CN108796300A - One kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon - Google Patents
One kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon Download PDFInfo
- Publication number
- CN108796300A CN108796300A CN201810759533.6A CN201810759533A CN108796300A CN 108796300 A CN108796300 A CN 108796300A CN 201810759533 A CN201810759533 A CN 201810759533A CN 108796300 A CN108796300 A CN 108796300A
- Authority
- CN
- China
- Prior art keywords
- alloy
- rose
- temperature
- billon
- elastic modulus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Having high elastic modulus the invention discloses one kind and corrosion resistant 18K rose golds imitate billon.According to weight percent, the ingredient of the alloy is:Ca:0.6-0.8wt.%,In:1.0-1.5wt.%,Cr:0.2-0.5wt.%,Mo:1.0-1.4wt.%,Sm:0.2-0.4wt.%,Co:2.0-2.5wt.%,Zn:8.0-10.0wt.%,Cu:35.0-40.0wt.%, surplus are tin.The patent is providing a kind of imitative billon for the rose gold replacement having extremely excellent properties simultaneously, has also greatly enriched the type of jewellery in the market and decorative material material.
Description
Technical field
The present invention relates to technical field of alloy, specifically, being related to a kind of imitative billon.
Background technology
Rose gold is after sparkling gold ornament with classical graceful platinum ornaments, the soft charming rose of tone
Gold ornaments gradually become the new lover of fashion personage.The rose gold of pink colour not only signifies love, more contains warm meaningful feelings
Sincere feeling deduces the another brand-new world of precious metal jewelry.In general, gold and other composition of alloy of the rose gold by 75%.Hardness
Compared with proof gold height, compared with traditional gold and platinum, pink rose gold not only can make the color of colored gemstone denser,
Exquisiteness, the exquisiteness of metal material is also presented.The warm tones such as its pink, rose bring it is warm with it is happy;On style
It is also in different poses and with different expressions, there is pointed heart, olive, oval, pyriform, Emerald.The ornaments of various different styles are bright credit
Eye, women either business wear or evening dress and suspender skirt, match all show graceful makings therewith.
Why rose gold ornaments receives an acclaim, and is because they are modish better than proof gold jewellery style in many aspects.Rose
Rare gold utensil has the wearability that higher hardness becomes reconciled, corrosion resistance, is unlikely to deform and the characteristics such as good castability.Due to golden hard
The raising of degree promotes the fast development of jewellery industry, also changes originally backward processing technology, can be added with mass production
The material inlayed is synthesized using high-tech, is reached and natural high-grade true and false difficult point of the degree of product.Therefore, alloy inlays material with difference
The combination of material keeps the style of karat gold jewellery more rich and varied, up to tens of thousands of kinds, ten tens of thousands of kinds, its novelty, aesthetic feeling is complete
It entirely can be with times.
The bullion consumption in China is developed so far from early 1980s, from the early stage of development to buy based on ornaments,
Focus on value preserving effect, but style, style changes little, kind are dull.The rose gold ornaments till now that develops starts largely to appear on the market, and
And growth momentum is swift and violent.Apparent can see, and the consumption idea of people pursues personalization by focusing on being worth turning to, and is particular about head
The style of decorations, technique are particular about jewellery and itself individual character, the matching of dress.Karat gold jewellery are since style is modish, various colors, price
Low, diversification, personalization style meet consumer demand, and therefore it is also continued to develop.
Gold serves many purposes in national economy, but price of gold costliness and resource scarcity.In decoration material field,
Countries in the world just strive to find its substitute material from different perspectives.People often will replace gold material, referred to as it is artificial gold or
Imitation gold copper-base alloy.Imitation gold copper-base alloy be free from gold but with karat gold color and luster multicomponent alloy, usually have with 18K gold utensils similar quite color,
Good anti-tarnishing ability, casting, processing and polishing performance.It is liked by people for Jewelry Accessories and artistic article depth
Love.In recent years, rose golden is splendid with its, magnificent pleasing feature becomes fashionable Inter colour so that state
The development and production of inside and outside imitation gold copper-base alloy rapidly develop, and product involves the indoor dress sulphur, architectural hardware, technique of important building
Product and tourist souvenir etc..With the development of China's economic situation, the gradually improvement and continuous improvement of people's lives, to imitative gold
The requirement of product, will be potential new application prospect.
But regrettably, although jewellery and trim-alloy currently on the market can pass through the method for ion plating
On its surface, plating last layer has roseate TiCN coating.But such coating does not have excellent anti-corrosion capability.?
Fallen off using coating will occur after some months, coating color, coating fade the phenomenon that.Not only affect the sight of such material
Sense, also seriously reduces the market sales volume and the marketing of such material.
Although the absolute number of China's jewelry and decoration industry industry in quantity and yield is larger, scope of the enterprise is small,
Core competitiveness is not strong.In evolution, jewelry enterprise is not created during productive accumulation usually as processor
Newly, the characteristic of oneself is formed out.For a long time, most domestic jewelry enterprise all rests on the OEM forms of order processing,
Using the production line of oneself, the product of oneself is produced, finally but sticks other people brand.Even some larger enterprises,
Jewellery and the critical material of trim-alloy production but almost rely on import, in terms of Novel decoration material development almost
Blank out.Therefore, research and development and industrialization high-performance have the imitation gold copper-base alloy and its system for having rose gold of independent intellectual property right
Standby technology, the competitiveness for enhancing China's jewelry and decoration industry will have the function of very positive.
Invention content
The purpose of the present invention is to overcome the deficiency in the prior art, provides one kind and having high elastic modulus and corrosion resistant 18K
Rose gold imitates billon.
To achieve the goals above, the present invention adopts the following technical scheme that:
One kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon.By weight percentage, the composition of alloy
For: Ca:0.6-0.8wt.%,In:1.0-1.5wt.%,Cr:0.2-0.5wt.%,Mo:1.0-1.4wt.%,Sm:0.2-
0.4wt.%,Co:2.0-2.5wt.%,Zn:8.0-10.0wt.%,Cu:35.0-40.0wt.%, surplus are tin.
A kind of above-mentioned preparation method having high elastic modulus and the imitative billon of corrosion resistant 18K rose golds, including it is as follows
Step:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;It is used after metal molten
The argon gas of low discharge is protected, and big air-flow is avoided to make the serious scaling loss of alloying element;10 minutes are kept the temperature at 1250 degree when melting, by height
Frequency induction furnace electromagnetic agitation is uniform;1 minute being kept the temperature at 1250 degree after stirring evenly and being cast come out of the stove;Alloy casting uses diameter
The punching block of 100-200mm, and cooled down by the way of water cooling.The ingot casting of gained is rolled at room temperature, under every time is rolled
Amount is 20-30%;It is 620 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Material, which is finally rolled into thickness, is
The alloy sheets of 10-15mm;In forming process, needs to carry out intermediate annealing process, eliminate the stress in process;Wherein,
Homogenization temperature is 400 degree, and the time is 2-3 hours.
Compared with prior art, the present invention has the advantages that:
(1)There are the imitation gold copper-base alloy development for being dedicated to having rose gold and miniaturization production currently on the market, has also there is production in addition
Product plate last layer TiCN layer come so that surface has rose color and luster by the method for ion plating in material surface.But these materials
It does not have at present in atmospheric conditions and uses color stability constant in artificial sweat environment, and have both good processing
Property, wearability, weldability.As above in order to solve the problems, such as, this patent tries hard to be closed with rose instead of jewellery using cheap metal alloy
Gold, and carried out innovative development and industrialization work.
(2)It crosses and alloying component is screened from the angle of electrochemistry, the alloying element of selection can be in material surface shape
At passivating film, to play the role of protection to the corrosion of ambient enviroment.Secondly, alloying element is compared to price for noble metal
It is cheap, it is resourceful.Third, in order to improve corrosion stability and processability, the number of phases of alloying element and the matrix element formation of selection
Amount will be lacked, and whole phase content will level off to single matrix phase.Finally, the jewellery of preparation or the most important of decoration are asked
Topic is the anti-discoloration improved in atmospheric conditions and its in use environment.This patent is exactly to be adopted under these harsh requirements
With the method for orthogonal design come to alloying element selection and addition to the color and luster of alloy, corrosion-resistant behavior, processability
Influence optimize, so that it is determined that the screening of alloying element and the determination of its ingredient.
(3)Alloy good casting property can be cast into imitative golden casting or imitative metal type.Its natural in color is true to nature, technique
It is easy to operate, it is easily mastered, it is of low cost.The crystallization range of the alloy is narrow, has good mobility, is formed transgranular inclined
Analysis and loose tendency are small.In addition, the alloy has the body contraction and linear shrinkage of very little, linear shrinkage ratio 0.1%, it is not easy to shape
At concentrating shrinkage cavity.The alloy will not generate the flowing that more oxide inclusion hinders alloy in fusion process, cause casting
Surface Wrinkle in iron and scab defects.Due to having carried out optimizing components in crystal boundary and transgranular low melting point element will not occur for the material
In the case of enrichment, intercrystalline corrosion tendency will not be promoted to increase.The alloy is meeting the requirement to tensile strength and case hardness
Under, also there is extremely excellent elastic property.The yield strength of the material is 200-230MPa, tensile strength 350-
390MPa, elongation percentage 20-30%, elasticity modulus 180-190GPa.These excellent performances allow the alloy extensive
Production for aciculiform object and spring object.
(4)Material has the same color and luster of rose gold and appearance.Under the light of standard sources D65, and use CM-700d
Type spectrophotometric color measurement instrument (Japanese Konica Minolta) measures the brightness value L of its color*, green angle value a*With champac chromatic value b*.It is right
For traditional rose gold, L*, a*With b*Respectively 84.0,11.0 and 16.0, and these parameters of this material are respectively 82.5,
11.6 with 15.4.The thus visual effect of product and the aberration unobvious of rose gold have very excellent decorative effect.
(5)The aerial corrosion resistance of the material belongs to compared with stabilizing material, belongs to stable proximate matter in weak acid, weak base sweat
Material, corrosion resistance is by being added the higher alloying element of thermodynamic stability, in corrosive environment, can form the protective film of passivation,
This film is in different media, since unpolarizing is as a result, to show different corrosion resistances.The alloy
Discoloration-resisting can evaluate its corrosion resistance by synthetic perspiration's experiment.Experimental period is 60hr, and (60hr is placed to sweat
The variation of front and back alloy measuring alloy color is impregnated afterwards).The result shows that the alloy, after sweat corrosion test, surface is not
Have and decolourize, fade or surface generate corrosion pit the phenomenon that.In comparison, the rose gold plate used at present is using
Just there is a phenomenon where change colour and fall off after 6 months.The alloy after daily wearing, surface do not occur apparent corrosion phenomenon or
Person's surface scratch occurs, and the ability with good artificial perspiration resistance's corrosion.It is contemplated that the implementation and industrialization of the material
Excellent economic benefit and social benefit will be obtained.
Specific implementation mode
Embodiment 1
One kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon.By weight percentage, the composition of alloy
For: Ca:0.6wt.%,In:1.0wt.%,Cr:0.2wt.%,Mo:1.0wt.%,Sm:0.2wt.%,Co:2.0wt.%,Zn:
8.0wt.%,Cu:35.0wt.%, surplus are tin.Above-mentioned one kind having high elastic modulus and the imitative gold of corrosion resistant 18K rose golds closes
Golden preparation method, includes the following steps:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite
Crucible;It is protected using the argon gas of low discharge after metal molten, big air-flow is avoided to make the serious scaling loss of alloying element;When melting
1250 degree keep the temperature 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1250 degree after stirring evenly and being poured cast out
Stove;Alloy casting uses the punching block of diameter 100-200mm, and is cooled down by the way of water cooling.At room temperature by the ingot casting of gained
It is rolled, it is 20-30% that every time, which rolls lower amount,;It is 620 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Most
Material is rolled into the alloy sheets that thickness is 10-15mm afterwards;In forming process, needs to carry out intermediate annealing process, eliminate and add
Stress during work;Wherein, homogenization temperature is 400 degree, and the time is 2-3 hours.
The alloy good casting property can be cast into imitative golden casting or imitative metal type.Crystallization range is narrow, has good
Good mobility, forms microsegregation and loose tendency is small.The material is due to having carried out optimizing components, in crystal boundary and transgranular
In the case of low melting point element enrichment will not occur, intercrystalline corrosion tendency will not be promoted to increase.The material has rose gold same
Color and luster and appearance.The thus visual effect of product and the aberration unobvious of rose gold have very excellent decorative effect.It should
Alloy also has extremely excellent elastic property in the case where meeting the requirement to tensile strength and case hardness.The surrender of the material
Intensity is 200-230MPa, tensile strength 350-390MPa, elongation percentage 20-30%, elasticity modulus 180-190GPa.This
A little excellent performances allow the production that the alloy is widely used in aciculiform object and spring object.The alloy is rotten by sweat
The phenomenon that after corrosion test, surface is not decolourized, and colour fading or surface generate corrosion pit.In comparison, it uses at present
Rose gold plate after using 6 months just occur discoloration and fall off.The alloy after daily wearing, do not send out by surface
Raw apparent corrosion phenomenon or surface scratch occur, and the ability with good artificial perspiration resistance's corrosion.
Embodiment 2
One kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon.By weight percentage, the composition of alloy
For: Ca:0.8wt.%,In:1.5wt.%,Cr:0.5wt.%,Mo:1.4wt.%,Sm:0.4wt.%,Co:2.5wt.%,Zn:
10.0wt.%,Cu:40.0wt.%, surplus are tin.Above-mentioned one kind having high elastic modulus and the imitative gold of corrosion resistant 18K rose golds closes
Golden preparation method, includes the following steps:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite
Crucible;It is protected using the argon gas of low discharge after metal molten, big air-flow is avoided to make the serious scaling loss of alloying element;When melting
1250 degree keep the temperature 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1250 degree after stirring evenly and being poured cast out
Stove;Alloy casting uses the punching block of diameter 100-200mm, and is cooled down by the way of water cooling.At room temperature by the ingot casting of gained
It is rolled, it is 20-30% that every time, which rolls lower amount,;It is 620 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Most
Material is rolled into the alloy sheets that thickness is 10-15mm afterwards;In forming process, needs to carry out intermediate annealing process, eliminate and add
Stress during work;Wherein, homogenization temperature is 400 degree, and the time is 2-3 hours.
The alloy good casting property can be cast into imitative golden casting or imitative metal type.Crystallization range is narrow, has good
Good mobility, forms microsegregation and loose tendency is small.The material is due to having carried out optimizing components, in crystal boundary and transgranular
In the case of low melting point element enrichment will not occur, intercrystalline corrosion tendency will not be promoted to increase.The material has rose gold same
Color and luster and appearance.The thus visual effect of product and the aberration unobvious of rose gold have very excellent decorative effect.It should
Alloy also has extremely excellent elastic property in the case where meeting the requirement to tensile strength and case hardness.The surrender of the material
Intensity is 200-230MPa, tensile strength 350-390MPa, elongation percentage 20-30%, elasticity modulus 180-190GPa.This
A little excellent performances allow the production that the alloy is widely used in aciculiform object and spring object.The alloy is rotten by sweat
The phenomenon that after corrosion test, surface is not decolourized, and colour fading or surface generate corrosion pit.In comparison, it uses at present
Rose gold plate after using 6 months just occur discoloration and fall off.The alloy after daily wearing, do not send out by surface
Raw apparent corrosion phenomenon or surface scratch occur, and the ability with good artificial perspiration resistance's corrosion.
Embodiment 3
One kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon.By weight percentage, the composition of alloy
For: Ca:0.7wt.%,In:1.2wt.%,Cr:0.4wt.%,Mo:1.2wt.%,Sm:0.3wt.%,Co:2.4wt.%,Zn:
9.0wt.%,Cu:36.0wt.%, surplus are tin.Above-mentioned one kind having high elastic modulus and the imitative gold of corrosion resistant 18K rose golds closes
Golden preparation method, includes the following steps:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite
Crucible;It is protected using the argon gas of low discharge after metal molten, big air-flow is avoided to make the serious scaling loss of alloying element;When melting
1250 degree keep the temperature 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1250 degree after stirring evenly and being poured cast out
Stove;Alloy casting uses the punching block of diameter 100-200mm, and is cooled down by the way of water cooling.At room temperature by the ingot casting of gained
It is rolled, it is 20-30% that every time, which rolls lower amount,;It is 620 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Most
Material is rolled into the alloy sheets that thickness is 10-15mm afterwards;In forming process, needs to carry out intermediate annealing process, eliminate and add
Stress during work;Wherein, homogenization temperature is 400 degree, and the time is 2-3 hours.
The alloy good casting property can be cast into imitative golden casting or imitative metal type.Crystallization range is narrow, has good
Good mobility, forms microsegregation and loose tendency is small.The material is due to having carried out optimizing components, in crystal boundary and transgranular
In the case of low melting point element enrichment will not occur, intercrystalline corrosion tendency will not be promoted to increase.The material has rose gold same
Color and luster and appearance.The thus visual effect of product and the aberration unobvious of rose gold have very excellent decorative effect.It should
Alloy also has extremely excellent elastic property in the case where meeting the requirement to tensile strength and case hardness.The surrender of the material
Intensity is 200-230MPa, tensile strength 350-390MPa, elongation percentage 20-30%, elasticity modulus 180-190GPa.This
A little excellent performances allow the production that the alloy is widely used in aciculiform object and spring object.The alloy is rotten by sweat
The phenomenon that after corrosion test, surface is not decolourized, and colour fading or surface generate corrosion pit.In comparison, it uses at present
Rose gold plate after using 6 months just occur discoloration and fall off.The alloy after daily wearing, do not send out by surface
Raw apparent corrosion phenomenon or surface scratch occur, and the ability with good artificial perspiration resistance's corrosion.
Claims (3)
1. one kind having high elastic modulus and corrosion resistant 18K rose golds imitate billon;According to weight percent, the alloy at
It is divided into:Ca:0.6-0.8wt.%,In:1.0-1.5wt.%,Cr:0.2-0.5wt.%,Mo:1.0-1.4wt.%,Sm:0.2-
0.4wt.%,Co:2.0-2.5wt.%,Zn:8.0-10.0wt.%,Cu:35.0-40.0wt.%, surplus are tin.
2. one kind described in claim 1 has high elastic modulus and corrosion resistant 18K rose golds imitate billon, it is characterised in that packet
Include following smelting step:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;Metal
It is protected using the argon gas of low discharge after fusing, big air-flow is avoided to make the serious scaling loss of alloying element;It is kept the temperature at 1250 degree when melting
It is 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1250 degree after stirring evenly and being cast come out of the stove;Alloy pours
Casting uses the punching block of diameter 100-200mm, and is cooled down by the way of water cooling.
3. having high elastic modulus according to one kind described in claim 1 and corrosion resistant 18K rose golds imitating billon, it is characterised in that
Including using step as follows:The ingot casting of gained is rolled at room temperature, it is 20-30% that every time, which rolls lower amount,;It is every to roll twice
Intermediate anneal temperature is 620 degree afterwards, keeps the temperature 0.5 hour;Material is finally rolled into the alloy sheets that thickness is 10-15mm;At
During type, needs to carry out intermediate annealing process, eliminate the stress in process;Wherein, homogenization temperature is 400 degree, when
Between be 2-3 hours.