CN108530704A - A kind of solid tyre compounded rubber and preparation method thereof - Google Patents
A kind of solid tyre compounded rubber and preparation method thereof Download PDFInfo
- Publication number
- CN108530704A CN108530704A CN201810584574.6A CN201810584574A CN108530704A CN 108530704 A CN108530704 A CN 108530704A CN 201810584574 A CN201810584574 A CN 201810584574A CN 108530704 A CN108530704 A CN 108530704A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- agent
- carbon black
- butadiene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of solid tyre compounded rubbers and preparation method thereof, include the raw material of following parts by weight:12 18 parts of butadiene rubber, 8 12 parts of butadiene-styrene rubber, 10 20 parts of natural rubber, 23 parts of vulcanizing agent DCP, 48 parts of nano silicon dioxide, 10 16 parts of absolute ethyl alcohol, 26 parts of anti-wear agent, 12 16 parts of carbon black, aramid fiber be fine 26 parts short, 15 parts of foaming agent, 12 parts of anti-aging agent, 24 parts of anti-wear agent.The present invention solves the problems, such as conventional pneumatic by environmental restrictions failure risk and poor reliability, and invention enhances the reliabilities of tire so that tire tread is not in the phenomenon that blowing out to severe ground etc., and temperature tolerance is good, highly reliable.
Description
Technical field
The present invention relates to solid tyre technical field, especially a kind of solid tyre compounded rubber and preparation method thereof.
Background technology
Solid tyre is a kind of special automobile tire, does not have to cord as framework, it is not necessary to inflate, therefore be not required to the inner tube of a tyre or airtight
Layer.Solid tyre is only used for the high load capacity vehicle or machinery run at a low speed or the machinery of fixed position, is primarily adapted for use in anti-riot
The special cars such as vehicle, armoured van, anti-terror vehicle, engineering truck, forestry machinery.
With the enhancing of social environment consciousness and awareness of saving energy, the demand to energy-saving environmentally protective tire is stepped up.
According to associated specialist, it is expected that demand of the China to energy-saving environmentally protective tire will quickly be increased with annual 8%~10% speed.
With the increase of the development and green tire demand of tire industry, it is contemplated that the 2011 and 2016 energy-saving environmentally protective wheels of China
The demand of tire will respectively reach 2,500,000 and 6,000,000.It can be seen that the market demand of energy-saving environmentally protective tire is very
It is huge.
Invention content
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of solid tyre compounded rubber and its preparation sides
Method, the present invention solve the problems, such as conventional pneumatic by environmental restrictions failure risk and poor reliability, invention enhances
The reliability of tire so that tire tread is not in the phenomenon that blowing out to severe ground etc., and temperature tolerance is good, highly reliable.
The purpose of the present invention is achieved through the following technical solutions:
A kind of solid tyre compounded rubber, includes the raw material of following parts by weight:
12-18 parts of butadiene rubber, 8-12 parts of butadiene-styrene rubber, 10-20 parts of natural rubber, 2-3 parts of vulcanizing agent DCP, nanometer titanium dioxide
4-8 parts of silicon, 10-16 parts of absolute ethyl alcohol, 2-6 parts of anti-wear agent, 12-16 parts of carbon black, aramid fiber short 2-6 parts of fibre, are prevented 1-5 parts of foaming agent
Old agent 1-2 parts, 2-4 parts of anti-wear agent.
Preferably, in the present invention, include the raw material of following parts by weight:
It is 12 parts of butadiene rubber, 10 parts of butadiene-styrene rubber, 16 parts of natural rubber, 2 parts of vulcanizing agent DCP, 6 parts of nano silicon dioxide, anhydrous
14 parts of ethyl alcohol, 4 parts of anti-wear agent, 14 parts of carbon black, aramid fiber be fine 4 parts short, 4 parts of foaming agent, 2 parts of anti-aging agent, 2 parts of anti-wear agent.
Preferably, in the present invention, the fibre length of the short fibre of the aramid fiber is 2-10mm.
Preferably, in the present invention, the carbon black is in carbon black N330, carbon black N234, carbon black N110 and carbon black N220
At least one.
A kind of preparation method of solid tyre compounded rubber, including following preparation process:
S1, natural rubber, butadiene-styrene rubber, butadiene rubber and carbon black are weighed according to proportioning, sequentially add in mixer and be kneaded,
Then dumping obtains rubber compound at a temperature of 160-170 DEG C;
S2, rubber compound and graphene, stearic acid, silane coupling agent are added in mixer and are kneaded, in 135-145 DEG C of item
Dumping obtains glue refining body under part;
S3, it will be kneaded in glue refining body and remaining raw material addition mixer, dumping obtains reality under conditions of 90-100 DEG C
Heart tire material.
Preferably, in the present invention, in step s 2, further include being cooled in air often after being kneaded in mixer
Temperature.
Beneficial effects of the present invention are:
The present invention solves the problems, such as conventional pneumatic by environmental restrictions failure risk and poor reliability, invention enhances
The reliability of tire so that tire tread is not in the phenomenon that blowing out to severe ground etc., and temperature tolerance is good, highly reliable.
Specific implementation mode
Technical scheme of the present invention is detailed further below, but protection scope of the present invention is not limited to following institute
It states.
Embodiment 1:
A kind of solid tyre compounded rubber, includes the raw material of following parts by weight:
It is 12 parts of butadiene rubber, 8 parts of butadiene-styrene rubber, 10 parts of natural rubber, 2 parts of vulcanizing agent DCP, 4 parts of nano silicon dioxide, anhydrous
10 parts of ethyl alcohol, 2 parts of anti-wear agent, 12 parts of carbon black, aramid fiber be fine 2 parts short, 1 part of foaming agent, 1 part of anti-aging agent, 2 parts of anti-wear agent.
A kind of preparation method of solid tyre compounded rubber, including following preparation process:
S1, natural rubber, butadiene-styrene rubber, butadiene rubber and carbon black are weighed according to proportioning, sequentially add in mixer and be kneaded,
Then dumping obtains rubber compound at a temperature of 160 DEG C;
S2, rubber compound and graphene, stearic acid, silane coupling agent are added in mixer and are kneaded, under conditions of 135 DEG C
Dumping obtains glue refining body;
S3, it will be kneaded in glue refining body and remaining raw material addition mixer, dumping obtains solid wheel under conditions of 90 DEG C
Tire tire material.
Embodiment 2:
A kind of solid tyre compounded rubber, includes the raw material of following parts by weight:
It is 18 parts of butadiene rubber, 12 parts of butadiene-styrene rubber, 20 parts of natural rubber, 3 parts of vulcanizing agent DCP, 8 parts of nano silicon dioxide, anhydrous
16 parts of ethyl alcohol, 6 parts of anti-wear agent, 16 parts of carbon black, aramid fiber be fine 6 parts short, 5 parts of foaming agent, 2 parts of anti-aging agent, 4 parts of anti-wear agent.
A kind of preparation method of solid tyre compounded rubber, including following preparation process:
S1, natural rubber, butadiene-styrene rubber, butadiene rubber and carbon black are weighed according to proportioning, sequentially add in mixer and be kneaded,
Then dumping obtains rubber compound at a temperature of 170 DEG C;
S2, rubber compound and graphene, stearic acid, silane coupling agent are added in mixer and are kneaded, under conditions of 145 DEG C
Dumping obtains glue refining body;
S3, it will be kneaded in glue refining body and remaining raw material addition mixer, dumping obtains solid wheel under conditions of 100 DEG C
Tire tire material.
Embodiment 3:
A kind of solid tyre compounded rubber, includes the raw material of following parts by weight:
It is 16 parts of butadiene rubber, 10 parts of butadiene-styrene rubber, 16 parts of natural rubber, 3 parts of vulcanizing agent DCP, 6 parts of nano silicon dioxide, anhydrous
14 parts of ethyl alcohol, 4 parts of anti-wear agent, 14 parts of carbon black, aramid fiber be fine 4 parts short, 4 parts of foaming agent, 2 parts of anti-aging agent, 4 parts of anti-wear agent.
A kind of preparation method of solid tyre compounded rubber, including following preparation process:
S1, natural rubber, butadiene-styrene rubber, butadiene rubber and carbon black are weighed according to proportioning, sequentially add in mixer and be kneaded,
Then dumping obtains rubber compound at a temperature of 170 DEG C;
S2, rubber compound and graphene, stearic acid, silane coupling agent are added in mixer and are kneaded, under conditions of 140 DEG C
Dumping obtains glue refining body;
S3, it will be kneaded in glue refining body and remaining raw material addition mixer, dumping obtains solid wheel under conditions of 100 DEG C
Tire tire material.
Embodiment 4:
A kind of solid tyre compounded rubber, includes the raw material of following parts by weight:
It is 14 parts of butadiene rubber, 12 parts of butadiene-styrene rubber, 18 parts of natural rubber, 2 parts of vulcanizing agent DCP, 4 parts of nano silicon dioxide, anhydrous
12 parts of ethyl alcohol, 6 parts of anti-wear agent, 14 parts of carbon black, aramid fiber be fine 6 parts short, 2 parts of foaming agent, 2 parts of anti-aging agent, 4 parts of anti-wear agent.
A kind of preparation method of solid tyre compounded rubber, including following preparation process:
S1, natural rubber, butadiene-styrene rubber, butadiene rubber and carbon black are weighed according to proportioning, sequentially add in mixer and be kneaded,
Then dumping obtains rubber compound at a temperature of 160 DEG C;
S2, rubber compound and graphene, stearic acid, silane coupling agent are added in mixer and are kneaded, under conditions of 145 DEG C
Dumping obtains glue refining body;
S3, it will be kneaded in glue refining body and remaining raw material addition mixer, dumping obtains solid wheel under conditions of 100 DEG C
Tire tire material.
Specific implementation mode of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
Cannot the limitation to the scope of the claims of the present invention therefore be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect range.
Claims (6)
1. a kind of solid tyre compounded rubber, which is characterized in that include the raw material of following parts by weight:
12-18 parts of butadiene rubber, 8-12 parts of butadiene-styrene rubber, 10-20 parts of natural rubber, 2-3 parts of vulcanizing agent DCP, nanometer titanium dioxide
4-8 parts of silicon, 10-16 parts of absolute ethyl alcohol, 2-6 parts of anti-wear agent, 12-16 parts of carbon black, aramid fiber short 2-6 parts of fibre, are prevented 1-5 parts of foaming agent
Old agent 1-2 parts, 2-4 parts of anti-wear agent.
2. a kind of solid tyre compounded rubber according to claim 1, which is characterized in that include the raw material of following parts by weight:
It is 12 parts of butadiene rubber, 10 parts of butadiene-styrene rubber, 16 parts of natural rubber, 2 parts of vulcanizing agent DCP, 6 parts of nano silicon dioxide, anhydrous
14 parts of ethyl alcohol, 4 parts of anti-wear agent, 14 parts of carbon black, aramid fiber be fine 4 parts short, 4 parts of foaming agent, 2 parts of anti-aging agent, 2 parts of anti-wear agent.
3. a kind of solid tyre compounded rubber according to claim 1, which is characterized in that the fibre length of the short fibre of aramid fiber
For 2-10mm.
4. a kind of solid tyre compounded rubber according to claim 1, which is characterized in that the carbon black is carbon black N330, charcoal
At least one of black N234, carbon black N110 and carbon black N220.
5. a kind of preparation method of solid tyre compounded rubber, which is characterized in that including following preparation process:
S1, natural rubber, butadiene-styrene rubber, butadiene rubber and carbon black are weighed according to proportioning, sequentially add in mixer and be kneaded,
Then dumping obtains rubber compound at a temperature of 160-170 DEG C;
S2, rubber compound and graphene, stearic acid, silane coupling agent are added in mixer and are kneaded, in 135-145 DEG C of item
Dumping obtains glue refining body under part;
S3, it will be kneaded in glue refining body and remaining raw material addition mixer, dumping obtains reality under conditions of 90-100 DEG C
Heart tire material.
6. a kind of preparation method of solid tyre compounded rubber according to claim 5, which is characterized in that in step s 2,
Further include being cooled to room temperature in air after being kneaded in mixer.