CN108794844A - A kind of environmental protection type solid tyre sizing composition - Google Patents
A kind of environmental protection type solid tyre sizing composition Download PDFInfo
- Publication number
- CN108794844A CN108794844A CN201810584481.3A CN201810584481A CN108794844A CN 108794844 A CN108794844 A CN 108794844A CN 201810584481 A CN201810584481 A CN 201810584481A CN 108794844 A CN108794844 A CN 108794844A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon black
- agent
- environmental protection
- type solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection type solid tyre sizing compositions, including the raw material of following parts by weight to be prepared：20-30 parts of sizing material of vulcanization regeneration, 12-18 parts of standard rubbers, 2-8 parts of silane coupling agent, 1-2 parts of accelerating agent, 1-2 parts of anti-aging agent, 3-4 parts of adhesive, 2-3 parts of zinc oxide, 0-2 parts of carbon black, 0-2 parts of stearic acid, 1-3 parts of softening agent, 6-8 parts of resin.The invention enables tire wear, ageing resistance are good, not only there is preferable molding effect, also there is stronger reliability and the feature of environmental protection.
Description
Technical field
The present invention relates to solid tyre technical field, especially a kind of environmental protection type solid tyre sizing composition.
Background technology
Solid tyre is a kind of tire corresponding with air core tyre, and carcass is solid, does not have to cord as framework, it is not necessary to
Inflation, therefore it is not required to the inner tube of a tyre or inner liner.Earliest tire is exactly solid tyre.Solid tyre is currently only used for the height run at a low speed
Load vehicle or machinery are also used for the machinery of fixed position.Rolling resistance, anti-slippery and wearability are tire " three big rows
Sail performance ", it influences each other between three performances, restrict, the balance optimizing being difficult to realize between three.
Invention content
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of environmental protection type solid tyre sizing composition,
The tyre stock composition so that tire wear, ageing resistance are good, not only has preferable molding effect, also has stronger
Reliability and the feature of environmental protection.
The purpose of the present invention is achieved through the following technical solutions：
A kind of environmental protection type solid tyre sizing composition, including the raw material of following parts by weight are prepared：
20-30 parts of sizing material of vulcanization regeneration, 12-18 parts of standard rubbers, 2-8 parts of silane coupling agent, 1-2 parts of accelerating agent, anti-aging agent 1-2
Part, 3-4 parts of adhesive, 2-3 parts of zinc oxide, 0-2 parts of carbon black, 0-2 parts of stearic acid, 1-3 parts of softening agent, 6-8 parts of resin.
Preferably, in the present invention, including the raw material of following parts by weight is prepared：
20 parts of sizing material of vulcanization regeneration, 14 parts of standard rubbers, 6 parts of silane coupling agent, 2 parts of accelerating agent, 1 part of anti-aging agent, adhesive 3
Part, 2 parts of zinc oxide, 1 part of carbon black, 2 parts of stearic acid, 3 parts of softening agent, 8 parts of resin.
Preferably, in the present invention, the bonding agent is PL-600.
Preferably, in the present invention, the carbon black is in carbon black N330, carbon black N234, carbon black N110 and carbon black N220
At least one.
Beneficial effects of the present invention are：
（1）There is this tyre stock preferable molding effect, also preferable wear-resisting, ageing resistance to be used for the system of solid tyre
It is standby, provide reliability for the traveling of automobile；
（2）It is simple and easy to get to prepare raw material, is prepared using carbon black, the molding reliability between each raw material can be effectively improved, it can be effective
Improve the safety in utilization of tire.
Specific implementation mode
Technical scheme of the present invention is detailed further below, but protection scope of the present invention is not limited to following institute
It states.
Embodiment 1：
A kind of environmental protection type solid tyre sizing composition, including the raw material of following parts by weight are prepared：
20 parts of sizing material of vulcanization regeneration, 12 parts of standard rubbers, 2 parts of silane coupling agent, 1 part of accelerating agent, 1 part of anti-aging agent, adhesive 4
Part, 2 parts of zinc oxide, 2 parts of carbon black, 1 part of stearic acid, 1 part of softening agent, 6 parts of resin.
Preferably, in the present invention, the bonding agent is PL-600.
Preferably, in the present invention, the carbon black is in carbon black N330, carbon black N234, carbon black N110 and carbon black N220
At least one.
Embodiment 2：
A kind of environmental protection type solid tyre sizing composition, including the raw material of following parts by weight are prepared：
30 parts of sizing material of vulcanization regeneration, 16 parts of standard rubbers, 8 parts of silane coupling agent, 2 parts of accelerating agent, 2 parts of anti-aging agent, adhesive 4
Part, 3 parts of zinc oxide, 2 parts of carbon black, 2 parts of stearic acid, 3 parts of softening agent, 8 parts of resin.
Preferably, in the present invention, the bonding agent is PL-600.
Preferably, in the present invention, the carbon black is in carbon black N330, carbon black N234, carbon black N110 and carbon black N220
At least one.
Embodiment 3：
A kind of environmental protection type solid tyre sizing composition, including the raw material of following parts by weight are prepared：
25 parts of sizing material of vulcanization regeneration, 16 parts of standard rubbers, 6 parts of silane coupling agent, 1 part of accelerating agent, 1 part of anti-aging agent, adhesive 3
Part, 3 parts of zinc oxide, 1 part of carbon black, 1 part of stearic acid, 1 part of softening agent, 6 parts of resin.
Preferably, in the present invention, the bonding agent is PL-600.
Preferably, in the present invention, the carbon black is in carbon black N330, carbon black N234, carbon black N110 and carbon black N220
At least one.
Embodiment 4：
A kind of environmental protection type solid tyre sizing composition, including the raw material of following parts by weight are prepared：
20 parts of sizing material of vulcanization regeneration, 14 parts of standard rubbers, 6 parts of silane coupling agent, 2 parts of accelerating agent, 1 part of anti-aging agent, adhesive 3
Part, 2 parts of zinc oxide, 1 part of carbon black, 2 parts of stearic acid, 3 parts of softening agent, 8 parts of resin.
Preferably, in the present invention, the bonding agent is PL-600.
Preferably, in the present invention, the carbon black is in carbon black N330, carbon black N234, carbon black N110 and carbon black N220
At least one.
Specific implementation mode of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
Cannot the limitation to the scope of the claims of the present invention therefore be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect range.
Claims (4)
1. a kind of environmental protection type solid tyre sizing composition, which is characterized in that the raw material including following parts by weight is prepared：
20-30 parts of sizing material of vulcanization regeneration, 12-18 parts of standard rubbers, 2-8 parts of silane coupling agent, 1-2 parts of accelerating agent, anti-aging agent 1-2
Part, 3-4 parts of adhesive, 2-3 parts of zinc oxide, 0-2 parts of carbon black, 0-2 parts of stearic acid, 1-3 parts of softening agent, 6-8 parts of resin.
2. a kind of environmental protection type solid tyre sizing composition according to claim 1, which is characterized in that including following parts by weight
Raw material be prepared：
20 parts of sizing material of vulcanization regeneration, 14 parts of standard rubbers, 6 parts of silane coupling agent, 2 parts of accelerating agent, 1 part of anti-aging agent, adhesive 3
Part, 2 parts of zinc oxide, 1 part of carbon black, 2 parts of stearic acid, 3 parts of softening agent, 8 parts of resin.
3. a kind of environmental protection type solid tyre sizing composition according to claim 1, which is characterized in that the bonding agent is
PL-600。
4. a kind of environmental protection type solid tyre sizing composition according to claim 1, which is characterized in that the carbon black is carbon black
At least one of N330, carbon black N234, carbon black N110 and carbon black N220.