CN108793846A - A kind of foam glass insulated fire plate and preparation method thereof - Google Patents
A kind of foam glass insulated fire plate and preparation method thereof Download PDFInfo
- Publication number
- CN108793846A CN108793846A CN201810765133.6A CN201810765133A CN108793846A CN 108793846 A CN108793846 A CN 108793846A CN 201810765133 A CN201810765133 A CN 201810765133A CN 108793846 A CN108793846 A CN 108793846A
- Authority
- CN
- China
- Prior art keywords
- parts
- foam
- glass
- water
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of foam glass insulated fire plates, including metal shielding and insulating foam laminate, the both sides of the metal shielding are provided with insulating foam layer, and insulating foam layer wraps up metal shielding, and insulating foam layer side is provided with layer of glass cloth;Insulating foam layer, it is made of the component of following parts by weight:40-50 parts of scrap glass, 30-50 parts of foam glass fragment, 15-25 parts of coal mine slag, 2-5 parts of foaming agent, 0.5-1 parts of foam stabilizer, 10-15 parts of tossa, 4-9 parts of chrysotile asbestos fibre, 5-9 parts of boron fibre, 4-11 parts of pitch, 12-20 parts of nano mica powder, 4-6 parts of nano silicon dioxide, 3-5 parts of hydroxymethyl cellulose ether, 30-40 parts of cement, 23-33 parts of phenol formaldehyde foam particle, 2-8 parts of lime, 2-5 parts of fire retardant, 4-6 parts of early strength agent, 25-45 parts of water, 2-4 parts of borax, 1-4 parts of water-reducing agent.
Description
Technical field
The present invention relates to fireproof and heat-insulating material field, specifically a kind of foam glass insulated fire plate and preparation method thereof.
Background technology
Fireproof and heat-insulating material is inorganic active thermal insulation material with ordinary cement, insulation stone, calcium powder, campanulaceae, etc. as main
Raw material, the closed pore inorganic active thermal insulation material made of advanced production technology and Chemical Engineering Technology are studied through test of many times, production
Product have fire protection flame retarding, and deformation coefficient is small, anti-aging, and performance is stablized, and eco-environmental prote is good, with plinth course and float coat compatibility
Good, safety and firmness is good, can be with the building same service life.
Foam glass is that foaming agent, fluxing agent and other various property-modifying additives, warp is added in one kind in glass phase raw material
Prepared by high temperature sintering a kind of inside be full of uniform stomata porous material, due to it is low with density, thermal coefficient is low, no
Combustion property etc. excellent performances and obtained the attention of people.But the production cost of foam glass is higher, product price it is high and can not
More it is widely applied.
Invention content
The purpose of the present invention is to provide a kind of foam glass insulated fire plates and preparation method thereof, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides the following technical solutions:
A kind of foam glass insulated fire plate, including metal shielding and insulating foam laminate, the metal shielding
Both sides are provided with insulating foam layer, and the insulating foam layer wraps up metal shielding, and insulating foam layer side is provided with
Layer of glass cloth.
The insulating foam layer, it is made of the component of following parts by weight:
40-50 parts of scrap glass, 30-50 parts of foam glass fragment, 15-25 parts of coal mine slag, 2-5 parts of foaming agent, foam stabilizer
0.5-1 parts, 10-15 parts of tossa, 4-9 parts of chrysotile asbestos fibre, 5-9 parts of boron fibre, 4-11 parts of pitch, nano mica powder 12-
20 parts, 4-6 parts of nano silicon dioxide, 3-5 parts of hydroxymethyl cellulose ether, 30-40 parts of cement, 23-33 parts of phenol formaldehyde foam particle, stone
2-8 parts grey, 2-5 parts of fire retardant, 4-6 parts of early strength agent, 25-45 parts of water, 2-4 parts of borax, 1-4 parts of water-reducing agent.
The insulating foam layer, it is made of the component of following parts by weight:
40 parts of scrap glass, 30 parts of foam glass fragment, 15 parts of coal mine slag, 2-5 parts of foaming agent, 0.5-1 parts of foam stabilizer, Huang
10 parts of flaxen fiber, 4-9 parts of chrysotile asbestos fibre, 5-9 parts of boron fibre, 4 parts of pitch, 12 parts of nano mica powder, nano silicon dioxide 4-6
Part, 3-5 parts of hydroxymethyl cellulose ether, 30 parts of cement, 23 parts of phenol formaldehyde foam particle, 2-8 parts of lime, 2-5 parts of fire retardant, early strength agent
4-6 parts, 25 parts of water, 2-4 parts of borax, 1-4 parts of water-reducing agent.
The insulating foam layer, it is made of the component of following parts by weight:
50 parts of scrap glass, 50 parts of foam glass fragment, 25 parts of coal mine slag, 5 parts of foaming agent, 1 part of foam stabilizer, tossa
15 parts, 9 parts of chrysotile asbestos fibre, 9 parts of boron fibre, 11 parts of pitch, 20 parts of nano mica powder, 6 parts of nano silicon dioxide, methylol are fine
Plain 5 parts of the ether of dimension, 40 parts of cement, 33 parts of phenol formaldehyde foam particle, 8 parts of lime, 5 parts of fire retardant, 6 parts of early strength agent, 45 parts of water, borax 4
Part, 4 parts of water-reducing agent.
The insulating foam layer, it is made of the component of following parts by weight:
45 parts of scrap glass, 40 parts of foam glass fragment, 20 parts of coal mine slag, 3.5 parts of foaming agent, 0.8 part of foam stabilizer, jute
13 parts of fiber, 7 parts of chrysotile asbestos fibre, 7 parts of boron fibre, 8 parts of pitch, 16 parts of nano mica powder, 5 parts of nano silicon dioxide, hydroxyl first
4 parts of base cellulose ether, 35 parts of cement, 27 parts of phenol formaldehyde foam particle, 5 parts of lime, 3.5 parts of fire retardant, 5 parts of early strength agent, 35 parts of water,
3 parts of borax, 3 parts of water-reducing agent.
Preferably, the foaming agent is gas-phase silica.
Preferably, the foam stabilizer is nano zine oxide.
Preferably, the water-reducing agent is naphthalene water reducer.
Compared with prior art, the beneficial effects of the invention are as follows:
It using in the both sides of metal shielding is provided with insulating foam layer to the present invention, and insulating foam layer is by metal shielding
Package has good insulation effect, and insulating foam layer side be provided with layer of glass cloth, has good intensity, resistance to
Time property and heat barriering effect, ensure that service life;Using metal shielding as insulating foam layer inner core, can play good
Good support effect has good firm effect, and insulating foam layer scrap glass of the invention, coal mine slag are as main original
Material, not only realizes the regeneration of waste product, advantageously reduces scrap glass, the influence that coal mine slag generates environment;Simultaneously
The production cost for effectively reducing foam glass is conducive to application of the foam glass in building thermal insulation material field.Each original
Expect to make it have the advantages that density is big, compression strength is big, thermal coefficient is low, heat insulation effect is good by reasonably combined between component,
It is a kind of fireproof and heat-insulating material of high comprehensive performance.
Specific implementation mode
Embodiment 1
A kind of foam glass insulated fire plate, including metal shielding and insulating foam laminate, the metal shielding
Both sides are provided with insulating foam layer, and the insulating foam layer wraps up metal shielding, and insulating foam layer side is provided with
Layer of glass cloth.
The insulating foam layer, it is made of the component of following parts by weight:
45 parts of scrap glass, 40 parts of foam glass fragment, 20 parts of coal mine slag, 3.5 parts of foaming agent, 0.8 part of foam stabilizer, jute
13 parts of fiber, 7 parts of chrysotile asbestos fibre, 7 parts of boron fibre, 8 parts of pitch, 16 parts of nano mica powder, 5 parts of nano silicon dioxide, hydroxyl first
4 parts of base cellulose ether, 35 parts of cement, 27 parts of phenol formaldehyde foam particle, 5 parts of lime, 3.5 parts of fire retardant, 5 parts of early strength agent, 35 parts of water,
3 parts of borax, 3 parts of water-reducing agent.
The foaming agent is gas-phase silica.
The foam stabilizer is nano zine oxide.
The water-reducing agent is naphthalene water reducer.
Embodiment 2
A kind of foam glass insulated fire plate, including metal shielding and insulating foam laminate, the metal shielding
Both sides are provided with insulating foam layer, and the insulating foam layer wraps up metal shielding, and insulating foam layer side is provided with
Layer of glass cloth.
The insulating foam layer, it is made of the component of following parts by weight:
40 parts of scrap glass, 30 parts of foam glass fragment, 15 parts of coal mine slag, 2-5 parts of foaming agent, 0.5-1 parts of foam stabilizer, Huang
10 parts of flaxen fiber, 4-9 parts of chrysotile asbestos fibre, 5-9 parts of boron fibre, 4 parts of pitch, 12 parts of nano mica powder, nano silicon dioxide 4-6
Part, 3-5 parts of hydroxymethyl cellulose ether, 30 parts of cement, 23 parts of phenol formaldehyde foam particle, 2-8 parts of lime, 2-5 parts of fire retardant, early strength agent
4-6 parts, 25 parts of water, 2-4 parts of borax, 1-4 parts of water-reducing agent.
The foaming agent is gas-phase silica.
The foam stabilizer is nano zine oxide.
The water-reducing agent is naphthalene water reducer.
Embodiment 3
A kind of foam glass insulated fire plate, including metal shielding and insulating foam laminate, the metal shielding
Both sides are provided with insulating foam layer, and the insulating foam layer wraps up metal shielding, and insulating foam layer side is provided with
Layer of glass cloth.
The insulating foam layer, it is made of the component of following parts by weight:
50 parts of scrap glass, 50 parts of foam glass fragment, 25 parts of coal mine slag, 5 parts of foaming agent, 1 part of foam stabilizer, tossa
15 parts, 9 parts of chrysotile asbestos fibre, 9 parts of boron fibre, 11 parts of pitch, 20 parts of nano mica powder, 6 parts of nano silicon dioxide, methylol are fine
Plain 5 parts of the ether of dimension, 40 parts of cement, 33 parts of phenol formaldehyde foam particle, 8 parts of lime, 5 parts of fire retardant, 6 parts of early strength agent, 45 parts of water, borax 4
Part, 4 parts of water-reducing agent.
The foaming agent is gas-phase silica.
The foam stabilizer is nano zine oxide.
The water-reducing agent is naphthalene water reducer.
Claims (7)
1. a kind of foam glass insulated fire plate, which is characterized in that including metal shielding and insulating foam laminate, the metal
The both sides of enhancement layer are provided with insulating foam layer, and the insulating foam layer wraps up metal shielding, the insulating foam layer one
Side is provided with layer of glass cloth;
The insulating foam layer, it is made of the component of following parts by weight:
40-50 parts of scrap glass, 30-50 parts of foam glass fragment, 15-25 parts of coal mine slag, 2-5 parts of foaming agent, foam stabilizer 0.5-1
Part, 10-15 parts of tossa, 4-9 parts of chrysotile asbestos fibre, 5-9 parts of boron fibre, 4-11 parts of pitch, 12-20 parts of nano mica powder,
4-6 parts of nano silicon dioxide, 3-5 parts of hydroxymethyl cellulose ether, 30-40 parts of cement, 23-33 parts of phenol formaldehyde foam particle, lime 2-8
Part, 2-5 parts of fire retardant, 4-6 parts of early strength agent, 25-45 parts of water, 2-4 parts of borax, 1-4 parts of water-reducing agent.
2. foam glass insulated fire plate according to claim 1, which is characterized in that the insulating foam layer, it be by
The component of following parts by weight is made:
40 parts of scrap glass, 30 parts of foam glass fragment, 15 parts of coal mine slag, 2-5 parts of foaming agent, 0.5-1 parts of foam stabilizer, jute are fine
10 parts of dimension, 4-9 parts of chrysotile asbestos fibre, 5-9 parts of boron fibre, 4 parts of pitch, 12 parts of nano mica powder, 4-6 parts of nano silicon dioxide,
3-5 parts of hydroxymethyl cellulose ether, 30 parts of cement, 23 parts of phenol formaldehyde foam particle, 2-8 parts of lime, 2-5 parts of fire retardant, early strength agent 4-6
Part, 25 parts of water, 2-4 parts of borax, 1-4 parts of water-reducing agent.
3. foam glass insulated fire plate according to claim 1, which is characterized in that the insulating foam layer, it be by
The component of following parts by weight is made:
50 parts of scrap glass, 50 parts of foam glass fragment, 25 parts of coal mine slag, 5 parts of foaming agent, 1 part of foam stabilizer, tossa 15
Part, 9 parts of chrysotile asbestos fibre, 9 parts of boron fibre, 11 parts of pitch, 20 parts of nano mica powder, 6 parts of nano silicon dioxide, hydroxylmethyl cellulose
5 parts of plain ether, 40 parts of cement, 33 parts of phenol formaldehyde foam particle, 8 parts of lime, 5 parts of fire retardant, 6 parts of early strength agent, 45 parts of water, 4 parts of borax,
4 parts of water-reducing agent.
4. foam glass insulated fire plate according to claim 1, which is characterized in that the insulating foam layer, it be by
The component of following parts by weight is made:
45 parts of scrap glass, 40 parts of foam glass fragment, 20 parts of coal mine slag, 3.5 parts of foaming agent, 0.8 part of foam stabilizer, tossa
13 parts, 7 parts of chrysotile asbestos fibre, 7 parts of boron fibre, 8 parts of pitch, 16 parts of nano mica powder, 5 parts of nano silicon dioxide, methylol are fine
Plain 4 parts of the ether of dimension, 35 parts of cement, 27 parts of phenol formaldehyde foam particle, 5 parts of lime, 3.5 parts of fire retardant, 5 parts of early strength agent, 35 parts of water, borax
3 parts, 3 parts of water-reducing agent.
5. foam glass insulated fire plate according to claim 1, which is characterized in that the foaming agent is gas phase hard charcoal
It is black.
6. foam glass insulated fire plate according to claim 1, which is characterized in that the foam stabilizer is nano oxidized
Zinc.
7. foam glass insulated fire plate according to claim 1, which is characterized in that the water-reducing agent is naphthalene system diminishing
Agent.