CN108728227A - Anti-oxidant self-restoring lubricating oil - Google Patents
Anti-oxidant self-restoring lubricating oil Download PDFInfo
- Publication number
- CN108728227A CN108728227A CN201810785827.6A CN201810785827A CN108728227A CN 108728227 A CN108728227 A CN 108728227A CN 201810785827 A CN201810785827 A CN 201810785827A CN 108728227 A CN108728227 A CN 108728227A
- Authority
- CN
- China
- Prior art keywords
- butyl
- parts
- lanthanum fluoride
- lubricating oil
- molybdenum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The anti-oxidant self-restoring lubricating oil of the present invention, including 50~55 parts of polyalphaolefin PAO4,18~27 parts of polyalphaolefin PAO6,12~18 parts of hexanedioic acid esters, 8~12 parts of VI improver SV260,0.2~0.6 part of pour-point depressant T248,7~8 part of 55501 additive and 5~10 parts of organic molybdenum additives and 1^5 parts of nanometer lanthanum fluoride additives；Nanometer lanthanum fluoride additive uses ethanol-water solution as reaction medium, and ethyl alcohol is 3 with water volume ratio:1, and include coating material and lanthanum fluoride；Coating material is 2 with lanthanum fluoride molar ratio:1；It is 10m or so that the Property of Capped Inorganic Nanoparticles average grain diameter that nanometer lanthanum fluoride additive includes is synthesized in alcohol-water system, and without apparent agglomeration.
Description
Technical field
The present invention relates to chemical industry grease and preparation method thereof technical field, more particularly to lubricating oil and preparation method thereof, specifically
, show a kind of anti-oxidant self-restoring lubricating oil.
Background technology
The lubricant by-product that the oxygen in by air, fuel combustion generate in use is (sulfur-containing compound, nitrogenous
Compound etc.), the catalytic action of high temperature and some metals etc., it may occur that a series of oxidations, polymerization such as decompose at the chemical changes,
Cause to generate a series of consequences, such as burn into oil viscosity changes, generates paint film and greasy filth；Oxidation is lubricant deterioration deterioration
The main reason for, it substantially reduces the service life of lubricant.
The phenomenon that fretting wear is generally existing in friction process, according to statistics, more than a world's one third performance
The loss in source carrys out self-friction, and therefore, economic loss caused by reducing friction and wear is of great significance.And it is drop to lubricate
Low friction, the effective technology for reducing or avoiding abrasion.Current most of lubricants are improved so that a variety of lubricating additives are added
Its performance, and traditional additive is to realize good tribological property by physical absorption, and chemical reaction, it cannot
Accomplish the zero abrasion of material and repair is played to the damage of material.
Therefore, it is necessary to provide a kind of anti-oxidant self-restoring lubricating oil to solve the above problems.
Invention content
The object of the present invention is to provide a kind of anti-oxidant self-restoring lubricating oils.
Technical solution is as follows：
A kind of anti-oxidant self-restoring lubricating oil, including 50~55 parts of polyalphaolefin PAO4,18~27 parts of polyalphaolefin PAO6,12~
18 parts of hexanedioic acid esters, 8~12 parts of VI improver SV260,0.2~0.6 part of pour-point depressant T248,7~8 part of 55501 addition
Agent and 5~10 parts of organic molybdenum additives and 1^5 parts of nanometer lanthanum fluoride additives；
Nanometer lanthanum fluoride additive uses ethanol-water solution as reaction medium, and ethyl alcohol is 3 with water volume ratio:1, and include table
Face dressing agent and lanthanum fluoride；Coating material is 2 with lanthanum fluoride molar ratio:1；The addition of nanometer lanthanum fluoride is synthesized in alcohol-water system
The Property of Capped Inorganic Nanoparticles average grain diameter that agent includes is 10m or so, and without apparent agglomeration.
Further, coating material is that dioctyl two is thio（Slightly）DDPPY), two is pungent（Slightly）Dicyclohexyl amine salt
(DDPDA), the double β ethoxy octadecylamine salt of dioctyl phosphordithiic acid T152 salt (DDPT152), dioctyl phosphordithiic acid
(DDPE18A) or one of double β ethoxy octadecylamine salt (OAE18A) of oleic acid or in which three be composed.
Further, organic molybdenum additive is configured to：The antioxidant of 30%-75%, 7% ~ 12% extreme pressure agent and remaining
The organic-molybdenum of component；Antioxidant can inhibit the oxidation process of oil product, catalytic action of the passive metal to oxidation to play extension
Oil product uses and protects the purpose of machine；Extreme pressure agent can make lubricant in low speed high load or high speed impact load friction condition
Under, i.e., prevent rubbing surface from sintering, scratch occurs under the conditions of so-called extreme pressure；Organic-molybdenum under localized hyperthermia's condition of high voltage with
Wear surface acts on, and micro-bulge is rolled generation plastic deformation, and groove, rough friction are filled and led up by micro- theomorphism
Surface is formed more smooth friction surface by break-in again, i.e., has a degree of repair to friction perished surface, to
Reduce abrasion.
Further, the antioxidant is 2,4,6- tri-butyl-phenols, 2,6- di-t-butyl -4- nonyl phenols, 2,6- bis-
Butylated Hydroxytoluene, iso-octyl -3- (3,5 di-t-butyls-hydroxy phenyl) propionic ester, β-(3,5- di-t-butyl -4- hydroxy benzenes
Base) propionic acid isoctanol ester, one or both of β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid n-octadecyl alcohol ester with
On mixture.
Further, the antioxidant is 2,4,6- tri-butyl-phenols, 2,6- di-t-butyl -4- nonyl phenols, 2,6- bis-
Butylated Hydroxytoluene, iso-octyl -3- (3,5 di-t-butyls-hydroxy phenyl) propionic ester, β-(3,5- di-t-butyl -4- hydroxy benzenes
Base) propionic acid isoctanol ester, three kinds or more of mixing in β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid n-octadecyl alcohol ester
Object, wherein 2,6-di-tert-butyl p-cresol, β-(3,5- di-t-butyl -4- hydroxy phenyls) propionic acid isoctanol esters and β-must be contained
(3,5- di-tert-butyl-hydroxy phenyls) propionic acid n-octadecyl alcohol ester.
Further, the organic-molybdenum is two (2- ethylhexyls) molybdenum dithiophosphates or vulcanization dialkyl dithio ammonia
Base formic acid oxygen molybdenum.
Compared with prior art, the present invention has high antioxidant and extreme pressure property, is provided simultaneously with to being generated when equipment use
Abrasion there is surface reconditioning effect, ensure lubrication routine use while extending the service life of equipment.
Specific implementation mode
Embodiment：
The present embodiment shows anti-oxidant self-restoring lubricating oil preparation process, includes the following steps：
1）Polyalphaolefin PAO4, polyalphaolefin PAO6 and the mixing of hexanedioic acid ester, are then added VI improver SV260 and drop
Solidifying agent T248, is heated to 58~62 DEG C；
2）Insulated and stirred is up to standard to kinematic viscosity and pour point, continues to keep the temperature；
3）55501 additives are added and are stirred fusion；
4）Prepare organic molybdenum additive：By the antioxidant of 30%-75%, 7% ~ 12% extreme pressure agent and remaining component it is organic
Molybdenum mixes, and heats, stirring, and the temperature of the heating is 50~70 DEG C；The time of the stirring is 30~60min；
5）Addition prepares organic molybdenum additive, is stirred fusion；
6）Nanometer lanthanum fluoride additive is prepared, and stirring fusion is added.
7）It at the uniform velocity stirs, and in being heated to 62~66 DEG C, subsequent continuation of insurance temperature 30min in 10min, and obtains finished product.
Mixing speed is 960r/min.
It is stirred with the air-cooled portable air compressor of three-level.
(100 DEG C) of kinematic viscosity is (12.5~16.3) mm2/s, while pour point is not higher than -40 DEG C, as up to standard.
Nanometer lanthanum fluoride additive uses ethanol-water solution as reaction medium, and ethyl alcohol is 3 with water volume ratio:1, and include
There are coating material and lanthanum fluoride；Coating material is 2 with lanthanum fluoride molar ratio:1；Nanometer lanthanum fluoride is synthesized in alcohol-water system
The Property of Capped Inorganic Nanoparticles average grain diameter that additive includes is 10m or so, and without apparent agglomeration.
Coating material is that dioctyl two is thio（Slightly）DDPPY), two is pungent（Slightly）Dicyclohexyl amine salt (DDPDA), dioctyl two
The double β ethoxy octadecylamine salt (DDPE18A) of D2EHDTPA T152 salt (DDPT152), dioctyl phosphordithiic acid or the double β of oleic acid
One of ethoxy octadecylamine salt (OAE18A) or in which three be composed.
Organic molybdenum additive is configured to：The antioxidant of 30%-75%, 7% ~ 12% extreme pressure agent and remaining component have
Machine molybdenum；Antioxidant can inhibit the oxidation process of oil product, catalytic action of the passive metal to oxidation to play and extend oil product use
With the purpose of protection machine；Extreme pressure agent can make lubricant under low speed high load or high speed impact load friction condition, that is, exist
Prevent rubbing surface from sintering, scratch occurs under the conditions of so-called extreme pressure；Organic-molybdenum under localized hyperthermia's condition of high voltage with wear surface
Effect, micro-bulge are rolled generation plastic deformation, fill and lead up groove by micro- theomorphism, rough friction surface is again
More smooth friction surface is formed by break-in, i.e., has a degree of repair to friction perished surface, to reduce mill
Damage.
The antioxidant is 2,4,6- tri-butyl-phenols, 2,6- di-t-butyl -4- nonyl phenols, 2,6- di-t-butyls pair
Cresols, iso-octyl -3- (3,5 di-t-butyls-hydroxy phenyl) propionic ester, β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid are different
The mixing of one or more of octanol ester, β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid n-octadecyl alcohol ester
Object.
The antioxidant is 2,4,6- tri-butyl-phenols, 2,6- di-t-butyl -4- nonyl phenols, 2,6- di-t-butyls pair
Cresols, iso-octyl -3- (3,5 di-t-butyls-hydroxy phenyl) propionic ester, β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid are different
Three kinds or more of mixture in octanol ester, β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid n-octadecyl alcohol ester, wherein must
Contain DBPC 2,6 ditertiary butyl p cresol, β-(3,5- di-t-butyl -4- hydroxy phenyls) propionic acid isoctanol esters and β-(bis- uncles of 3,5-
Butyl -4- hydroxy phenyls) propionic acid n-octadecyl alcohol ester.
Further, the organic-molybdenum is two (2- ethylhexyls) molybdenum dithiophosphates or vulcanization dialkyl dithio ammonia
Base formic acid oxygen molybdenum.
Compared with prior art, the lubricating oil that the present embodiment prepares gained has high antioxidant and extreme pressure property, has simultaneously
It is standby that there is surface reconditioning effect to the abrasion generated when equipment use, ensure that lubrication routine use extended equipment simultaneously uses the longevity
Life.
Above-described is only some embodiments of the present invention.For those of ordinary skill in the art, not
Under the premise of being detached from the invention design, various modifications and improvements can be made, these belong to the protection model of the present invention
It encloses.
Claims (6)
1. a kind of anti-oxidant self-restoring lubricating oil, it is characterised in that：Including 50~55 parts of polyalphaolefin PAO4,18~27 parts of poly- α alkene
Hydrocarbon PAO6,12~18 parts of hexanedioic acid esters, 8~12 parts of VI improver SV260,0.2~0.6 part of pour-point depressant T248,7~8
55501 additives of part and 5~10 parts of organic molybdenum additives and 1^5 parts of nanometer lanthanum fluoride additives；
Nanometer lanthanum fluoride additive uses ethanol-water solution as reaction medium, and ethyl alcohol is 3 with water volume ratio:1, and include table
Face dressing agent and lanthanum fluoride；Coating material is 2 with lanthanum fluoride molar ratio:1；The addition of nanometer lanthanum fluoride is synthesized in alcohol-water system
The Property of Capped Inorganic Nanoparticles average grain diameter that agent includes is 10m or so, and without apparent agglomeration.
2. a kind of anti-oxidant self-restoring lubricating oil according to claim 1, it is characterised in that：Coating material is dioctyl
Two thio (summary) DDPPY), two pungent (summary) dicyclohexyl amine salt (DDPDA), dioctyl phosphordithiic acid T152 salt (DDPT152), two
Its of the double β ethoxy octadecylamine salt (DDPE18A) of octyl phosphordithiic acid or the double β ethoxy octadecylamine salt (OAE18A) of oleic acid
One of or in which three be composed.
3. a kind of anti-oxidant self-restoring lubricating oil according to claim 2, it is characterised in that：Organic molybdenum additive is constituted
For：The organic-molybdenum of the antioxidant of 30%-75%, 7%~12% extreme pressure agent and remaining component；Antioxidant can inhibit
The oxidation process of oil product, catalytic action of the passive metal to oxidation are played and extend the purpose that oil product used and protected machine；Extreme pressure
Agent can make lubricant under low speed high load or high speed impact load friction condition, i.e., prevent from rubbing under the conditions of so-called extreme pressure
Sintering, scratch occur for wiping face；Organic-molybdenum acts under localized hyperthermia's condition of high voltage with wear surface, and micro-bulge is rolled generation modeling
Property deformation, groove is filled and led up by micro- theomorphism, rough friction surface is formed more smooth friction table by break-in again
There is a degree of repair in face to friction perished surface, to reduce abrasion.
4. a kind of anti-oxidant self-restoring lubricating oil according to claim 3, it is characterised in that：The antioxidant is 2,4,6-
Tri-butyl-phenol, 2,6- di-t-butyl -4- nonyl phenols, DBPC 2,6 ditertiary butyl p cresol, iso-octyl -3- (3,5 di-t-butyls -
Hydroxy phenyl) propionic ester, β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid isoctanol ester, β-(3,5- di-t-butyl -4- hydroxyls
Base phenyl) one or more of propionic acid n-octadecyl alcohol ester mixture.
5. a kind of anti-oxidant self-restoring lubricating oil according to claim 4, it is characterised in that：The antioxidant is 2,4,6-
Tri-butyl-phenol, 2,6- di-t-butyl -4- nonyl phenols, DBPC 2,6 ditertiary butyl p cresol, iso-octyl -3- (3,5 di-t-butyls -
Hydroxy phenyl) propionic ester, β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid isoctanol ester, β-(3,5- di-t-butyl -4- hydroxyls
Base phenyl) three kinds or more of mixture in propionic acid n-octadecyl alcohol ester, wherein must contain 2,6-di-tert-butyl p-cresol, β-(3,
5- di-tert-butyl-hydroxy phenyls) propionic acid isoctanol ester and the positive octadecanol of β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid
Ester.
6. a kind of anti-oxidant self-restoring lubricating oil according to claim 5, it is characterised in that：The organic-molybdenum is two (2-
Ethylhexyl) molybdenum dithiophosphate or vulcanization dialkyldithiocarbamacompositions oxygen molybdenum.