CN108794044A - High-strength anti-rotten fused alumina zirconia ceramic honey comb of one kind and preparation method thereof - Google Patents
High-strength anti-rotten fused alumina zirconia ceramic honey comb of one kind and preparation method thereof Download PDFInfo
- Publication number
- CN108794044A CN108794044A CN201810600318.1A CN201810600318A CN108794044A CN 108794044 A CN108794044 A CN 108794044A CN 201810600318 A CN201810600318 A CN 201810600318A CN 108794044 A CN108794044 A CN 108794044A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- fused alumina
- alumina zirconia
- ceramic honey
- honey comb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-strength anti-rotten fused alumina zirconia ceramic honey combs and preparation method thereof, including following raw material and its weight fraction：Fused alumina zirconia is 10-25g mass parts；Quartz is 20-30g mass parts；Kaolin is 15-35g mass parts；Talcum is 5-15g mass parts；Feldspar 10-25g mass parts；Potassium feldspar is 50-80g mass parts；Calcite is 20-40g mass parts；Antimitotic agent is 25-35g mass parts；Alumina powder is 10-20g mass parts；Emulsifier is 20-43g mass parts；Shaping assistant is 10-32g mass parts；Binder is 5-10g mass parts；Pore creating material is 10-20g mass parts.Pass through the increase of fused alumina zirconia, ceramic honey comb can be effectively allowed to have wear-resistant, high temperature resistant, it is corrosion-resistant, the features such as high intensity, good insulation preformance, enhance the toughness during ceramic honey comb use, the damage probability for reducing ceramic honey comb, extends the service life of ceramic honey comb, improves the stability during the use of ceramic honey comb.
Description
Technical field
The present invention relates to a kind of ceramic technology field, specially a kind of high-strength anti-rotten fused alumina zirconia ceramic honey comb and its preparation side
Method.
Background technology
Chinese have just invented pottery early in about B.C. 8000-2000 (Neolithic Age).The device fired with clay
Ware is pottery, and the vessel fired with china clay are porcelain.It is ceramic then be pottery, the general name of stoneware and porcelain.Ancients' ceramics are referred to as bowl.
Every with clay and china clay both clays of different nature is raw material, by technological processes such as dispensing, molding, drying, roastings
Manufactured implements can be ceramics.Currently, there is also the places of some shortcomings for existing jade ceramic honey comb, such as；It is existing
Beautiful ceramic honey comb do not have wear-resistant, high temperature resistant, it is corrosion-resistant, the features such as high intensity, good insulation preformance, and existing honeycomb
Toughness during ceramic use is relatively low, improves the damage probability of ceramic honey comb, shortens the service life of ceramic honey comb,
Reduce the stability during the use of ceramic honey comb.
Invention content
The purpose of the present invention is to provide a kind of high-strength anti-rotten fused alumina zirconia ceramic honey combs and preparation method thereof, solve background
The problem of proposed in technology.
To achieve the above object, the present invention provides the following technical solutions：A kind of high-strength anti-rotten fused alumina zirconia ceramic honey comb and its
Preparation method, including following raw material and its weight fraction：Fused alumina zirconia is 10-25g mass parts；Quartz is 20-30g mass parts；
Kaolin is 15-35g mass parts；Talcum is 5-15g mass parts；Feldspar 10-25g mass parts；Potassium feldspar is 50-80g matter
Measure part；Calcite is 20-40g mass parts；Antimitotic agent is 25-35g mass parts；Alumina powder is 10-20g mass parts；Breast
Agent is 20-43g mass parts；Shaping assistant is 10-32g mass parts；Binder is 5-10g mass parts；Pore creating material is 10-
20g mass parts.
As a kind of preferred embodiment of the present invention, the high-strength anti-rotten fused alumina zirconia ceramic honey comb, including following original
Material and its weight fraction：Fused alumina zirconia is 10g mass parts；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g matter
Measure part；Feldspar 10g mass parts；Potassium feldspar is 50g mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Oxidation
Aluminium powder is 10g mass parts；Emulsifier is 20g mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore-creating
Agent is 10g mass parts.
As a kind of preferred embodiment of the present invention, the high-strength anti-rotten fused alumina zirconia ceramic honey comb, including following original
Material and its weight fraction：Fused alumina zirconia is 25g mass parts；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g matter
Measure part；Feldspar 10g mass parts；Potassium feldspar is 50g mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Oxidation
Aluminium powder is 10g mass parts；Emulsifier is 20g mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore-creating
Agent is 20g mass parts.
As a kind of preferred embodiment of the present invention, the preparation method of the high-strength anti-rotten fused alumina zirconia ceramic honey comb,
Steps are as follows for preparation method：
A. above-mentioned raw materials are weighed according to parts by weight first；
B. after the completion of waiting for step a, then the quartz weighed, kaolin, talcum and feldspar is put into pulverizer and carried out
It crushes, then the good quartz, kaolin, talcum and the feldspar that crush is put into 10-15 mesh leakage sieve and screened, then again
Screening good quartz, kaolin, talcum and feldspar powder are poured into mixer plus water carries out being mixed to form glaze slip, then again will
The glaze slip mixed is poured into container；
C. after the completion of waiting for step b, then fused alumina zirconia, potassium feldspar and calcite is put into pulverizer and crushed, then will
Good fused alumina zirconia, potassium feldspar and the calcite crushed is put into 35-45 mesh leakage sieve and is screened；
D. after the completion of waiting for step c, then fused alumina zirconia, potassium feldspar and calcite powder will have been screened and be poured into mixer, so
After add antimitotic agent, alumina powder, emulsifier, pore creating material, binder and suitable water and mixed, then again will molding
Auxiliary agent is added in mixer and is mixed again, and finally the raw material mixed is poured into mold again；
E. after the completion of waiting for step d, then mold is put into stove and is calcined, then again take out the idiosome calcined,
Then it by glaze slip brushing on the surface of idiosome, then swiped through idiosome will be applied is put into stove and calcine；
F. after the completion of waiting for step e, the ceramics calcined is taken out again from stove finally and are cooled down.
As a kind of preferred embodiment of the present invention, glaze slip temperature in mixed process is 30~45 in the step b
DEG C, the mixed time is 15~20min.
As a kind of preferred embodiment of the present invention, fused alumina zirconia, potassium feldspar and calcite are put into powder in the step c
It is crushed in broken machine, for pulverizer using twin-screw pulverizer, the rotating speed of motor is 3000r/min when crushing, be crushed
Temperature in journey is 20~30 DEG C.
Be added as a kind of preferred embodiment of the present invention, in the step d antimitotic agent, alumina powder, emulsifier,
Pore creating material, binder and suitable water are mixed, and temperature when mixing is 40~60 DEG C, and the mixed time is 30~40min,
Speed when mixing is 1200r/min.
Compared with prior art, beneficial effects of the present invention are as follows：
A kind of high-strength anti-rotten fused alumina zirconia ceramic honey comb of the invention and preparation method thereof, can be effective by the increase of fused alumina zirconia
Allow ceramic honey comb that there is wear-resistant, high temperature resistant, corrosion-resistant, the features such as high intensity, good insulation preformance, enhancing ceramic honey comb makes
With toughness in the process, the damage probability of ceramic honey comb is reduced, the service life of ceramic honey comb is extended, improves honeycomb pottery
Stability during the use of porcelain.
Specific implementation mode
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, with reference to
Specific implementation mode, the present invention is further explained.
The present invention provides a kind of technical solution：High-strength anti-rotten fused alumina zirconia ceramic honey comb of one kind and preparation method thereof, including with
Lower raw material and its weight fraction：Fused alumina zirconia is 10-25g mass parts；Quartz is 20-30g mass parts；Kaolin is 15-35g
Mass parts；Talcum is 5-15g mass parts；Feldspar 10-25g mass parts；Potassium feldspar is 50-80g mass parts；Calcite is
20-40g mass parts；Antimitotic agent is 25-35g mass parts；Alumina powder is 10-20g mass parts；Emulsifier is 20-43g
Mass parts；Shaping assistant is 10-32g mass parts；Binder is 5-10g mass parts；Pore creating material is 10-20g mass parts.
The high-strength anti-rotten fused alumina zirconia ceramic honey comb, including following raw material and its weight fraction：Fused alumina zirconia is 10g mass
Part；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g mass parts；Feldspar 10g mass parts；Potassium feldspar is 50g
Mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Alumina powder is 10g mass parts；Emulsifier is 20g
Mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore creating material is 10g mass parts.
The high-strength anti-rotten fused alumina zirconia ceramic honey comb, including following raw material and its weight fraction：Fused alumina zirconia is 25g mass
Part；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g mass parts；Feldspar 10g mass parts；Potassium feldspar is 50g
Mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Alumina powder is 10g mass parts；Emulsifier is 20g
Mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore creating material is 20g mass parts.
The preparation method of the high-strength anti-rotten fused alumina zirconia ceramic honey comb, steps are as follows for preparation method：
A. above-mentioned raw materials are weighed according to parts by weight first；
B. after the completion of waiting for step a, then the quartz weighed, kaolin, talcum and feldspar is put into pulverizer and carried out
It crushes, then the good quartz, kaolin, talcum and the feldspar that crush is put into 10-15 mesh leakage sieve and screened, then again
Screening good quartz, kaolin, talcum and feldspar powder are poured into mixer plus water carries out being mixed to form glaze slip, then again will
The glaze slip mixed is poured into container；
C. after the completion of waiting for step b, then fused alumina zirconia, potassium feldspar and calcite is put into pulverizer and crushed, then will
Good fused alumina zirconia, potassium feldspar and the calcite crushed is put into 35-45 mesh leakage sieve and is screened；
D. after the completion of waiting for step c, then fused alumina zirconia, potassium feldspar and calcite powder will have been screened and be poured into mixer, so
After add antimitotic agent, alumina powder, emulsifier, pore creating material, binder and suitable water and mixed, then again will molding
Auxiliary agent is added in mixer and is mixed again, and finally the raw material mixed is poured into mold again；
E. after the completion of waiting for step d, then mold is put into stove and is calcined, then again take out the idiosome calcined,
Then it by glaze slip brushing on the surface of idiosome, then swiped through idiosome will be applied is put into stove and calcine；
F. after the completion of waiting for step e, the ceramics calcined is taken out again from stove finally and are cooled down.
Glaze slip temperature in mixed process is 30~45 DEG C in the step b, and the mixed time is 15~20min.
Fused alumina zirconia, potassium feldspar and calcite, which are put into pulverizer, in the step c crushes, pulverizer using
Twin-screw pulverizer, the rotating speed of motor is 3000r/min when crushing, and the temperature in crushing process is 20~30 DEG C.
Antimitotic agent, alumina powder, emulsifier, pore creating material, binder and suitable water are added in the step d to be mixed
It closes, temperature when mixing is 40~60 DEG C, and the mixed time is 30~40min, and speed when mixing is 1200r/min.
Embodiment one
The high-strength anti-rotten fused alumina zirconia ceramic honey comb, including following raw material and its weight fraction：Fused alumina zirconia is 25g mass
Part；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g mass parts；Feldspar 10g mass parts；Potassium feldspar is 50g
Mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Alumina powder is 10g mass parts；Emulsifier is 20g
Mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore creating material is 20g mass parts.
Steps are as follows for preparation method：
A. above-mentioned raw materials are weighed according to parts by weight first；
B. after the completion of waiting for step a, then the quartz weighed, kaolin, talcum and feldspar is put into pulverizer and carried out
It crushes, then the good quartz, kaolin, talcum and the feldspar that crush is put into 10-15 mesh leakage sieve and screened, then again
Screening good quartz, kaolin, talcum and feldspar powder are poured into mixer plus water carries out being mixed to form glaze slip, then again will
The glaze slip mixed is poured into container；
C. after the completion of waiting for step b, then fused alumina zirconia, potassium feldspar and calcite is put into pulverizer and crushed, then will
Good fused alumina zirconia, potassium feldspar and the calcite crushed is put into 35-45 mesh leakage sieve and is screened；
D. after the completion of waiting for step c, then fused alumina zirconia, potassium feldspar and calcite powder will have been screened and be poured into mixer, so
After add antimitotic agent, alumina powder, emulsifier, pore creating material, binder and suitable water and mixed, then again will molding
Auxiliary agent is added in mixer and is mixed again, and finally the raw material mixed is poured into mold again；
E. after the completion of waiting for step d, then mold is put into stove and is calcined, then again take out the idiosome calcined,
Then it by glaze slip brushing on the surface of idiosome, then swiped through idiosome will be applied is put into stove and calcine；
F. after the completion of waiting for step e, the ceramics calcined is taken out again from stove finally and are cooled down.
Traditional ceramics data parameters table 1 is as follows：
Ceramics data parameters table 2 of the invention is as follows：
It to sum up states, is obtained with reference to the data comparison of Tables 1 and 2, by the increase of fused alumina zirconia, can effectively allow ceramic honey comb
It is corrosion-resistant with wear-resistant, high temperature resistant, the features such as high intensity, good insulation preformance, enhance tough during ceramic honey comb use
Property, the damage probability of ceramic honey comb is reduced, the service life of ceramic honey comb is extended, improves the use process of ceramic honey comb
In stability.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (7)
1. a kind of high-strength anti-rotten fused alumina zirconia ceramic honey comb, it is characterised in that：Including following raw material and its weight fraction：Fused alumina zirconia is
10-25g mass parts；Quartz is 20-30g mass parts；Kaolin is 15-35g mass parts；Talcum is 5-15g mass parts；It is long
Stone 10-25g mass parts；Potassium feldspar is 50-80g mass parts；Calcite is 20-40g mass parts；Antimitotic agent is 25-35g matter
Measure part；Alumina powder is 10-20g mass parts；Emulsifier is 20-43g mass parts；Shaping assistant is 10-32g mass parts；
Binder is 5-10g mass parts；Pore creating material is 10-20g mass parts.
2. the high-strength anti-rotten fused alumina zirconia ceramic honey comb of one kind according to claim 1, it is characterised in that：Including following raw material and
Its weight fraction：Fused alumina zirconia is 10g mass parts；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g mass
Part；Feldspar 10g mass parts；Potassium feldspar is 50g mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Aluminium oxide
Powder is 10g mass parts；Emulsifier is 20g mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore creating material
For 10g mass parts.
3. the high-strength anti-rotten fused alumina zirconia ceramic honey comb of one kind according to claim 1, it is characterised in that：Including following raw material and
Its weight fraction：Fused alumina zirconia is 25g mass parts；Quartz is 20g mass parts；Kaolin is 15g mass parts；Talcum is 5g mass
Part；Feldspar 10g mass parts；Potassium feldspar is 50g mass parts；Calcite is 20g mass parts；Antimitotic agent is 25g mass parts；Aluminium oxide
Powder is 10g mass parts；Emulsifier is 20g mass parts；Shaping assistant is 10g mass parts；Binder is 5g mass parts；Pore creating material
For 20g mass parts.
4. a kind of preparation method of high-strength anti-rotten fused alumina zirconia ceramic honey comb according to claim 1, it is characterised in that：It prepares
Method and step is as follows：
A. above-mentioned raw materials are weighed according to parts by weight first；
B. after the completion of waiting for step a, then the quartz weighed, kaolin, talcum and feldspar is put into pulverizer and crushed,
The good quartz, kaolin, talcum and the feldspar that crush are put into 10-15 mesh leakage sieve again and screened, it then again will sieve
Choosing quartz, kaolin, talcum and feldspar powder and being poured into mixer adds water to carry out being mixed to form glaze slip, then again will mixing
Good glaze slip is poured into container；
C. after the completion of waiting for step b, then fused alumina zirconia, potassium feldspar and calcite is put into pulverizer and crushed, then will crushed
Good good fused alumina zirconia, potassium feldspar and calcite is put into 35-45 mesh leakage sieve and is screened；
D. after the completion of waiting for step c, then fused alumina zirconia, potassium feldspar and calcite powder will have been screened and be poured into mixer, then again
Antimitotic agent, alumina powder, emulsifier, pore creating material, binder and suitable water is added to be mixed, then again by shaping assistant
It is added in mixer and is mixed again, finally the raw material mixed is poured into mold again；
E. after the completion of waiting for step d, then mold is put into stove and is calcined, then again taken out the idiosome calcined, then
By glaze slip brushing on the surface of idiosome, then swiped through idiosome will be applied it is put into stove and calcine；
F. after the completion of waiting for step e, the ceramics calcined is taken out again from stove finally and are cooled down.
5. a kind of preparation method of high-strength anti-rotten fused alumina zirconia ceramic honey comb according to claim 4, it is characterised in that：It is described
Glaze slip temperature in mixed process is 30~45 DEG C in step b, and the mixed time is 15~20min.
6. a kind of preparation method of high-strength anti-rotten fused alumina zirconia ceramic honey comb according to claim 4, it is characterised in that：It is described
Fused alumina zirconia, potassium feldspar and calcite, which are put into pulverizer, in step c crushes, and pulverizer is crushed using twin-screw
Machine, the rotating speed of motor is 3000r/min when crushing, and the temperature in crushing process is 20~30 DEG C.
7. a kind of preparation method of high-strength anti-rotten fused alumina zirconia ceramic honey comb according to claim 4, it is characterised in that：It is described
Antimitotic agent is added in step d, alumina powder, emulsifier, pore creating material, binder and suitable water are mixed, when mixing
Temperature is 40~60 DEG C, and the mixed time is 30~40min, and speed when mixing is 1200r/min.