CN108819150A - A kind of manufacture craft of massage health-care insole - Google Patents
A kind of manufacture craft of massage health-care insole Download PDFInfo
- Publication number
- CN108819150A CN108819150A CN201810693719.6A CN201810693719A CN108819150A CN 108819150 A CN108819150 A CN 108819150A CN 201810693719 A CN201810693719 A CN 201810693719A CN 108819150 A CN108819150 A CN 108819150A
- Authority
- CN
- China
- Prior art keywords
- insole
- tpu
- massage
- manufacture craft
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacture craft of massage health-care insole, including step 1, the TPU examinations of materials；Step 2, baking material are dry；Colorant is mixed in step 3, stirring；Step 4 heats injection molding；Step 5, demoulding；Step 6 repairs edge grinding shaping；Step 7 is examined；Step 8, packaging；The insole of technique production includes insole body, integrally formed with massage column corresponding with human body sole acupuncture point and massage convex point on insole body, use TPU for main material simultaneously, flexibility is good, and elasticity is high, and ductility is good, nano silver and active carbon powder are injected in TPU material, nano silver and active carbon inject during melt, can not only be modified to TPU, have enhancing insole tensile strength and elastic effect.And nano silver particles and active carbon powder can also be made to be crosslinked in TPU material, after mold is extruded into insole, nano silver particles and active carbon powder uniform adsorption are on the surface of insole and the surface of massage column and massage convex point, not only act as the effect of antibiotic health, but also enhance the connectivity robustness between massage column and massage convex point and insole body, it is not fallen off after long.
Description
Technical field
The present invention relates to insole manufacture technology field, specially a kind of manufacture craft of massage health-care insole.
Background technique
Insole is widely used in shoe industry, health care, specifically functional；It is generally divided into the applied shoes of the applied Shoes Factory of shoe industry
Pad and marketing type both of which.The insole of shoe industry application mainly cooperates shoes outsole, indsole, makes corresponding type
Body；Size plate is made according to last carving bottom plate or panel, and produces corresponding shape.Marketing type insole is mainly insole
Directly as a kind of commodity selling, by exploitation teacher's design, the product to circulate on the market, since skin of sole of foot sweat gland is richer
Richness perspires more, causes the wet environment for being conducive to fungus growth.And footgear is worn, local environment is sultry, and foot sweat is difficult to send out
And it is moist, to be more advantageous to the growth and breeding of mould, tinea pedis is caused, insole on the market does not have deodorization and mitigates tinea pedis at present
Function, and material therefor poor ductility, elasticity is low.
Summary of the invention
The purpose of the present invention is to provide a kind of manufacture crafts of massage health-care insole, to solve to mention in above-mentioned background technique
Out the problem of.
In order to solve the above technical problem, the present invention provides following technical solutions：
A kind of manufacture craft of massage health-care insole, including step 1, the TPU examination of materials；Step 2, baking material are dry；Step 3,
Colorant is mixed in stirring；Step 4 heats injection molding；Step 5, demoulding；Step 6 repairs edge grinding shaping；Step 7 is examined；Step
Eight, packaging；In said step 1, the detection of PAHS and EN71 is carried out to TPU raw material and passed through；In the step 2, will
TPU raw material in step 1 is dried using baking oven or materal drier；In the step 3, by the TPU raw material in step 2
It is added in blender and stirs evenly with colorant；In the step 4, the mixture in step 3 is molded and is extruded into
Type includes the following steps；
1) it pre-processes：Plastic injection molded barrel temperature is increased to 300-350 DEG C, first goes over plastic injection molded barrel with PC true qualities, then with PE by plastic injection molded barrel
In remaining PC expected completely, plastic injection molded barrel then to be cooled to temperature required for TPU, cross plastic injection molded barrel with TPU；
2) raw material is heated:During the heating raw material by the way of progressive solution, i.e., heated using three-level, it first will be former
Material be slowly heated to 200-250 DEG C so that TPU and colorant sufficiently melt it is crosslinked together；After constant temperature 0.5-1h, temperature is heated up
It is filled with inert gas to 300-350 DEG C, while into the heating container of raw material, is then maintained the temperature within the scope of 300-350 DEG C,
Nano silver particles and active carbon powder are sprayed into raw material, after stirring, are cooled to 250-300 DEG C of heat preservation 0.5-1h, then
It is squeezed out to molding process；
3) it squeezes out to mold；
4) it is cooled and shaped：The insole of cooling and shaping includes insole body, on the insole body integrally formed with human body sole
The corresponding massage column in acupuncture point and massage convex point.
In the step 5, model after cooling is demoulded；
In the step 6, carry out insole prototype obtained in step 5 to repair edge grinding shaping.
The nano silver particles and active carbon powder additional amount account for the 0.5-1% of TPU total amount.
PAHS refers to the inspection of polycyclic aromatic hydrocarbon in the step 1, and EN71 refers to the inspection of content of beary metal.
The temperature of baking oven or materal drier is 100-110 DEG C in the step 2, drying time 2-3h.
Mixing time is no less than 0.5h in the step 3.
Mixture forming temperature is 170-230 DEG C in the step 4, and mould temperature is 20-40 DEG C, back pressure 0.3-4MPA, Luo
Bar revolving speed 30-75r/min, injection time 6-15s, pressure maintaining is in 5-10s, cooling 20-60s.
Compared with prior art, the beneficial effects obtained by the present invention are as follows being：The health insoles manufacture craft, use TPU for
The main material of insole, flexibility is good, and elasticity is high, and ductility is good, while injection nano silver and active powdered carbon in TPU material
End, nano silver and active carbon inject during melt, can not only be modified to TPU, have enhancing insole tensile strength
With elastic effect, and nano silver particles and active carbon powder can also be made to be crosslinked in TPU material, be squeezed out by mold
After forming insole, nano silver particles and active carbon powder uniform adsorption are in the surface of insole and the table of massage column and massage convex point
Face, not only acts as the effect of antibiotic health, but also enhances being connected firmly between massage column and massage convex point and insole body
Property, it is not fallen off after long.Thus simultaneously, the massage column of insole obtained and the elasticity of massage convex point are preferable through this process,
And it is soft, good to human body sole massage comfort, after using long, resilience is able to maintain as before.
Detailed description of the invention
Fig. 1 is the structural schematic diagram for the massage health-care insole that the present invention makes.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
A kind of manufacture craft of massage health-care insole, including step 1, the TPU examination of materials；Step 2, baking material are dry；Step
Rapid three, colorant is mixed in stirring；Step 4 heats injection molding；Step 5, demoulding；Step 6 repairs edge grinding shaping；Step 7, inspection
It tests；Step 8, packaging；In said step 1, the detection of PAHS and EN71 is carried out to TPU raw material and passed through；In the step
In two, the TPU raw material in step 1 is dried using baking oven or materal drier；It, will be in step 2 in the step 3
TPU raw material and colorant, which are added in blender, to stir evenly；In the step 4, the mixture in step 3 is molded simultaneously
Extrusion molding includes the following steps；1) it pre-processes：Plastic injection molded barrel temperature is increased to 300-350 DEG C, first goes over injection molding with PC true qualities
Bucket, then expected PC remaining in plastic injection molded barrel with PE completely, plastic injection molded barrel then to be cooled to temperature required for TPU, with TPU mistake
Plastic injection molded barrel once；2) raw material is heated:During the heating raw material by the way of progressive solution, i.e., heated using three-level, it is first
Raw material is first slowly heated to 200-250 DEG C so that TPU and colorant sufficiently melt it is crosslinked together；It, will be warm after constant temperature 0.5-1h
Degree is warming up to 300-350 DEG C, while being filled with inert gas into the heating container of raw material, then maintains the temperature at 300-350 DEG C
In range, nano silver particles and active carbon powder are sprayed into raw material, after stirring, are cooled to 250-300 DEG C of heat preservation 0.5-
Then 1h is squeezed out to molding process.3) it squeezes out to mold；4) it is cooled and shaped.
In the step 5, model after cooling is demoulded；
In the step 6, insole prototype obtained in step 5 is carried out to repair edge grinding shaping, insole obtained includes insole
Ontology, integrally formed with massage column corresponding with human body sole acupuncture point and massage convex point on the insole body（Such as China
Patent CN108113118A）.
The nano silver particles and active carbon powder additional amount account for the 0.5-1% of TPU total amount.
PAHS refers to the inspection of polycyclic aromatic hydrocarbon in the step 1, and EN71 refers to the inspection of content of beary metal.
The temperature of baking oven or materal drier is 100-110 DEG C in the step 2, drying time 2-3h.
Mixing time is no less than 0.5h in the step 3.
Mixture forming temperature is 170-230 DEG C in the step 4, and mould temperature is 20-40 DEG C, back pressure 0.3-4MPA, Luo
Bar revolving speed 30-75r/min, injection time 6-15s, pressure maintaining is in 5-10s, cooling 20-60s.
The health insoles manufacture craft, uses TPU for the main material of insole, and flexibility is good, and elasticity is high, and ductility
It is good, while injection nano silver and active carbon powder, nano silver and active carbon inject during melt in TPU material, it can not only
It is enough that TPU is modified, there is enhancing insole tensile strength and elastic effect, and nano silver particles and work can also be made
Property carbon powder crosslinking in TPU material, after mold is extruded into insole, nano silver particles and active carbon powder uniform adsorption
On the surface of insole and the surface of massage column and massage convex point, the effect of antibiotic health is not only acted as, but also enhances massage
Connectivity robustness between column and massage convex point and insole body is not fallen off after long.Thus simultaneously, obtained through this process
Insole（As shown in Figure 1）Massage column and massage convex point elasticity preferably, and it is soft, it is good to human body sole massage comfort,
After using long, resilience is able to maintain as before.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (8)
1. a kind of manufacture craft of massage health-care insole, including step 1, the TPU examination of materials；Step 2, baking material are dry；Step
Three, colorant is mixed in stirring；Step 4 heats injection molding；Step 5, demoulding；Step 6 repairs edge grinding shaping；Step 7 is examined；
Step 8, packaging；It is characterized in that：
In said step 1, the detection of PAHS and EN71 is carried out to TPU raw material and passed through；
In the step 2, the TPU raw material in step 1 is dried using baking oven or materal drier；
In the step 3, it will be stirred evenly in the TPU raw material and colorant addition blender in step 2；
In the step 4, the mixture in step 3 be molded simultaneously extrusion molding, is included the following steps；
Pretreatment：Plastic injection molded barrel temperature is increased to 300-350 DEG C, first goes over plastic injection molded barrel with PC true qualities, then will be in plastic injection molded barrel with PE
Remaining PC expected completely, plastic injection molded barrel then to be cooled to temperature required for TPU, crossed plastic injection molded barrel with TPU；
Heat raw material；
It squeezes out to mold；
It is cooled and shaped；
In the step 5, model after cooling is demoulded；
In the step 6, carry out insole prototype obtained in step 5 to repair edge grinding shaping.
2. a kind of manufacture craft of massage health-care insole according to claim 1, it is characterised in that：The heating raw material mistake
In journey by the way of progressive solution, i.e., using three-level heat, raw material is slowly heated to 200-250 DEG C first so that TPU and
Colorant sufficiently melts crosslinked together；After constant temperature 0.5-1h, temperature is warming up to 300-350 DEG C, while holding to the heating of raw material
It is filled with inert gas in device, then maintains the temperature within the scope of 300-350 DEG C, nano silver particles and active carbon are sprayed into raw material
Powder is cooled to 250-300 DEG C of heat preservation 0.5-1h, is then squeezed out to molding process after stirring.
3. a kind of manufacture craft of massage health-care insole according to claim 2, it is characterised in that：The nano silver particles
The 0.5-1% of TPU total amount is accounted for active carbon powder additional amount.
4. a kind of manufacture craft of massage health-care insole according to claim 1, it is characterised in that：The cooling and shaping
Insole includes insole body, integrally formed with massage column corresponding with human body sole acupuncture point and massage on the insole body
Salient point.
5. a kind of manufacture craft of massage health-care insole according to claim 1, it is characterised in that：In the step 1
PAHS refers to the inspection of polycyclic aromatic hydrocarbon, and EN71 refers to the inspection of content of beary metal.
6. a kind of manufacture craft of massage health-care insole according to claim 1, it is characterised in that：It is dried in the step 2
The temperature of case or materal drier is 100-110 DEG C, drying time 2-3h.
7. a kind of manufacture craft of massage health-care insole according to claim 1, it is characterised in that：It is stirred in the step 3
Mixing the time is no less than 0.5h.
8. a kind of manufacture craft of massage health-care insole according to claim 1, it is characterised in that：It is mixed in the step 4
Closing object forming temperature is 170-230 DEG C, and mould temperature is 20-40 DEG C, back pressure 0.3-4MPA, Luo bar revolving speed 30-75r/min, injection
Time 6-15s, pressure maintaining is in 5-10s, cooling 20-60s.