CN108863309A - A kind of preparation method for exempting from glazing ceramic whiteware - Google Patents
A kind of preparation method for exempting from glazing ceramic whiteware Download PDFInfo
- Publication number
- CN108863309A CN108863309A CN201810847124.1A CN201810847124A CN108863309A CN 108863309 A CN108863309 A CN 108863309A CN 201810847124 A CN201810847124 A CN 201810847124A CN 108863309 A CN108863309 A CN 108863309A
- Authority
- CN
- China
- Prior art keywords
- stage
- weight
- parts
- preparation
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of preparation methods of ceramics, a kind of preparation method for exempting from glazing ceramic whiteware is provided, glazing step after firing is omitted using this method, shorten life cycle of the product, the especially reduction of production cost, product obtained remains the smooth, bright of pottery surface simultaneously, and product appearance still has like through glazing, treated penetrating clean feels.Each raw material including following parts by weight:The kaolin of 52~54 parts by weight, the potassium albite of 40~43 parts by weight, the quartz of 3~5 parts by weight, the talcum powder of 1~2 parts by weight, 1750~1770 parts by weight water glass solution;The step of preparation method includes:Above-mentioned raw materials processing be moulded pottery not yet put in a kiln to bake after fire when, moulded pottery not yet put in a kiln to bake is gradually heated up firing by room temperature by linear temperature increase mode stage by stage, the heating curve of every step-up temperature is y=k × P × t, and y is temperature DEG C, P is that kiln power, t are time min, and the value of coefficient k is 0≤k≤1.
Description
The application is a kind of divisional application for the patent application that invention and created name is preparation method for exempting from glazing ceramic whiteware, former
The applying date of application is 2016-06-23, and application No. is 201610461510.8.
Technical field
The present invention relates to a kind of preparation method of ceramics more particularly to a kind of preparation methods for exempting from glazing ceramic whiteware.
Background technique
The preparation method of ceramic generally includes the moulded pottery not yet put in a kiln to bake product surface glazing face for first firing moulded pottery not yet put in a kiln to bake then at firing, jointly
The composition modern times highlight bright and clean pottery, and Dehua ceramic whiteware is fine with its production, and quality heavily fortified point is close, and sparkling and crystal-clear as beautiful, glaze paint is grown
Profit has the laudatory titles such as " ivory white ", " lard white ware ", " goose down is white " like rouge, has unique style in China's ceramic whiteware system, existing
Having ceramic whiteware preparation method is to reach such effect even more to be unable to do without first-class china clay and special glaze, however special glaze exists
Also therefore increase porcelain surface by process while achieving the desired results and extend Production Time, raising production cost, and glaze
Content of beary metal is relatively easy to cause the worry of modern people in ceramics ware for daily use.
The patent of invention of Chinese patent CN104058727B provides a kind of natural quality porcelain modelled after an antique, proposes production not glazing
Ceramic product production method, solve the problems, such as that glaze contains heavy metal in the prior art, but can only in the quality of manufactured goods
With texture modelled after an antique, without the pure white crystalistic sense of advanced ceramics especially Dehua ceramic whiteware, market audient is limited.
Summary of the invention
Therefore, for the above content, the present invention provides a kind of preparation method for exempting from glazing ceramic whiteware, is omitted using this method
Glazing step after firing shortens the reduction of life cycle of the product, especially production cost, while product obtained remains pottery
Porcelain product surface it is smooth, bright, product appearance still has like through glazing, treated penetrating clean feels.
In order to achieve the above objectives, the present invention is achieved by the following technical solutions:
A kind of preparation method for exempting from glazing ceramic whiteware, it is characterised in that:Each raw material including following parts by weight:50~55 parts by weight
Kaolin, the potassium albite of 38~42 parts by weight, the quartz of 3~5 parts by weight, 1~2 parts by weight talcum powder;
The step of preparation method includes:Above-mentioned raw materials handle, when firing, to incite somebody to action by linear temperature increase mode stage by stage after moulded pottery not yet put in a kiln to bake
Moulded pottery not yet put in a kiln to bake is gradually heated up firing by room temperature, and the heating curve of every step-up temperature is y=k × P × t, y is temperature DEG C, P be kiln power,
T is time min, and the value of coefficient k is 0≤k≤1;
Kiln power invariability when firing can be controlled by coefficient k, and the temperature set in kiln is gradually raised to temperature in time t
Y heats up into the temperature of next stage after reaching the temperature y in the stage;Specific each phase temperature and time control are as follows:
First stage y=390~410 DEG C, t=80~100, k=0.7;
Second stage y=790~810 DEG C, t=80~100, k=0.9;
Phase III y=1150~1170 DEG C, t=120~150, k=1;
Fourth stage y=1270~1290 DEG C, t=100~150min, k=1;
5th stage y=1310~1330 DEG C, t=50~70, k=1;
6th stage y=1311~1331 DEG C, t=8~15, k=1;
7th stage y=1260~1280 DEG C, t=5~10, k=0.01;
8th stage y=1260~1280 DEG C, t=50~80, k=1;
A further improvement is that:Each raw material is the Guangxi kaolin of 50~55 parts by weight, 38~42 parts by weight by weight
Indonesia's potassium albite, 3~5 parts by weight Jiangxi quartz, the Fujian talcum powder of 1~2 parts by weight.
A further improvement is that:Each raw material including following parts by weight:The Guangxi kaolin of 54 parts by weight, 40 parts by weight
Indonesia's potassium albite, 5 parts by weight Jiangxi quartz, 1 parts by weight Fujian talcum powder.
A further improvement is that:It further include the waterglass of 1750~1770 parts by weight.
A further improvement is that:It further include the water glass solution of 1765 parts by weight.
A further improvement is that:Also raw material is handled before linear temperature increase stage by stage, the feedstock processing mode is:
It is ground 38 hours after each raw material of kaolin is mixed and obtains base powder;120 meshes are crossed to base powder, obtain smart base repeatedly for three times
Powder;Except iron;Injecting treatment is slurry;Injection mold is shaped to moulded pottery not yet put in a kiln to bake.
A further improvement is that:The ramp case in the per stage of linear temperature increase stage by stage is:First stage y=400 DEG C, t
=90, k=0.7;Second stage y=800 DEG C, t 90, k=0.9;Phase III y=1160 DEG C, t 140min, k=1;Fourth stage
Y=1280 DEG C, t=120min, k=1;5th stage y=1320 DEG C, t=60, k=1;6th stage y=1321 DEG C, t=10, k=1;The
Seven stage y=1270 DEG C, t=5, k=0.01;8th stage y=1270 DEG C, t=60, k=1.
By using preceding solution, the beneficial effects of the invention are as follows:A kind of preparation for exempting from glazing ceramic whiteware of the invention
Method only uses kaolin, potassium albite, quartz, talcum powder from the screening of raw material, and the moulded pottery not yet put in a kiln to bake obtained after ground sieving influences
The metal ingredient of firing is less, and silica type is more, constitutes good firing basis, then fire through the linear temperature increase under control,
Moulded pottery not yet put in a kiln to bake is set to obtain solid densification, lubricious pure white, surface exquisiteness is such as beautiful, the penetrating feature spent, and remains china clay after natural cooling
True qualities, and there is in the case where not glazing the surface effect of similar glazing, the special glaze of modulation and glazing can be saved
Processing step, thus save the production time and reduce production cost.
Specific embodiment
Carry out the embodiment that the present invention will be described in detail below with reference to specific embodiment, how skill is applied to the present invention whereby
Art means solve technical problem, and the realization process for reaching technical effect can fully understand and implement.
Unless otherwise specified, the conventional hand that technological means employed in embodiment is well known to those skilled in the art
Section, used reagent and product are also available commercial.The source of agents useful for same, trade name and it is necessary to list it
Constituent person is indicated on the first occurrence.
The embodiment of the present invention one:
A kind of preparation method for exempting from glazing ceramic whiteware:
Step 1, by raw material by weight:The kaolin of 52 parts by weight, the potassium albite of 43 parts by weight, 3 parts by weight stone
The talcum powder of English, 2 parts by weight grinds 38 hours after being mixed with the water glass solution of 1765 parts by weight and obtains base powder;
Above-mentioned base powder is crossed 120 meshes by step 2, repeatedly for three times, obtains smart base powder;
Step 3, to treated that smart base powder is carried out except iron through step 2;
Step 4, to step 3, treated that smart base powder injecting treatment is slurry;
Step 5, slurry injection mold are shaped to moulded pottery not yet put in a kiln to bake;
The moulded pottery not yet put in a kiln to bake is gradually heated up firing, the work in per stage by room temperature by linear temperature increase curve y=kpt stage by stage by step 6
Skill numerical value is as follows:
First stage y=390 DEG C, t=90, k=0.7 carry out moulded pottery not yet put in a kiln to bake drying, exclude moisture;
Second stage y=790 DEG C, t 90, k=0.9, preheating firing, undertaking further heat up, and guarantee that moulded pottery not yet put in a kiln to bake is heated evenly;Third
Stage y=1150 DEG C, t 140min, k=1;Fourth stage y=1270 DEG C, t=120min, k=1;5th stage y=1310 DEG C, t=
60,k=1;Above-mentioned firing keeps the internal-response of moulded pottery not yet put in a kiln to bake mild, is conducive to form penetrating clean sense after silica is fired;
6th stage y=1313 DEG C, t=10, k=1;The position between moulded pottery not yet put in a kiln to bake and bearing plate is cooked, it is inconsistent not leave quality
Region;
7th stage y=1260 DEG C, t=5, k=0.01;The cooling of low-power is handled, and the compactness of moulded pottery not yet put in a kiln to bake is made to be formed, and surface is kept
Smooth stabilization;8th stage y=1260 DEG C, t=60, k=1, sizing;
Step 7, natural cooling obtain pottery.
Embodiment two:
A kind of preparation method for exempting from glazing ceramic whiteware:
By raw material by weight:The Guangxi kaolin of 54 parts by weight, Indonesia's potassium albite of 40 parts by weight, 5 parts by weight
Jiangxi quartz, the Fujian talcum powder of 1 parts by weight grind 38 hours after being mixed with the water glass solution of 1765 parts by weight and obtain
Base powder;120 meshes are crossed to base powder, obtain smart base powder repeatedly for three times;Except iron;Injecting treatment is slurry;Injection mold is shaped to mud
Base.
The firing of the moulded pottery not yet put in a kiln to bake is:
First stage y=350 DEG C, t=90, k=0.7 carry out moulded pottery not yet put in a kiln to bake drying, exclude moisture;
Second stage y=750 DEG C, t 90, k=0.9, preheating firing, undertaking further heat up, and guarantee that moulded pottery not yet put in a kiln to bake is heated evenly;Third
Stage y=1100 DEG C, t 140min, k=1;Fourth stage y=1250 DEG C, t=120min, k=1;5th stage y=1300 DEG C, t=
60,k=1;Above-mentioned firing keeps the internal-response of moulded pottery not yet put in a kiln to bake mild, is conducive to form penetrating clean sense after silica is fired;
6th stage y=1321 DEG C, t=10, k=1;The position between moulded pottery not yet put in a kiln to bake and bearing plate is cooked, it is inconsistent not leave quality
Region;
7th stage y=1270 DEG C, t=5, k=0.01;The cooling of low-power is handled, and the compactness of moulded pottery not yet put in a kiln to bake is made to be formed, and surface is kept
Smooth stabilization;8th stage y=1270 DEG C, t=60, k=1, sizing;
Step 7, natural cooling obtain pottery.
Above-mentioned Guangxi kaolin is place of production China Guangxi province area, and Indonesia's potassium albite is place of production Indonesia area,
Jiangxi quartz is place of production China Jiangxi Area, and it is that can clearly purchase in the market that Fujian talcum powder, which is place of production China In Fujian Province,
The product bought.
The foregoing descriptions are merely the embodiment using this origination techniques content, any those skilled in the art use this wound
Make done modifications and changes, all belong to the scope of the patents of this creation opinion, and is not limited to those disclosed embodiments.
Claims (6)
1. a kind of preparation method for exempting from glazing ceramic whiteware, it is characterised in that:Each raw material including following parts by weight:52~54 parts by weight
Kaolin, the potassium albite of 40~43 parts by weight, the quartz of 3~5 parts by weight, the talcum powder of 1~2 parts by weight, 1750~
The water glass solution of 1770 parts by weight;
The step of preparation method includes:Above-mentioned raw materials handle, when firing, to incite somebody to action by linear temperature increase mode stage by stage after moulded pottery not yet put in a kiln to bake
Moulded pottery not yet put in a kiln to bake is gradually heated up firing by room temperature, and the heating curve of every step-up temperature is y=k × P × t, y is temperature DEG C, P be kiln power,
T is time min, and the value of coefficient k is 0≤k≤1;
First stage y=350~390 DEG C, t=80~100, k=0.7;
Second stage y=750~790 DEG C, t=80~100, k=0.9;
Phase III y=1100~1150 DEG C, t=120~150, k=1;
Fourth stage y=1250~1270 DEG C, t=100~150min, k=1;
5th stage y=1300~1330 DEG C, t=50~70, k=1;
6th stage y=1313~1331 DEG C, t=8~15, k=1;
7th stage y=1260~1280 DEG C, t=5~10, k=0.01;
8th stage y=1260~1280 DEG C, t=50~80, k=1.
2. the preparation method according to claim 1 for exempting from glazing ceramic whiteware, it is characterised in that:Each original including following parts by weight
Material:The kaolin of 52 parts by weight, the potassium albite of 43 parts by weight, the quartz of 3 parts by weight, the talcum powder of 2 parts by weight, 1765 weight
The water glass solution of part.
3. the preparation method according to claim 2 for exempting from glazing ceramic whiteware, it is characterised in that:The linear temperature increase stage by stage
The ramp case in per stage is:First stage y=390 DEG C, t=90, k=0.7;Second stage y=790 DEG C, t 90, k=0.9;The
Three stage y=1150 DEG C, t 140min, k=1;Fourth stage y=1270 DEG C, t=120min, k=1;5th stage y=1310 DEG C, t
=60,k=1;6th stage y=1313 DEG C, t=10, k=1;7th stage y=1260 DEG C, t=5, k=0.01;8th stage y=1260
DEG C, t=60, k=1.
4. the preparation method according to claim 1 for exempting from glazing ceramic whiteware, it is characterised in that:Each original including following parts by weight
Material:The Guangxi kaolin of 54 parts by weight, Indonesia's potassium albite of 40 parts by weight, 5 parts by weight Jiangxi quartz, 1 parts by weight good fortune
Build the water glass solution of talcum powder, 1765 parts by weight.
5. the preparation method according to claim 4 for exempting from glazing ceramic whiteware, it is characterised in that:The linear temperature increase stage by stage
The ramp case in per stage is:First stage y=350 DEG C, t=90, k=0.7;Second stage y=750 DEG C, t 90, k=0.9;The
Three stage y=1100 DEG C, t 140min, k=1;Fourth stage y=1250 DEG C, t=120min, k=1;5th stage y=1300 DEG C, t
=60,k=1;6th stage y=1321 DEG C, t=10, k=1;7th stage y=1270 DEG C, t=5, k=0.01;8th stage y=1270
DEG C, t=60, k=1.
6. the preparation method according to claim 1 for exempting from glazing ceramic whiteware, it is characterised in that:Before linear temperature increase stage by stage also
Raw material is handled, the feedstock processing mode is:It is ground 38 hours after each raw material is mixed and obtains base powder;To base powder
120 meshes are crossed, obtain smart base powder repeatedly for three times;Except iron;Injecting treatment is slurry;Injection mold is shaped to moulded pottery not yet put in a kiln to bake.