CN108866732A - A kind of preparation method of moisture absorption polyster fibre sewing thread - Google Patents

A kind of preparation method of moisture absorption polyster fibre sewing thread Download PDF

Info

Publication number
CN108866732A
CN108866732A CN201810879056.7A CN201810879056A CN108866732A CN 108866732 A CN108866732 A CN 108866732A CN 201810879056 A CN201810879056 A CN 201810879056A CN 108866732 A CN108866732 A CN 108866732A
Authority
CN
China
Prior art keywords
sewing thread
polyster fibre
moisture absorption
fibre sewing
twist
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810879056.7A
Other languages
Chinese (zh)
Inventor
卢崇国
卢静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Zhong Xiang Wire Belt Co Ltd
Original Assignee
Jiangsu Zhong Xiang Wire Belt Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Zhong Xiang Wire Belt Co Ltd filed Critical Jiangsu Zhong Xiang Wire Belt Co Ltd
Priority to CN201810879056.7A priority Critical patent/CN108866732A/en
Publication of CN108866732A publication Critical patent/CN108866732A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of preparation methods of moisture absorption polyster fibre sewing thread, include the following steps：1）Terylene chips are reeled off raw silk from cocoons, are formed and wound, and continuity composite monofilament is made；2）To composite monofilament plus first twist；3）Final twist is carried out to a plurality of yarn with first twist, embryo yarn is made；4）It carries out dyeing smooth processing；5）Coiling and molding is dispensed, polyster fibre sewing thread is made；6）Moisture absorption polyster fibre sewing thread is prepared, by polyster fibre sewing thread after 40% metacresol impregnates swelling 2 hours, is impregnated 1 hour using the acetone soln of benzophenone, with ultraviolet light, moisture absorption polyster fibre sewing thread is made in radiation grafting.Moisture absorption polyster fibre sewing thread preparation method of the invention, polyster fibre sewing thread obtained have good hygroscopicity.

Description

A kind of preparation method of moisture absorption polyster fibre sewing thread
Technical field
The present invention relates to a kind of preparation methods of moisture absorption polyster fibre sewing thread, belong to textile technology field.
Background technique
Polyster fibre sewing thread refers to the sewing threads produced using terylene as raw material.Terylene is that a quasi polymer is made through spinning At fiber, refer to the fiber that produces using polyethylene terephthalate as raw material, by the English name " polyethylene of its raw material more Terephthalate " abbreviation, referred to as " PET " fiber.Sewing thread is line needed for being knitted clothes product, and sewing thread presses raw material Natural fiber, synthetic fibers sewing thread and mixing sewing thread three categories can be divided into.Sewing thread uses pure polyester fiber as its raw material Compare more.
The conventional polyster fibre sewing thread shortcoming bad there is hygroscopicity.
Summary of the invention
The purpose of the present invention is to overcome the deficiencies of the prior art, provides a kind of preparation side of moisture absorption polyster fibre sewing thread Method.
The preparation method of moisture absorption polyster fibre sewing thread of the invention, includes the following steps：
1）Terylene chips are reeled off raw silk from cocoons, are formed and wound, and continuity composite monofilament is made；
2）To composite monofilament plus first twist；
3）Final twist is carried out to a plurality of yarn with first twist, embryo yarn is made；
4）It carries out dyeing smooth processing；
5）Coiling and molding is dispensed, polyster fibre sewing thread is made；
6）Moisture absorption polyster fibre sewing thread is prepared, by polyster fibre sewing thread after 40% metacresol impregnates swelling 2 hours, using hexichol first The acetone soln of ketone impregnates 1 hour, and with ultraviolet light, moisture absorption polyster fibre sewing thread is made in radiation grafting.
The step 6）In, the acetone soln concentration of benzophenone is 0.1-0.3mol/L, and the time of ultraviolet irradiation is 80-120min。
Moisture absorption polyster fibre sewing thread preparation method of the invention, polyster fibre sewing thread obtained have good hygroscopicity.
Specific embodiment
Embodiment 1
The preparation method of moisture absorption polyster fibre sewing thread of the invention, includes the following steps：
1）Terylene chips are reeled off raw silk from cocoons, are formed and wound, and continuity composite monofilament is made；
2）To composite monofilament plus first twist；
3）Final twist is carried out to a plurality of yarn with first twist, embryo yarn is made；
4）It carries out dyeing smooth processing；
5）Coiling and molding is dispensed, polyster fibre sewing thread is made；
6）Moisture absorption polyster fibre sewing thread is prepared, by polyster fibre sewing thread after 40% metacresol impregnates swelling 2 hours, using hexichol first The acetone soln of ketone impregnates 1 hour, and with ultraviolet light, moisture absorption polyster fibre sewing thread is made in radiation grafting.
The step 6）In, the acetone soln concentration of benzophenone is 0.1mol/L, and the time of ultraviolet irradiation is 80min。
Embodiment 2
The preparation method of moisture absorption polyster fibre sewing thread of the invention, includes the following steps：
1）Terylene chips are reeled off raw silk from cocoons, are formed and wound, and continuity composite monofilament is made；
2）To composite monofilament plus first twist；
3）Final twist is carried out to a plurality of yarn with first twist, embryo yarn is made；
4）It carries out dyeing smooth processing；
5）Coiling and molding is dispensed, polyster fibre sewing thread is made；
6）Moisture absorption polyster fibre sewing thread is prepared, by polyster fibre sewing thread after 40% metacresol impregnates swelling 2 hours, using hexichol first The acetone soln of ketone impregnates 1 hour, and with ultraviolet light, moisture absorption polyster fibre sewing thread is made in radiation grafting.
The step 6）In, the acetone soln concentration of benzophenone is 0.3mol/L, and the time of ultraviolet irradiation is 120min。

Claims (2)

1. a kind of preparation method of moisture absorption polyster fibre sewing thread, which is characterized in that include the following steps：
1）Terylene chips are reeled off raw silk from cocoons, are formed and wound, and continuity composite monofilament is made；
2）To composite monofilament plus first twist；
3）Final twist is carried out to a plurality of yarn with first twist, embryo yarn is made；
4）It carries out dyeing smooth processing；
5）Coiling and molding is dispensed, polyster fibre sewing thread is made；
6）Moisture absorption polyster fibre sewing thread is prepared, by polyster fibre sewing thread after 40% metacresol impregnates swelling 2 hours, using hexichol first The acetone soln of ketone impregnates 1 hour, and with ultraviolet light, moisture absorption polyster fibre sewing thread is made in radiation grafting.
2. a kind of preparation method of moisture absorption polyster fibre sewing thread according to claim 1, which is characterized in that the step 6） In, the acetone soln concentration of benzophenone is 0.1-0.3mol/L, and the time of ultraviolet irradiation is 80-120min.
CN201810879056.7A 2018-08-03 2018-08-03 A kind of preparation method of moisture absorption polyster fibre sewing thread Pending CN108866732A (en)