CN107650228A - A kind of production method of bamboo wood - Google Patents

A kind of production method of bamboo wood Download PDF

Info

Publication number
CN107650228A
CN107650228A CN201710936808.4A CN201710936808A CN107650228A CN 107650228 A CN107650228 A CN 107650228A CN 201710936808 A CN201710936808 A CN 201710936808A CN 107650228 A CN107650228 A CN 107650228A
Authority
CN
China
Prior art keywords
bamboo
bamboo chip
production method
chip
bamboo wood
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710936808.4A
Other languages
Chinese (zh)
Inventor
覃正道
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou Longtai Bamboo Industry Co Ltd
Original Assignee
Liuzhou Longtai Bamboo Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou Longtai Bamboo Industry Co Ltd filed Critical Liuzhou Longtai Bamboo Industry Co Ltd
Priority to CN201710936808.4A priority Critical patent/CN107650228A/en
Publication of CN107650228A publication Critical patent/CN107650228A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of production method of bamboo wood, comprise the following steps：S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time is 1 5h, and cooking pressure is in 1.1 2Mpa；Bamboo chip after boiling is pulled out and is dried to water content to 10 15%；S1.3：The S1.2 bamboo chips obtained are put into vegetable oil under vacuum and carry out heating immersion, oil temperature is 150 170 DEG C, and soak time is 2 3h, after the bamboo chip after immersion is pulled out, stood under vacuum after bamboo chip upper and lower surface coats sponge, time of repose is 2 3h；S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 20 40min, takes out drying, is made.The production method of bamboo wood disclosed in this invention, technological design is scientific and reasonable, very according to the self performance feature of bamboo wood, bamboo wood is modified using scientific method in bamboo flooring production process, ensure that bamboo wood has good performance, do not ftracture indeformable, improve the stability of bamboo wood.

Description

A kind of production method of bamboo wood
Technical field
The present invention relates to building material product technical field, more particularly to a kind of production method of bamboo wood.
Background technology
In order to conserve forests, prevent erosion, pursuit wood substituted by bamboo turns into trend of the times；Bamboo will be used widely The operational support bamboo clappers that bamboo clappers and bamboo nail must be made does not rupture the pursuit that could realize wood substituted by bamboo.Existing bamboo wood Because the presence of processing mode method is not scientific, cause bamboo wood mutability, easy to crack, short life, poor quality, on building materials market Consumer perceptions' degree is poor.
The content of the invention
To solve problems of the prior art, the invention provides a kind of production method of bamboo wood.
The purpose of the present invention implements by the following technical programs：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 1-5h, cooking pressure is in 1.1- 2Mpa；Bamboo chip after boiling is pulled out and is dried to water content to 10-15%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, and oil temperature is 150-170 DEG C, soak time 2-3h, after the bamboo chip after immersion is pulled out, in vacuum after bamboo chip upper and lower surface coats sponge Under the conditions of stand, time of repose 2-3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 20-40min, takes out drying, is made.
Further, in S1.2, digestion time 3h.
Further, in S1.2, cooking pressure 1.4MPa.
Further, in S1.2, the bamboo chip after boiling is pulled out and is dried to water content to 12%.
Further, in S1.3, oil temperature is 160 DEG C.
Further, in S1.3, soak time 2.5h.
Further, in S1.3, time of repose 2.5h.
Further, in S1.3, oil temperature is 155 DEG C.
Further, in S1.3, soak time 2.2h.
The production method of bamboo wood disclosed in this invention, technological design is scientific and reasonable, very according to the self performance feature of bamboo wood, Bamboo wood is modified using scientific method in bamboo flooring production process, ensures that bamboo wood has good performance, does not ftracture not Deformation, greatly improve the stability of bamboo wood.
Embodiment
With reference to specific embodiment, specific embodiments of the present invention is described in detail.
Embodiment 1：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 1h, cooking pressure is in 1.1Mpa； Bamboo chip after boiling is pulled out and is dried to water content to 10%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 150 DEG C, soak time 2-3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 2h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 20min, takes out drying, is made.
Embodiment 2：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 5h, cooking pressure is in 2Mpa；Will Bamboo chip after boiling, which is pulled out, is dried to water content to 15%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 170 DEG C, soak time 3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 40min, takes out drying, is made.
Embodiment 3：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 2h, cooking pressure is in 1.2Mpa； Bamboo chip after boiling is pulled out and is dried to water content to 11%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 155 DEG C, soak time 2.4h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 2.1h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 22min, takes out drying, is made.
Embodiment 4：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 1-5h, cooking pressure exists 1.3Mpa；Bamboo chip after boiling is pulled out and is dried to water content to 13%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 153 DEG C, soak time 23h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 23h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 23min, takes out drying, is made.
Embodiment 5：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 1-5h, cooking pressure is in 1.1- 2Mpa；Bamboo chip after boiling is pulled out and is dried to water content to 13%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 156 DEG C, soak time 2h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 24min, takes out drying, is made.
Embodiment 6：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 4h, cooking pressure is in 1.6Mpa； Bamboo chip after boiling is pulled out and is dried to water content to 14%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 160 DEG C, soak time 2.6h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 2.3h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 32min, takes out drying, is made.
Embodiment 7：A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 3.6h, cooking pressure exists 1.6Mpa；Bamboo chip after boiling is pulled out and is dried to water content to 10-15%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 156 DEG C, soak time 3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 2h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 20min, takes out drying, is made.
Embodiment 8：
A kind of production method of bamboo wood, comprises the following steps：
S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 4h, cooking pressure is in 1.5Mpa； Bamboo chip after boiling is pulled out and is dried to water content to 10-15%；
S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 156 DEG C, soak time 2.5h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 2.5h；
S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 35min, takes out drying, is made.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic. Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in the present invention's Within protection domain.

Claims (10)

  1. A kind of 1. production method of bamboo wood, it is characterised in that：Comprise the following steps：
    S1.1：Raw bamboo is cut into bamboo chip, bamboo chip is tied, it is yellow to remove outer of bamboo；
    S1.2：Bamboo chip after processing is put into pressure cooking in boiling water, digestion time 1-5h, cooking pressure is in 1.1-2Mpa； Bamboo chip after boiling is pulled out and is dried to water content to 10-15%；
    S1.3：The bamboo chip that S1.2 is obtained carries out heating immersion being put under vacuum in vegetable oil, oil temperature 150-170 DEG C, soak time 2-3h is quiet under vacuum after bamboo chip upper and lower surface coats sponge after the bamboo chip after immersion is pulled out Put, time of repose 2-3h；
    S1.4：The bamboo chip that S1.3 is obtained is placed in organic solvent, soaks 20-40min, takes out drying, is made.
  2. A kind of 2. production method of bamboo wood according to claim 1, it is characterised in that：In S1.2, digestion time 3h.
  3. A kind of 3. production method of bamboo wood according to claim 1, it is characterised in that：In S1.2, cooking pressure is 1.4MPa。
  4. A kind of 4. production method of bamboo wood according to claim 1, it is characterised in that：In S1.2, by the bamboo after boiling Piece, which is pulled out, is dried to water content to 12%.
  5. A kind of 5. production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, oil temperature is 160 DEG C.
  6. A kind of 6. production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, soak time is 2.5h。
  7. A kind of 7. production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, time of repose is 2.5h。
  8. A kind of 8. production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, time of repose is 2.3h。
  9. A kind of 9. production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, oil temperature is 155 DEG C.
  10. A kind of 10. production method of bamboo wood according to claim 1, it is characterised in that：In S1.3, soak time is 2.2h。
CN201710936808.4A 2017-10-10 2017-10-10 A kind of production method of bamboo wood Pending CN107650228A (en)