CN108858638A - The manufacturing method of the moisture-proof composite wood door of insect prevention - Google Patents

The manufacturing method of the moisture-proof composite wood door of insect prevention Download PDF

Info

Publication number
CN108858638A
CN108858638A CN201811042843.2A CN201811042843A CN108858638A CN 108858638 A CN108858638 A CN 108858638A CN 201811042843 A CN201811042843 A CN 201811042843A CN 108858638 A CN108858638 A CN 108858638A
Authority
CN
China
Prior art keywords
plate
particulate material
moisture
manufacturing
composite wood
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811042843.2A
Other languages
Chinese (zh)
Inventor
张天俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Tiantian Wood Industry Co Ltd
Original Assignee
Chengdu Tiantian Wood Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Tiantian Wood Industry Co Ltd filed Critical Chengdu Tiantian Wood Industry Co Ltd
Priority to CN201811042843.2A priority Critical patent/CN108858638A/en
Publication of CN108858638A publication Critical patent/CN108858638A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses the manufacturing methods of the moisture-proof composite wood door of insect prevention, pass through stalk, reed rod carries out spray insect powder and carries out expelling parasite, place three days or more, internal worm's ovum is killed, expel internal polypide, then stalk is handled, reed rod carries out dries pulverizing into particle, ACQ preservative treatment is carried out to particulate material again, so that raw material do not allow it is perishable, it is uniformly mixed by natural resin, so that granular materials is freezing together, it is flattened by being laid with repeatedly on the plate with fence, centre uses viscose glue pressing drying, eventually form the solid Regenerated plate of multilayer, it is used to make a core using the multi-layer board, it is compared with traditional timber and is not easy crack；The problem of entire door panel all uses stalk, reed rod that solid Regenerated plate is made, and density is small, light weight, convenient transportation, and waste utilization while also solves traditional timber crack.

Description

The manufacturing method of the moisture-proof composite wood door of insect prevention
Technical field
The present invention relates to a kind of timber processing methods, and in particular to the manufacturing method of the moisture-proof composite wood door of insect prevention.
Background technique
Solid Door is constantly subjected to masses and likes, Solid Door is made using natural large-scale timber, large-scale wood raw material Resource consumption waste of resource and not environmentally；The present invention, which provides, a kind of to be carried out utilizing processing, environmental protection using discarded fibrous plant Healthy not waste of resource.
Summary of the invention
The present invention provides the manufacturing methods of the moisture-proof composite wood door of the insect prevention solved the problems, such as in above-mentioned background technique.
The present invention is achieved through the following technical solutions：
The manufacturing method of the moisture-proof composite wood door of insect prevention, includes the following steps：
S1, spray insect powder progress expelling parasite is carried out using stalk, reed rod, place three days or more, then carry out at dries pulverizing Reason obtains particulate material, then carries out ACQ preservative treatment to particulate material；
S2, prepare natural resin, natural resin is diluted, by the natural resin after particulate material mixed diluting, then Uniformly being laid in surrounding has on the plate of fence, and tile thickness 2-4cm, then does pressing processing, on the rectangular block after pressing Gluing, then continue to be laid with one layer of particulate material for being mixed with natural resin above, then pressing drying；Form the double-deck pressing Plate；
The double-deck force fit plate formed after S3, step S2 repeats step S2 on the double-deck force fit plate, forms Multi-layer force fit plate, Until the thickness of Multi-layer force fit plate is in 3-4cm；
S4, Multi-layer force fit plate is cut into gate, the core plate as door-plate；
S5, the two sides that core plate is bonded in using wood panel carry out planing processing to corner；
S6, edge sealing processing is carried out to the corner after planing.
Spray insect powder, which is carried out, by stalk, reed rod carries out expelling parasite, place three days or more, internal worm's ovum is killed, is driven Then internal polypide out handles stalk, reed rod progress dries pulverizing at particle, then to particulate material and carries out ACQ preservative treatment, So that raw material is not allowed perishable, uniformly mixed by the natural resin after dilution, so that granular materials is freezing together, After natural resin dilutes, it is easy stirring particulate material；It is flattened by being laid with repeatedly on the plate with fence, centre uses Viscose glue pressing drying, eventually forms the solid Regenerated plate of multilayer, is used to make a core using the multi-layer board, with traditional timber compared to not Be easy crack, finally reuse panel bonding, achieve the effect that beauty, entire door-plate it is whole without mortise at, it is wooden to avoid tradition Door is combined by core plate with frame, the assembling of frame mortise, and wooden contraction causes to form crack at assembling and at mortise；Entire door core Plate all uses stalk, reed rod that solid Regenerated plate is made, and density is small, light weight, convenient transportation, and waste utilization while also solves Determined traditional timber crack the problem of.
Further, after the thickness of laying particulate material is compressed depending on one layer of particulate material of laying in the step S2 Thickness, it is described by compressed thickness be less than 1cm.By multi-tiered compression, so that the solid density in raw plate of last multilayer More stable, fastness is more preferable.
Further, compacting drying is used after panel bonding.
Further, edge sealing processing is pressed using viscose glue, then firm with text nail.Edge sealing only uses viscose glue since area is small Therefore easy degumming reuses text nail and fixes, keep it more durable, the hidden effect of text nail is good, guarantees the smooth of edge sealing surface Property.
Further, the carving of panel, whole japanning processing are carried out after step S6 again.
The present invention has the advantage that and beneficial effect：
1, the present invention carries out spray insect powder by stalk, reed rod and carries out expelling parasite, place three days or more, internal worm's ovum is killed It goes out, expels internal polypide, it is anti-at particle, then to particulate material progress ACQ then to handle stalk, reed rod progress dries pulverizing Corruption processing so that raw material do not allow it is perishable, by dilution after natural resin uniformly mixed so that granular materials solidification Together, after natural resin dilution, it is easy stirring particulate material；It is flattened by being laid with repeatedly on the plate with fence, Centre eventually forms the solid Regenerated plate of multilayer using viscose glue pressing drying, is used to make a core using the multi-layer board, with traditional wood Door finally reuses panel bonding compared to being not easy crack, achievees the effect that beauty, entire door-plate integrally without mortise at, avoid Traditional timber combine by core plate with frame, the assembling of frame mortise, and wooden contraction causes at assembling and formation crack at mortise； Entire door panel all uses stalk, reed rod that solid Regenerated plate is made, and density is small, light weight, convenient transportation, waste utilization The problem of also solving traditional timber crack simultaneously；
2, the present invention is by multi-tiered compression, so that the solid density in raw plate of last multilayer is more stable, fastness is more It is good.
Specific embodiment
To make the objectives, technical solutions, and advantages of the present invention clearer, below with reference to embodiment, the present invention is made Further to be described in detail, exemplary embodiment of the invention and its explanation for explaining only the invention, are not intended as to this The restriction of invention.
Embodiment 1
The manufacturing method of the moisture-proof composite wood door of insect prevention, includes the following steps：
S1, dries pulverizing processing is carried out using stalk, reed rod, obtains particulate material；
S2, by the natural resin after particulate material mixed diluting, be then uniformly laid in the plate that surrounding has fence On, tile thickness 2-4cm, then does pressing processing, gluing on the rectangular block after pressing, then continues to be laid with one layer of mixing above There is the particulate material of natural resin, then pressing drying；Form the double-deck force fit plate；
The double-deck force fit plate formed after S3, step S2 repeats step S2 on the double-deck force fit plate, forms Multi-layer force fit plate, Until the thickness of Multi-layer force fit plate is in 3-4cm；
S4, Multi-layer force fit plate is cut into gate, the core plate as door-plate；
S5, the two sides that core plate is bonded in using wood panel carry out planing processing to corner；
S6, edge sealing processing is carried out to the corner after planing.
When implementation, the thickness that particulate material is laid in the step S2 is compressed depending on being laid with one layer of particulate material Thickness, it is described that 1cm is less than by compressed thickness；Compacting drying is used after panel bonding；Edge sealing processing is pressed using viscose glue, then It is firm with text nail；The carving of panel, whole japanning processing are carried out after step S6 again.When stalk, reed rod are dried, it should dry It does to 50%-70% moisture level is removed, avoids crushing in crushing process too thin.
Above-described specific embodiment has carried out further the purpose of the present invention, technical scheme and beneficial effects It is described in detail, it should be understood that being not intended to limit the present invention the foregoing is merely a specific embodiment of the invention Protection scope, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should all include Within protection scope of the present invention.

Claims (5)

1. the manufacturing method of the moisture-proof composite wood door of insect prevention, which is characterized in that include the following steps：
S1, spray insect powder progress expelling parasite is carried out using stalk, reed rod, place three days or more, then dries pulverizing processing is carried out, it obtains ACQ preservative treatment is carried out to particulate material, then to particulate material；
S2, prepare natural resin, natural resin is diluted, by the natural resin after particulate material mixed diluting, then uniformly The surrounding that is laid in have on the plate of fence, tile thickness 2-4cm, then do pressing processing, gluing on the rectangular block after pressing, Continue to be laid with one layer of particulate material for being mixed with natural resin above again, then pressing drying；Form the double-deck force fit plate；
The double-deck force fit plate formed after S3, step S2 repeats step S2 on the double-deck force fit plate, forms Multi-layer force fit plate, until The thickness of Multi-layer force fit plate is in 3-4cm；
S4, Multi-layer force fit plate is cut into gate, the core plate as door-plate；
S5, the two sides that core plate is bonded in using wood panel carry out planing processing to corner；
S6, edge sealing processing is carried out to the corner after planing.
2. the manufacturing method of the moisture-proof composite wood door of insect prevention according to claim 1, which is characterized in that the step S2 The middle thickness for being laid with particulate material depends on being laid with one layer of particulate material by compressed thickness, described small by compressed thickness In 1cm.
3. the manufacturing method of the moisture-proof composite wood door of insect prevention according to claim 1, which is characterized in that after panel bonding It is dried using compacting.
4. the manufacturing method of the moisture-proof composite wood door of insect prevention according to claim 1, which is characterized in that at the edge sealing Reason is pressed using viscose glue, then firm with text nail.
5. the manufacturing method of the moisture-proof composite wood door of insect prevention according to claim 1, which is characterized in that after step S6 The carving of panel, whole japanning processing are carried out again.
CN201811042843.2A 2018-09-07 2018-09-07 The manufacturing method of the moisture-proof composite wood door of insect prevention Withdrawn CN108858638A (en)