CN108748508A - A kind of pretreating process of wooden bathroom cabinet board - Google Patents
A kind of pretreating process of wooden bathroom cabinet board Download PDFInfo
- Publication number
- CN108748508A CN108748508A CN201810415651.5A CN201810415651A CN108748508A CN 108748508 A CN108748508 A CN 108748508A CN 201810415651 A CN201810415651 A CN 201810415651A CN 108748508 A CN108748508 A CN 108748508A
- Authority
- CN
- China
- Prior art keywords
- wooden boards
- wooden
- bathroom cabinet
- cabinet board
- pretreating process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to bathroom suite technical fields, and in particular to a kind of pretreating process of wooden bathroom cabinet board, including：(1) molding wooden boards immersion treatment will be cut, then lifts and drains；It (2) will be in the wooden boards pile to vacuum drying chamber in step (1), low temperature drying, then it takes out and is immersed into immersion treatment in protective liquid, then lift and drain and again in pile to vacuum drying chamber, 140~150 DEG C are warming up to, by wooden boards surface carbonation, then stops heating, closed to be cooled to room temperature, pressure release obtains semi-finished product；(3) surface of semi-finished obtained in step (2) is brushed at least protects paint three times, per minor tick 10min or more；The present invention is handled successively from the inside of wooden boards to outside, solves mould rotten problem on deformation caused by the worm's ovum, microorganism that wooden boards itself may contain, wooden boards are handled from inside to outside simultaneously, improve the hardness of wooden boards, the ability of waterproof ability and anti-mildew corruption deformation.
Description
Technical field
The invention belongs to bathroom suite technical fields, and in particular to a kind of pretreating process of wooden bathroom cabinet board.
Background technology
Bathroom cabinet board is chronically in the environment of dark humidity, and bathroom cabinet made of wooden boards is easy to happen mould rotten change
The problem of shape, growth bacterial micro-organism.Protection processing often is carried out to the surface of wooden boards in the prior art, cost is higher, and
After undergoing long-term high and low temperature environment, wooden boards easily deform, and the protective layer on surface is easy to happen peeling, falls off
Phenomenon also will produce mould rotten the problem of deforming, and be easy accumulation steam at peeling, become the hotbed of microbial reproduction, not only shadow
The appearance for ringing bathroom cabinet board, can also influence the service life of bathroom cabinet board.
Invention content
For the problems of the prior art, the purpose of the present invention is to provide a kind of pretreatments for wooden bathroom cabinet board
Technique avoids wooden boards that mould rotten deformation occurs in dark wet environment, improves the service life of bathroom cabinet board.
To achieve the goals above, the present invention is achieved by the following scheme：
A kind of pretreating process of wooden bathroom cabinet board, includes the following steps：
(1) molding wooden boards immersion treatment will be cut 3~10 days, and will then lift and drains；
(2) by step (1) wooden boards dislocation pile to vacuum drying chamber in, low temperature drying, then by wood based panel
Material takes out and is immersed into 30~60min of immersion treatment in protective liquid, then lift drain and again dislocation pile to be dried in vacuo
In case, 140~150 DEG C are warming up to, by wooden boards surface carbonation, then stops heating, closed to be cooled to room temperature, pressure release obtains half
Finished product；
(3) surface of semi-finished obtained in step (2) is brushed at least protects paint three times, per minor tick 10min or more.
Preferably, in step (1), the soak for impregnating wooden boards is that sodium bicarbonate and water are 1 in mass ratio：
The mixed solution of (25~30).
Preferably, in step (1), the temperature of the soak for impregnating wooden boards is 40~55 DEG C.
Preferably, in step (1), wooden boards are aided with air blower blowing auxiliary and drain, cool down during draining.
Preferably, the protective liquid is that dimethyl didecyl ammonium chloride and inertia latex mix.
Preferably, in step (2), the thickness of the carburization zone of wooden boards is 0.5~2mm.
Compared with prior art, the present invention has the following technical effects：
In the present invention, by carrying out immersion treatment to cutting molding wooden boards, the oil contained in wooden boards is removed
Fat ingredient, and the worm's ovum contained in wooden boards, microorganism are killed, prevent wooden boards from occurring during subsequent use
The problem of inside goes mouldy, damages by worms；
After preliminary treatment, by wooden boards low temperature drying, then the immersion treatment in protective liquid, makes inside wooden boards
The active ingredient in protective liquid is adsorbed, high-temperature baking then is carried out to wooden boards again, is formed on its surface carburization zone, to
The problem of having prevented that mould rotten deformation occurs during the follow-up use of wooden boards, in addition, the carburization zone tool that the surface is formed
There is certain hardness so that the hardness on wooden boards surface increases, and improves the wear-resisting property of wooden bathroom cabinet board；
In last processing stage, surface, which is formed on the wooden boards of carburization zone, brushes protection paint, and protection paint immerses
To the inside of wooden boards, during the follow-up use of wooden boards, when the inside expanded by heating of wooden boards, inside is immersed
Protection paint there is certain water repellent ability, avoid the absorption expansion of wooden boards, and when wooden boards are by cold events, it is interior
The protection paint that portion is immersed is by the surface for being expressed into wooden boards of a part, to form a waterproof layer, to prevent wood
The problem of lumber is invaded when high/low temperature changes by steam.
The pretreating process of wooden bathroom cabinet board provided by the invention is handled successively from the inside of wooden boards to outside,
Solve mould rotten problem on deformation caused by the worm's ovum, microorganism that wooden boards itself may contain, at the same to wooden boards by
It is interior to be handled to outer, improve the hardness of wooden boards, the ability of waterproof ability and anti-mildew corruption deformation.
Specific implementation mode
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is furture elucidated.
It is easy to happen mould rotten deformation when being used in dark wet environment in conjunction with wooden bathroom cabinet board in the prior art, uses
The technical issues of short life, the present invention provides a kind of pretreating process of wooden bathroom cabinet board, include the following steps：
(1) molding wooden boards immersion treatment will be cut 3~10 days, and will then lift and drains；
(2) by step (1) wooden boards dislocation pile to vacuum drying chamber in, low temperature drying, then by wood based panel
Material takes out and is immersed into 30~60min of immersion treatment in protective liquid, then lift drain and again dislocation pile to be dried in vacuo
In case, 140~150 DEG C are warming up to, by wooden boards surface carbonation, then stops heating, closed to be cooled to room temperature, pressure release obtains half
Finished product；
(3) surface of semi-finished obtained in step (2) is brushed at least protects paint three times, per minor tick 10min or more.
In step (1), by the purpose of wooden boards immersion treatment be to kill the worm's ovum that contains of wooden boards itself and
Microorganism, and the lubricant component that immersion keeps it internal is carried out to wooden boards and is adequately soaked out；In addition, this immersion
The mode of processing can also make to cause in wooden boards the extract of sapstain to be impregnated removing so that wooden boards are follow-up
Color is kept during use.Soak for wooden boards immersion treatment can select in a wider scope, as excellent
Choosing, use sodium bicarbonate and water in mass ratio for 1：The mixed solution that (25~30) mix.
It is further preferred that in order to improve the efficiency of immersion, the temperature of the soak for impregnating wooden boards is 40~
55℃。
After the completion of immersion treatment, the soak on wooden boards is carried out to drain processing, processing is drained in order to improve
Efficiency is aided with air blower blowing auxiliary during wooden boards drain and drains, cools down.Accelerating the speed of the step can subtract
Again attachment of the microorganism to wooden boards in few environment, inventor has found in actual experiment, if Draining time is long,
Some bacteriums, microorganism can be penetrated into again again inside wooden boards.
In the present invention, the technique toasted using cryogenic vacuum is removed the moisture being rich in wooden boards, specifically
In technique, the vacuum degree for controlling vacuum drying chamber is 0.09~0.40Mpa, and the temperature of baking is 45~50 DEG C, by wooden boards
The preliminary moisture content that is baked to is 15% or so.Cryogenic vacuum baking process in this way, avoids wooden boards and is going
The cracking phenomena caused by variation is too fast during moisture removal；Dislocation pile of the present invention, i.e., interlock wooden boards
It piles up, improves the ventilation effect between wooden boards.
After the completion of drying and processing, wooden boards are immersed into protective liquid and carry out immersion treatment, makes having in protective liquid
Effect ingredient is immersed in the inside of wooden boards, and plays a role during the follow-up use of wooden boards, preferably, institute
The protective liquid stated is that dimethyl didecyl ammonium chloride and inertia latex mix.
The dimethyl didecyl ammonium chloride is a kind of common mothproofing agent, can effectively control insect pest, inertia latex conduct
Adhesive can enumerate synthetic latex well-known to those skilled in the art, such as polybutadiene latex, styrene-butadiene latex, admittedly contain
Amount is 20~30%.
In the present invention, by wooden boards into line misregistration pile, and it is warming up to 140~150 DEG C under vacuum conditions, it will be wooden
The surface of plank carries out carbonization treatment, during carbonization treatment, to prevent wooden boards to be burnt excessively, controls vacuum degree
Stop heating after the completion of carbonization treatment for 0.09~0.40Mpa, and be cooled to room temperature in confined conditions, then let out
Pressure obtains the wooden boards of surface carbonation completion.Further, in the present invention, carbonization layer thickness is too low, it is difficult to ensure preferable
Hardness and protection effect, and the layer thickness that is carbonized is excessively high, the time of high-temperature baking needs to extend, and does not bring more effects but,
Cost performance is too low.Preferably, the thickness of the carburization zone on wooden boards surface is 0.5~2mm,
It in the present invention, is painted by brushing multiple protection in surface of semi-finished, makes to suck preservative oil inside wooden boards
Paint plays the function and effect of protection, and protection paint can be selected as those skilled in the art institute is commonly anti-for plank
The paint of shield, such as wood wax oil, tung oil.
Below by way of specific embodiment, the present invention is described further：
Embodiment 1
A kind of pretreating process of wooden bathroom cabinet board, includes the following steps：
(1) molding wooden boards immersion treatment will be cut 7 days, soak used be sodium bicarbonate and water in mass ratio
It is 1：The temperature of 28 mixed solution, soak is 45 DEG C；Then lift and drain, and be aided with air blower during draining and blow
Wind auxiliary is drained, is cooled down；
(2) by the wooden boards dislocation pile to vacuum drying chamber in step (1), the vacuum degree of vacuum drying chamber is controlled
Temperature for 0.25Mpa, baking is 45 DEG C, and it is 15% to be dried to moisture content through wooden boards, then takes out wooden boards simultaneously
It is immersed into immersion treatment 40min in protective liquid, the protective liquid is that dimethyl didecyl ammonium chloride and inertia latex press quality
Than 1：0.4 mixes；
Then lift drain and again misplace pile to vacuum drying chamber in, control vacuum degree be 0.30Mpa, be warming up to
145 DEG C, by wooden boards surface carbonation, then stop heating, closed to be cooled to room temperature, pressure release obtains semi-finished product, wooden boards table
The thickness of face carburization zone is 1.8mm；
(3) it is (limited purchased from Dongguan City money woods environmental protection science and technology to brush wood wax oil three times for the surface of semi-finished obtained in step (2)
The superpower infiltration wood wax oil of company's production), per minor tick 15min.
Embodiment 2
A kind of pretreating process of wooden bathroom cabinet board, includes the following steps：
(1) molding wooden boards immersion treatment will be cut 3 days, soak used be sodium bicarbonate and water in mass ratio
It is 1：The temperature of 25 mixed solution, soak is 55 DEG C；Then lift and drain, and be aided with air blower during draining and blow
Wind auxiliary is drained, is cooled down；
(2) by the wooden boards dislocation pile to vacuum drying chamber in step (1), the vacuum degree of vacuum drying chamber is controlled
Temperature for 0.09Mpa, baking is 45 DEG C, and it is 15% to be dried to moisture content through wooden boards, then takes out wooden boards simultaneously
It is immersed into immersion treatment 30min in protective liquid, the protective liquid is that dimethyl didecyl ammonium chloride and inertia latex press quality
Than 1：0.2) it mixes；
Then lift drain and again misplace pile to vacuum drying chamber in, control vacuum degree be 0.09Mpa, be warming up to
140 DEG C, by wooden boards surface carbonation, then stop heating, closed to be cooled to room temperature, pressure release obtains semi-finished product, wooden boards table
The thickness of face carburization zone is 0.5mm；
(3) it is (limited purchased from Dongguan City money woods environmental protection science and technology to brush wood wax oil three times for the surface of semi-finished obtained in step (2)
The superpower infiltration wood wax oil of company's production), per minor tick 15min.
Embodiment 3
A kind of pretreating process of wooden bathroom cabinet board, includes the following steps：
(1) molding wooden boards immersion treatment will be cut 10 days, soak used is that sodium bicarbonate and water press quality
Than being 1：The temperature of 30 mixed solution, soak is 40 DEG C；Then lift and drain, and be aided with air blower during draining
Blowing auxiliary is drained, is cooled down；
(2) by the wooden boards dislocation pile to vacuum drying chamber in step (1), the vacuum degree of vacuum drying chamber is controlled
Temperature for 0.40Mpa, baking is 45 DEG C, and it is 15% to be dried to moisture content through wooden boards, then takes out wooden boards simultaneously
It is immersed into immersion treatment 60min in protective liquid, the protective liquid is that dimethyl didecyl ammonium chloride and inertia latex press quality
Than 1：0.5 mixes；
Then lift drain and again misplace pile to vacuum drying chamber in, control vacuum degree be 0.40Mpa, be warming up to
150 DEG C, by wooden boards surface carbonation, then stop heating, closed to be cooled to room temperature, pressure release obtains semi-finished product, wooden boards table
The thickness of face carburization zone is 2mm；
(3) it is (limited purchased from Dongguan City money woods environmental protection science and technology to brush wood wax oil three times for the surface of semi-finished obtained in step (2)
The superpower infiltration wood wax oil of company's production), per minor tick 15min.
Comparative example 1
The present embodiment is identical as the pretreating process of wooden bathroom cabinet board of embodiment 1, unlike, rate-determining steps (2)
The time of middle vacuum high-temperature baking, it is 0.2mm to make the thickness for the carburization zone to be formed.Remaining treatment process is consistent.
Comparative example 2
The present embodiment is identical as the pretreating process of wooden bathroom cabinet board of embodiment 1, unlike, in step (2),
Baking is not carried out to wooden bathroom cabinet board and form carburization zone, remaining treatment process is consistent, specifically：
A kind of pretreating process of wooden bathroom cabinet board, includes the following steps：
(1) molding wooden boards immersion treatment will be cut 7 days, soak used be sodium bicarbonate and water in mass ratio
It is 1：The temperature of 28 mixed solution, soak is 45 DEG C；Then lift and drain, and be aided with air blower during draining and blow
Wind auxiliary is drained, is cooled down；
(2) by the wooden boards dislocation pile to vacuum drying chamber in step (1), the vacuum degree of vacuum drying chamber is controlled
Temperature for 0.25Mpa, baking is 45 DEG C, and it is 15% to be dried to moisture content through wooden boards, then takes out wooden boards simultaneously
It is immersed into immersion treatment 40min in protective liquid, the protective liquid is that dimethyl didecyl ammonium chloride and inertia latex press quality
Than 1：0.4 mixes, and then lifts and drains, obtains semi-finished product；
(3) it is (limited purchased from Dongguan City money woods environmental protection science and technology to brush wood wax oil three times for the surface of semi-finished obtained in step (2)
The superpower infiltration wood wax oil of company's production), per minor tick 15min.
Comparative example 3
The present embodiment is identical as the pretreating process of wooden bathroom cabinet board of embodiment 1, unlike, in step (2),
The immersion treatment of protective liquid is not carried out to wooden bathroom cabinet board, remaining treatment process is consistent, specifically：
A kind of pretreating process of wooden bathroom cabinet board, includes the following steps：
(1) molding wooden boards immersion treatment will be cut 7 days, soak used be sodium bicarbonate and water in mass ratio
It is 1：The temperature of 28 mixed solution, soak is 45 DEG C；Then lift and drain, and be aided with air blower during draining and blow
Wind auxiliary is drained, is cooled down；
(2) by the wooden boards dislocation pile to vacuum drying chamber in step (1), the vacuum degree of vacuum drying chamber is controlled
Temperature for 0.25Mpa, baking is 45 DEG C, and it is 15% to be dried to moisture content through wooden boards, then continues to be warming up to 145 DEG C,
By wooden boards surface carbonation, then stop heating, closed to be cooled to room temperature, pressure release obtains semi-finished product, wooden boards surface carbonation
The thickness of layer is 1.8mm；
(3) it is (limited purchased from Dongguan City money woods environmental protection science and technology to brush wood wax oil three times for the surface of semi-finished obtained in step (2)
The superpower infiltration wood wax oil of company's production), per minor tick 15min.
Performance test：
1, each 3 pieces of wooden bathroom cabinet board plank being prepared in above-described embodiment is taken, is put into high temperature and humidity alternation case
The testing experiment for carrying out letter patience, using the high/low temperature of the model HS-100 of Nanjing Stettlen testing equipment Co., Ltd production
Alternating temperature humidity test chamber is tested.
(1) Control experiment condition is 60 DEG C, 90%RH, and test period 480h records the appearance feelings of wooden boards
In condition to table 1.
(2) Control experiment condition is -20 DEG C~60 DEG C alternations, and residence time 1h, the number of alternations is 120 times, record wood
In the appearance situation to table 1 of lumber.
The appearance situation of wooden boards is differentiated with following standard：
○：Surface is intact, and wooden boards do not deform upon；
△：Slightly peeling, having slight bending occur in surface；
╳：There is more serious skin effect phenomenon in surface, and plank both ends warpage is serious.
2, each 3 pieces of wooden bathroom cabinet board plank being prepared in above-described embodiment is taken, moist open air, observation 1 are put into
The mould rotten situation of month rear surface.
Table 1：
Can be seen that wooden bathroom cabinet board provided by the invention by above-mentioned test data has higher-strength, Yi Jikang
The ability of mould corruption deformation.
The basic principles and main features and the features of the present invention of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement is both fallen in the range of claimed invention.The scope of protection of present invention is by appended claims
And its equivalent thereof.
Claims (6)
1. a kind of pretreating process of wooden bathroom cabinet board, it is characterised in that：Include the following steps：
(1) molding wooden boards immersion treatment will be cut 3~10 days, and will then lift and drains；
(2) by the wooden boards dislocation pile to vacuum drying chamber in step (1), low temperature drying then takes wooden boards
Go out and be immersed into 30~60min of immersion treatment in protective liquid, then lift drain and again misplace pile to vacuum drying chamber in,
140~150 DEG C are warming up to, by wooden boards surface carbonation, then stops heating, closed to be cooled to room temperature, pressure release obtains semi-finished product；
(3) surface of semi-finished obtained in step (2) is brushed at least protects paint three times, per minor tick 10min or more.
2. the pretreating process of wooden bathroom cabinet board according to claim 1, it is characterised in that：In step (1), for soaking
The soak of bubble wood lumber is that sodium bicarbonate and water are 1 in mass ratio：The mixed solution of (25~30).
3. the pretreating process of wooden bathroom cabinet board according to claim 1, it is characterised in that：In step (1), for soaking
The temperature of the soak of bubble wood lumber is 40~55 DEG C.
4. the pretreating process of wooden bathroom cabinet board according to claim 1, it is characterised in that：In step (1), wood based panel
Material is aided with air blower blowing auxiliary and drains, cools down during draining.
5. the pretreating process of wooden bathroom cabinet board according to claim 1, it is characterised in that：The protective liquid is two
Methyl didecyl ammonium chloride and inertia latex mix.
6. the pretreating process of wooden bathroom cabinet board according to claim 1, it is characterised in that：In step (2), wood based panel
The thickness of the carburization zone of material is 0.5~2mm.