CN108748561A - A kind of high-quality colouring method of maize peel - Google Patents
A kind of high-quality colouring method of maize peel Download PDFInfo
- Publication number
- CN108748561A CN108748561A CN201810571342.7A CN201810571342A CN108748561A CN 108748561 A CN108748561 A CN 108748561A CN 201810571342 A CN201810571342 A CN 201810571342A CN 108748561 A CN108748561 A CN 108748561A
- Authority
- CN
- China
- Prior art keywords
- maize peel
- immersion treatment
- colouring method
- treatment
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-quality colouring methods of maize peel, include the following steps：（1）Maize peel pretreatment,（2）Steam explosion treatment,（3）Immersion treatment,（4）Dyeing processing,（5）It is dried.Dyeing treatment processing step collocation of the present invention is reasonable, and integrated operation is simple, convenient for promoting, hence it is evident that improves the effect of dyeing processing, maize peel stay in grade that treated, fugitive color, does not have the good market competitiveness and economic benefit.
Description
Technical field
The invention belongs to weaving fields, and in particular to a kind of high-quality colouring method of maize peel.
Background technology
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project for becoming selected areas of China foreign exchange earning gradually.The whole nation has three big
Wicker plaiting article production base：Shandong, Henan and Anhui.
Maize peel is a kind of important wicker plaiting article raw material, and maize peel has excellent flexibility and tensile strength, very suitable
It closes and carries out wicker plaiting article, but maize peel is not easy to be dyed, and is easy to fade after dyeing, causes the color of product single, or dyeing
Afterwards, maize peel uneven color influences the quality of flax and cornstraw weaving fabric.Therefore, constantly improve the dyeing treatment process of maize peel
It is the most important thing of those skilled in the art.
Invention content
The purpose of the present invention is for existing problem, provide a kind of high-quality colouring method of maize peel.
The present invention is achieved by the following technical solutions：
A kind of high-quality colouring method of maize peel, includes the following steps：
（1）Maize peel pre-processes：
After maize peel is rinsed well, then be cut to width be 1.5 ~ 2cm strip it is spare；
（2）Steam explosion treatment：
By step（1）Treated, and maize peel is put into progress Steam explosion treatment in steam blasting tank, specifically first to steam
It is passed through temperature in cavity charge containers and is 103 ~ 106 DEG C of vapor, and the pressure in steam blasting tank is increased into 0.35 ~ 0.40MPa, protects
It after warm pressurize handles 14 ~ 16min, then quickly unloads to normal temperature and pressure, and maize peel is taken out spare；
（3）Immersion treatment：
By step（2）Treated, and maize peel is put into the immersion treatment liquid of surface, takes maize peel after 1 ~ 1.5h of immersion treatment
Go out spare, is during which continuously applied ultrasonic wave and is handled；The surface immersion treatment liquid by following parts by weight material composition：
2 ~ 4 parts of sodium bicarbonates, 0.1 ~ 0.2 part of nano-carbon powder, 1 ~ 3 part of chitosan, 0.5 ~ 1 part of sodium pyrophosphate, 1 ~ 1.5 part of tween, 100 ~
120 parts of water；
（4）Dyeing is handled：
By step（3）Treated, and maize peel is put into dyeing liquor, is taken out maize peel after 1 ~ 2h of immersion treatment spare；It is soaking
Direct current treatment is also applied with into dyeing liquor during bubble processing；
（5）It is dried：
By step（4）Treated maize peel is put into dry in drying box to water content no more than 8% after.
Further, step（2）Described in quickly to unload to normal temperature and pressure processing be in will be in steam blasting tank in 2min
Temperature and pressure unload to normal temperature and pressure.
Further, step（3）Described in ultrasonication when frequency be 400 ~ 450kHz.
Further, step（3）Described in nano-carbon powder grain diameter be 20 ~ 70nm.
Further, step（4）Described in immersion treatment when heating keep dyeing liquor temperature be 40 ~ 45 DEG C.
Further, step（4）Described in Direct current treatment when control electric current intensity be 40 ~ 45mA.
Further, step（5）Described in drying process when control drying box in temperature be 90 ~ 95 DEG C.
The present invention has the following advantages compared with prior art：
Present invention improves the dyeing treatments of existing maize peel, improve the effect of dyeing processing well.Wherein, first right
It has carried out Steam explosion treatment, and effective loose structure of fibrous tissue expands the gaps such as pit membrane, is subsequent processing
It lays a good foundation, has then carried out immersion treatment, a kind of surface immersion treatment liquid has been prepared, in the effect of weak base and ultrasonic wave
Under, the nano-carbon powder ingredient included has penetrated into the textura epidermoidea gap of maize peel, when then carrying out dyeing processing, dyestuff
The same absorption of grain is fixed in the textura epidermoidea gap of maize peel, is contacted with nano-carbon powder particle, is then applied at direct current
Reason, under the action of direct current, nano-carbon powder conduction generates charge, then surface-active enhancing is reticulated with chitosan complex
Dye granule is fixed in tissue, enhances the stability of dyeing, and moisture removal is finally dried and completes dyeing.The present invention
The collocation of dyeing treatment processing step is reasonable, and integrated operation is simple, convenient for promoting, hence it is evident that the effect of dyeing processing is improved,
Maize peel stay in grade that treated, fugitive color, does not have the good market competitiveness and economic benefit.
Specific implementation mode
Embodiment 1
A kind of high-quality colouring method of maize peel, includes the following steps：
（1）Maize peel pre-processes：
After maize peel is rinsed well, then be cut to width be 1.5 ~ 2cm strip it is spare；
（2）Steam explosion treatment：
By step（1）Treated, and maize peel is put into progress Steam explosion treatment in steam blasting tank, specifically first to steam
It is 103 DEG C of vapor that temperature is passed through in cavity charge containers, and the pressure in steam blasting tank is increased to 0.35MPa, at heat-insulation pressure keeping
It after managing 14min, then quickly unloads to normal temperature and pressure, and maize peel is taken out spare；
（3）Immersion treatment：
By step（2）Treated, and maize peel is put into the immersion treatment liquid of surface, is taken out maize peel after immersion treatment 1h standby
With being during which continuously applied ultrasonic wave and handled；The surface immersion treatment liquid by following parts by weight material composition：2 parts
Sodium bicarbonate, 0.1 part of nano-carbon powder, 1 part of chitosan, 0.5 part of sodium pyrophosphate, 1 part of tween, 100 parts of water；
（4）Dyeing is handled：
By step（3）Treated, and maize peel is put into dyeing liquor, is taken out maize peel after immersion treatment 1h spare；It is impregnating
Direct current treatment is also applied with during processing into dyeing liquor；
（5）It is dried：
By step（4）Treated maize peel is put into dry in drying box to water content no more than 8% after.
Further, step（2）Described in quickly to unload to normal temperature and pressure processing be in will be in steam blasting tank in 2min
Temperature and pressure unload to normal temperature and pressure.
Further, step（3）Described in ultrasonication when frequency be 400kHz.
Further, step（3）Described in nano-carbon powder grain diameter be 20 ~ 70nm.
Further, step（4）Described in immersion treatment when heating keep dyeing liquor temperature be 40 DEG C.
Further, step（4）Described in Direct current treatment when control electric current intensity be 40mA.
Further, step（5）Described in drying process when control drying box in temperature be 90 DEG C.
Embodiment 2
A kind of high-quality colouring method of maize peel, includes the following steps：
（1）Maize peel pre-processes：
After maize peel is rinsed well, then be cut to width be 1.5 ~ 2cm strip it is spare；
（2）Steam explosion treatment：
By step（1）Treated, and maize peel is put into progress Steam explosion treatment in steam blasting tank, specifically first to steam
It is 105 DEG C of vapor that temperature is passed through in cavity charge containers, and the pressure in steam blasting tank is increased to 0.38MPa, at heat-insulation pressure keeping
It after managing 15min, then quickly unloads to normal temperature and pressure, and maize peel is taken out spare；
（3）Immersion treatment：
By step（2）Treated, and maize peel is put into the immersion treatment liquid of surface, takes out maize peel after immersion treatment 1.2h
It is spare, it is during which continuously applied ultrasonic wave and is handled；The surface immersion treatment liquid by following parts by weight material composition：3
Part sodium bicarbonate, 0.15 part of nano-carbon powder, 2 parts of chitosans, 0.8 part of sodium pyrophosphate, 1.3 parts of tweens, 110 parts of water；
（4）Dyeing is handled：
By step（3）Treated, and maize peel is put into dyeing liquor, is taken out maize peel after immersion treatment 1.5h spare；It is soaking
Direct current treatment is also applied with into dyeing liquor during bubble processing；
（5）It is dried：
By step（4）Treated maize peel is put into dry in drying box to water content no more than 8% after.
Further, step（2）Described in quickly to unload to normal temperature and pressure processing be in will be in steam blasting tank in 2min
Temperature and pressure unload to normal temperature and pressure.
Further, step（3）Described in ultrasonication when frequency be 430kHz.
Further, step（3）Described in nano-carbon powder grain diameter be 20 ~ 70nm.
Further, step（4）Described in immersion treatment when heating keep dyeing liquor temperature be 42 DEG C.
Further, step（4）Described in Direct current treatment when control electric current intensity be 43mA.
Further, step（5）Described in drying process when control drying box in temperature be 92 DEG C.
Embodiment 3
A kind of high-quality colouring method of maize peel, includes the following steps：
（1）Maize peel pre-processes：
After maize peel is rinsed well, then be cut to width be 1.5 ~ 2cm strip it is spare；
（2）Steam explosion treatment：
By step（1）Treated, and maize peel is put into progress Steam explosion treatment in steam blasting tank, specifically first to steam
It is 106 DEG C of vapor that temperature is passed through in cavity charge containers, and the pressure in steam blasting tank is increased to 0.40MPa, at heat-insulation pressure keeping
It after managing 16min, then quickly unloads to normal temperature and pressure, and maize peel is taken out spare；
（3）Immersion treatment：
By step（2）Treated, and maize peel is put into the immersion treatment liquid of surface, takes out maize peel after immersion treatment 1.5h
It is spare, it is during which continuously applied ultrasonic wave and is handled；The surface immersion treatment liquid by following parts by weight material composition：4
Part sodium bicarbonate, 0.2 part of nano-carbon powder, 3 parts of chitosans, 1 part of sodium pyrophosphate, 1.5 parts of tweens, 120 parts of water；
（4）Dyeing is handled：
By step（3）Treated, and maize peel is put into dyeing liquor, is taken out maize peel after immersion treatment 2h spare；It is impregnating
Direct current treatment is also applied with during processing into dyeing liquor；
（5）It is dried：
By step（4）Treated maize peel is put into dry in drying box to water content no more than 8% after.
Further, step（2）Described in quickly to unload to normal temperature and pressure processing be in will be in steam blasting tank in 2min
Temperature and pressure unload to normal temperature and pressure.
Further, step（3）Described in ultrasonication when frequency be 450kHz.
Further, step（3）Described in nano-carbon powder grain diameter be 20 ~ 70nm.
Further, step（4）Described in immersion treatment when heating keep dyeing liquor temperature be 45 DEG C.
Further, step（4）Described in Direct current treatment when control electric current intensity be 45mA.
Further, step（5）Described in drying process when control drying box in temperature be 95 DEG C.
Comparative example 1
This comparative example 1 compared with Example 2, in step（3）Receiving in the immersion treatment liquid of surface is eliminated in immersion treatment
Rice carbon dust ingredient, method and step all same in addition to this.
Comparative example 2
This comparative example 2 compared with Example 2, in step（4）Direct current treatment operation is eliminated in dyeing processing, in addition to this
Method and step all same.
Comparative example 3
This comparative example 3 compared with Example 2, in step（3）Receiving in the immersion treatment liquid of surface is eliminated in immersion treatment
Rice carbon dust ingredient, while in step（4）Direct current treatment operation is eliminated in dyeing processing, method and step in addition to this is homogeneous
Together.
In order to compare effect of the present invention, the maize peel with a batch harvesting is selected as experimental subjects, respectively with above-mentioned implementation
Example 2, comparative example 1, comparative example 2,3 corresponding method of comparative example carry out dyeing processing, used in dye
Liquid is the reactive brilliant bule K-GR aqueous solutions that mass fraction is 7%, carries out dyeing quality survey to the maize peel after dyeing after the completion
Examination, specific correction data are as shown in table 1 below：
Table 1
Note：Colour fading duration described in upper table 1 is that maize peel is put into the saline solution that temperature is 58 DEG C, mass fraction is 4.7%
Middle immersion treatment, the most short immersion duration when apparent fade occurs in maize peel is colour fading duration；The aberration rate is same
After kind method different batches dye maize peel, utilizes " L*a*b* colour systems " to be detected comparison and converse difference
Average dye aberration rate between batch, with the harmony and stability of characterization dyeing.
The method of the present invention can effectively promote the dyeing treatment effect to maize peel it can be seen from upper table 1, well
The coloring quality of maize peel is improved, there is good application value and the market competitiveness.
Claims (7)
1. a kind of high-quality colouring method of maize peel, which is characterized in that include the following steps：
（1）Maize peel pre-processes：
After maize peel is rinsed well, then be cut to width be 1.5 ~ 2cm strip it is spare；
（2）Steam explosion treatment：
By step（1）Treated, and maize peel is put into progress Steam explosion treatment in steam blasting tank, specifically first to steam
It is passed through temperature in cavity charge containers and is 103 ~ 106 DEG C of vapor, and the pressure in steam blasting tank is increased into 0.35 ~ 0.40MPa, protects
It after warm pressurize handles 14 ~ 16min, then quickly unloads to normal temperature and pressure, and maize peel is taken out spare；
（3）Immersion treatment：
By step（2）Treated, and maize peel is put into the immersion treatment liquid of surface, takes maize peel after 1 ~ 1.5h of immersion treatment
Go out spare, is during which continuously applied ultrasonic wave and is handled；The surface immersion treatment liquid by following parts by weight material composition：
2 ~ 4 parts of sodium bicarbonates, 0.1 ~ 0.2 part of nano-carbon powder, 1 ~ 3 part of chitosan, 0.5 ~ 1 part of sodium pyrophosphate, 1 ~ 1.5 part of tween, 100 ~
120 parts of water；
（4）Dyeing is handled：
By step（3）Treated, and maize peel is put into dyeing liquor, is taken out maize peel after 1 ~ 2h of immersion treatment spare；It is soaking
Direct current treatment is also applied with into dyeing liquor during bubble processing；
（5）It is dried：
By step（4）Treated maize peel is put into dry in drying box to water content no more than 8% after.
2. a kind of high-quality colouring method of maize peel according to claim 1, which is characterized in that step（2）Described in
Quickly to unload to normal temperature and pressure processing be in unloading the temperature and pressure in steam blasting tank to normal temperature and pressure in 2min.
3. a kind of high-quality colouring method of maize peel according to claim 1, which is characterized in that step（3）Described in
Ultrasonication when frequency be 400 ~ 450kHz.
4. a kind of high-quality colouring method of maize peel according to claim 1, which is characterized in that step（3）Described in
Nano-carbon powder grain diameter be 20 ~ 70nm.
5. a kind of high-quality colouring method of maize peel according to claim 1, which is characterized in that step（4）Described in
Immersion treatment when heating keep dyeing liquor temperature be 40 ~ 45 DEG C.
6. a kind of high-quality colouring method of maize peel according to claim 1, which is characterized in that step（4）Described in
Direct current treatment when control electric current intensity be 40 ~ 45mA.
7. a kind of high-quality colouring method of maize peel according to claim 1, which is characterized in that step（5）Described in
Drying process when control drying box in temperature be 90 ~ 95 DEG C.