CN108757791A - A kind of high-performance electric contact spring leaf - Google Patents
A kind of high-performance electric contact spring leaf Download PDFInfo
- Publication number
- CN108757791A CN108757791A CN201810652023.9A CN201810652023A CN108757791A CN 108757791 A CN108757791 A CN 108757791A CN 201810652023 A CN201810652023 A CN 201810652023A CN 108757791 A CN108757791 A CN 108757791A
- Authority
- CN
- China
- Prior art keywords
- parts
- accounts
- copper
- contact spring
- base layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention is disclosed a kind of high-performance electric contact spring leafs, including internal Hard base layer and external electric contacting layer, the electric contacting layer package is arranged in the Hard base layer outer surface, and the Hard base layer is made of iron, copper, nickel and manganese, and parts by weight are respectively shared by each ingredient:The iron accounts for 81-91 parts, and the copper accounts for 12-20 parts, and the nickel accounts for 8-15 parts, and the manganese accounts for 3-8 parts, and the electric contacting layer is made of gold, copper, chromium and palladium, and parts by weight are respectively shared by each ingredient:The gold accounts for 45-54 parts, and the copper accounts for 29-36 parts, and the chromium accounts for 9-17 parts, and the palladium accounts for 6-12 parts.The present invention has the characteristics that intensity is high, hardness is big, good conductivity, with long service life.
Description
Technical field
The present invention relates to a kind of high-performance electric contact spring leafs.
Background technology
Hot-water heating hardware refers to the general designation of the handware of building water drainage-supply system, heating system and toilet.Usually
Including water nozzle, shower, overboard, closet accessory, bidet accessory, hydro-peening message bathtub accessory, valve, conduit coupling and defend
Other handwares between life.The existing electric contact piece generally use copper material used, soft texture are easy to damage when use
It is bad.
Invention content
Having the characteristics that intensity is high, hardness is big, good conductivity, with long service life the purpose of the present invention is to provide a kind of
High-performance electric contact spring leaf.
The technical scheme is that a kind of high-performance electric contact spring leaf, including internal Hard base layer and outside
Electric contacting layer, the setting of electric contacting layer package in the Hard base layer outer surface, the Hard base layer by iron, copper, nickel with
And manganese forms, parts by weight are respectively shared by each ingredient:The iron accounts for 81-91 parts, and the copper accounts for 12-20 parts, and the nickel accounts for 8-
15 parts, the manganese accounts for 3-8 parts, and the electric contacting layer is made of gold, copper, chromium and palladium, and parts by weight are respectively shared by each ingredient:
The gold accounts for 45-54 parts, and the copper accounts for 29-36 parts, and the chromium accounts for 9-17 parts, and the palladium accounts for 6-12 parts.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient are specially in the Hard base layer:It is described
Iron accounts for 81 parts, and the copper accounts for 12 parts, and the nickel accounts for 8 parts, and the manganese accounts for 3 parts.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient are specially in the electric contacting layer:It is described
Gold accounts for 45 parts, and the copper accounts for 29 parts, and the chromium accounts for 9 parts, and the palladium accounts for 6 parts.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient are specially in the Hard base layer:It is described
Iron accounts for 85 parts, and the copper accounts for 16 parts, and the nickel accounts for 11 parts, and the manganese accounts for 5 parts.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient are specially in the electric contacting layer:It is described
Gold accounts for 49 parts, and the copper accounts for 32 parts, and the chromium accounts for 13 parts, and the palladium accounts for 9 parts.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient are specially in the Hard base layer:It is described
Iron accounts for 91 parts, and the copper accounts for 20 parts, and the nickel accounts for 15 parts, and the manganese accounts for 8 parts.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient are specially in the electric contacting layer:It is described
Gold accounts for 54 parts, and the copper accounts for 36 parts, and the chromium accounts for 17 parts, and the palladium accounts for 12 parts.
Of the present invention is a kind of high-performance electric contact spring leaf, has big intensity height, hardness, good conductivity, use
The characteristics of long lifespan.
Specific implementation mode
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
Of the present invention is a kind of high-performance electric contact spring leaf, including internal Hard base layer and external electrical contact
Layer, the electric contacting layer package are arranged in the Hard base layer outer surface, and the Hard base layer is made of iron, copper, nickel and manganese,
Parts by weight are respectively shared by each ingredient:The iron accounts for 81-91 parts, and the copper accounts for 12-20 parts, and the nickel accounts for 8-15 parts, described
Manganese accounts for 3-8 parts, and the electric contacting layer is made of gold, copper, chromium and palladium, and parts by weight are respectively shared by each ingredient:The gold accounts for
45-54 parts, the copper accounts for 29-36 parts, and the chromium accounts for 9-17 parts, and the palladium accounts for 6-12 parts.
Embodiment one
A kind of high-performance electric contact spring leaf, including internal Hard base layer and external electric contacting layer, the electric contacting layer
Package be arranged in the Hard base layer outer surface, the Hard base layer is made of iron, copper, nickel and manganese, the electric contacting layer by
Gold, copper, chromium and palladium form, and parts by weight shared by each ingredient are specially in the Hard base layer:The iron accounts for 81 parts, the copper
Account for 12 parts, the nickel accounts for 8 parts, and the manganese accounts for 3 parts, and parts by weight shared by each ingredient are specially in the electric contacting layer:The gold
45 parts are accounted for, the copper accounts for 29 parts, and the chromium accounts for 9 parts, and the palladium accounts for 6 parts.
Embodiment two
A kind of high-performance electric contact spring leaf, including internal Hard base layer and external electric contacting layer, the electric contacting layer
Package be arranged in the Hard base layer outer surface, the Hard base layer is made of iron, copper, nickel and manganese, the electric contacting layer by
Gold, copper, chromium and palladium form, and parts by weight shared by each ingredient are specially in the Hard base layer:The iron accounts for 85 parts, the copper
Account for 16 parts, the nickel accounts for 11 parts, and the manganese accounts for 5 parts, and parts by weight shared by each ingredient are specially in the electric contacting layer:The gold
49 parts are accounted for, the copper accounts for 32 parts, and the chromium accounts for 13 parts, and the palladium accounts for 9 parts.
Embodiment three
A kind of high-performance electric contact spring leaf, including internal Hard base layer and external electric contacting layer, the electric contacting layer
Package be arranged in the Hard base layer outer surface, the Hard base layer is made of iron, copper, nickel and manganese, the electric contacting layer by
Gold, copper, chromium and palladium form, and parts by weight shared by each ingredient are specially in the Hard base layer:The iron accounts for 91 parts, the copper
Account for 20 parts, the nickel accounts for 15 parts, and the manganese accounts for 8 parts, and parts by weight shared by each ingredient are specially in the electric contacting layer:The gold
54 parts are accounted for, the copper accounts for 36 parts, and the chromium accounts for 17 parts, and the palladium accounts for 12 parts.
Of the present invention is a kind of high-performance electric contact spring leaf, and the present invention is high with intensity, hardness is big, electric conductivity
Good, feature with long service life.
The foregoing is merely the specific implementation modes of the present invention, but scope of protection of the present invention is not limited thereto, any
Those skilled in the art within the technical scope disclosed by the invention, can without the variation that creative work is expected or
It replaces, should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be limited with claims
Subject to fixed protection domain.
Claims (7)
1. a kind of high-performance electric contact spring leaf, it is characterised in that:The high-performance electric contact spring leaf includes internal
Hard base layer and external electric contacting layer, the electric contacting layer package are arranged in the Hard base layer outer surface, the hard base
Layer is made of iron, copper, nickel and manganese, and parts by weight are respectively shared by each ingredient:The iron accounts for 81-91 parts, and the copper accounts for 12-20
Part, the nickel accounts for 8-15 parts, and the manganese accounts for 3-8 parts, and the electric contacting layer is made of gold, copper, chromium and palladium, weight shared by each ingredient
Measuring number is respectively:The gold accounts for 45-54 parts, and the copper accounts for 29-36 parts, and the chromium accounts for 9-17 parts, and the palladium accounts for 6-12 parts.
2. high-performance electric contact spring leaf according to claim 1, it is characterised in that:Each ingredient institute in the Hard base layer
Accounting for parts by weight is specially:The iron accounts for 81 parts, and the copper accounts for 12 parts, and the nickel accounts for 8 parts, and the manganese accounts for 3 parts.
3. high-performance electric contact spring leaf according to claim 2, it is characterised in that:Each ingredient institute in the electric contacting layer
Accounting for parts by weight is specially:The gold accounts for 45 parts, and the copper accounts for 29 parts, and the chromium accounts for 9 parts, and the palladium accounts for 6 parts.
4. high-performance electric contact spring leaf according to claim 1, it is characterised in that:Each ingredient institute in the Hard base layer
Accounting for parts by weight is specially:The iron accounts for 85 parts, and the copper accounts for 16 parts, and the nickel accounts for 11 parts, and the manganese accounts for 5 parts.
5. high-performance electric contact spring leaf according to claim 4, it is characterised in that:Each ingredient institute in the electric contacting layer
Accounting for parts by weight is specially:The gold accounts for 49 parts, and the copper accounts for 32 parts, and the chromium accounts for 13 parts, and the palladium accounts for 9 parts.
6. high-performance electric contact spring leaf according to claim 1, it is characterised in that:Each ingredient institute in the Hard base layer
Accounting for parts by weight is specially:The iron accounts for 91 parts, and the copper accounts for 20 parts, and the nickel accounts for 15 parts, and the manganese accounts for 8 parts.
7. high-performance electric contact spring leaf according to claim 6, it is characterised in that:Each ingredient institute in the electric contacting layer
Accounting for parts by weight is specially:The gold accounts for 54 parts, and the copper accounts for 36 parts, and the chromium accounts for 17 parts, and the palladium accounts for 12 parts.