CN108724832A - Carbon porcelain arculae - Google Patents
Carbon porcelain arculae Download PDFInfo
- Publication number
- CN108724832A CN108724832A CN201710290627.9A CN201710290627A CN108724832A CN 108724832 A CN108724832 A CN 108724832A CN 201710290627 A CN201710290627 A CN 201710290627A CN 108724832 A CN108724832 A CN 108724832A
- Authority
- CN
- China
- Prior art keywords
- carbon
- ceramic foam
- arculae
- porcelain
- foam layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of carbon porcelain arculaes, it is characterised in that：The carbon porcelain arculae is made of carbon fiber layer and ceramic foam layer, ceramic foam layer is located at middle part, ceramic foam layer both sides are equipped with 45 ° of longitude and latitude Carbon fibe layers, longitudinal carbon fiber layer and 45 ° of longitude and latitude Carbon fibe layers successively outward, and ceramic foam material is made of each component of following mass percent used by the ceramic foam layer：The epoxy resin of 55%-65%, the polyamide of 8%-12%, the polyetheramine of 5%-7%, the curing agent of 8%-10%, 12%-18% glass in ball, the antifoaming agent of 0.5%-1%, 55%-65% colorant；The ceramic foam obtained by the formula, technique is applied in carbon porcelain arculae, be can effectively improve the production qualification rate and properties of product of product, can be mitigated quality 20% or so, while improving arrow speed.
Description
Technical field
The present invention relates to sports equipment technical field more particularly to a kind of carbon porcelain arculaes.
Background technology
Arculae on Vehicles Collected from Market is mainly the sports contrary flexure arculae of glass mat and wooden combination production, main material
The deficiencies of material is glass mat and wooden combination, and that there are stability is poor, heavier, arrow is fast slow, vibration is big, mutability cracking.
Invention content
In order to solve deficiency in the prior art, the purpose of the present invention is to provide a kind of carbon porcelain arculaes.
The technical solution adopted by the present invention to solve the technical problems is：
A kind of carbon porcelain arculae, it is characterised in that：The carbon porcelain arculae is made of carbon fiber layer and ceramic foam layer, ceramics
Froth bed is located at middle part, and ceramic foam layer both sides are equipped with 45 ° of longitude and latitude Carbon fibe layers, longitudinal carbon fiber layer and 45 ° of warps successively outward
Latitude Carbon fibe layer.
Ceramic foam material used by the ceramic foam layer is made of each component of following mass percent：
The epoxy resin of 55%-65%, the polyamide of 8%-12%, the polyetheramine of 5%-7%, the curing agent of 8%-10%, 12%-
The colorant of ball, the antifoaming agent of 0.5%-1%, 55%-65% in 18% glass.
The ceramic foam material is obtained using following production technology：By ball, antifoaming agent merging in epoxy resin, glass
Vacuum halves 20-30min in reaction kettle, then imports curing agent, polyetheramine, polyamide, colorant stirring 10-20min, and temperature exists
Within 40 DEG C, mold is poured into liquid releasing and is heated up to 50 DEG C -150 DEG C, time 1.5-4h.
The beneficial effects of the invention are as follows：
1, carbon porcelain arculae production center fraction defective is within 2%, and glass fibre and wooden combination arculae fraction defective highest are then
Reach 35%, minimum this technique greatly promotes product qualification rate, effectively increases productivity 12%, reduces production cost.
2, carbon porcelain arculae improves the stability of arculae, and enhancing arrow speed is specious.
3, the addition of ceramic foam is effectively reduced the total quality of arculae.
Description of the drawings
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is the structural schematic diagram of carbon porcelain arculae.
In figure：1 ceramic foam layer, 2 45 ° of longitude and latitude Carbon fibe layers, 3 longitudinal carbon fiber layers.
Specific implementation mode
Illustrate that embodiments of the present invention, those skilled in the art can be by this explanations by particular specific embodiment below
Content disclosed by book understands other advantages and effect of the present invention easily.
As shown in Figure 1：A kind of carbon porcelain arculae, it is characterised in that：The carbon porcelain arculae is by carbon fiber layer and ceramic foam
Layer 1 is constituted, and ceramic foam layer 1 is located at middle part, and 1 both sides of ceramic foam layer are equipped with 45 ° of longitude and latitude Carbon fibe layers 2, longitudinal direction successively outward
Carbon fiber layer 3 and 45 ° of longitude and latitude Carbon fibe layers 2.
Ceramic foam material used by the ceramic foam layer is made of each component of following mass percent：
60.4% epoxy resin, 8.7% polyamide, 5.8% polyetheramine, 8.7% curing agent, 15.4% glass in ball,
0.8% antifoaming agent, 0.2% colorant.
The ceramic foam material is obtained using following production technology：By ball, antifoaming agent merging in epoxy resin, glass
Vacuum halves 20-30min in reaction kettle, then imports curing agent, polyetheramine, polyamide, colorant stirring 10-20min, and temperature exists
Within 40 DEG C, mold is poured into liquid releasing and is heated up to 50 DEG C -150 DEG C, time 1.5-4h.
By being formulated above, technique obtain ceramic foam be applied in carbon porcelain arculae, can effectively improve the life of product
Qualification rate and properties of product are produced, quality 20% or so can be mitigated, while improving arrow speed.
The foregoing is merely the preferred embodiments of the present invention, as long as achieving the object of the present invention skill with essentially identical means
Art scheme, belongs within protection scope of the present invention.
Claims (2)
1. a kind of carbon porcelain arculae, it is characterised in that：The carbon porcelain arculae is made of carbon fiber layer and ceramic foam layer, ceramic bubbles
Foam layer is located at middle part, and ceramic foam layer both sides are equipped with 45 ° of longitude and latitude Carbon fibe layers, longitudinal carbon fiber layer and 45 ° of longitudes and latitudes successively outward
Carbon fibe layer, ceramic foam material used by the ceramic foam layer are made of each component of following mass percent：
The epoxy resin of 55%-65%, the polyamide of 8%-12%, the polyetheramine of 5%-7%, the curing agent of 8%-10%, 12%-
The colorant of ball, the antifoaming agent of 0.5%-1%, 55%-65% in 18% glass.
2. carbon porcelain arculae according to claim 1, which is characterized in that the ceramic foam material uses following production work
Skill obtains：Ball, antifoaming agent in epoxy resin, glass are placed in vacuum in reaction kettle and halve 20-30min, then imports curing agent, gather
Ether amines, polyamide, colorant stir 10-20min, temperature within 40 DEG C, by liquid releasing pour into mold be heated up to 50 DEG C-
150 DEG C, time 1.5-4h.