CN108819392A - 一种布料 - Google Patents

一种布料 Download PDF

Info

Publication number
CN108819392A
CN108819392A CN201810496866.4A CN201810496866A CN108819392A CN 108819392 A CN108819392 A CN 108819392A CN 201810496866 A CN201810496866 A CN 201810496866A CN 108819392 A CN108819392 A CN 108819392A
Authority
CN
China
Prior art keywords
flame
layer
retardant
mass ratio
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810496866.4A
Other languages
English (en)
Inventor
狄冬祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rugao Dongxiang Yarn Dyed Fabric Co Ltd
Original Assignee
Rugao Dongxiang Yarn Dyed Fabric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rugao Dongxiang Yarn Dyed Fabric Co Ltd filed Critical Rugao Dongxiang Yarn Dyed Fabric Co Ltd
Priority to CN201810496866.4A priority Critical patent/CN108819392A/zh
Publication of CN108819392A publication Critical patent/CN108819392A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种布料，其特征在于：该布料包括基布层、中间层及阻燃层。基布层及中间层分别采用聚己内酰胺纤维、涤纶纤维，阻燃层采用阻燃腈氯纶纤维以及黏胶纤维构成，其中聚己内酰胺纤维的所占的质量比为40‑45％，涤纶纤维所占的质量比为30‑35％，阻燃腈氯纶纤维所占的质量比为20‑25％，黏胶纤维所占的质量比为8‑12％。本发明与现有技术相比所具有的优点是：通过增加阻燃层，具有防火的效果，工艺简单，成本较低，安全性更强，使用范围广。

Description

一种布料
技术领域
本发明涉及一种布料。
背景技术
现有的布料品种众多，但随着人们生活水平的提高，需要提供能满足不同人群需要的新品种。
发明内容
本发明解决其技术问题所采用的技术方案是：一种布料，其特征是：该布料包括基布层、中间层及阻燃层。基布层及中间层分别采用聚己内酰胺纤维、涤纶纤维，阻燃层采用阻燃腈氯纶纤维以及黏胶纤维构成，其中聚己内酰胺纤维的所占的质量比为40-45％，涤纶纤维所占的质量比为30-35％，阻燃腈氯纶纤维所占的质量比为20-25％，黏胶纤维所占的质量比为8-12％。
本发明的有益效果是：通过增加阻燃层，具有防火的效果，工艺简单，成本较低，安全性更强，使用范围广。
具体实施方式
具体实施例：一种布料，其特征是：该布料包括基布层、中间层及阻燃层。基布层及中间层分别采用聚己内酰胺纤维、涤纶纤维，阻燃层采用阻燃腈氯纶纤维以及黏胶纤维构成，其中聚己内酰胺纤维的所占的质量比为40-45％，涤纶纤维所占的质量比为30-35％，阻燃腈氯纶纤维所占的质量比为20-25％，黏胶纤维所占的质量比为8-12％。
本发明的有益效果是：通过增加阻燃层，具有防火的效果，工艺简单，成本较低，安全性更强，使用范围广。
显然，上述实施例仅仅是为清楚地说明所作的举例，而并非对实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引伸出的显而易见的变化或变动仍处于本发明创造的保护范围之中。

Claims (1)

1.一种布料，其特征是：该布料包括基布层、中间层及阻燃层。基布层及中间层分别采用聚己内酰胺纤维、涤纶纤维，阻燃层采用阻燃腈氯纶纤维以及黏胶纤维构成，其中聚己内酰胺纤维的所占的质量比为40-45％，涤纶纤维所占的质量比为30-35％，阻燃腈氯纶纤维所占的质量比为20-25％，黏胶纤维所占的质量比为8-12％。
CN201810496866.4A 2018-05-22 2018-05-22 一种布料 Withdrawn CN108819392A (zh)