CN108795186A - A kind of modified propylene acid primer and preparation method thereof - Google Patents
A kind of modified propylene acid primer and preparation method thereof Download PDFInfo
- Publication number
- CN108795186A CN108795186A CN201810770842.3A CN201810770842A CN108795186A CN 108795186 A CN108795186 A CN 108795186A CN 201810770842 A CN201810770842 A CN 201810770842A CN 108795186 A CN108795186 A CN 108795186A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- propylene acid
- modified
- acid primer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of coatings, a kind of modified propylene acid primer and preparation method thereof is specifically disclosed, modified propylene acid primer of the invention includes the component of following parts by weight:Nano-meter CaCO33It is acrylic resin modified:40~60 parts, acetylbutyrylcellulose:10~15 parts, rust resisting pigment:5~10 parts, butyl acetate:10~15 parts, pH neutralizers:5~10 parts, initiator:1~5 part, emulsifier:1~5 part, stabilizer:1~5 part, dispersant:1~5 part, wetting agent:1~5 part, levelling agent:1~5 part, Nano-meter CaCO33:1~3 part of isopropanol:10~20 parts, deionized water:30~40 parts.The modified propylene acid primer of the present invention sees state, water resistance, self-cleaning and storage stability etc. and all improves significantly effect outside, can be obviously improved its splitting resistance and water resistance, has preferable application value.
Description
Technical field
The present invention relates to technical field of coatings, are specifically related to one kind and changing modified propylene acid primer and preparation method thereof.
Background technology
Priming paint is the first layer of paint system, for improving the adhesive force of finishing coat, the richness for increasing finishing coat, providing alkali resistant
Property, anti-corrosion function etc. is provided, while can ensure the uniform pickup of finishing coat, paint system is made to play optimum efficiency.Surface paint quality
Priming paint can not be had to well, this saying is not right, because finishing coat is different from the function of priming paint, finishing coat more lays particular emphasis on final dress
Decorations and apparent effect, and priming paint then lays particular emphasis on and improves adhesive force, anti-corrosion function, alkali resistance etc..
Priming paint refers to the coating for being directly applied to body surface as finishing coat solid foundation.It is required that the adhesion-tight on object plane,
To increase the adhesive force of upper coating, the dicoration of finishing coat is improved.It can be divided into priming coat, base coat according to coating specification
Deng.
The effect of priming paint is that:
1. closing:Some metope alkalinity are stronger, and alkali flower, scientific name " accumulation of salt in the surface soil ", such case are generated after the immersions such as damp gas and water
It causes coating surface to form crateriform protrusion, forms one layer of alkali frost in coating surface when serious, finally paint film is made to destroy.Latex
Paint priming paint can play sealing process, alleviate such case.This requires priming paint to have preferable water resistance.
2. adhesive force:Emulsion content is higher in priming paint, and adhesive force is stronger.The binding force of emulsion paint film and metope can be improved.
This requirement just needs requirement priming paint to have the performance of cracking resistance, because being had out once priming paint cracks finishing coat inevitably
The phenomenon that splitting influences the beauty of figure layer.
One layer of wash coats are brushed before brushing finish paint can not only save decoration cost, come from long-range and decorative effect
It sees, applying priming more has the advantages of getting twice the result with half the effort.Meanwhile the good adhesive force of priming paint makes metope more flatten out cunning, and finishing coat is enabled to be more easy to
It brushes, reduces the usage amount of finishing coat.Thus, which metope not only avoids paint disease, but also brushing effects are applied conducive to longer time holding.
But the scarce capacity of existing priming paint often water resistance and cracking resistance, this requires it is proposed that a kind of new bottom
It paints to improve this phenomenon.
Invention content
The purpose of the present invention is to provide a kind of modified propylene acid primers and preparation method thereof, to solve above-mentioned background technology
The problem of middle proposition, hence it is evident that the splitting resistance and water resistance for improving base coat reach preferable application value.
To achieve the above object, the present invention provides the following technical solutions:
A kind of modified propylene acid primer, includes the ingredient of following parts by weight:
Nano-meter CaCO33It is acrylic resin modified:40~60 parts, acetylbutyrylcellulose:10~15 parts, rust resisting pigment:5~
10 parts, butyl acetate:10~15 parts, pH neutralizers:5~10 parts, initiator:1~5 part, emulsifier:1~5 part, stabilizer:1
~5 parts, dispersant:1~5 part, wetting agent:1~5 part, levelling agent:1~5 part, Nano-meter CaCO33:1~3 part of isopropanol:10~20
Part, deionized water:30~40 parts.
Preferably, the modified propylene acid primer includes the ingredient of following parts by weight:Nano-meter CaCO33Modified acroleic acid tree
Fat:50~60 parts, acetylbutyrylcellulose:10~13 parts, rust resisting pigment:5~8 parts, butyl acetate:10~13 parts, pH is neutralized
Agent:5~8 parts, initiator:1~3 part, emulsifier:1~3 part, stabilizer:1~3 part, dispersant:1~3 part, wetting agent:1~3
Part, levelling agent:1~3 part, Nano-meter CaCO33:2~3 parts, isopropanol:11~15 parts, deionized water:35~40 parts.
Preferably, the modified propylene acid primer includes the ingredient of following parts by weight:Nano-meter CaCO33Modified acroleic acid tree
Fat:55 parts, acetylbutyrylcellulose:12 parts, rust resisting pigment:6 parts, butyl acetate:12 parts, pH neutralizers:6 parts, initiator:2
Part, emulsifier:2 parts, stabilizer:2 parts, dispersant:2 parts, wetting agent:2 parts, levelling agent:2 parts, Nano-meter CaCO33:2 parts, isopropyl
Alcohol:13 parts, deionized water:40 parts.
Preferably, the wetting dispersing agent is glyceryl tristearate.
Preferably, the initiator is potassium peroxydisulfate or ammonium persulfate.
Preferably, the pH neutralizers are triethylamine, 2-amino-2-methyl-1-propanol or triethanolamine.
Preferably, the emulsifier is sodium vinyl sulfonate, methallylsulfonic acid sodium or allyl hydroxypropyl azochlorosulfonate acid sodium.
Preferably, the levelling agent is fluorin modified crylic acid levelling agent or phosphate modified acrylic acid levelling agent.
Preferably, the dispersant is the mixture that polyethylene wax and polyethylene glycol are formed.
The preparation method of the modified propylene acid primer, includes the following steps:
1) each component material, is weighed by weight, and Nano-meter CaCO3 is sequentially added into reaction kettle3It is acrylic resin modified,
Acetylbutyrylcellulose, rust resisting pigment, butyl acetate, initiator, dispersant, control rotating speed is 800 revs/min, at 55 DEG C
It is stirred 20 minutes;
2) pH neutralizers, are added into reaction kettle, stir 20 minutes, and adjust pH to 7~8;
3) emulsifier, stabilizer, wetting agent, levelling agent, Nano-meter CaCO3, are sequentially added into reaction kettle3, isopropanol goes
Ionized water, control rotating speed is 600 revs/min, is stirred at 50 DEG C 40 minutes;?.
Compared with prior art, the beneficial effects of the invention are as follows:
The nano composite dope of nm level CaCO_3 is added in apparent condition, water resistance, self-cleaning and storage stability etc.
All improve significantly effect, can be obviously improved its splitting resistance and water resistance, has preferable application value.
Specific implementation mode
Example 1:
Various raw materials are taken according to following weight parts formula:Nano-meter CaCO33It is acrylic resin modified:40 parts, acetate butyrate is fine
Dimension element:10 parts, rust resisting pigment:5 parts, butyl acetate:12 parts, pH neutralizers:6 parts, initiator:1 part, emulsifier:1 part, stablize
Agent:1 part, dispersant:1 part, wetting agent:1 part, levelling agent:1 part, Nano-meter CaCO33:1 part of isopropanol:10 parts, deionized water:30
Part.
By above-mentioned formula, wetting dispersing agent is glyceryl tristearate.
By above-mentioned formula, initiator is ammonium persulfate.
By above-mentioned formula, pH neutralizers are triethylamine.
By above-mentioned formula, emulsifier is sodium vinyl sulfonate.
By above-mentioned formula, levelling agent is fluorin modified crylic acid levelling agent.
By above-mentioned formula, dispersant is the mixture that polyethylene wax and polyethylene glycol are formed.
The preparation method of the modified propylene acid primer, includes the following steps:
1) each component material, is weighed by weight, and Nano-meter CaCO3 is sequentially added into reaction kettle3It is acrylic resin modified,
Acetylbutyrylcellulose, rust resisting pigment, butyl acetate, initiator, dispersant, control rotating speed is 800 revs/min, at 55 DEG C
It is stirred 20 minutes;
2) pH neutralizers, are added into reaction kettle, stir 20 minutes, and adjust pH to 7~8;
3) emulsifier, stabilizer, wetting agent, levelling agent, Nano-meter CaCO3, are sequentially added into reaction kettle3, isopropanol goes
Ionized water, control rotating speed is 600 revs/min, is stirred at 50 DEG C 40 minutes;?.
Example 2:
Various raw materials are taken according to following weight parts formula:Nano-meter CaCO33It is acrylic resin modified:50 parts, acetate butyrate is fine
Dimension element:13 parts, rust resisting pigment:10 parts, butyl acetate:10 parts, pH neutralizers:8 parts, initiator:3 parts, emulsifier:3 parts, stablize
Agent:4 parts, dispersant:4 parts, wetting agent:3 parts, levelling agent:4 parts, Nano-meter CaCO33:2.5 parts, isopropanol:10 parts, deionized water:
40 parts.
By above-mentioned formula, wetting dispersing agent is glyceryl tristearate.
By above-mentioned formula, initiator is potassium peroxydisulfate.
By above-mentioned formula, pH neutralizers are 2-amino-2-methyl-1-propanol.
By above-mentioned formula, emulsifier is methallylsulfonic acid sodium.
By above-mentioned formula, levelling agent is fluorin modified crylic acid levelling agent.
By above-mentioned formula, dispersant is the mixture that polyethylene wax and polyethylene glycol are formed.
The preparation method of the modified propylene acid primer, includes the following steps:
1) each component material, is weighed by weight, and Nano-meter CaCO3 is sequentially added into reaction kettle3It is acrylic resin modified,
Acetylbutyrylcellulose, rust resisting pigment, butyl acetate, initiator, dispersant, control rotating speed is 800 revs/min, at 55 DEG C
It is stirred 20 minutes;
2) pH neutralizers, are added into reaction kettle, stir 20 minutes, and adjust pH to 7~8;
3) emulsifier, stabilizer, wetting agent, levelling agent, Nano-meter CaCO3, are sequentially added into reaction kettle3, isopropanol goes
Ionized water, control rotating speed is 600 revs/min, is stirred at 50 DEG C 40 minutes;?.
Example 3:
Various raw materials are taken according to following weight parts formula:Nano-meter CaCO33It is acrylic resin modified:55 parts, acetate butyrate is fine
Dimension element:12 parts, rust resisting pigment:6 parts, butyl acetate:12 parts, pH neutralizers:6 parts, initiator:2 parts, emulsifier:2 parts, stablize
Agent:2 parts, dispersant:2 parts, wetting agent:2 parts, levelling agent:2 parts, Nano-meter CaCO33:2 parts, isopropanol:13 parts, deionized water:40
Part.
By above-mentioned formula, wetting dispersing agent is glyceryl tristearate.
By above-mentioned formula, initiator was ammonium persulfate.
By above-mentioned formula, pH neutralizers are triethanolamine.
By above-mentioned formula, emulsifier is allyl hydroxypropyl azochlorosulfonate acid sodium.
By above-mentioned formula, levelling agent is phosphate modified acrylic acid levelling agent.
By above-mentioned formula, dispersant is the mixture that polyethylene wax and polyethylene glycol are formed.
The preparation method of the modified propylene acid primer, includes the following steps:
1) each component material, is weighed by weight, and Nano-meter CaCO3 is sequentially added into reaction kettle3It is acrylic resin modified,
Acetylbutyrylcellulose, rust resisting pigment, butyl acetate, initiator, dispersant, control rotating speed is 800 revs/min, at 55 DEG C
It is stirred 20 minutes;
2) pH neutralizers, are added into reaction kettle, stir 20 minutes, and adjust pH to 7~8;
3) emulsifier, stabilizer, wetting agent, levelling agent, Nano-meter CaCO3, are sequentially added into reaction kettle3, isopropanol goes
Ionized water, control rotating speed is 600 revs/min, is stirred at 50 DEG C 40 minutes;?.
Bound, section value and the technological parameter of each raw material and each raw material of the present invention cited by the present invention
Bound, the section value of (such as temperature, time) can realize the present invention, embodiment numerous to list herein.
The above is the preferred embodiment of the present invention, cannot limit the right model of the present invention with this certainly
It encloses, it is noted that for those skilled in the art, without departing from the principle of the present invention, may be used also
To make several improvement and variation, these are improved and variation is also considered as protection scope of the present invention.
Claims (10)
1. a kind of modified propylene acid primer, which is characterized in that include the ingredient of following parts by weight:
Nano-meter CaCO33It is acrylic resin modified:40~60 parts,
Acetylbutyrylcellulose:10~15 parts,
Rust resisting pigment:5~10 parts,
Butyl acetate:10~15 parts,
PH neutralizers:5~10 parts,
Initiator:1~5 part,
Emulsifier:1~5 part,
Stabilizer:1~5 part,
Dispersant:1~5 part,
Wetting agent:1~5 part,
Levelling agent:1~5 part,
Nano-meter CaCO33:1~3 part,
Isopropanol:10~20 parts,
Deionized water:30~40 parts.
2. modified propylene acid primer according to claim 1, which is characterized in that include the ingredient of following parts by weight:
Nano-meter CaCO33It is acrylic resin modified:50~60 parts,
Acetylbutyrylcellulose:10~13 parts,
Rust resisting pigment:5~8 parts,
Butyl acetate:10~13 parts,
PH neutralizers:5~8 parts,
Initiator:1~3 part,
Emulsifier:1~3 part,
Stabilizer:1~3 part,
Dispersant:1~3 part,
Wetting agent:1~3 part,
Levelling agent:1~3 part,
Nano-meter CaCO33:2~3 parts,
Isopropanol:11~15 parts,
Deionized water:35~40 parts.
3. modified propylene acid primer according to claim 1, which is characterized in that include the ingredient of following parts by weight:
Nano-meter CaCO33It is acrylic resin modified:55 parts,
Acetylbutyrylcellulose:12 parts,
Rust resisting pigment:6 parts,
Butyl acetate:12 parts,
PH neutralizers:6 parts,
Initiator:2 parts,
Emulsifier:2 parts,
Stabilizer:2 parts,
Dispersant:2 parts,
Wetting agent:2 parts,
Levelling agent:2 parts,
Nano-meter CaCO33:2 parts,
Isopropanol:13 parts,
Deionized water:40 parts.
4. modified propylene acid primer according to claim 1, which is characterized in that the wetting dispersing agent is that three stearic acid are sweet
Grease.
5. modified propylene acid primer according to claim 1, which is characterized in that the initiator is potassium peroxydisulfate or over cure
Sour ammonium.
6. modified propylene acid primer according to claim 1, which is characterized in that the pH neutralizers are triethylamine, 2- ammonia
Base -2- methyl-1s-propyl alcohol or triethanolamine.
7. modified propylene acid primer according to claim 1, which is characterized in that the emulsifier be sodium vinyl sulfonate,
Methallylsulfonic acid sodium or allyl hydroxypropyl azochlorosulfonate acid sodium.
8. modified propylene acid primer according to claim 1, which is characterized in that the levelling agent is fluorin modified crylic acid stream
Flat agent or phosphate modified acrylic acid levelling agent.
9. nano combined antifouling paint according to claim 1, which is characterized in that the dispersant is polyethylene wax and gathers
The mixture that ethylene glycol is formed.
10. a kind of preparation method of modified propylene acid primer according to any one of claims 1 to 9, which is characterized in that including
Following steps:
1) each component material, is weighed by weight, and Nano-meter CaCO3 is sequentially added into reaction kettle3It is acrylic resin modified, acetic acid fourth
Acid cellulose, rust resisting pigment, butyl acetate, initiator, dispersant, control rotating speed is 800 revs/min, is stirred at 55 DEG C mixed
It closes 20 minutes;
2) pH neutralizers, are added into reaction kettle, stir 20 minutes, and adjust pH to 7~8;
3) emulsifier, stabilizer, wetting agent, levelling agent, nm level CaCO_3, isopropanol, deionization, are sequentially added into reaction kettle
Water, control rotating speed is 600 revs/min, is stirred at 50 DEG C 40 minutes;?.