CN108867175A - A kind of Study of Paper-Strengthening Agent Based - Google Patents
A kind of Study of Paper-Strengthening Agent Based Download PDFInfo
- Publication number
- CN108867175A CN108867175A CN201810668325.5A CN201810668325A CN108867175A CN 108867175 A CN108867175 A CN 108867175A CN 201810668325 A CN201810668325 A CN 201810668325A CN 108867175 A CN108867175 A CN 108867175A
- Authority
- CN
- China
- Prior art keywords
- paper
- parts
- study
- mass ratio
- strengthening agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Study of Paper-Strengthening Agent Based, belong to chemical field.The present invention is using the compounding such as fiberfill, modified starch compound, the nano magnesia of fiberfill adsorption can effectively improve fiber surface roughness, the mechanical snap power between three network structures to improve the formation such as fiberfill and modified starch compound, when papermaking acts on, the hole of different pore size in system can be filled, the binding site in system between each component can be improved, to make system internal bond strength further increase, play the role of filling and toughening, it is ensured that long-term resistance to compression folding effect.The present invention solves the problems, such as that current Study of Paper-Strengthening Agent Based is ineffective to folding strength, ring crush index, pop strength is improved.
Description
Technical field
The invention belongs to chemical fields, and in particular to a kind of Study of Paper-Strengthening Agent Based.
Background technique
Drying strengthening agent be in paper industry enhance paper strength a kind of important chemical, commonly used in compensation addition filler or
The decline of paper intensity caused by the fiber of inferior grade.In recent years, waste paper resources utilization rate rises year by year, and development potentiality is huge
Greatly.But the raising of waste paper utilization rate means that the increase of number is recycled in waste paper, will cause declining to a great extent for paper intensity index,
So needing to add drying strengthening agent to increase paper strength.Continuous rising with people to paper and cardboard demand pulls
The swift and violent growth of drying strengthening agent demand.Study of Paper-Strengthening Agent Based has been widely used in the production process of all kinds of paper and paper, to
It dramatically increases the dry strength of paper and cardboard, reduces high-quality raw material consumption, improves product specification, constantly proposed with to meet user
Higher and higher quality requirement.Paper is mainly to be made of paper fiber through network structure, and paper has a layer structure, in plane
Paper fiber is interlaced, disordered arrangements, and paper also has pore structure.Therefore, although at paper intensity by many factors shadow
It rings, but the binding force between most important reason or paper fiber.If can be led in paper containing largely unbonded staple fiber
Paper strength is caused to be decreased obviously, this not only has an impact performance, the quality at paper, also will affect the runnability of paper machine, drops
Low production efficiency.Therefore in the production process of papermaking, by the use of papermaking dry-strengthening agent, paper quality can be improved, reduced
Production cost, retention in addition also can be improved, increase paper formation, the runnability for improving paper machine etc..
The structure of paper fiber is determined containing the functional groups that can form Hydrogenbond with paper fiber(Hydroxyl, amide groups)
Water-soluble polymer can be used as papermaking dry-strengthening agent.Currently used drying strengthening agent has natural polymer such as starch and its modification
Object(Such as cationic starch, anionic starch, amphoteric starch), synthetic polymer such as polyacrylamide, glyoxal polyacrylamide
Amine and polyvinyl alcohol etc. and other water-soluble natural product type drying strengthening agents.In most cases, mass fraction is only added
0.1% ~ 1% substance can reach does potent fruit well.But produce in actual use paper folding strength,
Pop strength is poor.Therefore, producing a kind of drying strengthening agent that can solve the above problem has the very big market demand.
Summary of the invention
The technical problems to be solved by the invention:For current Study of Paper-Strengthening Agent Based to improving folding strength, ring crush index, resistance to broken
The bad problem of intensity effect, provides a kind of Study of Paper-Strengthening Agent Based.
In order to solve the above technical problems, the present invention is using technical solution as described below:
A kind of Study of Paper-Strengthening Agent Based, according to the mass fraction, including following component:5 ~ 10 parts of redispersibility rubber powders, 20 ~ 30 parts of acryloyls
Amine, 3 ~ 7 parts of sodium sulphate, 3 ~ 5 parts of auxiliary agents, 5 ~ 10 parts of curing agents, 5 ~ 10 parts of regulators, 50 ~ 70 parts of water, which is characterized in that also wrap
It includes:30 ~ 50 parts of modified starch compounds, 8 ~ 15 parts of fiberfill.
The auxiliary agent:In mass ratio 10:2~5:0.01 takes sodium carbonate liquor, sodium citrate, dopamine mixing to get helping
Agent.
The curing agent:Sodium sulfite, sodium hydrogensulfite, any one in ethylene glycol amine.
The regulator:Hydrochloric acid, sulfuric acid, acetic acid, acetic acid, any one in citric acid.
The redispersibility rubber powder:It is in mass ratio 4:1~2:1 takes ethylene-vinyl acetate copolymer, styrene-butadiene
Rubber and vinylacetate-ethylene-acrylate copolymer mix.
The preparation of the modified starch compound:It is in mass ratio 10:1~3:25 ~ 50 take starch, glycerol, zirconium oxide ball milling
Pearl mixing is poured into ball grinder, and ball milling obtains ball milling material, takes ball milling material in mass ratio 1:2 ~ 5, which are added oxidation solution, is mixed, quiet
It sets, obtains reaction solution A, extract reaction solution A in mass ratio 4 ~ 7:1:6 are added diethyl malonate, pyridine is mixed, and obtain reaction solution B,
In 35 ~ 50 DEG C, B in mass ratio 5 is extracted reaction solution:1~2:3 are added NaOCl and NaOH solution mixing, stand and form sediment to get modified
Flour complexes.
The oxidation solution:In mass ratio 1 ~ 2:5 ~ 7 take periodic acid, methylene chloride mixing to get oxidation solution.
The preparation of the fiberfill:At 55 ~ 65 DEG C, according to the mass fraction, 10 ~ 20 parts of nano magnesias, 10 ~ 15 are taken
Part silane coupling agent, 80 ~ 100 parts of dehydrated alcohols are mixed, then the glass of nano magnesia quality 10 ~ 20% are added into beaker
The thiocarbamide of glass fiber, nano magnesia quality 15 ~ 30% stirs 3 ~ 5h, and filtering takes filtration cakes torrefaction, discharges to get fiberfill.
The silane coupling agent is any one in KH550, KH560, KH570.
The additive:In mass ratio 1:3 ~ 5 take thiocarbamide, sodium carbonate liquor mixing to get additive.
The present invention is compared with other methods, and advantageous effects are:
(1)The present invention handles starch, activates through ball milling, through periodate oxidation, after producing neighbour's dialdehyde structural compounds,
Condensation is reacted through Borneo camphor text lid with diethyl malonate, then generates chloroform and COO through NaOCl effect haloform reaction-With paper pulp
In-OH effect, improve connecting forces between tissue, by introduce hydroxyl on active group and cellulose generate it is strong it is intermolecular mutually
Effect, hydrogen bond high efficiency dispersion, so that the fiber in slurry is evenly distributed causes fiber and intermolecular binding site to enhance, and improves dry strong
Degree activates the ball milling of starch, so that starch crystals plot structure is destroyed with granule-morphology, crystallinity is effectively dropped
It is low, to make mobility enhancing of the starch after activation in system, declines the diffusional resistance of other compositions in system, be easy to
It is diffused into starch molecule, forms Hydrogenbond with the hydroxyl in starch, to further increase the cohesive strength of system, make this
Invention adhesion strength is further promoted, and the thiocarbamide ingredient in fiberfill, and the starch molecule after activation can be made to be scattered in friendship
It networks in network, collaboration improves the bond strength inside drying strengthening agent system, is applied to papermaking, can greatly improve folding strength;
(2)For the present invention using the compounding such as fiberfill, modified starch compound, the nano magnesia of fiberfill adsorption can
Effectively improve fiber surface roughness, thus improve the formation such as fiberfill and modified starch compound three network structures it
Between mechanical snap power, papermaking act on when, the hole of different pore size in system can be filled, each component in system can be improved
Between binding site play the role of filling and toughening so that system internal bond strength be made to further increase, it is ensured that it is long-term
Resistance to compression folding effect.
Specific embodiment
Auxiliary agent:In mass ratio 10:2~5:0.01 sodium carbonate liquor, sodium citrate, dopamine for taking mass fraction to be 10% mixes
It closes to get auxiliary agent.
Curing agent:Sodium sulfite, sodium hydrogensulfite, any one in ethylene glycol amine.
Regulator:Hydrochloric acid, sulfuric acid, acetic acid, acetic acid, any one in citric acid.
Additive:In mass ratio 1:3 ~ 5 take the sodium carbonate liquor of thiocarbamide, concentration 0.1mol/L to mix to get additive.
Oxidation solution:In mass ratio 1 ~ 2:5 ~ 7 take periodic acid, methylene chloride mixing to get oxidation solution.
The preparation of modified starch compound:It is in mass ratio 10:1~3:25 ~ 50 take starch, glycerol, zirconium oxide ball milling pearl mixed
Conjunction is poured into ball grinder, with 300 ~ 350r/min, 1 ~ 3h of ball milling, obtains ball milling material, takes ball milling material in mass ratio 1:2 ~ 5 are added oxidation
Liquid is mixed, and stands 20 ~ 40min, obtains reaction solution A, extract reaction solution A in mass ratio 4 ~ 7:1:6 are added diethyl malonate, pyrrole
Pyridine mixing stirs 20 ~ 35min with 220 ~ 300r/min, obtains reaction solution B, in 35 ~ 50 DEG C of water-bath, extract reaction solution B in mass ratio 5:
1~2:3 NaOH solutions that NaOCl and concentration 0.01mol/L is added are mixed, and stand 30 ~ 45min of reaction to get modified starch
Compound.
The preparation of fiberfill:At 55 ~ 65 DEG C, according to the mass fraction, 10 ~ 20 parts of nano magnesias, 10 ~ 15 parts of silicon are taken
Alkane coupling agent, 80 ~ 100 parts of dehydrated alcohol mixing, stir 45 ~ 60min with 300 ~ 500r/min constant temperature, then be added and receive into beaker
The thiocarbamide of the glass fibre of rice magnesia quality 10 ~ 20%, nano magnesia quality 15 ~ 30%, stirs 3 ~ 5h, filtering takes filter cake
It is placed in baking oven, dry 6 ~ 8h, discharges to get fiberfill at 85 ~ 95 DEG C.
Redispersibility rubber powder:It is in mass ratio 4:1~2:1 takes ethylene-vinyl acetate copolymer, SBR styrene butadiene rubbers
It is mixed with vinylacetate-ethylene-acrylate copolymer.
A kind of preparation method of Study of Paper-Strengthening Agent Based, includes the following steps:
(1)According to the mass fraction, 30 ~ 50 parts of modified starch compounds, 8 ~ 15 parts of fiberfill, 5 ~ 10 parts of redispersibility glue are taken
Powder, 20 ~ 30 parts of acrylamides, 3 ~ 7 parts of sodium sulphate, 3 ~ 5 parts of auxiliary agents, 5 ~ 10 parts of curing agents, 5 ~ 10 parts of regulators, 50 ~ 70 parts of water;
(2)In 40 ~ 55 DEG C of water-bath, modified starch compound, redispersibility rubber powder, sodium sulphate, water mixing are taken, with 400 ~ 500r/
Min stirs 25 ~ 40min, is warming up to 65 ~ 80 DEG C, and fiberfill, auxiliary agent, regulator, acrylamide mixing, ultrasonic wave vibration is added
10 ~ 20min is swung, is evaporated under reduced pressure, is concentrated in vacuo to the 20 ~ 35% of original volume, obtains concentrate, takes concentrate that curing agent is added, in 65
DEG C ~ 75 DEG C, 2 ~ 4h is aged to get Study of Paper-Strengthening Agent Based.
Auxiliary agent:In mass ratio 10:2:0.01 sodium carbonate liquor, sodium citrate, dopamine for taking mass fraction to be 10% mixes
It closes to get auxiliary agent.
Curing agent:Sodium sulfite.
Regulator:Hydrochloric acid.
Additive:In mass ratio 1:3 take the sodium carbonate liquor of thiocarbamide, concentration 0.1mol/L to mix to get additive.
Oxidation solution:In mass ratio 1:5 take periodic acid, methylene chloride mixing to get oxidation solution.
The preparation of modified starch compound:It is in mass ratio 10:1:25 take starch, glycerol, the mixing of zirconium oxide ball milling pearl to fall
Enter in ball grinder, with 300r/min ball milling 1h, obtain ball milling material, takes ball milling material in mass ratio 1:2, which are added oxidation solution, is mixed, quiet
20min is set, reaction solution A is obtained, extracts reaction solution A in mass ratio 4:1:6 are added diethyl malonate, pyridine mixing, with 220r/min
20min is stirred, reaction solution B is obtained, in 35 DEG C of water-bath, extracts reaction solution B in mass ratio 5:1:3 are added NaOCl and concentration 0.01mol/L
NaOH solution be mixed, stand reaction 30min to get modified starch compound.
The preparation of fiberfill:At 55 DEG C, according to the mass fraction, take 10 parts of nano magnesias, 10 parts of silane coupling agents,
80 parts of dehydrated alcohol mixing, stir 45min with 300r/min constant temperature, then the glass of nano magnesia quality 10% is added into beaker
The thiocarbamide of glass fiber, nano magnesia quality 15% stirs 3h, and filtering takes filter cake to be placed in baking oven, the dry 6h at 85 DEG C, out
Material is to get fiberfill.
Redispersibility rubber powder:It is in mass ratio 4:1:1 take ethylene-vinyl acetate copolymer, SBR styrene butadiene rubbers and
Vinylacetate-ethylene-acrylate copolymer mixes.
A kind of preparation method of Study of Paper-Strengthening Agent Based, includes the following steps:
(1)According to the mass fraction, 30 parts of modified starch compounds, 8 parts of fiberfill, 5 parts of redispersibility rubber powders, 20 parts of propylene are taken
Amide, 3 parts of sodium sulphate, 3 parts of auxiliary agents, 5 parts of curing agents, 5 parts of regulators, 50 parts of water;
(2)In 40 DEG C of water-bath, modified starch compound, redispersibility rubber powder, sodium sulphate, water mixing are taken, is stirred with 400r/min
25min is warming up to 65 DEG C, and fiberfill, auxiliary agent, regulator, acrylamide mixing, supersonic oscillations 10min is added, and decompression is steamed
Hair, is concentrated in vacuo to the 20% of original volume, obtains concentrate, takes concentrate that curing agent is added, and in 65 DEG C, it is dry to get paper to be aged 2h
Strong agent.
Auxiliary agent:In mass ratio 10:5:0.01 sodium carbonate liquor, sodium citrate, dopamine for taking mass fraction to be 10% mixes
It closes to get auxiliary agent.
Curing agent:Sodium hydrogensulfite.
Regulator:Acetic acid.
Additive:In mass ratio 1:5 take the sodium carbonate liquor of thiocarbamide, concentration 0.1mol/L to mix to get additive.
Oxidation solution:In mass ratio 2:7 take periodic acid, methylene chloride mixing to get oxidation solution.
The preparation of modified starch compound:It is in mass ratio 10:3:50 take starch, glycerol, the mixing of zirconium oxide ball milling pearl to fall
Enter in ball grinder, with 350r/min ball milling 3h, obtain ball milling material, takes ball milling material in mass ratio 1:5, which are added oxidation solution, is mixed, quiet
40min is set, reaction solution A is obtained, extracts reaction solution A in mass ratio 7:1:6 are added diethyl malonate, pyridine mixing, with 300r/min
35min is stirred, reaction solution B is obtained, in 50 DEG C of water-bath, extracts reaction solution B in mass ratio 5:2:3 are added NaOCl and concentration 0.01mol/L
NaOH solution be mixed, stand reaction 45min to get modified starch compound.
The preparation of fiberfill:At 65 DEG C, according to the mass fraction, take 20 parts of nano magnesias, 15 parts of silane coupling agents,
100 parts of dehydrated alcohol mixing, stir 60min with 500r/min constant temperature, then the glass of nano magnesia quality 20% is added into beaker
The thiocarbamide of glass fiber, nano magnesia quality 30% stirs 5h, and filtering takes filter cake to be placed in baking oven, the dry 8h at 95 DEG C, out
Material is to get fiberfill.
Redispersibility rubber powder:It is in mass ratio 4:2:1 take ethylene-vinyl acetate copolymer, SBR styrene butadiene rubbers and
Vinylacetate-ethylene-acrylate copolymer mixes.
A kind of preparation method of Study of Paper-Strengthening Agent Based, includes the following steps:
(1)According to the mass fraction, 50 parts of modified starch compounds, 15 parts of fiberfill, 10 parts of redispersibility rubber powders, 30 part third are taken
Acrylamide, 7 parts of sodium sulphate, 5 parts of auxiliary agents, 10 parts of curing agents, 10 parts of regulators, 70 parts of water;
(2)In 55 DEG C of water-bath, modified starch compound, redispersibility rubber powder, sodium sulphate, water mixing are taken, is stirred with 500r/min
40min is warming up to 80 DEG C, and fiberfill, auxiliary agent, regulator, acrylamide mixing, supersonic oscillations 20min is added, and decompression is steamed
Hair, is concentrated in vacuo to the 35% of original volume, obtains concentrate, takes concentrate that curing agent is added, and in 75 DEG C, it is dry to get paper to be aged 4h
Strong agent.
Auxiliary agent:In mass ratio 10:3:0.01 sodium carbonate liquor, sodium citrate, dopamine for taking mass fraction to be 10% mixes
It closes to get auxiliary agent.
Curing agent:Ethylene glycol amine.
Regulator:Citric acid.
Additive:In mass ratio 1:4 take the sodium carbonate liquor of thiocarbamide, concentration 0.1mol/L to mix to get additive.
Oxidation solution:In mass ratio 1:6 take periodic acid, methylene chloride mixing to get oxidation solution.
The preparation of modified starch compound:It is in mass ratio 10:2:37 take starch, glycerol, the mixing of zirconium oxide ball milling pearl to fall
Enter in ball grinder, with 325r/min ball milling 2h, obtain ball milling material, takes ball milling material in mass ratio 1:3, which are added oxidation solution, is mixed, quiet
30min is set, reaction solution A is obtained, extracts reaction solution A in mass ratio 5:1:6 are added diethyl malonate, pyridine mixing, with 260r/min
27min is stirred, reaction solution B is obtained, in 42 DEG C of water-bath, extracts reaction solution B in mass ratio 5:1:3 are added NaOCl and concentration 0.01mol/L
NaOH solution be mixed, stand reaction 37min to get modified starch compound.
The preparation of fiberfill:At 60 DEG C, according to the mass fraction, take 15 parts of nano magnesias, 13 parts of silane coupling agents,
90 parts of dehydrated alcohol mixing, stir 52min with 400r/min constant temperature, then the glass of nano magnesia quality 15% is added into beaker
The thiocarbamide of glass fiber, nano magnesia quality 23% stirs 4h, and filtering takes filter cake to be placed in baking oven, the dry 7h at 90 DEG C, out
Material is to get fiberfill.
Redispersibility rubber powder:It is in mass ratio 4:1:1 take ethylene-vinyl acetate copolymer, SBR styrene butadiene rubbers and
Vinylacetate-ethylene-acrylate copolymer mixes.
A kind of preparation method of Study of Paper-Strengthening Agent Based, includes the following steps:
(1)According to the mass fraction, 40 parts of modified starch compounds, 10 parts of fiberfill, 7 parts of redispersibility rubber powders, 25 part third are taken
Acrylamide, 5 parts of sodium sulphate, 4 parts of auxiliary agents, 7 parts of curing agents, 7 parts of regulators, 60 parts of water;
(2)In 47 DEG C of water-bath, modified starch compound, redispersibility rubber powder, sodium sulphate, water mixing are taken, is stirred with 450r/min
32min is warming up to 72 DEG C, and fiberfill, auxiliary agent, regulator, acrylamide mixing, supersonic oscillations 15min is added, and decompression is steamed
Hair, is concentrated in vacuo to the 27% of original volume, obtains concentrate, takes concentrate that curing agent is added, and in 70 DEG C, it is dry to get paper to be aged 3h
Strong agent.
Comparative example 1:It is identical as the preparation method of embodiment 1, it has only the difference is that lacking modified starch compound.
Comparative example 2:It is identical as the preparation method of embodiment 1, it has only the difference is that lacking fiberfill.
Comparative example 3:The papermaking dry-strengthening agent of company of Beijing production.
The drying strengthening agent of embodiment and reference examples preparation is subjected to papermaking test, measures tensile strength according to GB/T453-2002
And test its burst index etc..Test result is shown in Table 1.
Table 1:
Test item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | Comparative example 3 |
Dry tensile index N.m/g | 19.15 | 19.53 | 19.42 | 14.36 | 15.11 | 10.21~12.16 |
Burst index Kpam2/g | 1.67 | 1.66 | 1.65 | 1.43 | 1.41 | 0.89~1.11 |
Ring crush index N.m/g | 12.31 | 12.37 | 12.19 | 11.15 | 11.14 | 9.13~10.32 |
Folding strength/time | 97 | 102 | 100 | 84 | 83 | 34~38 |
In summary, effect is more preferable in actual use for drying strengthening agent of the invention, and be worth promoting use.
Claims (10)
1. a kind of Study of Paper-Strengthening Agent Based, according to the mass fraction, including following component:5 ~ 10 parts of redispersibility rubber powders, 20 ~ 30 parts of propylene
Amide, 3 ~ 7 parts of sodium sulphate, 3 ~ 5 parts of auxiliary agents, 5 ~ 10 parts of curing agents, 5 ~ 10 parts of regulators, 50 ~ 70 parts of water, which is characterized in that also
Including:30 ~ 50 parts of modified starch compounds, 8 ~ 15 parts of fiberfill.
2. a kind of Study of Paper-Strengthening Agent Based according to claim 1, which is characterized in that the auxiliary agent:In mass ratio 10:2~5:0.01
Take sodium carbonate liquor, sodium citrate, dopamine mixing to get auxiliary agent.
3. a kind of Study of Paper-Strengthening Agent Based according to claim 1, which is characterized in that the curing agent:Sodium sulfite, bisulfite
Any one in sodium, ethylene glycol amine.
4. a kind of Study of Paper-Strengthening Agent Based according to claim 1, which is characterized in that the regulator:Hydrochloric acid, sulfuric acid, acetic acid, second
Acid, any one in citric acid.
5. a kind of Study of Paper-Strengthening Agent Based according to claim 1, which is characterized in that the redispersibility rubber powder:It is in mass ratio
4:1~2:1 takes ethylene-vinyl acetate copolymer, SBR styrene butadiene rubbers and vinylacetate-ethylene-acrylic ester copolymer
Object mixes.
6. a kind of Study of Paper-Strengthening Agent Based according to claim 1, which is characterized in that the preparation of the modified starch compound:It presses
Mass ratio is 10:1~3:25 ~ 50 take starch, glycerol, the mixing of zirconium oxide ball milling pearl to pour into ball grinder, and ball milling obtains ball milling material, takes
Ball milling material in mass ratio 1:2 ~ 5, which are added oxidation solution, is mixed, and stands, obtains reaction solution A, extract reaction solution A in mass ratio 4 ~ 7:1:6
Diethyl malonate, pyridine mixing is added, obtains reaction solution B, in 35 ~ 50 DEG C, extracts reaction solution B in mass ratio 5:1~2:3 add
Enter NaOCl and NaOH solution is mixed, stands to get modified starch compound.
7. a kind of Study of Paper-Strengthening Agent Based according to claim 6, which is characterized in that the oxidation solution:In mass ratio 1 ~ 2:5 ~ 7 take
Periodic acid, methylene chloride mixing are to get oxidation solution.
8. a kind of Study of Paper-Strengthening Agent Based according to claim 1, which is characterized in that the preparation of the fiberfill:In 55 ~ 65 DEG C
Under, according to the mass fraction, 10 ~ 20 parts of nano magnesias, 10 ~ 15 parts of silane coupling agents, 80 ~ 100 parts of dehydrated alcohol mixing is taken to stir
It mixes, then the thiocarbamide of the glass fibre of nano magnesia quality 10 ~ 20%, nano magnesia quality 15 ~ 30% is added into beaker, stir
3 ~ 5h is mixed, is filtered, filtration cakes torrefaction is taken, is discharged to get fiberfill.
9. a kind of Study of Paper-Strengthening Agent Based according to claim 8, which is characterized in that the silane coupling agent be KH550, KH560,
Any one in KH570.
10. a kind of Study of Paper-Strengthening Agent Based according to claim 8, which is characterized in that the additive:In mass ratio 1:3 ~ 5 take
Thiocarbamide, sodium carbonate liquor mixing are to get additive.