CN108677550A - A kind of graphene fabric coating and its coating method - Google Patents
A kind of graphene fabric coating and its coating method Download PDFInfo
- Publication number
- CN108677550A CN108677550A CN201810519926.XA CN201810519926A CN108677550A CN 108677550 A CN108677550 A CN 108677550A CN 201810519926 A CN201810519926 A CN 201810519926A CN 108677550 A CN108677550 A CN 108677550A
- Authority
- CN
- China
- Prior art keywords
- coating
- graphene
- cloth
- fabric
- yardage roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of graphene fabric coating and its coating method, the material for preparing of the coating includes：Graphene, polyolefin, dibenzoyl peroxide, binder, ethyl alcohol, N hydroxymethyl acrylamide, emulsifier, inorganic pigment and deionization pure water.The material for preparing of the coating includes by mass percentage：Graphene 0.1%~5%, polyolefin 3%~5%, dibenzoyl peroxide 0.3%~0.9%, binder 1.5%~6.0%, ethyl alcohol 0.4%~0.6%, N hydroxymethyl acrylamide 1.5%~1.8%, emulsifier 4%~5%, inorganic pigment 0%~5.5%, surplus are deionization pure water.The present invention also provides the coating methods of the graphene fabric coating.Graphene fabric coating and its coating method provided by the invention, can assign the functions such as antibacterial fabric, uvioresistant, Far-infrared Heating.
Description
Technical field
The present invention relates to a kind of fabric coating and its coating methods, and in particular, to a kind of graphene fabric coating and its
Coating method.
Background technology
Coated fabric is a kind of textile, coating bonding material fabric one side or obverse and reverse sides be formed in situ single layer or
Laminated coating.It is made of two layers or two layers or more of material, it is textile wherein at least to have one layer, and another layer is completely continuous
Polymer coating.It is bound tightly together between layers by the viscosity of additional adhesive or material itself.Coating
Processing can assign the variation of appearance of fabrics and function, and main processing purpose is：1. changing appearance of fabrics：It is pearl effect, anti-
Light effect, dual-sided two color effect, leather appearance, luster effect etc.；2. changing Fabric Style：It is soft and full feel, hard
Very and high-elastic recovery etc.；3. increasing fabric functional：Water-proof and oil-proof, acid-proof, alkali prevention, radiation protection, UV resistance and far infrared radiation
Deng.Coated fabric is widely used in gym suit, down jackets rain-proof Parker, housing, tent, footgear, curtain, luggage and advanced anti-
The ski-wear of water moisture-inhibiting function, anorak, wind coat etc..
As described above, the involved coating of coated fabric printing and dyeing includes all polymorphic types, such as antistatic, crease-resistant etc., but
Be current coating finishing agent performance it is not good enough, the functionality of single coating finishing agent is single, and stability is poor, and pollution is big,
It also needs to be further improved.
Invention content
The object of the present invention is to provide a kind of fabric coating and its coating method, can assign antibacterial fabric, uvioresistant,
The functions such as Far-infrared Heating.
In order to achieve the above object, the present invention provides a kind of graphene fabric coatings, wherein the preparation of the coating
Material includes：Graphene raw material, polyolefin, dibenzoyl peroxide, binder, ethyl alcohol, N hydroxymethyl acrylamide, emulsification
Agent, inorganic pigment and deionization pure water.Polyolefin is the polymer of alkene, by ethylene, propylene, 1- butylene, 1- amylenes,
The alpha-olefins such as 1- hexenes, 1- octenes, 4-methyl-1-pentene and certain cycloolefins be polymerized alone or combined polymerization obtained from it is a kind of
The general name of thermoplastic resin.
Above-mentioned graphene fabric coating, wherein the material for preparing of the coating includes by mass percentage：Graphite
Alkene raw material 0.1%~5%, polyolefin 3%~5%, dibenzoyl peroxide 0.3%~0.9%, binder 1.5%~
6.0%, ethyl alcohol 0.4%~0.6%, N hydroxymethyl acrylamide 1.5%~1.8%, emulsifier 4%~5%, inorganic pigment
0%~5.5%, surplus is deionization pure water.
Above-mentioned graphene fabric coating, wherein the graphene raw material includes graphene, graphene oxide, reduction
Any one or more in graphene oxide and modified graphene oxide.
Above-mentioned graphene fabric coating, wherein the binder is crylic acid resin binder.
Above-mentioned graphene fabric coating, wherein the emulsifier is polyacrylamide amine emulsifier.
The present invention also provides the coating methods of above-mentioned graphene fabric coating, wherein the method includes：Step
1, it unreels：Selection needs the yardage roll that is coated, and being unreeled automatically on unreeling machine on cloth roll stands；Step 2, tensile force control
System：Cloth after unreeling makes fabric be tensioned by the traction of two draggers by adjusting rate, keeps certain tensile force；
Step 3, sanding：Cloth after tensioning first uses roughing-up machine to carry out the fine sanding on surface, and fabric fibre surface is made pit occur
Or minute protrusions, increase the bond area of coating adhesive；Step 4, it is coated with：The conventional method prepared in proportion by coating prepares stone
Black alkene fabric coating adhesive, and it is injected into glue spreader, even spread is carried out after heating；Step 5, it dries：Cloth after gluing into
Enter dryer and carries out heating, drying；Step 6, it winds：Cloth after drying carries out natural air drying cooling, then carries out automatic winding
Storage.
The coating method of above-mentioned graphene fabric coating, wherein yardage roll in the step 1 include terylene yardage roll,
Any one in polyamide fibre yardage roll, linen-cotton yardage roll, synthetic fibers yardage roll and blended yardage roll.
The coating method of above-mentioned graphene fabric coating, wherein the drying condition of the step 5 be temperature 130~
150 DEG C, 30~60min of drying time.
Graphene fabric coating and its coating method provided by the invention have the following advantages：
Woven graphite ene coatings prepared by the present invention can make the fabric after arrangement have antibacterial, antiultraviolet and remote red
The functions such as outer fever.And coating method is simple, efficient, can be used for producing the fabric with this graphite ene coatings.
Specific implementation mode
The specific implementation mode of the present invention is further described below.
The material for preparing of graphene fabric coating provided by the invention, the coating includes：Graphene raw material, polyolefin, mistake
Aoxidize dibenzoyl, binder, ethyl alcohol, N hydroxymethyl acrylamide, emulsifier, inorganic pigment and deionization pure water.It is poly-
Alkene is the polymer of alkene, by α-such as ethylene, propylene, 1- butylene, 1- amylenes, 1- hexenes, 1- octenes, 4-methyl-1-pentenes
Alkene and certain cycloolefins be polymerized alone or combined polymerization obtained from a kind of thermoplastic resin general name.
Preferably, the material for preparing of the coating includes by mass percentage：Graphene raw material 0.1%~5%, polyolefin
3%~5%, dibenzoyl peroxide 0.3%~0.9%, binder 1.5%~6.0%, ethyl alcohol 0.4%~0.6%, N- hydroxyls
Methacrylamide 1.5%~1.8%, emulsifier 4%~5%, inorganic pigment 0%~5.5%, surplus are that deionization is pure
Water.
Graphene raw material includes in graphene, graphene oxide, redox graphene and modified graphene oxide
Any one or more.Binder is crylic acid resin binder.Emulsifier is polyacrylamide amine emulsifier.
The present invention also provides the coating method of the graphene fabric coating, this method includes：Step 1, it unreels：Selection needs
The yardage roll to be coated, and being unreeled automatically on unreeling machine on cloth roll stands；Step 2, tensile force controls：Cloth after unreeling
Material makes fabric be tensioned by the traction of two draggers by adjusting rate, keeps certain tensile force；Step 3, sanding：
Next cloth first uses roughing-up machine to carry out the fine sanding on surface, and fabric fibre surface is made pit or minute protrusions occur, increases
Add the bond area of coating adhesive；Step 4, it is coated with：The conventional method prepared in proportion by coating prepares graphene fabric coating
Glue, and it is injected into glue spreader, even spread is carried out after heating；Step 5, it dries：Cloth after gluing enters dryer progress
Heating, drying；Step 6, it winds：Cloth after drying carries out natural air drying cooling, then carries out automatic winding storage.
Yardage roll in step 1 includes terylene yardage roll, polyamide fibre yardage roll, linen-cotton yardage roll, synthetic fibers yardage roll and blended yardage roll
In any one.
The drying condition of step 5 is 130~150 DEG C of temperature, 30~60min of drying time.
Graphene fabric coating provided by the invention and its coating method are further described with reference to embodiment.
Examples 1 to 5
The proportioning for preparing material of a kind of graphene fabric coating, the coating is as shown in table 1 below.
1 ingredient composition table of table.
The present invention also provides the coating method of the graphene fabric coating, this method includes：
Step 1, it unreels：Selection needs the yardage roll that is coated, and being unreeled automatically on unreeling machine on cloth roll stands；Cloth
Volume includes any one in terylene yardage roll, polyamide fibre yardage roll, linen-cotton yardage roll, synthetic fibers yardage roll and blended yardage roll.
Step 2, tensile force controls：Cloth after unreeling makes fabric by the traction of two draggers by adjusting rate
Tensioning, keeps certain tensile force；
Step 3, sanding：Cloth after tensioning first uses roughing-up machine to carry out the fine sanding on surface, makes fabric fibre surface
There are pit or minute protrusions, increases the bond area of coating adhesive；
Step 4, it is coated with：In the ratio of arbitrary an example in Examples 1 to 5, the conventional method prepared by coating prepares stone
Black alkene fabric coating adhesive, and it is injected into glue spreader, even spread is carried out after heating；
Step 5, it dries：Cloth after gluing enters dryer and carries out heating, drying；Drying condition is temperature 130~150
DEG C, 30~60min of drying time.
Step 6, it winds：Cloth after drying carries out natural air drying cooling, then carries out automatic winding storage.
Graphene fabric coating and its coating method provided by the invention, the woven graphite ene coatings of preparation can make whole
Fabric after reason has the function of antibacterial, antiultraviolet and far infrared heating etc..And coating method is simple, efficient, can be used for giving birth to
Produce the fabric with this graphite ene coatings.
Although present disclosure is discussed in detail by above preferred embodiment, but it should be appreciated that above-mentioned
Description is not considered as limitation of the present invention.After those skilled in the art have read the above, for the present invention's
A variety of modifications and substitutions all will be apparent.Therefore, protection scope of the present invention should be limited to the appended claims.
Claims (8)
1. a kind of graphene fabric coating, which is characterized in that the material for preparing of the coating includes：Graphene raw material, polyene
Hydrocarbon, dibenzoyl peroxide, binder, ethyl alcohol, N hydroxymethyl acrylamide, emulsifier, inorganic pigment and deionization are pure
Water.
2. graphene fabric coating as described in claim 1, which is characterized in that the coating prepares material by quality hundred
Divide and includes than meter：Graphene raw material 0.1%~5%, dibenzoyl peroxide 0.3%~0.9%, is glued polyolefin 3%~5%
Tie agent 1.5%~6.0%, ethyl alcohol 0.4%~0.6%, N hydroxymethyl acrylamide 1.5%~1.8%, emulsifier 4%~
5%, inorganic pigment 0%~5.5%, surplus are deionization pure water.
3. graphene fabric coating as claimed in claim 2, which is characterized in that the graphene raw material include graphene,
Any one or more in graphene oxide, redox graphene and modified graphene oxide.
4. graphene fabric coating as claimed in claim 2, which is characterized in that the binder is viscous for crylic acid resin
Tie agent.
5. graphene fabric coating as claimed in claim 2, which is characterized in that the emulsifier emulsifies for polyacrylamide
Agent.
6. a kind of coating method of graphene fabric coating as described in any one of Claims 1 to 5, which is characterized in that
The method includes：
Step 1, it unreels：Selection needs the yardage roll that is coated, and being unreeled automatically on unreeling machine on cloth roll stands；
Step 2, tensile force controls：Cloth after unreeling passes through the traction of two draggers, by adjusting rate, makes fabric
Tightly；
Step 3, sanding：Cloth after tensioning first uses roughing-up machine to carry out the fine sanding on surface, increases the attachment surface of coating adhesive
Product；
Step 4, it is coated with：Graphene fabric coating adhesive is prepared in proportion, and is injected into glue spreader, is uniformly applied after heating
Cloth；
Step 5, it dries：Cloth after gluing enters dryer and carries out heating, drying；
Step 6, it winds：Cloth after drying carries out natural air drying cooling, then carries out automatic winding storage.
7. the coating method of graphene fabric coating as claimed in claim 6, which is characterized in that the cloth in the step 1
Volume includes any one in terylene yardage roll, polyamide fibre yardage roll, linen-cotton yardage roll, synthetic fibers yardage roll and blended yardage roll.
8. the coating method of graphene fabric coating as claimed in claim 6, which is characterized in that the drying of the step 5
Condition is 130~150 DEG C of temperature, 30~60min of drying time.