CN108673672A - A kind of production method of bamboo wood - Google Patents
A kind of production method of bamboo wood Download PDFInfo
- Publication number
- CN108673672A CN108673672A CN201810497699.5A CN201810497699A CN108673672A CN 108673672 A CN108673672 A CN 108673672A CN 201810497699 A CN201810497699 A CN 201810497699A CN 108673672 A CN108673672 A CN 108673672A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo chip
- production method
- chip
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of production methods of bamboo wood, include the following steps：S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, removal outer of bamboo is yellow；S1.2：By treated, bamboo chip is put into pressure cooking in boiling water, and digestion time is 1 5h, and cooking pressure is in 1.1 2Mpa；The dry machine of dried disinfecting carbon is put into after bamboo chip after boiling is pulled out, the temperature of the dry machine heating of dried disinfecting carbon is 160-190 DEG C, and 2-4 hours heating times, bamboo chip carbonization, carbonizing degree is 5%-30%；S1.3：The S1.2 bamboo chips obtained are put under vacuum in vegetable oil and carry out heating immersion, oil temperature is 150 170 DEG C, and soaking time is 2 3h, after the bamboo chip after immersion is pulled out, it is stood under vacuum after bamboo chip upper and lower surface coats sponge, time of repose is 2 3h；S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, and 20 40min are impregnated, and takes out drying, is made.
Description
Technical field
The present invention relates to building material product technical field, more particularly to a kind of production method of bamboo wood.
Background technology
In order to conserve forests, prevent erosion, pursuit wood substituted by bamboo has become trend of the times；Bamboo will be used widely
The operational support bamboo clappers that bamboo clappers and bamboo nail must be made does not rupture, could realize the pursuit of wood substituted by bamboo.Existing bamboo wood
Since processing method method presence is not scientific, lead to bamboo wood mutability, easy to crack, short life, poor quality, on building materials market
Consumer perceptions' degree is poor.
Invention content
To solve problems of the prior art, the present invention provides a kind of production methods of bamboo wood.
To achieve the above object, the present invention is implemented by the following technical solutions：
A kind of production method of bamboo wood, includes the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, removal outer of bamboo is yellow；
S1.2：By treated, bamboo chip is put into pressure cooking in boiling water, and digestion time 1-5h, cooking pressure is in 1.1-
2Mpa；The dry machine of dried disinfecting carbon is put into after bamboo chip after boiling is pulled out, the temperature of the dry machine heating of dried disinfecting carbon is 160-
190 DEG C, 2-4 hours heating times, bamboo chip carbonization, carbonizing degree is 5%-30%；
S1.3：The bamboo chip that S1.2 is obtained is subjected to heating immersion being put under vacuum in vegetable oil, oil temperature is
150-170 DEG C, soaking time 2-3h, after the bamboo chip after immersion is pulled out, in vacuum after bamboo chip upper and lower surface coats sponge
Under the conditions of stand, time of repose 2-3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, and 20-40min is impregnated, and takes out drying, is made.
Preferably, in S1.2, digestion time 3h.
Preferably, in S1.2, cooking pressure 1.4MPa.
Preferably, in S1.3, oil temperature is 160 DEG C.
Preferably, in S1.3, soaking time 2.5h.
Preferably, in S1.3, time of repose 2.5h.
The beneficial effects of the invention are as follows：
The production method of bamboo wood disclosed in this invention, technological design is scientific and reasonable, very according to the self performance feature of bamboo wood,
Bamboo wood is modified using scientific method in bamboo flooring production process, ensures that bamboo wood is with good performance, does not crack not
Deformation, greatly improves the stability of bamboo wood.
Specific implementation mode
Embodiments of the present invention are further described with reference to embodiment, but are not limitation of the invention.
Embodiment 1
A kind of production method of bamboo wood, includes the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, removal outer of bamboo is yellow；
S1.2：By treated, bamboo chip is put into pressure cooking in boiling water, and digestion time 1h, cooking pressure is in 1.1Mpa；
It is put into the dry machine of dried disinfecting carbon after bamboo chip after boiling is pulled out, the temperature of the dry machine heating of dried disinfecting carbon is 160 DEG C, when heating
Between 2 hours, bamboo chip carbonization, carbonizing degree 5；
S1.3：The bamboo chip that S1.2 is obtained is subjected to heating immersion being put under vacuum in vegetable oil, oil temperature 150
DEG C, soaking time 2-3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after pulling the bamboo chip after immersion out
It sets, time of repose 2h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, and 20min is impregnated, and takes out drying, is made.
Embodiment 2：
A kind of production method of bamboo wood, includes the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, removal outer of bamboo is yellow；
S1.2：By treated, bamboo chip is put into pressure cooking in boiling water, and digestion time 5h, cooking pressure is in 2Mpa；It will
Bamboo chip after boiling is put into the dry machine of dried disinfecting carbon after pulling out, the temperature of the dry machine heating of dried disinfecting carbon is 170 DEG C, heating time
3 hours, bamboo chip carbonization, carbonizing degree 15%；
S1.3：The bamboo chip that S1.2 is obtained is subjected to heating immersion being put under vacuum in vegetable oil, oil temperature 170
DEG C, soaking time 3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after pulling the bamboo chip after immersion out
It sets, time of repose 3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, and 40min is impregnated, and takes out drying, is made.
Embodiment 3：
A kind of production method of bamboo wood, includes the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, removal outer of bamboo is yellow；
S1.2：By treated, bamboo chip is put into pressure cooking in boiling water, and digestion time 2h, cooking pressure is in 1.2Mpa；
It is put into the dry machine of dried disinfecting carbon after bamboo chip after boiling is pulled out, the temperature of the dry machine heating of dried disinfecting carbon is 190 DEG C, when heating
Between 4 hours, bamboo chip carbonization, carbonizing degree 30%；
S1.3：The bamboo chip that S1.2 is obtained is subjected to heating immersion being put under vacuum in vegetable oil, oil temperature 155
DEG C, soaking time 2.4h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after pulling the bamboo chip after immersion out
It sets, time of repose 2.1h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, and 22min is impregnated, and takes out drying, is made.
The above described is only a preferred embodiment of the present invention, not making any form to technical scheme of the present invention
On limitation.Every essence according to the present invention is to any simple modification, equivalent change and modification made by above example,
It falls within the scope of protection of the present invention.
Claims (6)
1. a kind of production method of bamboo wood, it is characterised in that：Include the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, removal outer of bamboo is yellow；
S1.2：By treated, bamboo chip is put into pressure cooking in boiling water, and digestion time 1-5h, cooking pressure is in 1.1-2Mpa；
The dry machine of dried disinfecting carbon is put into after bamboo chip after boiling is pulled out, the temperature of the dry machine heating of dried disinfecting carbon is 160-190 DEG C,
2-4 hours heating times, bamboo chip carbonization, carbonizing degree are 5%-30%；
S1.3：The bamboo chip that S1.2 is obtained is subjected to heating immersion being put under vacuum in vegetable oil, oil temperature 150-170
DEG C, soaking time 2-3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after pulling the bamboo chip after immersion out
It sets, time of repose 2-3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, and 20-40min is impregnated, and takes out drying, is made.
2. a kind of production method of bamboo wood according to claim 1, it is characterised in that：In S1.2, digestion time 3h.
3. a kind of production method of bamboo wood according to claim 1, it is characterised in that：In S1.2, cooking pressure is
1.4MPa。
4. a kind of production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, oil temperature is 160 DEG C.
5. a kind of production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, soaking time is
2.5h。
6. a kind of production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, time of repose is
2.5h。