CN108787401A - The painting method of tension and the high stainless steel surface nylon coating of yield strength - Google Patents
The painting method of tension and the high stainless steel surface nylon coating of yield strength Download PDFInfo
- Publication number
- CN108787401A CN108787401A CN201810594775.4A CN201810594775A CN108787401A CN 108787401 A CN108787401 A CN 108787401A CN 201810594775 A CN201810594775 A CN 201810594775A CN 108787401 A CN108787401 A CN 108787401A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- nylon
- priming paint
- stainless steel
- methacrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of painting methods of the high stainless steel surface nylon coating of tension and yield strength, include the following steps:A. it pre-processes;Workpiece is impregnated in an acidic solution;B. basecoat paint;To workpiece surface spraying priming paint;C. drying heating:By solidifying priming paint and workpiece preheating;D. nylon coated:The workpiece of preheating is immersed in nylon powder so that nylon powder forms nylon coating in workpiece surface;E. levelling, it is cooling.Stainless steel surface nylon coated method coating adhesion of the present invention is good, durable.
Description
Technical field
The present invention relates to a kind of method of stainless steel surface nylon coated, especially a kind of tension and yield strength are high not
The painting method of rust steel surface nylon coating.
Background technology
Currently, coating nylon on metal surface, generally uses high pressure electrostatic painting method, this method that can make the gold of complicated shape
It is uneven to belong to the covering of rack surface nylon layer, will produce bottom drain phenomenon, while requirement is not achieved in the adhesive force of coating, repeatedly
It will produce blistering or decortication phenomenon after high-temperature sterilization disinfection, be absolutely unacceptable in medical device industry.
Invention content
The technical problem to be solved by the present invention is to propose that a kind of coating adhesion is good, long-lived stainless steel surface Buddhist nun
Imperial painting method, and pass through product made from the method.
A kind of technical solution that the present invention proposes to solve above-mentioned technical problem is:A kind of stainless steel surface nylon coated side
Method includes the following steps:
A. it pre-processes;Workpiece is impregnated into 20min~25min in an acidic solution, the ingredient of the acid solution be 3wt%~
The hydrochloric acid of 5wt%, the nitric acid of 5wt%~8wt%, the ethanedioic acid of 2wt%~3wt%, remaining is water;
B. basecoat paint;The priming paint for being 10 μm to 30 μm to workpiece surface spraying thickness, the priming paint is by following mass percent
Component mix:Amino modified acrylate 20%~30%, methacrylate 15%~20% are nano-silicon dioxide modified
Acrylate 5%~8%, curing agent 0.3%~2%, silane coupling agent 5%~10%, dispersant 8%~15%, remaining is organic solvent;
C. drying heating:It is 5min~6min in 250 DEG C~280 DEG C of baking oven that workpiece, which is placed in temperature, so that solidifying priming paint and
Workpiece preheats;
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 3s~6s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 100 μm to 500 μm;
E. levelling, it is cooling.
The mass percentage content of amino modified acrylate is 25%~28% in the priming paint, the matter of methacrylate
It is 18%~20% to measure degree, and the mass percentage content of nano-silicon dioxide modified acrylic ester is 7%~8%.
The amino modified acrylate is aliphatic urethane acrylate.
The methacrylate is hydroxyethyl methacrylate, methyl methacrylate or dimethacrylate second two
Ester;
The organic solvent is one or more in N-butyl, ethyl acetate, ethyl alcohol and acetone.
The curing agent is Isocyanates curing agent;
The dispersant is fatty alcohol polyoxyethylene ether.
Workpiece is first carried out to deburring, sandblasting, bending processing successively in the step A, then is impregnated in an acidic solution.
In the step E, the planarization on surface is checked after workpiece cooling, then packaging and storage.
A kind of technical solution that the present invention proposes to solve above-mentioned technical problem is:It is a kind of to use above-mentioned stainless steel surface Buddhist nun
Product obtained by imperial painting method.
The present invention has the effect of positive:The method that the stainless steel surface nylon coated method of the present invention uses acid corrosion
Both the impurity for having washed away surface obtains the roughness of needs further through pore corrosion so that the painting of stainless steel substrate and surface
Layer combination is even closer, and does not interfere with the dimensional accuracy of workpiece.The stainless steel surface nylon coated method of the present invention uses
Special priming paint, adhesive force is good, excellent combination property so that the combination of stainless steel substrate and nylon coating is more secured.It is made
Medical device box stent surface smoothing it is thick and solid, make supported equipment surfaces will not be by scratch or friction.Wearability is not
3 times or more of rust steel, tension and yield strength are high, and holder can be remained intact by 30 degree of coating surfaces of bending, 25 continuous high temperatures
Sterilizing test, any deformation does not occur, can be durable by 2000 hours salt spray tests.
Specific implementation mode
Embodiment 1
The stainless steel surface nylon coated method of the present embodiment, including step in detail below:
A. it pre-processes;Workpiece is first carried out to deburring, sandblasting, bending processing successively, then workpiece is impregnated in an acidic solution
22min, the ingredient of the acid solution are the hydrochloric acid of 5wt%, and the nitric acid of 7wt%, the ethanedioic acid of 2.5wt%, remaining is water.It is acid
Solution can remove the impurity of workpiece surface, while carry out pore corrosion to workpiece surface, form 12 μm to 18 μm of micropore, make
Obtaining workpiece surface has certain roughness, and cost is relatively low compared with blasting craft, and can ensure that workpiece will not deform, will not
Influence dimensional accuracy.It is tested using above-mentioned special acid solution, the bond strength of follow-up coating is not up to when being less than 20min
To requirement, coating can be caused the case where out-of-flatness locally occur when more than 25min, therefore, workpiece impregnates in an acidic solution
Time preferred 20min to 25min.
B. basecoat paint;The priming paint for being 25 μm to 30 μm to workpiece surface spraying thickness, the priming paint is by following quality hundred
The component of ratio is divided to mix:Amino modified acrylate 26%, methacrylate 18%, nano-silicon dioxide modified acrylic
Ester 8%, curing agent 1.5%, silane coupling agent 8%, dispersant 10%, remaining is organic solvent.
Wherein, amino modified acrylate use Zhongshan city's Ke Tian Electron Material Co., Ltd trade mark for 3295 aliphatic
Urethane acrylate.Nano-silicon dioxide modified acrylic ester is by acrylic resin and the nanometer for accounting for acrylic resin dosage 6%
Silicon dioxide gel is combined.Methacrylate uses hydroxyethyl methacrylate.Silane coupling agent is KH550.It is organic
Solvent is ethyl acetate.Curing agent is TDI tripolymers.Dispersant is fatty alcohol polyoxyethylene ether.
Aliphatic urethane acrylate is conducive to improve the flexibility and elasticity of adhesive force and coating.Nanometer titanium dioxide
Fluorine-silicon modified acrylic ester is conducive to reinforce the physical mechanical strength of coating, improves bend-resistance.The base paint formulation dispersion effect is good,
With suitable surface tension and film forming.
C. drying heating:Workpiece is placed in 5min in the baking oven that temperature is 280 DEG C so that solidifying priming paint and workpiece preheating.
The temperature of workpiece surface commonly reaches 230 DEG C or so.
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 3s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 150 μm.Also fluidized bed dipping technique can be replaced with electrostatic painting process.
E. levelling, it is cooling, the planarization of workpiece surface is checked, then packaging and storage.
Embodiment 2
The stainless steel surface nylon coated method of the present embodiment, including step in detail below:
A. it pre-processes;Workpiece is first carried out to deburring, sandblasting, bending processing successively, then workpiece is impregnated in an acidic solution
25min, the ingredient of the acid solution are the hydrochloric acid of 4wt%, and the nitric acid of 6wt%, the ethanedioic acid of 3wt%, remaining is water.
B. basecoat paint;The priming paint for being 15 μm to 20 μm to workpiece surface spraying thickness, the priming paint is by following quality hundred
The component of ratio is divided to mix:Amino modified acrylate 25%, methacrylate 19%, nano-silicon dioxide modified acrylic
Ester 7%, curing agent 1.2%, silane coupling agent 10%, dispersant 12%, remaining is organic solvent.
C. drying heating:Workpiece is placed in 5min in the baking oven that temperature is 280 DEG C so that solidifying priming paint and workpiece preheating.
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 6s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 300 μm.
E. levelling, it is cooling, the planarization of workpiece surface is checked, then packaging and storage.
Embodiment 3
The stainless steel surface nylon coated method of the present embodiment, including step in detail below:
A. it pre-processes;Workpiece is first carried out to deburring, sandblasting, bending processing successively, then workpiece is impregnated in an acidic solution
20min, the ingredient of the acid solution are the hydrochloric acid of 3wt%, and the nitric acid of 8wt%, the ethanedioic acid of 3wt%, remaining is water.
B. basecoat paint;The priming paint for being 25 μm to 30 μm to workpiece surface spraying thickness, the priming paint is by following quality hundred
The component of ratio is divided to mix:Amino modified acrylate 28%, methacrylate 20%, nano-silicon dioxide modified acrylic
Ester 7.5%, curing agent 1.5%, silane coupling agent 9%, dispersant 11%, remaining is organic solvent.
C. drying heating:Workpiece is placed in 5min in the baking oven that temperature is 280 DEG C so that solidifying priming paint and workpiece preheating.
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 3s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 150 μm.
E. levelling, it is cooling, the planarization of workpiece surface is checked, then packaging and storage.
Embodiment 4
The stainless steel surface nylon coated method of the present embodiment, including step in detail below:
A. it pre-processes;Workpiece is first carried out to deburring, sandblasting, bending processing successively, then workpiece is impregnated in an acidic solution
20min, the ingredient of the acid solution are the hydrochloric acid of 4.5wt%, and the nitric acid of 6wt%, the ethanedioic acid of 2wt%, remaining is water.
B. basecoat paint;The priming paint for being 12 μm to 18 μm to workpiece surface spraying thickness, the priming paint is by following quality hundred
The component of ratio is divided to mix:Amino modified acrylate 27%, methacrylate 19%, nano-silicon dioxide modified acrylic
Ester 8%, curing agent 1.5%, silane coupling agent 8%, dispersant 10%, remaining is organic solvent.
C. drying heating:Workpiece is placed in 5min in the baking oven that temperature is 280 DEG C so that solidifying priming paint and workpiece preheating.
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 6s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 300 μm.
E. levelling, it is cooling, the planarization of workpiece surface is checked, then packaging and storage.
Embodiment 5
The stainless steel surface nylon coated method of the present embodiment, including step in detail below:
A. it pre-processes;Workpiece is first carried out to deburring, sandblasting, bending processing successively, then workpiece is impregnated in an acidic solution
25min, the ingredient of the acid solution are the hydrochloric acid of 3.5wt%, and the nitric acid of 5wt%, the ethanedioic acid of 3wt%, remaining is water.
B. basecoat paint;The priming paint for being 25 μm to 30 μm to workpiece surface spraying thickness, the priming paint is by following quality hundred
The component of ratio is divided to mix:Amino modified acrylate 26%, methacrylate 19%, nano-silicon dioxide modified acrylic
Ester 7.5%, curing agent 1.2%, silane coupling agent 5%, dispersant 15%, remaining is organic solvent.
C. drying heating:Workpiece is placed in 5min in the baking oven that temperature is 280 DEG C so that solidifying priming paint and workpiece preheating.
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 3s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 150 μm
E. levelling, it is cooling, the planarization of workpiece surface is checked, then packaging and storage.
Obviously, the above embodiment is merely an example for clearly illustrating the present invention, and is not to the present invention
The restriction of embodiment.For those of ordinary skill in the art, it can also be made on the basis of the above description
Its various forms of variation or variation.There is no necessity and possibility to exhaust all the enbodiments.And these belong to this hair
The obvious changes or variations that bright spirit is extended out are still in the protection scope of this invention.
Claims (1)
1. a kind of stainless steel surface nylon coated method, includes the following steps:
A. it pre-processes;Workpiece is impregnated into 20min~25min in an acidic solution, the ingredient of the acid solution be 3wt%~
The hydrochloric acid of 5wt%, the nitric acid of 5wt%~8wt%, the ethanedioic acid of 2wt%~3wt%, remaining is water;
B. basecoat paint;The priming paint for being 10 μm to 30 μm to workpiece surface spraying thickness, the priming paint is by following mass percent
Component mix:Amino modified acrylate 20%~30%, methacrylate 15%~20% are nano-silicon dioxide modified
Acrylate 5%~8%, curing agent 0.3%~2%, silane coupling agent 5%~10%, dispersant 8%~15%, remaining is organic solvent;
C. drying heating:It is 5min~6min in 250 DEG C~280 DEG C of baking oven that workpiece, which is placed in temperature, so that solidifying priming paint and
Workpiece preheats;
D. nylon coated:Using fluidized bed dipping technique, the workpiece of preheating is immersed into 3s~6s in nylon powder so that nylon powder exists
Workpiece surface forms the nylon coating that thickness is 100 μm to 500 μm;
E. levelling, it is cooling;
The mass percentage content of amino modified acrylate is 25%~28% in the priming paint, the quality hundred of methacrylate
It is 18%~20% to divide than content, and the mass percentage content of nano-silicon dioxide modified acrylic ester is 7%~8%;
The methacrylate is Ethylene-glycol-dimethacrylate;
The organic solvent is acetone;
The curing agent is Isocyanates curing agent;
The dispersant is fatty alcohol polyoxyethylene ether;
Workpiece is first carried out to deburring, sandblasting, bending processing successively in the step A, then is impregnated in an acidic solution;
In the step E, the planarization on surface is checked after workpiece cooling, then packaging and storage.