CN108691242A - A kind of Cypres and preparation method thereof of addition nano-particle - Google Patents
A kind of Cypres and preparation method thereof of addition nano-particle Download PDFInfo
- Publication number
- CN108691242A CN108691242A CN201810272654.8A CN201810272654A CN108691242A CN 108691242 A CN108691242 A CN 108691242A CN 201810272654 A CN201810272654 A CN 201810272654A CN 108691242 A CN108691242 A CN 108691242A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- particle
- added
- cypres
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Cypres and preparation method thereof of addition nano-particle, which includes:Plant amylum, cellulose, cationic styrene-acrylic emulsion, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, phyllosilicate, antifoaming agent;Modified Nano particle includes:Nano-titanium dioxide, nano silicon dioxide, silane coupling agent, methyl methacrylate, potassium peroxydisulfate.Preparation method is first to mix nano-titanium dioxide, nano silicon dioxide, silane coupling agent grinding is added, obtained surface modification stuff and other stuff is subjected to graft modification with methyl methacrylate water again, finally by the colloidal solution of phyllosilicate and modified Nano particle be added in gelatinized corn starch liquid to get.The jelly that intensity is high, water-resistance is good is made by the way that bentonite is modified and be added to nano-particle in the present invention.
Description
Technical field
The invention belongs to field of adhesive technology, and in particular to it is a kind of addition nano-particle Cypres and its preparation
Method.
Background technology
Paper products product indispensable in being people's production and living, especially food-grade packaging paper product and people's health
It is closely bound up.Since the dimensional stability, mechanical property and barrier property of body paper itself are poor, general paper product of packing all is body paper
By special process.Surface coating/sizing is highly developed sheet processing technology, is usually located at the baking of paper machine
Cadre end sprays one layer of glue, through follow-up drying process, in paper and paperboard surface when not being completely dried in page surface
One layer of glued membrane is formed, to achieve the purpose that improve Paper or cardboard surface property.
Currently, the natural polymer Cypres of paper grade (stock) mainly have starch, functional cellulose, animal glue and chitosan
And their modified product.For a long time, native starch due to cheap always in occupation of the head of domestic Cypres
Want status.Native starch is as a kind of high-molecular compound, cheap and enjoy great popularity because of rich reserves, still, gelatinization
Afterwards, mobility is poor, transparent also not satisfactory, and is easy gelation again after cooling down and is not therefore directly used as surface generally and applies
Jelly needs to be modified it.
Common starch Cypres and fiber affinity are relatively poor, and are covered in the starch film on page surface
In the drying process, it is easy to happen rupture, causes that surface strength of paper is low, hair and powder dropping phenomenon is serious in printing process.In recent years
Coming, application study of the nanotechnology in paper surface processing deepens continuously, by Application of micron in paper surface processing,
The performances such as the special optics of paper, mechanics can not only be assigned, the printing performance of paper can also be improved, therefore, by nano-particle
It is added to starch Cypres and has preferable application prospect.
Invention content
The technical problem that present invention aim to address existing starch Cypres intensity is low, water-resistance is poor, provides
A kind of Cypres and preparation method thereof of addition nano-particle.
A kind of Cypres of addition nano-particle, include following raw material in parts by weight:50-80 parts of plant amylum,
10-15 parts of cellulose, 2-4 parts of cationic styrene-acrylic emulsion, 2-4 parts of sodium carboxymethylcellulose, 3-7 parts of polyvinyl alcohol, modified Nano
3-5 parts of particle, 1-4 parts of phyllosilicate, 1-2 parts of antifoaming agent;
The modified Nano particle includes following raw material in parts by weight:5-10 parts of nano-titanium dioxide, nanometer titanium dioxide
5-10 parts of silicon, 0.05-0.1 parts of silane coupling agent, 0.2-0.5 parts of methyl methacrylate, 0.05-0.1 parts of potassium peroxydisulfate.
Preferably, layered silicate is bentonite.
Preferably, the antifoaming agent is silicone emulsion.
Preferably, the plant amylum is cornstarch.
The preparation method of above-mentioned Cypres, includes the following steps:
Step 1, nano-titanium dioxide, nano silicon dioxide are mixed, silane coupling agent is added, grinding obtains to surface and changes
Property stuff and other stuff;
Step 2, surface modification stuff and other stuff is added in methyl methacrylate aqueous solution, over cure is added dropwise under stirring condition
Sour potassium, carry out graft reaction, after wash, dry, obtain modified Nano particle;
Step 3, phyllosilicate is added in the water of 5-10 times of weight, grinds, obtains colloidal solution;
Step 4, plant amylum is added in the water of 10-20 times of weight, is gelatinized, the stupid acrylic emulsion of cation is added dropwise, dispersion adds
Enter cellulose, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, colloidal solution and antifoaming agent, mixing to get.
Preferably, in the methyl methacrylate aqueous solution methyl methacrylate a concentration of 3-5wt.%.
Preferably, also contain emulsifier sodium lauryl sulfate, a concentration of 1- in the methyl methacrylate aqueous solution
2wt.%.
The present invention uses base-material of the cornstarch as adhesive, by methyl methacrylate to the nanometer of surface active
Titanium dioxide and nano silicon dioxide carry out graft modification, to enhance the binding force of nano-particle and cornstarch, are formed fine and close
Network structure, so as to improve the mechanical property of cornstarch;Phyllosilicate especially bentonite is after forming colloid
With good thixotropy and thermal stability, the bonding between cornstarch and modified Nano particle on the one hand can be promoted, separately
On the one hand cornstarch can be promoted to reset to form tight structure, to enhance the mechanical property and water-resistance of cornstarch.This hair
The bright jelly that by the way that bentonite is modified and be added to nano-particle, obtained intensity is high, water-resistance is good.
Specific implementation mode
Technical scheme of the present invention is described further with reference to specific embodiment.
Embodiment 1
A kind of Cypres of addition nano-particle, include following raw material in parts by weight:50 parts of plant amylum, fiber
10 parts of element, 2 parts of cationic styrene-acrylic emulsion, 2 parts of sodium carboxymethylcellulose, 3 parts of polyvinyl alcohol, 3 parts of modified Nano particle, stratiform silicon
1 part of hydrochlorate, 1 part of antifoaming agent;
The modified Nano particle includes following raw material in parts by weight:5 parts of nano-titanium dioxide, nano silicon dioxide 5
Part, 0.05 part of silane coupling agent, 0.2 part of methyl methacrylate, 0.05 part of potassium peroxydisulfate.
Preferably, layered silicate is bentonite, and the antifoaming agent is silicone emulsion, and the plant amylum is corn
Starch.
The preparation method of above-mentioned Cypres, includes the following steps:
Step 1, nano-titanium dioxide, nano silicon dioxide are mixed, silane coupling agent is added, grinding obtains to surface and changes
Property stuff and other stuff;
Step 2, surface modification stuff and other stuff is added in the methyl methacrylate aqueous solution of a concentration of 3wt.%, is stirred
Under the conditions of be added dropwise potassium peroxydisulfate, carry out graft reaction, after wash, dry, obtain modified Nano particle;
Step 3, phyllosilicate is added in the water of 7 times of weight, grinds, obtains colloidal solution;
Step 4, plant amylum is added in the water of 15 times of weight, is gelatinized, the stupid acrylic emulsion of cation is added dropwise, disperses, is added
Cellulose, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, colloidal solution and antifoaming agent, mixing to get.
Also contain emulsifier sodium lauryl sulfate, a concentration of 1wt.% in the methyl methacrylate aqueous solution.
Embodiment 2
A kind of Cypres of addition nano-particle, include following raw material in parts by weight:57 parts of plant amylum, fiber
12 parts of element, 3 parts of cationic styrene-acrylic emulsion, 2 parts of sodium carboxymethylcellulose, 4 parts of polyvinyl alcohol, 4 parts of modified Nano particle, stratiform silicon
2 parts of hydrochlorate, 1.5 parts of antifoaming agent;
The modified Nano particle includes following raw material in parts by weight:7 parts of nano-titanium dioxide, nano silicon dioxide 6
Part, 0.07 part of silane coupling agent, 0.3 part of methyl methacrylate, 0.06 part of potassium peroxydisulfate.
Preferably, layered silicate is bentonite, and the antifoaming agent is silicone emulsion, and the plant amylum is corn
Starch.
The preparation method of above-mentioned Cypres, includes the following steps:
Step 1, nano-titanium dioxide, nano silicon dioxide are mixed, silane coupling agent is added, grinding obtains to surface and changes
Property stuff and other stuff;
Step 2, surface modification stuff and other stuff is added in the methyl methacrylate aqueous solution of a concentration of 4wt.%, is stirred
Under the conditions of be added dropwise potassium peroxydisulfate, carry out graft reaction, after wash, dry, obtain modified Nano particle;
Step 3, phyllosilicate is added in the water of 5 times of weight, grinds, obtains colloidal solution;
Step 4, plant amylum is added in the water of 10 times of weight, is gelatinized, the stupid acrylic emulsion of cation is added dropwise, disperses, is added
Cellulose, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, colloidal solution and antifoaming agent, mixing to get.
Also contain emulsifier sodium lauryl sulfate, a concentration of 1.2wt.% in the methyl methacrylate aqueous solution.
Embodiment 3
A kind of Cypres of addition nano-particle, include following raw material in parts by weight:70 parts of plant amylum, fiber
13 parts of element, 3 parts of cationic styrene-acrylic emulsion, 4 parts of sodium carboxymethylcellulose, 5 parts of polyvinyl alcohol, 4 parts of modified Nano particle, stratiform silicon
3 parts of hydrochlorate, 1.5 parts of antifoaming agent;
The modified Nano particle includes following raw material in parts by weight:8 parts of nano-titanium dioxide, nano silicon dioxide 7
Part, 0.08 part of silane coupling agent, 0.4 part of methyl methacrylate, 0.07 part of potassium peroxydisulfate.
Preferably, layered silicate is bentonite, and the antifoaming agent is silicone emulsion, and the plant amylum is corn
Starch.
The preparation method of above-mentioned Cypres, includes the following steps:
Step 1, nano-titanium dioxide, nano silicon dioxide are mixed, silane coupling agent is added, grinding obtains to surface and changes
Property stuff and other stuff;
Step 2, surface modification stuff and other stuff is added in the methyl methacrylate aqueous solution of a concentration of 3wt.%, is stirred
Under the conditions of be added dropwise potassium peroxydisulfate, carry out graft reaction, after wash, dry, obtain modified Nano particle;
Step 3, phyllosilicate is added in the water of 8 times of weight, grinds, obtains colloidal solution;
Step 4, plant amylum is added in the water of 17 times of weight, is gelatinized, the stupid acrylic emulsion of cation is added dropwise, disperses, is added
Cellulose, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, colloidal solution and antifoaming agent, mixing to get.
Also contain emulsifier sodium lauryl sulfate, a concentration of 1wt.% in the methyl methacrylate aqueous solution.
Embodiment 4
A kind of Cypres of addition nano-particle, include following raw material in parts by weight:80 parts of plant amylum, fiber
15 parts of element, 4 parts of cationic styrene-acrylic emulsion, 4 parts of sodium carboxymethylcellulose, 7 parts of polyvinyl alcohol, 5 parts of modified Nano particle, stratiform silicon
4 parts of hydrochlorate, 2 parts of antifoaming agent;
The modified Nano particle includes following raw material in parts by weight:10 parts of nano-titanium dioxide, nano silicon dioxide
10 parts, 0.1 part of silane coupling agent, 0.5 part of methyl methacrylate, 0.1 part of potassium peroxydisulfate.
Preferably, layered silicate is bentonite, and the antifoaming agent is silicone emulsion, and the plant amylum is corn
Starch.
The preparation method of above-mentioned Cypres, includes the following steps:
Step 1, nano-titanium dioxide, nano silicon dioxide are mixed, silane coupling agent is added, grinding obtains to surface and changes
Property stuff and other stuff;
Step 2, surface modification stuff and other stuff is added in the methyl methacrylate aqueous solution of a concentration of 5wt.%, is stirred
Under the conditions of be added dropwise potassium peroxydisulfate, carry out graft reaction, after wash, dry, obtain modified Nano particle;
Step 3, phyllosilicate is added in the water of 10 times of weight, grinds, obtains colloidal solution;
Step 4, plant amylum is added in the water of 20 times of weight, is gelatinized, the stupid acrylic emulsion of cation is added dropwise, disperses, is added
Cellulose, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, colloidal solution and antifoaming agent, mixing to get.
Also contain emulsifier sodium lauryl sulfate, a concentration of 2wt.% in the methyl methacrylate aqueous solution.
By quantification of 90g/m2Body paper be laid on coating machine and fixed, glue application solution made from embodiment is coated on original
On paper, coating speed is 30rpm (coating weight 3-5g/m2), first coated paper is dried at room temperature, it is quick to place into pattern
In drier, 105 DEG C of dry 2min are to get to sized paper.Page is tested for the property, it is as a result as follows:
As seen from the above table, being applied with the mechanical performance of page after the glue of the present invention, (tensile strength, folding strength and tearing are strong
Degree) preferably.
Claims (7)
1. a kind of Cypres of addition nano-particle, it is characterised in that:Include following raw material in parts by weight:Plant amylum
50-80 parts, 10-15 parts of cellulose, 2-4 parts of cationic styrene-acrylic emulsion, 2-4 parts of sodium carboxymethylcellulose, 3-7 parts of polyvinyl alcohol,
3-5 parts of modified Nano particle, 1-4 parts of phyllosilicate, 1-2 parts of antifoaming agent;
The modified Nano particle includes following raw material in parts by weight:5-10 parts of nano-titanium dioxide, nano silicon dioxide 5-
10 parts, 0.05-0.1 parts of silane coupling agent, 0.2-0.5 parts of methyl methacrylate, 0.05-0.1 parts of potassium peroxydisulfate.
2. the Cypres of addition nano-particle according to claim 1, it is characterised in that:Layered silicate is
Bentonite.
3. the Cypres of addition nano-particle according to claim 1, it is characterised in that:The antifoaming agent is emulsification
Silicone oil.
4. the Cypres of addition nano-particle according to claim 1, it is characterised in that:The plant amylum is jade
Rice starch.
5. the preparation method of Cypres described in claim 1, it is characterised in that:Include the following steps:
Step 1, nano-titanium dioxide, nano silicon dioxide are mixed, silane coupling agent is added, it is mixed to obtain surface modification for grinding
Close particle;
Step 2, surface modification stuff and other stuff is added in methyl methacrylate aqueous solution, persulfuric acid is added dropwise under stirring condition
Potassium, carry out graft reaction, after wash, dry, obtain modified Nano particle;
Step 3, phyllosilicate is added in the water of 5-10 times of weight, grinds, obtains colloidal solution;
Step 4, plant amylum is added in the water of 10-20 times of weight, is gelatinized, the stupid acrylic emulsion of cation is added dropwise, dispersion is added fine
Tie up element, sodium carboxymethylcellulose, polyvinyl alcohol, modified Nano particle, colloidal solution and antifoaming agent, mix to get.
6. the preparation method of Cypres according to claim 5, it is characterised in that:The methyl methacrylate water
A concentration of 3-5wt.% of methyl methacrylate in solution.
7. the preparation method of Cypres according to claim 5, it is characterised in that:The methyl methacrylate water
Also contain emulsifier sodium lauryl sulfate, a concentration of 1-2wt.% in solution.