CN108774417A - A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance - Google Patents
A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance Download PDFInfo
- Publication number
- CN108774417A CN108774417A CN201810441844.8A CN201810441844A CN108774417A CN 108774417 A CN108774417 A CN 108774417A CN 201810441844 A CN201810441844 A CN 201810441844A CN 108774417 A CN108774417 A CN 108774417A
- Authority
- CN
- China
- Prior art keywords
- parts
- prtv
- coatings
- acting
- long
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material includes following components by weight：40-60 parts of acrylic emulsion,10-17 parts of filler,20-30 parts of resin group material,8.2-10 parts of fire retardant,3-6 parts of pigment,10-12 parts of bioantifouling agent,2-6 parts of styrene,This has the PRTV long-acting and anti-fouling flashing coatings of high hydrophobic and corrosion resistance,Applying coating is on electroceramics surface,One layer of glued membrane is formed after solidification,The glued membrane has excellent hydrophobicity under cleaning condition,In mist,Dew,Under the humid conditions such as drizzle,Pollution layer surface is difficult moistening,If after for a long time moistening pollution layer,Pollution layer surface will not form flow and moisture film,But it is individually present with numerous discontinuous droplets,To greatly control the generation of Leakage Current,Considerably improve the pollution flashover voltage of insulator,Fire-resistant waterproof,Toughness is strong,Power grid trouble-free operation is effectively ensured,Reduce the amount of labour of power worker.
Description
Technical field
The present invention relates to PRTV anti-pollution flashover coatings technical fields more particularly to a kind of with high hydrophobic and corrosion resistance
PRTV long-acting and anti-fouling flashing coatings.
Background technology
The Natural contamination phenomenon on electric system outdoor equipment electroceramics surface is inevitable, with the hair of China's economy
Exhibition, each ground contamination are on the increase, and salt density value range increases year by year, under severe meteorological condition, along moist insulation sublist
Flashover can occur for face, and electric system pollution flashover accident, pollution flashover is caused to threaten the safe and stable operation of electric system, less serious case's influence office
Portion powers, and severe one can impact power grid, or even entire power grid is made to generate cracking, and existing PRTV anti-pollution flashover coatings cannot have
Effect plays the role of antifouling work, and electric power personnel is needed manually to be cleaned, to ensure power grid and safety and trouble-free operation, but
The workload of electric power personnel is significantly increased, it is extremely inefficient.
Invention content
The purpose of the present invention is to solve disadvantage existing in the prior art, and the one kind proposed have high hydrophobic and
The PRTV long-acting and anti-fouling flashing coatings of corrosion resistance, materials and proportioning are reasonable, can form diaphragm on the surface of power equipment, have
Good hydrophobicity and anticorrosive property, antifouling work ensure that the trouble-free operation of power grid, high safety, using convenient.
To achieve the goals above, present invention employs following technical solutions：
A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material include following by weight
Component：40-60 parts of acrylic emulsion, 10-17 parts of filler, 20-30 parts of resin group material, 8.2-10 parts of fire retardant, pigment 3-6
Part, 10-12 parts of bioantifouling agent, 2-6 parts of styrene, 1-2 parts of zinc pyrithione, 1.2-2 parts of catalyst, 1-2 parts of maleic rosin.
As a preferred technical solution of the present invention, raw material includes following components by weight：Acrylic emulsion 45-
55 parts, 12-15 parts of filler, 22-26 parts of resin group material, 8.4-9 parts of fire retardant, 4-5 parts of pigment, bioantifouling agent 10.5-11
Part, 3-4 parts of styrene, 1.2-1.8 parts of zinc pyrithione, 1.4-1.7 parts of catalyst, 1.2-1.6 parts of maleic rosin.
As a preferred technical solution of the present invention, the raw materials used acrylic emulsion includes with the following group by weight
Point, 10-33 parts of butyl acrylate, 13-17 parts of methyl methacrylate, 0.6-1.4 parts of methacrylic acid, 50-63 parts of water, alkyl
1.2-1.6 parts of benzene polyethers sodium sulfonate, 0.2-0.6 parts of ammonium persulfate.
As a preferred technical solution of the present invention, the filler includes 4-8 parts of talcum powder, expanded perlite 3-6
Part, 1.4-2 parts of silica flour.
As a preferred technical solution of the present invention, the resin group material includes acrylic resin and organic-silicon-modified fluorine
Resin, and the mass ratio of acrylic resin and organic-silicon-modified fluororesin is 1.2: 3.
As a preferred technical solution of the present invention, the fire retardant includes 2.5-3 parts of antimony oxide, magnesium hydroxide
2.2-2.6 3-6 parts of part, aluminium hydroxide.
As a preferred technical solution of the present invention, the pigment is the mixture of acetylene carbon dust and carbon black, and acetylene
The mass ratio of carbon dust and carbon black is 1: 2.
As a preferred technical solution of the present invention, the bioantifouling agent includes 0.6-1.2 parts of alkylamine, aliphatic acid
0.2-0.6 parts of polyoxyethylene ether, 1.2-1.6 parts of polyethylene glycol.
Beneficial to benefit：This has the PRTV long-acting and anti-fouling flashing coatings of high hydrophobic and corrosion resistance, and applying coating is in electroceramics
Surface forms one layer of glued membrane after solidification, which has excellent hydrophobicity under cleaning condition, in tides such as mist, dew, drizzles
Under the conditions of moisture is waited, pollution layer surface is difficult moistening, if after for a long time moistening pollution layer, pollution layer surface will not form flow and water
Film, but be individually present with numerous discontinuous droplets, to greatly control the generation of Leakage Current, significantly carry
The high pollution flashover voltage of insulator, fire-resistant waterproof, toughness is strong, and power grid trouble-free operation is effectively ensured, reduces power worker's
The amount of labour.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment one：
A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material include following by weight
Component：45 parts of acrylic emulsion, 12 parts of filler, 22 parts of resin group material, 8.4 parts of fire retardant, 4.2 parts of pigment, bioantifouling agent
10.5 parts, 3.2 parts of styrene, 1.2 parts of zinc pyrithione, 1.4 parts of catalyst, 1.2 parts of maleic rosin.
In the present embodiment, the acrylic emulsion it is raw materials used by weight include following components, 10 parts of butyl acrylate,
13 parts of methyl methacrylate, 0.6 part of methacrylic acid, 50 parts of water, 1.2 parts of alkylbenzene polyethers sodium sulfonate, ammonium persulfate 0.2
Part.
In the present embodiment, the filler includes 4 parts of talcum powder, 3 parts of expanded perlite, 1.4 parts of silica flour.
In the present embodiment, the resin group material includes acrylic resin and organic-silicon-modified fluororesin, and acrylic resin
Mass ratio with organic-silicon-modified fluororesin is 1.2: 3.
In the present embodiment, the fire retardant includes 2.5 parts of antimony oxide, 2.2 parts of magnesium hydroxide, 3 parts of aluminium hydroxide.
In the present embodiment, the pigment is the mixture of acetylene carbon dust and carbon black, and the mass ratio of acetylene carbon dust and carbon black
It is 1: 2.
In the present embodiment, the bioantifouling agent includes 0.6 part of alkylamine, 0.2 part of aliphatic acid polyethenoxy ether, poly- second two
1.2 parts of alcohol.
Embodiment two：
A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material include following by weight
Component：48 parts of acrylic emulsion, 13 parts of filler, 23 parts of resin group material, 8.5 parts of fire retardant, 4.4 parts of pigment, bioantifouling agent
10.6 parts, 3.2 parts of styrene, 1.4 parts of zinc pyrithione, 1.5 parts of catalyst, 1.4 parts of maleic rosin.
In the present embodiment, the acrylic emulsion it is raw materials used by weight include following components, 15 parts of butyl acrylate,
14 parts of methyl methacrylate, 0.8 part of methacrylic acid, 55 parts of water, 1.3 parts of alkylbenzene polyethers sodium sulfonate, ammonium persulfate 0.3
Part.
In the present embodiment, the filler includes 5 parts of talcum powder, 4 parts of expanded perlite, 1.6 parts of silica flour.
In the present embodiment, the resin group material includes acrylic resin and organic-silicon-modified fluororesin, and acrylic resin
Mass ratio with organic-silicon-modified fluororesin is 1.2: 3.
In the present embodiment, the fire retardant includes 2.6 parts of antimony oxide, 2.3 parts of magnesium hydroxide, 4 parts of aluminium hydroxide.
In the present embodiment, the pigment is the mixture of acetylene carbon dust and carbon black, and the mass ratio of acetylene carbon dust and carbon black
It is 1: 2.
In the present embodiment, the bioantifouling agent includes 0.9 part of alkylamine, 0.3 part of aliphatic acid polyethenoxy ether, poly- second two
1.3 parts of alcohol.
Embodiment three：
A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material include following by weight
Component：50 parts of acrylic emulsion, 14 parts of filler, 24 parts of resin group material, 8.6 parts of fire retardant, 4.4 parts of pigment, bioantifouling agent
10.7 parts, 3.4 parts of styrene, 1.6 parts of zinc pyrithione, 1.5 parts of catalyst, 1.4 parts of maleic rosin.
In the present embodiment, the acrylic emulsion it is raw materials used by weight include following components, 20 parts of butyl acrylate,
15 parts of methyl methacrylate, 1 part of methacrylic acid, 58 parts of water, 1.4 parts of alkylbenzene polyethers sodium sulfonate, 0.4 part of ammonium persulfate.
In the present embodiment, the filler includes 6 parts of talcum powder, 5 parts of expanded perlite, 1.8 parts of silica flour.
In the present embodiment, the resin group material includes acrylic resin and organic-silicon-modified fluororesin, and acrylic resin
Mass ratio with organic-silicon-modified fluororesin is 1.2: 3.
In the present embodiment, the fire retardant includes 2.7 parts of antimony oxide, 2.4 parts of magnesium hydroxide, 4.5 parts of aluminium hydroxide.
In the present embodiment, the pigment is the mixture of acetylene carbon dust and carbon black, and the mass ratio of acetylene carbon dust and carbon black
It is 1: 2.
In the present embodiment, the bioantifouling agent includes 0.9 part of alkylamine, 0.4 part of aliphatic acid polyethenoxy ether, poly- second two
1.4 parts of alcohol.
Example IV：
A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material include following by weight
Component：52 parts of acrylic emulsion, 14.5 parts of filler, 25 parts of resin group material, 8.7 parts of fire retardant, 4.6 parts of pigment, bioantifouling
10.8 parts of agent, 3.6 parts of styrene, 1.7 parts of zinc pyrithione, 1.6 parts of catalyst, 1.5 parts of maleic rosin.
In the present embodiment, the acrylic emulsion it is raw materials used by weight include following components, 25 parts of butyl acrylate,
16 parts of methyl methacrylate, 1.2 parts of methacrylic acid, 60 parts of water, 1.4 parts of alkylbenzene polyethers sodium sulfonate, ammonium persulfate 0.5
Part.
In the present embodiment, the filler includes 7 parts of talcum powder, 4.5 parts of expanded perlite, 1.8 parts of silica flour.
In the present embodiment, the resin group material includes acrylic resin and organic-silicon-modified fluororesin, and acrylic resin
Mass ratio with organic-silicon-modified fluororesin is 1.2: 3.
In the present embodiment, the fire retardant includes 2.8 parts of antimony oxide, 2.5 parts of magnesium hydroxide, 4.5 parts of aluminium hydroxide.
In the present embodiment, the pigment is the mixture of acetylene carbon dust and carbon black, and the mass ratio of acetylene carbon dust and carbon black
It is 1: 2.
In the present embodiment, the bioantifouling agent includes 1 part of alkylamine, 0.5 part of aliphatic acid polyethenoxy ether, polyethylene glycol
1.5 part.
Embodiment five：A kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, raw material is by weight
Part includes following components：55 parts of acrylic emulsion, 15 parts of filler, 26 parts of resin group material, 9 parts of fire retardant, 5 parts of pigment, biology
11 parts of anti-fouling agent, 4 parts of styrene, 1.8 parts of zinc pyrithione, 1.7 parts of catalyst, 1.6 parts of maleic rosin.
In the present embodiment, the acrylic emulsion it is raw materials used by weight include following components, 33 parts of butyl acrylate,
17 parts of methyl methacrylate, 1.4 parts of methacrylic acid, 63 parts of water, 1.6 parts of alkylbenzene polyethers sodium sulfonate, ammonium persulfate 0.6
Part.
In the present embodiment, the filler includes 8 parts of talcum powder, 6 parts of expanded perlite, 2 parts of silica flour.
In the present embodiment, the resin group material includes acrylic resin and organic-silicon-modified fluororesin, and acrylic resin
Mass ratio with organic-silicon-modified fluororesin is 1.2: 3.
In the present embodiment, the fire retardant includes 3 parts of antimony oxide, 2.6 parts of magnesium hydroxide, 6 parts of aluminium hydroxide.
In the present embodiment, the pigment is the mixture of acetylene carbon dust and carbon black, and the mass ratio of acetylene carbon dust and carbon black
It is 1: 2.
In the present embodiment, the bioantifouling agent includes 1.2 parts of alkylamine, 0.6 part of aliphatic acid polyethenoxy ether, poly- second two
1.6 parts of alcohol.
Benefit of the invention：This has the PRTV long-acting and anti-fouling flashing coatings of high hydrophobic and corrosion resistance, materials and proportioning
Rationally, diaphragm can be formed on the surface of power equipment, there is good hydrophobicity and anticorrosive property, antifouling work ensure that electricity
The trouble-free operation of net, high safety, using convenient.
Claims (8)
1. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance, which is characterized in that its raw material is by weight
Part includes following components：40-60 parts of acrylic emulsion, 10-17 parts of filler, 20-30 parts of resin group material, fire retardant 8.2-10
Part, 3-6 parts of pigment, 10-12 parts of bioantifouling agent, 2-6 parts of styrene, 1-2 parts of zinc pyrithione, 1.2-2 parts of catalyst, Malaysia
1-2 parts of rosin.
2. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is that raw material includes following components by weight：45-55 parts of acrylic emulsion, 12-15 parts of filler, resin group material 22-
26 parts, 8.4-9 parts of fire retardant, 4-5 parts of pigment, 10.5-11 parts of bioantifouling agent, 3-4 parts of styrene, zinc pyrithione 1.2-
1.8 parts, 1.4-1.7 parts of catalyst, 1.2-1.6 parts of maleic rosin.
3. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is：The raw materials used acrylic emulsion includes following components, 10-33 parts of butyl acrylate, metering system by weight
Sour methyl esters 13-17 parts, 0.6-1.4 parts of methacrylic acid, 50-63 parts of water, 1.2-1.6 parts of alkylbenzene polyethers sodium sulfonate, persulfuric acid
0.2-0.6 parts of ammonium.
4. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is：The filler includes 4-8 parts of talcum powder, 3-6 parts of expanded perlite, 1.4-2 parts of silica flour.
5. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is：The resin group material includes acrylic resin and organic-silicon-modified fluororesin, and acrylic resin and organic-silicon-modified
The mass ratio of fluororesin is 1.2: 3.
6. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is：The fire retardant includes 2.5-3 parts of antimony oxide, 2.2-2.6 parts of magnesium hydroxide, 3-6 parts of aluminium hydroxide.
7. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is：The pigment is the mixture of acetylene carbon dust and carbon black, and the mass ratio of acetylene carbon dust and carbon black is 1: 2.
8. a kind of PRTV long-acting and anti-fouling flashing coatings with high hydrophobic and corrosion resistance according to claim 1, special
Sign is：The bioantifouling agent includes 0.6-1.2 parts of alkylamine, 0.2-0.6 parts of aliphatic acid polyethenoxy ether, polyethylene glycol
1.2-1.6 part.