide pigment of wollastonite, its feature
It is:The step(3)In the mean diameter of ultra-fine wollastonite be 2-90 μm, ultra-fine wollastonite consumption by mass percentage
For 20-69%.
4. a kind of titanium white according to claim 1 coats the manufacture method of the composite titanium dioxide pigment of wollastonite, its feature
It is:The step(3)In, it is 20-80% that titanium dioxide consumption used is coated by mass percentage.
5. a kind of titanium white according to claim 1 coats the manufacture method of the composite titanium dioxide pigment of wollastonite, its feature
It is:The step(3)In, coloring agent is chemical method Zinc Oxide, and by mass percentage consumption is 3-19%;Dispersant solution
For sodium hexameta phosphate, by mass percentage consumption is 0.5-8%.
6. a kind of titanium white according to claim 1 coats the manufacture method of the composite titanium dioxide pigment of wollastonite, its feature
It is:The step(3)In, titanium white powder content is 200-600g/L in titanium dioxide and wollastonite in powder slurry;Titanium dioxide and silicon ash
Wollastonite in powder content is 200-600g/L in stone powder slurry.