CN108676273A - A kind of abrasive floor glue and preparation method thereof - Google Patents
A kind of abrasive floor glue and preparation method thereof Download PDFInfo
- Publication number
- CN108676273A CN108676273A CN201810288016.5A CN201810288016A CN108676273A CN 108676273 A CN108676273 A CN 108676273A CN 201810288016 A CN201810288016 A CN 201810288016A CN 108676273 A CN108676273 A CN 108676273A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor glue
- abrasive floor
- calcium carbonate
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of abrasive floor glue of the present invention, according to weight ratio, 100 parts of Corvic, 20 30 parts of haloflex, 24 parts of barium stearate, 80 100 parts of calcium carbonate, 25 parts of superfine alumina silicate, 24 parts of calcium carbonate crystal whisker, 12 parts of nano-titanium oxide, 58 parts of chlorinated paraffin, 24 parts of sorbic acid, 24 parts of anti-skid wearable powder, the anti-skid wearable powder are the mixture of diamond dust, hollow ceramic micro mist and gluey graphite powder, and three's mass ratio is 10:10:3.The present invention has excellent wear-resisting property, and product compactness higher, wear-resisting and skid resistance is more preferable, and service life is long, is more suitable for hospital, airport, subway, the big public place of the flows of the people such as megastore uses.
Description
Technical field
The invention belongs to floor glue production fields, specifically, being related to a kind of abrasive floor glue and preparation method thereof.
Background technology
PVC floor is also referred to as " light body floor ", it is the floor using pvc material production.Simultaneously PVC floor because
The advantages that low with production cost, service life is long, and environment protecting is good and be increasingly used widely.
But there is also some shortcomingss for current PVC floor, are mainly manifested in non-skid property difference etc., these problems
Many puzzlements are brought to user, also hamper the promotion and popularization of PVC floor to a certain extent.
Invention content
The present invention overcomes the disadvantages of the prior art, provides a kind of abrasive floor glue and preparation method thereof, rises anti-skidding
Excellent effect increases the application scenario of floor glue, expands the use scope of floor glue.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions:
A kind of abrasive floor glue, according to weight ratio, 100 parts of Corvic, 20-30 parts of haloflex, stearic acid
2-4 parts of barium, 80-100 parts of calcium carbonate, 2-5 parts of superfine alumina silicate, 2-4 parts of calcium carbonate crystal whisker, 1-2 parts of nano-titanium oxide, chlorination stone
5-8 parts of wax, 2-4 parts of sorbic acid, 2-4 parts of anti-skid wearable powder, the anti-skid wearable powder are diamond dust, hollow ceramic micro mist and glue
The mixture of graphite powder, three's mass ratio are 10:10:3.
Further, according to weight ratio, 100 parts of Corvic, 25 parts of haloflex, 3 parts of barium stearate, calcium carbonate
90 parts, 3 parts of superfine alumina silicate, 3 parts of calcium carbonate crystal whisker, 1.5 parts of nano-titanium oxide, 6 parts of chlorinated paraffin, 2-4 parts of sorbic acid is anti-skidding
3 parts of abrasion-resistant powder, the anti-skid wearable powder are the mixture of diamond dust, hollow ceramic micro mist and gluey graphite powder, three's mass ratio
It is 10:10:3.
Further, it is additionally added 2-3 parts of zinc silicate.
Further, it is additionally added 2-3 parts of nano silicon dioxide.
Further, it is additionally added 2-5 parts of calcium zinc stabilizer.
A kind of preparation method of abrasive floor glue, includes the following steps:
1) raw material is put into stirring at low speed 3-4 minutes in batch mixer, is then transferred to high-speed stirred 6-7 minutes, temperature
90-100 DEG C is risen to, is transferred to stirring at low speed again 3-4 minutes, mixed material is discharged into the dispersion of stirring at low speed pot and is cooled to room
Temperature then drains into storage tank, then is sent into double screw extruder by screw conveyor and fully heats, and shears, and plasticizing enters back into list
Screw extruder further heats, plasticizing, is granulated by exporting cut-out, is finally cooled to room temperature the PVC granule being granulated;
2) calendering formation:PVC granule is transported to calender and is squeezed into coiled material;
3) heating plasticizing:Coiled material obtained by step 2) is sent into electrical heating baking oven, warm area drops to 190 again by 190 to 220 DEG C
DEG C, make the abundant heating plasticizing of material;
4) secondary calendering:Step 3) products obtained therefrom is entered into two calenders, in 150 DEG C of extrusion formings;
5) back segment is handled:Base material gluing is carried out heating at 180 DEG C with step 4) products obtained therefrom to be bonded, is then pressed
Flower, cooling, cutting edge, surface UV processing, thermal stress are eliminated, again cooling winding, and obtained product is abrasive floor glue.
6) abrasive floor glue surface passes through silicic acid immersion treatment.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention has excellent wear-resisting property, and product compactness higher, wear-resisting and skid resistance is more preferable, and service life is long,
It is more suitable for hospital, airport, subway, the big public place of the flows of the people such as megastore uses.
Specific implementation mode
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
A kind of abrasive floor glue of the present invention, 100 parts of Corvic, 25 parts of haloflex, barium stearate 3
Part, 90 parts of calcium carbonate, 3 parts of superfine alumina silicate, 3 parts of calcium carbonate crystal whisker, 1.5 parts of nano-titanium oxide, 6 parts of chlorinated paraffin, sorbic acid
2-4 parts, 3 parts of anti-skid wearable powder, the anti-skid wearable powder is the mixture of diamond dust, hollow ceramic micro mist and gluey graphite powder,
Three's mass ratio is 10:10:3, it is additionally added 2.5 parts of zinc silicate, is additionally added 2.3 parts of nano silicon dioxide, zinc silicate and nanometer two
Silica effectively increases the wearability of floor glue, and zinc silicate also makes floor glue surface generate small lines, increases frictional force, separately
Outer to be additionally added 2.5 parts of calcium zinc stabilizer, calcium zinc stabilizer promotes zinc silicate, nano silicon dioxide and Corvic to combine,
In conjunction with closer stabilization.
A kind of preparation method of abrasive floor glue, includes the following steps:
1) raw material is put into stirring at low speed 3-4 minutes in batch mixer, is then transferred to high-speed stirred 6-7 minutes, temperature
90-100 DEG C is risen to, is transferred to stirring at low speed again 3-4 minutes, mixed material is discharged into the dispersion of stirring at low speed pot and is cooled to room
Temperature then drains into storage tank, then is sent into double screw extruder by screw conveyor and fully heats, and shears, and plasticizing enters back into list
Screw extruder further heats, plasticizing, is granulated by exporting cut-out, is finally cooled to room temperature the PVC granule being granulated;
2) calendering formation:PVC granule is transported to calender and is squeezed into coiled material;
3) heating plasticizing:Coiled material obtained by step 2) is sent into electrical heating baking oven, warm area drops to 190 again by 190 to 220 DEG C
DEG C, make the abundant heating plasticizing of material;
4) secondary calendering:Step 3) products obtained therefrom is entered into two calenders, in 150 DEG C of extrusion formings;
5) back segment is handled:Base material gluing is carried out heating at 180 DEG C with step 4) products obtained therefrom to be bonded, is then pressed
Flower, cooling, cutting edge, surface UV processing, thermal stress are eliminated, again cooling winding, and obtained product is abrasive floor glue.
6) abrasive floor glue surface generates tiny pit and line on floor glue surface by silicic acid immersion treatment, silicic acid
Road increases its frictional force.
Obtained abrasive floor glue is tested for the property, result is as follows:
Finally it should be noted that:It these are only the preferred embodiment of the present invention, be not intended to restrict the invention, although
With reference to embodiment, invention is explained in detail, for those skilled in the art, still can be to aforementioned
Technical solution recorded in each embodiment is modified or equivalent replacement of some of the technical features, but it is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in the protection of the present invention
Within the scope of.
Claims (7)
1. a kind of abrasive floor glue, which is characterized in that according to weight ratio, 100 parts of Corvic, haloflex 20-30
Part, 2-4 parts of barium stearate, 80-100 parts of calcium carbonate, 2-5 parts of superfine alumina silicate, 2-4 parts of calcium carbonate crystal whisker, nano-titanium oxide 1-2
Part, 5-8 parts of chlorinated paraffin, 2-4 parts of sorbic acid, 2-4 parts of anti-skid wearable powder, the anti-skid wearable powder is diamond dust, hollow ceramic
The mixture of micro mist and gluey graphite powder, three's mass ratio are 10:10:3.
2. a kind of abrasive floor glue according to claim 1, which is characterized in that according to weight ratio, Corvic 100
Part, 25 parts of haloflex, 3 parts of barium stearate, 90 parts of calcium carbonate, 3 parts of superfine alumina silicate, 3 parts of calcium carbonate crystal whisker are nano oxidized
1.5 parts of titanium, 6 parts of chlorinated paraffin, 2-4 parts of sorbic acid, 3 parts of anti-skid wearable powder, the anti-skid wearable powder are diamond dust, hollow ceramic
The mixture of micro mist and gluey graphite powder, three's mass ratio are 10:10:3.
3. a kind of abrasive floor glue according to claim 1, which is characterized in that be additionally added 2-3 parts of zinc silicate.
4. a kind of abrasive floor glue according to claim 1, which is characterized in that be additionally added 2-3 parts of nano silicon dioxide.
5. a kind of abrasive floor glue according to claim 1, which is characterized in that be additionally added 2-5 parts of calcium zinc stabilizer.
6. a kind of preparation method of abrasive floor glue according to claim 1, which is characterized in that include the following steps:
1) raw material is put into stirring at low speed 3-4 minutes in batch mixer, is then transferred to high-speed stirred 6-7 minutes, temperature rise
To 90-100 DEG C, it is transferred to stirring at low speed again 3-4 minutes, mixed material is discharged into the dispersion of stirring at low speed pot and is cooled to room temperature, so
After be discharged into storage tank, then by screw conveyor be sent into double screw extruder fully heat, shear, plasticizing, enter back into single screw rod
Extruder further heats, plasticizing, is granulated by exporting cut-out, is finally cooled to room temperature the PVC granule being granulated;
2) calendering formation:PVC granule is transported to calender and is squeezed into coiled material;
3) heating plasticizing:Coiled material obtained by step 2) is sent into electrical heating baking oven, warm area drops to 190 DEG C by 190 to 220 DEG C, makes again
The abundant heating plasticizing of material;
4) secondary calendering:Step 3) products obtained therefrom is entered into two calenders, in 150 DEG C of extrusion formings;
5) back segment is handled:Base material gluing is carried out heating at 180 DEG C with step 4) products obtained therefrom to be bonded, is then embossed, it is cold
But, cutting edge, surface UV processing, thermal stress are eliminated, again cooling winding, and obtained product is abrasive floor glue.
7. a kind of preparation method of abrasive floor glue according to claim 6, which is characterized in that abrasive floor glue surface
Pass through silicic acid immersion treatment.