CN108673677A - A kind of preparation method of the hand-weaving product stalk of stable structure - Google Patents
A kind of preparation method of the hand-weaving product stalk of stable structure Download PDFInfo
- Publication number
- CN108673677A CN108673677A CN201810363245.9A CN201810363245A CN108673677A CN 108673677 A CN108673677 A CN 108673677A CN 201810363245 A CN201810363245 A CN 201810363245A CN 108673677 A CN108673677 A CN 108673677A
- Authority
- CN
- China
- Prior art keywords
- stalk
- hand
- wheat stalk
- wheat
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of the hand-weaving product stalk of stable structure, include the following steps：（1）Stalk cleaning,（2）Stalk immersion modification,（3）External force deformation process,（4）It is dried.Stalk neat appearance made from the method for the present invention, braided nature is good, improves the efficiency of braiding and the exquisite sophistication of craftwork, and its intensity, corrosion resistant, stability have also obtained apparent improvement.
Description
Technical field
The invention belongs to baskets craft technical fields, are related to a kind of braiding stalk, and in particular to a kind of stable structure
Hand-weaving product stalk preparation method.
Background technology
Funan County is under the jurisdiction of Anhui Province's Fuyang City, belongs to inland exploitation area earlier, on the Anhui Province northwestward, Huaihe River
Middle reaches engaging portion north bank.Funan County be known as " famous-brand and high-quality specialty county ", " Natural resources reservoir " title, be national grain-production great Xian, in
The unique agricultural in township, the whole nation of state's wicker plaiting article（Forestry）Circular economy demonstration pilot project county, Funan are the township of national wicker plaiting article, wicker products
It is sold abroad.
The raw material of wicker plaiting article can be wicker, rattan, timber, bamboo wood etc., it is possible to use crop waste stalk, such as rice straw
Stalk, wheat stalk etc. use stalk to be woven not only as raw material so that waste makes full use of, while being also avoided that stalk
It burns, is conducive to environmental protection.Although stalk knitting in some areas by a large amount of processing and fabricating, because stalk is from stature
Matter is soft, not corrosion resistant, non-watertight etc., easily occurs loose, deformation when causing subsequently to use, or even the problems such as damage.In addition, existing side
The figure appearances of stalk baskets craft made of method are less beautiful, and economic value is low.
Invention content
The purpose of the present invention is for existing problem, provide a kind of hand-weaving product stalk of stable structure
Preparation method.
The present invention is achieved by the following technical solutions：
A kind of preparation method of the hand-weaving product stalk of stable structure, includes the following steps：
（1）Stalk cleans：
By wheat stalk defoliation, remove fringe, root gone to handle after, then be rinsed with clear water, it is spare after removal dirt, particulate debris；
（2）Stalk impregnates modification：
A. by step（1）Treated wheat stalk is a bundle according to 80 ~ 100, is bundled with nylon rope, then with waddy at
The wheat stalk of bundle carries out beaing processing, spare after the completion；When carrying out beaing processing to wheat stalk with waddy, by the section of stalk
Between be crushed so that stalk be interconnected, be conducive to follow-up immersion treatment；
B. will operation a treated that wheat stalk is immersed in modification liquid, heating keep the temperature of modification liquid be 40 ~
45 DEG C, it is carried out at the same time ultrasonic irradiation processing, is taken out wheat stalk after 1 ~ 1.5h spare；The modification liquid is by as follows
The material composition of parts by weight：15 ~ 20 parts of aluminium foil powder, 10 ~ 15 parts of polyvinyl alcohol, 12 ~ 16 parts of silane coupling agents, 5 ~ 10 parts of stearic acid
Magnesium, 260 ~ 300 parts of deionized waters；
（3）External force deformation process：
A. by step（2）It is put into that keep away Yang Chu and dry to water content be 40 ~ 45% standby after bundled wheat stalk tears open bundle that treated
With；
B. with 10 ~ 15 it is a branch of by operation a treated wheat stalks, then by surface treatment liquid atomized spray in Wheat Straw
The surface of stalk, artificial one end for holding wheat stalk beam on the other hand, another hand-held plank strike wheat stalk Shu Jinhang after spraying uniformly
Processing is played, after beaing 1 ~ 1.5min of processing per beam；External force is carried out to wheat stalk with plank and beats processing so that Wheat Straw
Stalk shape becomes flat structure, so that stalk forming is conducive to enhancing, braiding；
（4）It is dried：
By step（3）Treated, and wheat stalk is put into drying box that processing is dried, and waits for that wheat stalk water content is little
It is taken out after 8%.
Further, step（2）The processing of beaing operated described in a is manually to beat processing, specifically holds one on the other hand
One end of wheat stalk is tied, the other hand is held waddy and beaten to the centre of wheat stalk and other end position, then again will
Wheat stalk turns around to continue to beat processing, and exerting oneself under often bundle wheat stalk beats 70 ~ 80, when beaing, consistent, position is uniform.
Further, step（2）The frequency for operating the ultrasonic irradiation processing described in b is 100 ~ 120kHz.
Further, step（2）The particle diameter for operating the aluminium foil powder described in b is 0.5 ~ 2mm.
Further, step（2）It is silane coupling agent kh550, silane coupling agent to operate the silane coupling agent described in b
Any one in kh560, silane coupling agent kh570.
Further, step（3）Operating the preparation method of the surface treatment liquid described in b is：By pine needle clear water of falling leaves
After rinsing one time, then 20 ~ 30s of immersion treatment in petroleum ether is put into, is after the completion filtered off fallen leaves pine needle, then evaporation is gone
Except petroleum ether obtains solid particle, finally by solid particle, neopelex, deionized water according to weight ratio 8 ~ 12:5~
10:After 90 ~ 100 are mixed evenly.The surface treatment liquid of preparation is the wax extracted from fallen leaves pine needle
Aqueous solution is sprayed on wheat stalk surface before beaing processing, prevents wheat stalk adhered to one another, and can further promote straw
The surface water repellent ability of stalk.
Further, step（3）The firmly consistent, position of control when beaing processing described in operation b when beaing is uniform.
Further, step（4）Described in drying process when control drying box in temperature be 65 ~ 70 DEG C.
The present invention has carried out special improvement to the preparation method of stalk and has handled, wherein with modification liquid to wheat stalk
Immersion treatment is carried out, the ingredients such as aluminium foil powder, polyvinyl alcohol in modification liquid penetrate into wheat stalk inner and outer surfaces, later
When carrying out beaing processing with plank, aluminium foil powder is bonded with wheat straw fiber, while being squeezed to combine between aluminium foil powder and being formed fiber
Skeleton structure improves the intensity, toughness of stalk entirety jointly, is attached to the aluminium foil powder on stalk surface etc. and can be obviously improved straw
Glossiness, the slickness of stalk enhance the efficiency and aesthetic appearance degree of braiding, and external force beats the effect with modification liquid
Under, wheat stalk is in finally flat, and the hollow structure of stalk disappears, and compactness improves, and is not only conducive to baskets craft and constructs
The promotion of fineness, and improve the water repellent of baskets craft, mould proof, stability etc..
The present invention has the following advantages compared with prior art：
Stalk neat appearance made from the method for the present invention, braided nature is good, and the fineness of the efficiency and craftwork that improve braiding is thin
Greasy degree, and its intensity, corrosion resistant, stability have also obtained apparent improvement, great popularizing value.
Specific implementation mode
Embodiment 1
A kind of preparation method of the hand-weaving product stalk of stable structure, includes the following steps：
（1）Stalk cleans：
By wheat stalk defoliation, remove fringe, root gone to handle after, then be rinsed with clear water, it is spare after removal dirt, particulate debris；
（2）Stalk impregnates modification：
A. by step（1）Treated wheat stalk is a bundle according to 80, is bundled with nylon rope, then with waddy to bundled
Wheat stalk carries out beaing processing, spare after the completion；Selected waddy shape is cylinder, and cross-sectional diameter is 6 ~ 7cm, long
Degree is 1 ~ 1.2m；
B. will operation a treated that wheat stalk is immersed in modification liquid, it is 40 that heating, which keeps the temperature of modification liquid,
DEG C, it is carried out at the same time ultrasonic irradiation processing, is taken out wheat stalk after 1h spare；The modification liquid is by following parts by weight
Material composition：15 parts of aluminium foil powder, 10 parts of polyvinyl alcohol, 12 parts of silane coupling agents, 5 parts of magnesium stearates, 260 parts of deionized waters；
（3）External force deformation process：
A. by step（2）It is put into that keep away Yang Chu and dry to water content be 40 ~ 45% standby after bundled wheat stalk tears open bundle that treated
With；
B. with 10 it is a branch of by operation a treated wheat stalks, then by surface treatment liquid atomized spray in wheat stalk
Surface, artificial one end for holding wheat stalk beam on the other hand, another hand-held plank beat wheat stalk Shu Jinhang after spraying uniformly
Processing, after processing 1min is beaten per beam；Plank shape used is cuboid, the length and width of cross section be 7 ~ 8cm × 0.5 ~
1cm, length are 80 ~ 100cm；
（4）It is dried：
By step（3）Treated, and wheat stalk is put into drying box that processing is dried, and waits for that wheat stalk water content is little
It is taken out after 8%.
Further, step（2）The processing of beaing operated described in a is manually to beat processing, specifically holds one on the other hand
One end of wheat stalk is tied, the other hand is held waddy and beaten to the centre of wheat stalk and other end position, then again will
Wheat stalk turns around to continue to beat processing, and exerting oneself under often bundle wheat stalk beats 70, when beaing, consistent, position is uniform.
Further, step（2）The frequency for operating the ultrasonic irradiation processing described in b is 100kHz.
Further, step（2）The particle diameter for operating the aluminium foil powder described in b is 0.5 ~ 2mm.
Further, step（2）It is silane coupling agent kh550 to operate the silane coupling agent described in b.
Further, step（3）Operating the preparation method of the surface treatment liquid described in b is：By pine needle clear water of falling leaves
After rinsing one time, then immersion treatment 20s in petroleum ether is put into, is after the completion filtered off fallen leaves pine needle, then evaporative removal
Petroleum ether obtains solid particle, finally by solid particle, neopelex, deionized water according to weight ratio 8:5:90 carry out
After being mixed evenly.
Further, step（3）The firmly consistent, position of control when beaing processing described in operation b when beaing is uniform.
Further, step（4）Described in drying process when control drying box in temperature be 65 DEG C.
The tensile strength of the present invention treated the more untreated common stalk of wheat stalk improves 100 ~ 120%, and anti-
Water, corrosion resistant performance enhance 2 ~ 3 times, and the improved efficiency of braiding 25% or more is suitable for the braiding of high-quality hand-made.
Embodiment 2
A kind of preparation method of the hand-weaving product stalk of stable structure, includes the following steps：
（1）Stalk cleans：
By wheat stalk defoliation, remove fringe, root gone to handle after, then be rinsed with clear water, it is spare after removal dirt, particulate debris；
（2）Stalk impregnates modification：
A. by step（1）Treated wheat stalk is a bundle according to 90, is bundled with nylon rope, then with waddy to bundled
Wheat stalk carries out beaing processing, spare after the completion；Selected waddy shape is cylinder, and cross-sectional diameter is 6 ~ 7cm, long
Degree is 1 ~ 1.2m；
B. will operation a treated that wheat stalk is immersed in modification liquid, it is 43 that heating, which keeps the temperature of modification liquid,
DEG C, it is carried out at the same time ultrasonic irradiation processing, is taken out wheat stalk after 1.2h spare；The modification liquid is by following weight
The material composition of part：18 parts of aluminium foil powder, 13 parts of polyvinyl alcohol, 14 parts of silane coupling agents, 8 parts of magnesium stearates, 280 parts of deionizations
Water；
（3）External force deformation process：
A. by step（2）It is put into that keep away Yang Chu and dry to water content be 40 ~ 45% standby after bundled wheat stalk tears open bundle that treated
With；
B. with 13 it is a branch of by operation a treated wheat stalks, then by surface treatment liquid atomized spray in wheat stalk
Surface, artificial one end for holding wheat stalk beam on the other hand, another hand-held plank beat wheat stalk Shu Jinhang after spraying uniformly
Processing, after processing 1.2min is beaten per beam；Plank shape used is cuboid, and the length and width of cross section are 7 ~ 8cm × 0.5
~ 1cm, length are 80 ~ 100cm；
（4）It is dried：
By step（3）Treated, and wheat stalk is put into drying box that processing is dried, and waits for that wheat stalk water content is little
It is taken out after 8%.
Further, step（2）The processing of beaing operated described in a is manually to beat processing, specifically holds one on the other hand
One end of wheat stalk is tied, the other hand is held waddy and beaten to the centre of wheat stalk and other end position, then again will
Wheat stalk turns around to continue to beat processing, and exerting oneself under often bundle wheat stalk beats 75, when beaing, consistent, position is uniform.
Further, step（2）The frequency for operating the ultrasonic irradiation processing described in b is 110kHz.
Further, step（2）The particle diameter for operating the aluminium foil powder described in b is 0.5 ~ 2mm.
Further, step（2）It is silane coupling agent kh560 to operate the silane coupling agent described in b.
Further, step（3）Operating the preparation method of the surface treatment liquid described in b is：By pine needle clear water of falling leaves
After rinsing one time, then immersion treatment 25s in petroleum ether is put into, is after the completion filtered off fallen leaves pine needle, then evaporative removal
Petroleum ether obtains solid particle, finally by solid particle, neopelex, deionized water according to weight ratio 10:8:95 into
After row is mixed evenly.
Further, step（3）The firmly consistent, position of control when beaing processing described in operation b when beaing is uniform.
Further, step（4）Described in drying process when control drying box in temperature be 68 DEG C.
The tensile strength of the present invention treated the more untreated common stalk of wheat stalk improves 100 ~ 120%, and anti-
Water, corrosion resistant performance enhance 2 ~ 3 times, and the improved efficiency of braiding 25% or more is suitable for the braiding of high-quality hand-made.
Embodiment 3
A kind of preparation method of the hand-weaving product stalk of stable structure, includes the following steps：
（1）Stalk cleans：
By wheat stalk defoliation, remove fringe, root gone to handle after, then be rinsed with clear water, it is spare after removal dirt, particulate debris；
（2）Stalk impregnates modification：
A. by step（1）Treated wheat stalk is a bundle according to 100, is bundled with nylon rope, then with waddy to bundled
Wheat stalk carry out beaing processing, it is spare after the completion；Selected waddy shape is cylinder, and cross-sectional diameter is 6 ~ 7cm,
Length is 1 ~ 1.2m；
B. will operation a treated that wheat stalk is immersed in modification liquid, it is 45 that heating, which keeps the temperature of modification liquid,
DEG C, it is carried out at the same time ultrasonic irradiation processing, is taken out wheat stalk after 1.5h spare；The modification liquid is by following weight
The material composition of part：20 parts of aluminium foil powder, 15 parts of polyvinyl alcohol, 16 parts of silane coupling agents, 10 parts of magnesium stearates, 300 parts of deionizations
Water；
（3）External force deformation process：
A. by step（2）It is put into that keep away Yang Chu and dry to water content be 40 ~ 45% standby after bundled wheat stalk tears open bundle that treated
With；
B. with 15 it is a branch of by operation a treated wheat stalks, then by surface treatment liquid atomized spray in wheat stalk
Surface, artificial one end for holding wheat stalk beam on the other hand, another hand-held plank beat wheat stalk Shu Jinhang after spraying uniformly
Processing, after processing 1.5min is beaten per beam；Plank shape used is cuboid, and the length and width of cross section are 7 ~ 8cm × 0.5
~ 1cm, length are 80 ~ 100cm；
（4）It is dried：
By step（3）Treated, and wheat stalk is put into drying box that processing is dried, and waits for that wheat stalk water content is little
It is taken out after 8%.
Further, step（2）The processing of beaing operated described in a is manually to beat processing, specifically holds one on the other hand
One end of wheat stalk is tied, the other hand is held waddy and beaten to the centre of wheat stalk and other end position, then again will
Wheat stalk turns around to continue to beat processing, and exerting oneself under often bundle wheat stalk beats 80, when beaing, consistent, position is uniform.
Further, step（2）The frequency for operating the ultrasonic irradiation processing described in b is 120kHz.
Further, step（2）The particle diameter for operating the aluminium foil powder described in b is 0.5 ~ 2mm.
Further, step（2）It is silane coupling agent kh570 to operate the silane coupling agent described in b.
Further, step（3）Operating the preparation method of the surface treatment liquid described in b is：By pine needle clear water of falling leaves
After rinsing one time, then immersion treatment 30s in petroleum ether is put into, is after the completion filtered off fallen leaves pine needle, then evaporative removal
Petroleum ether obtains solid particle, finally by solid particle, neopelex, deionized water according to weight ratio 6:5:50 carry out
After being mixed evenly.
Further, step（3）The firmly consistent, position of control when beaing processing described in operation b when beaing is uniform.
Further, step（4）Described in drying process when control drying box in temperature be 70 DEG C.
The tensile strength of the present invention treated the more untreated common stalk of wheat stalk improves 100 ~ 120%, and anti-
Water, corrosion resistant performance enhance 2 ~ 3 times, and the improved efficiency of braiding 25% or more is suitable for the braiding of high-quality hand-made.
Claims (8)
1. a kind of preparation method of the hand-weaving product stalk of stable structure, which is characterized in that include the following steps：
（1）Stalk cleans：
By wheat stalk defoliation, remove fringe, root gone to handle after, then be rinsed with clear water, it is spare after removal dirt, particulate debris；
（2）Stalk impregnates modification：
A. by step（1）Treated wheat stalk is a bundle according to 80 ~ 100, is bundled with nylon rope, then with waddy at
The wheat stalk of bundle carries out beaing processing, spare after the completion；
B. will operation a treated that wheat stalk is immersed in modification liquid, heating keep the temperature of modification liquid be 40 ~
45 DEG C, it is carried out at the same time ultrasonic irradiation processing, is taken out wheat stalk after 1 ~ 1.5h spare；The modification liquid is by as follows
The material composition of parts by weight：15 ~ 20 parts of aluminium foil powder, 10 ~ 15 parts of polyvinyl alcohol, 12 ~ 16 parts of silane coupling agents, 5 ~ 10 parts of stearic acid
Magnesium, 260 ~ 300 parts of deionized waters；
（3）External force deformation process：
A. by step（2）It is put into that keep away Yang Chu and dry to water content be 40 ~ 45% standby after bundled wheat stalk tears open bundle that treated
With；
B. with 10 ~ 15 it is a branch of by operation a treated wheat stalks, then by surface treatment liquid atomized spray in Wheat Straw
The surface of stalk, artificial one end for holding wheat stalk beam on the other hand, another hand-held plank strike wheat stalk Shu Jinhang after spraying uniformly
Processing is played, after beaing 1 ~ 1.5min of processing per beam；
（4）It is dried：
By step（3）Treated, and wheat stalk is put into drying box that processing is dried, and waits for that wheat stalk water content is little
It is taken out after 8%.
2. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（2）The processing of beaing operated described in a is manually to beat processing, specifically holds a bundle wheat stalk on the other hand
One end, the other hand are held waddy and are beaten to the centre of wheat stalk and other end position, then wheat stalk turns around again
Continue to beat processing, exerting oneself under often bundle wheat stalk beats 70 ~ 80, when beaing, consistent, position is uniform.
3. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（2）The frequency for operating the ultrasonic irradiation processing described in b is 100 ~ 120kHz.
4. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（2）The particle diameter for operating the aluminium foil powder described in b is 0.5 ~ 2mm.
5. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（2）Operate the silane coupling agent described in b be silane coupling agent kh550, it is silane coupling agent kh560, silane coupled
Any one in agent kh570.
6. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（3）Operating the preparation method of the surface treatment liquid described in b is：After the pine needle that will fall leaves is rinsed one time with clear water, then
20 ~ 30s of immersion treatment in petroleum ether is put into, is after the completion filtered off fallen leaves pine needle, then evaporative removal petroleum ether must be consolidated
Body particle, finally by solid particle, neopelex, deionized water according to weight ratio 8 ~ 12:5~10:90 ~ 100 carry out
After being mixed evenly.
7. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（3）The firmly consistent, position of control when beaing processing described in operation b when beaing is uniform.
8. a kind of preparation method of the hand-weaving product stalk of stable structure according to claim 1, feature
It is, step（4）Described in drying process when control drying box in temperature be 65 ~ 70 DEG C.