CN108888862A - A kind of physiotherapy electrode plate - Google Patents
A kind of physiotherapy electrode plate Download PDFInfo
- Publication number
- CN108888862A CN108888862A CN201810695368.2A CN201810695368A CN108888862A CN 108888862 A CN108888862 A CN 108888862A CN 201810695368 A CN201810695368 A CN 201810695368A CN 108888862 A CN108888862 A CN 108888862A
- Authority
- CN
- China
- Prior art keywords
- conductive
- electrode plate
- conductive core
- conductive layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to electrode slice fields, and in particular to a kind of physiotherapy electrode plate, including matrix and conductive core, conductive core are fixed on matrix, and insulating trip is provided in conductive core, and conductive core connects external plug by electric wire.Conductive core includes graphite column and conductive layer, and wherein conductive layer includes sodium alginate, water, elemental sulfur and conducting resinl.Wherein conductive layer includes 3-10 parts of sodium alginate, 7-22 parts of water, 2-6 parts of elemental sulfur and 2-6 parts of conducting resinl.Sodium alginate and conducting resinl are put into agitator, water is added, stirs 0.5-1h;Then elemental sulfur is added in mixture, then in stirring 2-3h;It is coated on graphite column, is dried in drying box to get conductive core after mixing evenly.Temperature in drying box is 60-80 DEG C.The conductive layer with a thickness of 5 μm -20 μm.Matrix is followed successively by desensitization medical gel layer, reservoir bed, tissue layer and film layer from inside to outside;Multiple air holes are offered on the desensitization medical gel layer.The physiotherapy electrode plate with insulating trip can be prepared.
Description
Technical field
The present invention relates to electrode slice technical fields, and in particular to a kind of physiotherapy electrode plate.
Background technique
With the gradually development of science and technology, electrode slice appears in the sight of the public as medical instruments, and electrode slice can
Current signal is uniformly transferred to be attached on human body, human body signal can also be received, common electrode piece includes silica gel electrode slice and oneself
Viscous electrode slice, usual silica gel electrode slice need bandage that silica gel electrode slice is fixed on human body when in use, and use process compares
Trouble, self-adhering electrode piece can be sticked to required position in use, but since the self-adhering electrode piece service life is shorter, product cost
Height, user are difficult to receive higher cost when in use.
Summary of the invention
The purpose of the present invention is to provide a kind of physiotherapy electrode plates, can prepare the physiotherapy electrode plate with insulating trip.
In order to solve the above technical problems, the present invention uses following technical scheme:
A kind of physiotherapy electrode plate, including matrix and conductive core, conductive core are fixed on matrix, and insulation is provided in conductive core
Piece, conductive core connect external plug by electric wire.
Further;Conductive core includes graphite column and conductive layer, wherein conductive layer include sodium alginate, water, elemental sulfur and
Conducting resinl.
Further;Wherein conductive layer includes 3-10 parts of sodium alginate, 7-22 parts of water, 2-6 parts of elemental sulfur and conducting resinl 2-
6 parts.
Further;The preparation process of conductive layer is:
S1, sodium alginate and conducting resinl are put into agitator, water is added, stir 0.5-1h;
S2, elemental sulfur is then added in the mixture of step S1, then in stirring 2-3h;
S3, it is coated on graphite column, is dried in drying box to get conductive core after mixing evenly.
Further;Temperature in drying box is 60-80 DEG C.
Further;The conductive layer with a thickness of 5 μm -20 μm.
Further;Matrix is divided into four layers, is followed successively by desensitization medical gel layer, reservoir bed, tissue layer and thin from inside to outside
Film layer;Multiple air holes are offered on the desensitization medical gel layer.
Compared with prior art, the present invention one of at least has the advantages that:
1. the physiotherapy electrode plate that present invention preparation has insulating trip.
2. preparing the preferable conductive core of electric conductivity.
3. the selection of conductive layer different ratios of raw materials prepares the preferable conductive core of electric conductivity.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1
A kind of physiotherapy electrode plate, including matrix and conductive core, conductive core are fixed on matrix, and insulation is provided in conductive core
Piece, conductive core connect external plug by electric wire;Preparation has the physiotherapy electrode plate of insulating trip.
Embodiment 2
On the basis of embodiment 1, conductive core includes graphite column and conductive layer, and wherein conductive layer includes sodium alginate, water, simple substance
Sulphur and conducting resinl;Prepare the preferable conductive core of electric conductivity.
Embodiment 3
On the basis of embodiment 1-2, wherein conductive layer includes 3 parts of sodium alginate, 7 parts of water, 2 parts of elemental sulfur and conducting resinl 2
Part;The selection of conductive layer different ratios of raw materials prepares the preferable conductive core of electric conductivity.
Embodiment 4
On the basis of embodiment 1-3, wherein conductive layer includes 10 parts of sodium alginate, 22 parts of water, 6 parts of elemental sulfur and conducting resinl -6
Part;The selection of conductive layer different ratios of raw materials prepares the preferable conductive core of electric conductivity.
Embodiment 5
On the basis of examples 1 to 4, wherein conductive layer includes 6.5 parts of sodium alginate, 14.5 parts of water, 4 parts of elemental sulfur and conduction
4 parts of glue;The selection of conductive layer different ratios of raw materials prepares the preferable conductive core of electric conductivity.
Embodiment 6
On the basis of embodiment 1-5, the preparation process of conductive layer is:
S1, sodium alginate and conducting resinl are put into agitator, water is added, stir 0.5h;
S2, elemental sulfur is then added in the mixture of step S1, then in stirring 2h;
S3, it is coated on graphite column, is dried in drying box to get conductive core after mixing evenly;Conductive layer is by alginic acid
Sodium and conducting resinl are put into agitator stirring, and elemental sulfur stirring is being added, is finally being coated on graphite column after mixing evenly,
It is dry in drying box, so that obtaining preferable conductive layer.
Embodiment 7
On the basis of embodiment 1-6, the preparation process of conductive layer is:
S1, sodium alginate and conducting resinl are put into agitator, water is added, stir 1h;
S2, elemental sulfur is then added in the mixture of step S1, then in stirring 3h;
S3, it is coated on graphite column, is dried in drying box to get conductive core after mixing evenly;Conductive layer is by alginic acid
Sodium and conducting resinl are put into agitator stirring, and elemental sulfur stirring is being added, is finally being coated on graphite column after mixing evenly,
It is dry in drying box, so that obtaining preferable conductive layer.
Embodiment 8
On the basis of embodiment 1-7, the preparation process of conductive layer is:
S1, sodium alginate and conducting resinl are put into agitator, water is added, stir 0.75h;
S2, elemental sulfur is then added in the mixture of step S1, then in stirring 2.5h;
S3, it is coated on graphite column, is dried in drying box to get conductive core after mixing evenly;Conductive layer is by alginic acid
Sodium and conducting resinl are put into agitator stirring, and elemental sulfur stirring is being added, is finally being coated on graphite column after mixing evenly,
It is dry in drying box, so that obtaining preferable conductive layer.
Embodiment 9
On the basis of embodiment 1-7, the temperature in drying box is 60 DEG C;The temperature control of drying box is conducive to improve product
Quality.
Embodiment 10
On the basis of embodiment 1-9, the temperature in drying box is 80 DEG C;The temperature control of drying box is conducive to improve product
Quality.
Embodiment 11
On the basis of embodiment 1-10, the temperature in drying box is 70 DEG C;The temperature control of drying box is conducive to improve product
Quality.
Embodiment 12
On the basis of embodiment 1-11, the conductive layer with a thickness of 5 μm;The thickness of conductive layer is advantageously selected for product
Quality.
Embodiment 13
On the basis of embodiment 1-12, the conductive layer with a thickness of 20 μm;The thickness of conductive layer is advantageously selected for product
Quality.
Embodiment 14
On the basis of embodiment 1-13, the conductive layer with a thickness of 12.5 μm;The thickness of conductive layer is advantageously selected for producing
The quality of product.
Embodiment 15
On the basis of embodiment 1-14, matrix is divided into four layers, is followed successively by desensitization medical gel layer from inside to outside, reservoir bed, knits
Nitride layer and film layer;Multiple air holes are offered on the desensitization medical gel layer;The layer structure of matrix designs, so that using effect
Preferably.
Although reference be made herein to invention has been described for multiple explanatory embodiments of the invention, however, it is to be understood that
Those skilled in the art can be designed that a lot of other modification and implementations, these modifications and implementations will fall in this Shen
It please be within disclosed scope and spirit.More specifically, it is disclosed, in the scope of the claims in the application, it can be to master
The building block and/or layout for inscribing composite configuration carry out a variety of variations and modifications.In addition to what is carried out to building block and/or layout
Outside modification and improvement, to those skilled in the art, other purposes also be will be apparent.
Claims (7)
1. a kind of physiotherapy electrode plate, it is characterised in that:Including matrix and conductive core, conductive core is fixed on matrix, conductive
Insulating trip is provided on core, conductive core connects external plug by electric wire.
2. a kind of physiotherapy electrode plate according to claim 1, it is characterised in that:Conductive core includes graphite column and conductive layer,
Wherein conductive layer includes sodium alginate, water, elemental sulfur and conducting resinl.
3. a kind of physiotherapy electrode plate according to claim 2, it is characterised in that:Wherein conductive layer includes sodium alginate 3-10
Part, 7-22 parts of water, 2-6 parts of elemental sulfur and 2-6 parts of conducting resinl.
4. a kind of physiotherapy electrode plate according to claim 2, it is characterised in that:The preparation process of conductive layer is:
S1, sodium alginate and conducting resinl are put into agitator, water is added, stir 0.5-1h;
S2, elemental sulfur is then added in the mixture of step S1, then in stirring 2-3h;
S3, it is coated on graphite column, is dried in drying box to get conductive core after mixing evenly.
5. a kind of physiotherapy electrode plate according to claim 4, it is characterised in that:Temperature in drying box is 60-80 DEG C.
6. a kind of physiotherapy electrode plate according to claim 4, it is characterised in that:The conductive layer with a thickness of 5 μm of -20 μ
m。
7. a kind of physiotherapy electrode plate according to claim 1, it is characterised in that:Matrix is divided into four layers, from inside to outside successively
For desensitization medical gel layer, reservoir bed, tissue layer and film layer;Multiple air holes are offered on the desensitization medical gel layer.