CN108797227A - A kind of new type of paper and its manufacturing method - Google Patents
A kind of new type of paper and its manufacturing method Download PDFInfo
- Publication number
- CN108797227A CN108797227A CN201810378378.3A CN201810378378A CN108797227A CN 108797227 A CN108797227 A CN 108797227A CN 201810378378 A CN201810378378 A CN 201810378378A CN 108797227 A CN108797227 A CN 108797227A
- Authority
- CN
- China
- Prior art keywords
- paper
- new type
- parts
- fluorescent powder
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of new type of paper, the manufacture material of the new type of paper includes paper pulp, fluorescent powder, adhesive, diluent, activating agent and curing agent, and the mass fraction of the new type of paper manufacture material is 100-120 parts of paper pulp, 8-10 parts of fluorescent powder, 1-2 parts of adhesive, 2-3 parts of diluent, 1-2 parts of activating agent, 0.5-0.8 parts of curing agent.The present invention uses traditional paper technique processed, and new type of paper in the present invention can be made to be convenient for volume production, and is used and visual effect with different when the fluorescent powder being wherein added can be such that paper uses.
Description
Technical field
The present invention relates to paper manufacturing technology field, specially a kind of new type of paper and its manufacturing method.
Background technology
Paper, (paper is the thin slice made of plant fiber to the general name of paper, can be used to write, draws a picture, prints title book, packaging
Deng), it is one of printing elemental, generally divides letterpress paper, newsprint, offset printing paper, art paper, paper for covering books, word
Allusion quotation paper, copy paper, paperboard etc. appropriately reasonably select and use paper, for ensureing the quality of publication and reducing publication
Cost be of great significance to.
Invention content
The purpose of the present invention is to provide a kind of new type of paper and its manufacturing methods.
To achieve the above object, the present invention provides the following technical solutions：A kind of new type of paper, the manufacture of the new type of paper
Material includes paper pulp, fluorescent powder, adhesive, diluent, activating agent and curing agent, the mass parts of the new type of paper manufacture material
Number is 100-120 parts of paper pulp, 8-10 parts of fluorescent powder, 1-2 parts of adhesive, 2-3 parts of diluent, 1-2 parts of activating agent, curing agent 0.5-
0.8 part.
A kind of manufacturing method of new type of paper, a kind of manufacturing method of new type of paper include the following steps：
(1) material weighs：Weigh paper pulp, fluorescent powder, adhesive, diluent, activating agent and the solidification of certain mass number
Agent is spare；
(2) pretreatment：The paper pulp of constant weight number is taken to be put into the inside of agitator, mixing time 15-
20min, whipping temp are 60-65 DEG C；
(3) product mix：The fluorescent powder, dilute of constant weight number is added in paper pulp after being completed to step (2) processing
It releases agent and activating agent and is stirred；
(4) cure：The spare curing agent of step (1) is added in product after being completed to step (3) mixing, and curing agent is added
It is stirred mixing later, whipping temp is 25-28 DEG C；
(5) paper processed：Product after the completion of step (2) is cured carries out tiling paper processed, paper thickness processed according to product demand into
Row control；
(6) it dries：The paper that step (5) is completed carries out drying and processing, and drying temperature is 60-65 DEG C, when drying
Between be 7-8min；
(7) cooling treatment：The paper that step (6) drying is completed is subjected to cooling treatment, cooling time, 5-8min, cooling
Temperature is 10-15 DEG C, and cooling treatment can be obtained a kind of new type of paper after completing.
The present invention uses traditional paper technique processed, the new type of paper in the present invention can be made to be convenient for volume production, and wherein add
It is used and visual effect with different when the fluorescent powder entered can be such that paper uses.
Specific implementation mode
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is only
It is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill people
The every other embodiment that member is obtained without making creative work, shall fall within the protection scope of the present invention.
Embodiment one：
The manufacture material of a kind of new type of paper, the new type of paper includes paper pulp, fluorescent powder, adhesive, diluent, activity
The mass fraction of agent and curing agent, the new type of paper manufacture material is 100 parts of paper pulp, 8 parts of fluorescent powder, 1 part of adhesive, dilution
2 parts of agent, 1 part of activating agent, 0.5 part of curing agent.
A kind of manufacturing method of new type of paper, a kind of manufacturing method of new type of paper include the following steps：
(1) material weighs：Weigh paper pulp, fluorescent powder, adhesive, diluent, activating agent and the solidification of certain mass number
Agent is spare；
(2) pretreatment：The paper pulp of constant weight number is taken to be put into the inside of agitator, mixing time 15min is stirred
It is 60 DEG C to mix temperature；
(3) product mix：The fluorescent powder, dilute of constant weight number is added in paper pulp after being completed to step (2) processing
It releases agent and activating agent and is stirred；
(4) cure：The spare curing agent of step (1) is added in product after being completed to step (3) mixing, and curing agent is added
It is stirred mixing later, whipping temp is 25 DEG C；
(5) paper processed：Product after the completion of step (2) is cured carries out tiling paper processed, paper thickness processed according to product demand into
Row control；
(6) it dries：The paper that step (5) is completed carries out drying and processing, and drying temperature is 60 DEG C, and drying time is
7min；
(7) cooling treatment：The paper that step (6) drying is completed is subjected to cooling treatment, cooling time, 5min, cooling warm
Degree is 10 DEG C, and cooling treatment can be obtained a kind of new type of paper after completing.
Embodiment two：
The manufacture material of a kind of new type of paper, the new type of paper includes paper pulp, fluorescent powder, adhesive, diluent, activity
Agent and curing agent, the mass fraction of the new type of paper manufacture material is 120 parts of paper pulp, 10 parts of fluorescent powder, 2 parts of adhesive, dilute
Release 3 parts of agent, 2 parts of activating agent, 0.8 part of curing agent.
A kind of manufacturing method of new type of paper, a kind of manufacturing method of new type of paper include the following steps：
(1) material weighs：Weigh paper pulp, fluorescent powder, adhesive, diluent, activating agent and the solidification of certain mass number
Agent is spare；
(2) pretreatment：The paper pulp of constant weight number is taken to be put into the inside of agitator, mixing time 20min is stirred
It is 65 DEG C to mix temperature；
(3) product mix：The fluorescent powder, dilute of constant weight number is added in paper pulp after being completed to step (2) processing
It releases agent and activating agent and is stirred；
(4) cure：The spare curing agent of step (1) is added in product after being completed to step (3) mixing, and curing agent is added
It is stirred mixing later, whipping temp is 28 DEG C；
(5) paper processed：Product after the completion of step (2) is cured carries out tiling paper processed, paper thickness processed according to product demand into
Row control；
(6) it dries：The paper that step (5) is completed carries out drying and processing, and drying temperature is 65 DEG C, and drying time is
8min；
(7) cooling treatment：The paper that step (6) drying is completed is subjected to cooling treatment, cooling time, 8min, cooling warm
Degree is 15 DEG C, and cooling treatment can be obtained a kind of new type of paper after completing.
Embodiment three：
The manufacture material of a kind of new type of paper, the new type of paper includes paper pulp, fluorescent powder, adhesive, diluent, activity
Agent and curing agent, the mass fraction of the new type of paper manufacture material is 110 parts of paper pulp, 9 parts of fluorescent powder, 1.5 parts of adhesive, dilute
Release 2.5 parts of agent, 1.5 parts of activating agent, 0.7 part of curing agent.
A kind of manufacturing method of new type of paper, a kind of manufacturing method of new type of paper include the following steps：
(1) material weighs：Weigh paper pulp, fluorescent powder, adhesive, diluent, activating agent and the solidification of certain mass number
Agent is spare；
(2) pretreatment：The paper pulp of constant weight number is taken to be put into the inside of agitator, mixing time 18min is stirred
It is 62 DEG C to mix temperature；
(3) product mix：The fluorescent powder, dilute of constant weight number is added in paper pulp after being completed to step (2) processing
It releases agent and activating agent and is stirred；
(4) cure：The spare curing agent of step (1) is added in product after being completed to step (3) mixing, and curing agent is added
It is stirred mixing later, whipping temp is 27 DEG C；
(5) paper processed：Product after the completion of step (2) is cured carries out tiling paper processed, paper thickness processed according to product demand into
Row control；
(6) it dries：The paper that step (5) is completed carries out drying and processing, and drying temperature is 63 DEG C, and drying time is
7.5min；
(7) cooling treatment：The paper that step (6) drying is completed is subjected to cooling treatment, cooling time, 6min, cooling warm
Degree is 13 DEG C, and cooling treatment can be obtained a kind of new type of paper after completing.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (2)
1. a kind of new type of paper, it is characterised in that：The manufacture material of the new type of paper includes paper pulp, fluorescent powder, adhesive, dilute
Agent, activating agent and curing agent are released, the mass fraction of the new type of paper manufacture material is 100-120 parts of paper pulp, fluorescent powder 8-10
Part, 1-2 parts of adhesive, 2-3 parts of diluent, 1-2 parts of activating agent, 0.5-0.8 parts of curing agent.
2. a kind of manufacturing method of new type of paper, it is characterised in that：A kind of manufacturing method of new type of paper includes following step
Suddenly：
(1) material weighs：Paper pulp, fluorescent powder, adhesive, diluent, activating agent and the curing agent for weighing certain mass number are standby
With；
(2) pretreatment：The paper pulp of constant weight number is taken to be put into the inside of agitator, mixing time 15-20min is stirred
It is 60-65 DEG C to mix temperature；
(3) product mix：Fluorescent powder, the diluent of constant weight number are added in paper pulp after being completed to step (2) processing
With activating agent and be stirred；
(4) cure：The spare curing agent of step (1) is added in product after being completed to step (3) mixing, after curing agent is added
It is stirred mixing, whipping temp is 25-28 DEG C；
(5) paper processed：Product after the completion of step (2) is cured carries out tiling paper processed, and paper thickness processed is controlled according to product demand
System；
(6) it dries：The paper that step (5) is completed carries out drying and processing, and drying temperature is 60-65 DEG C, and drying time is
7-8min；
(7) cooling treatment：By step (6) drying complete paper carry out cooling treatment, cooling time 5-8min, cooling temperature
It it is 10-15 DEG C, cooling treatment can be obtained a kind of new type of paper after completing.