CN108672245A - A kind of clear spraying process for embodying the original lines of wood skin - Google Patents

A kind of clear spraying process for embodying the original lines of wood skin Download PDF

Info

Publication number
CN108672245A
CN108672245A CN201810570866.4A CN201810570866A CN108672245A CN 108672245 A CN108672245 A CN 108672245A CN 201810570866 A CN201810570866 A CN 201810570866A CN 108672245 A CN108672245 A CN 108672245A
Authority
CN
China
Prior art keywords
changed
boiled water
plain boiled
temperature
done
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810570866.4A
Other languages
Chinese (zh)
Inventor
黄明辉
黄瑞榕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan City Jia Run Furniture Co Ltd
Original Assignee
Dongguan City Jia Run Furniture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan City Jia Run Furniture Co Ltd filed Critical Dongguan City Jia Run Furniture Co Ltd
Priority to CN201810570866.4A priority Critical patent/CN108672245A/en
Publication of CN108672245A publication Critical patent/CN108672245A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of clear spraying process for embodying the original lines of wood skin, the technique, which passes sequentially through, makes wood mill, jet background, spray wash coats, it polishes on head, first pass priming paint, first pass oil abrasion, second time priming paint, second time priming paint, second time oil abrasion, hardboard sand removal prints, it has a shave color, make color mill, first pass finishing coat, the face of beating mill, second time finishing coat and the polishing of wool ball are realized, finished product after the completion of enabling clearly embodies the original lines of wood skin, reduce the wood skin cracking during the bubble phenomenon occurred in manufacturing process and follow-up use, the phenomenon that effectivelying prevent paint delamination generates.

Description

A kind of clear spraying process for embodying the original lines of wood skin
Technical field
The present invention relates to plate grain technology fields, and more specifically more particularly to one kind can clearly embody wood skin original The spraying process of beginning lines.
Background technology
The brilliant production such as existing stick-skin furniture is typically that will substitute base material using wood and/or plank as base material is substituted and press Routine determines step, half-crystal is made by preliminary working in method:Natural veneer is sticked to make in the outer surface of half-crystal, inner surface At lagging half-crystal, lagging half-crystal is finished through spray paint, fabrics, packaging etc. to which stick-skin furniture be made into selection successively The wood skin of unlike material, you can all kinds of lagging products are made, but such lagging product easy tos produce bubble and shows in the production process As wood skin is cracked during follow-up use, and paint delamination generates, and can not embody the original lines of wood skin, can not expire The demand of sufficient client.
Invention content
The present invention is improved the prior art for disadvantages mentioned above, and the original lines of wood skin can clearly be embodied by providing one kind Spraying process, technical solution is as follows:
A kind of clear spraying process for embodying the original lines of wood skin, the technique pass sequentially through following steps realization:
Make wood mill:According to wood skin effect color matched color ash, technique staple hole is mended, the polishing of machine sand is with 240# sand paper along wood Line is beaten, and so that it is scratched to jump without seep through, offset printing of paper and is lacked, then with 320# sand paper sand removal veneer surfaces;
It waits doing after jet background:A is matched:Color essence 15g and Tianna solution 20kg is deployed into diluent, b:Allotment stirs evenly according to the ratio, Two crosses are sprayed, colored paint is sprayed into veneer surface with high-pressure oil pump, it is allowed to drench, the grain for appearing wood skin dodges shadow, if closing 0.5H to be done to 1H is painted, if open paint 2H to be done to 3H;
It waits doing after spray wash coats:A is matched:Host agent 0.6kg to 0.8kg is deployed into sealing bottom with curing agent 0.4 to 0.6 Paint, b:Two crosses are sprayed, equipment is sprayed apart from veneer surface 40-50m, common wood skin 3H to be done is extremely using oil pump or pump rifle 4H;
It polishes on head:Impulse- free robustness is polished smooth with 400# sand paper;
Spray first pass priming paint:A is matched:Blue plain boiled water collocation, 5 ° to 40 ° of temperature, host agent 100g, plain boiled water 0.5g to 3g, Lan Shui 0.5g to 2.5g, diluent 35 to 40, b:Humidity between 50% to 70% plus 5% plain boiled water can normal construction, as humidity is super Crossing 70% must stop constructing, c:Two crosses of first pass primer spray, after 22H to be done to 26H;
First pass oil abrasion:Platen surface crosses machine and sands flat platform, is locally beaten clearly with 180# hand mills and edge;
Spray second time priming paint:A is matched:Blue plain boiled water collocation, 5 ° to 40 ° of temperature, host agent 100g, plain boiled water 0.5g to 3g, Lan Shui 0.5g to 2.5g, diluent 30 to 35, b:Humidity between 50% to 70% plus 5% plain boiled water can normal construction, as humidity is super Crossing 70% must stop constructing, c:Second time primer spray, two crosses;
Second time priming paint waits doing:72H to be done to 76H;
Second time oil abrasion:Platen surface crosses machine and sands flat platform, is locally beaten clearly with 180# hand mills and edge, handles priming paint table The dirt in face and the thickness of paint;
Hardboard sand removal prints:Using hardboard manual operations, which is rubber slab, and the platform sand removal abrasive bands 240#, machine mill is clearly Sand 320# sand paper, is cleaned to no wave, Wu Keng, reaches the flatness of Glabrous thorn;
It has a shave and waits doing after color:A paint proportionings:Color essence 140g to 160g, host agent 18kg to 21kg, curing agent 8kg to 12kg, Tianna solution 58kg to 62kg, b:Color of having a shave, 4H to be done to 5H are carried out according to colour table;
Make color mill:Manual operations makes color mill with 1000# sand paper, keeps its surface smooth dustless;
It waits doing after spray first pass finishing coat:A is formulated:8 ° to 38 ° of temperature, host agent 100g, diluent 40 to 45, Lan Shui 0.6m are extremely 2m, plain boiled water 1m to 2.4m, b:When temperature >=85%, indigo plant water consumption suitably increases 0.1-0.2%, c:The complete 22H to be done of finishing coat is extremely 26H;
The face of beating mill:Face mill is made manually with 800# sand paper machines sand;
It waits doing after second time finishing coat of spray:A is formulated:8 ° to 38 ° of temperature, host agent 100g, diluent 40 to 45, Lan Shui 0.6m are extremely 2m, plain boiled water 1m to 2.4m, b:When temperature >=85%, indigo plant water consumption suitably increases 0.1-0.2%, c:The complete 46H to be done of finishing coat is extremely 50H;
Wool ball polishes:It is processed by shot blasting using wool ball.
In the step (2), the seal coat time to be done is preferably 0.5H, if the open paint time to be done is preferably 2H.
In the step (3), the proportioning of wash coats is preferably that host agent 0.8kg is mixed with curing agent 0.5, sprinkling distance wood Epidermis face is 50m, and the common wood skin time to be done is preferably 4H.
In the step (5), when temperature is 10 ° to 15 °, host agent 100g, plain boiled water 2.6g, Lan Shui 2.0g, diluent 35 To 40, humidity between 50% to 70% plus 5% plain boiled water can normal construction, if humidity is more than that 70% must stop constructing, the Two crosses of a time primer spray, after 24H to be done;When temperature is 15 ° to 20 °, plain boiled water is changed to 2.3g, Lan Shui and is changed to 1.8g, remaining proportioning are constant;When temperature is 20 ° to 25 °, plain boiled water is changed to 2.0g, Lan Shui and is changed to 1.6g, remaining proportioning is not Become;When temperature is 25 ° to 30 °, plain boiled water is changed to 1.6g, Lan Shui and is changed to 1.2g, remaining proportioning is constant;It it is 30 ° in temperature When to 35 °, plain boiled water is changed to 1.2g, Lan Shui and is changed to 1.0g, remaining proportioning is constant;When temperature is 35 ° or more, plain boiled water change It is changed to 0.8g for 1.0g, Lan Shui, remaining proportioning is constant.
In the step (7), when temperature is 10 ° to 15 °, host agent 100g, plain boiled water 2.6g, Lan Shui 2.0g, diluent 30 To 35, humidity between 50% to 70% plus 5% plain boiled water can normal construction, if humidity is more than that 70% must stop constructing, the Two crosses of a time primer spray, after 24H to be done;When temperature is 15 ° to 20 °, plain boiled water is changed to 2.3g, Lan Shui and is changed to 1.8g, remaining proportioning are constant;When temperature is 20 ° to 25 °, plain boiled water is changed to 2.0g, Lan Shui and is changed to 1.6g, remaining proportioning is not Become;When temperature is 25 ° to 30 °, plain boiled water is changed to 1.6g, Lan Shui and is changed to 1.2g, remaining proportioning is constant;It it is 30 ° in temperature When to 35 °, plain boiled water is changed to 1.2g, Lan Shui and is changed to 1.0g, remaining proportioning is constant;When temperature is 35 ° or more, plain boiled water change It is changed to 0.8g for 1.0g, Lan Shui, remaining proportioning is constant.
In the step (8), second time priming paint time to be done is preferably 72H.
In the step (11), paint proportioning preferably color essence 150g, host agent 20kg, curing agent 10kg, Tianna solution 60kg, Time to be done is preferably 4H.
In the step (13), in 36 ° to 40 ° of temperature, host agent 100g, diluent 40 to 45, Lan Shui 0.8m, plain boiled water 1.2m, when temperature >=85%, indigo plant water consumption suitably increases 0.1-0.2%, and the time to be done is preferably 24H;In 26 ° to 35 ° of temperature When, Lan Shui is changed to 1.2m, and plain boiled water is changed to 1.5m, remaining proportioning is constant;In 21 ° to 25 ° of temperature, Lan Shui is changed to 1.5m, plain boiled water are changed to 1.8m, remaining proportioning is constant;In 15 ° to 20 ° of temperature, Lan Shui is changed to 1.5m, and plain boiled water is changed to 2.0m, remaining proportioning are constant;In 10 ° to 15 ° of temperature, Lan Shui is changed to 1.8m, and plain boiled water is changed to 2.2m, remaining proportioning is not Become.
In the step (15), second time finishing coat proportioning is identical as the proportioning of first pass finishing coat in claim 8, when dry Between preferably after 48H.
Compared with prior art, beneficial effects of the present invention are:The present invention provides one kind, and can clearly to embody wood skin original The spraying process of lines keeps surface clean, is uniformly sprayed by high-pressure oil pump by repairing the defect of wooden model amendment, repair products Base coating makes it appear the grain of wood skin and dodge shadow and obtains original effect, then utilize wash coats oil by it is wooden it is intracutaneous naturally at Part seals, cures, and by being polished for a plurality of times, reaching not delamination impulse- free robustness keeps filling effect more preferable, effectively reduces the generation of bubble, leads to After crossing first time oil abrasion, second time priming paint filling can be convenient for and control paint thickness, after second of primer spray, passed through for a long time It waiting doing, process wood skin to be done has contraction, paint can sink, can handle and paint prolonged sagging and surface freezing action, The thickness of the dirt and paint of second time oil abrasion processing primed surface, then so that it is cleaned to no wave, nothing by hardboard sand removal print It cheats, as the flatness of glass type, the second last after dry, is polished after finishing coat by wool ball, and paint face will nothing after polishing Particle, can be more preferable without tangerine peel and glossiness, and can keep convenient for cleaning in practical process, and the polishing of wool ball will not destroy Painted surface.
Description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, required use in being described below to embodiment Attached drawing be briefly described:
Fig. 1 is the structural diagram of the present invention;
Including:Plate base 10, background color 12, wash coats 13,14, second times priming paint 15 of first pass priming paint, has a shave at wood skin 11 Color 16, first pass finishing coat 17, second times finishing coats 18, wax burnishings 19.
Specific implementation mode
With reference to the attached drawing in the embodiment of the present invention, technical solution in the embodiment of the present invention carries out clear, complete Ground describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on this The embodiment of invention, every other implementation obtained by those of ordinary skill in the art without making creative efforts Example, belongs to protection scope of the present invention.
The embodiment of the present invention is described in further detail below in conjunction with attached drawing, it is as follows in detail:
One, wood mill is made
1. according to wood skin effect color matched color ash, technique staple hole is mended;
2. the polishing of machine sand is along the grain beaten with 240# sand paper, it is made to scratch spring without seep through, offset printing of paper and lack;
3. process seam is required directly not scrape hand along corner;
4. using 320# sand paper sand removal veneer surfaces again;
5. the wooden mill effect:It corrects, the defect of repair products, keeps surface clean.
Two, it waits doing after jet background
1, it matches:Color essence 15g and Tianna solution 20kg are deployed into diluent ,-as background color do the 50% of effect colour table, proportioning Color essence 15g is conventional ratio with Tianna solution 20kg;
2, formula, which mixes up, stirs evenly, and sprays two crosses, can be sprayed uniformly with high-pressure oil pump;
3, the optimum efficiency of background color purpose, by colored paint spray veneer surface, allow it to drench, appear wood skin grain dodge shadow obtain Original effect;
4, such as seal coat 0.5H to be done, such as open paint 2H to be done.
Three, it waits doing after spraying wash coats
1, it matches:Host agent 0.8kg is deployed into wash coats with curing agent 0.5, sprays two crosses, and equipment uses oil pump, Sprinkling is apart from veneer surface 50m, common wood skin 4H to be done;
2, the purpose of sealing:It is to be sealed the intracutaneous natural components of wood with oil, cures.
Four, head is polished
1, impulse- free robustness is slided with the polishing polishing of 400# sand paper;
2, the purpose polished:Not delamination impulse- free robustness can make filling effect best.
Five, first pass priming paint is sprayed
1, it matches:Blue plain boiled water arranges in pairs or groups (humidity≤70%)
Temperature (degree) Host agent (g) Plain boiled water (g) Lan Shui (g) Diluent
10-15 100 2.6 2.0 35-40
15-20 100 2.3 1.8 35-40
20-25 100 2.0 1.6 35-40
25-30 100 1.6 1.2 35-40
30-35 100 1.2 1.0 35-40
35 or more 100 1.0 0.8 35-40
The above ratio such as humidity between 50% to 70% plus 5% plain boiled water can normal construction, if it exceeds 70% is necessary Stop construction.
2, two crosses of first time construction wait for dry preferably 24H.
Six, first pass oil abrasion
1, platen surface crosses machine and sands flat platform;
2, it is locally beaten clearly with 180# hand mills and edge;
3, key points for operation:Convenient for second time priming paint filling and control paint thickness.
Seven, second time priming paint is sprayed
1, diluent is changed to 30-35, other temperature humidities and proportioning and first time priming paint proportioning are constant.
Eight, second time priming paint waits doing
1, the time to be done is preferably 72H;
2, process wood skin to be done has contraction, paint can sink, can handle and paint prolonged sagging and surface solidification Effect etc..
Nine, it buys oil mill
1, platen surface crosses machine and sands flat platform, is locally beaten clearly with 180# hand mills and edge;
2, purpose:Handle the thickness of the dirt and paint of primed surface.
Ten, hardboard sand removal prints
1, the platform platform sand removal abrasive bands 240#;
2, machine grinds sand removal 320# sand paper;
3, hardboard manual operations;
4, it is cleaned to no wave, Wu Keng, reaches Glabrous thorn, as the flatness of glass type.
11, it has a shave and waits doing after color
1, paint proportioning:Color essence 150g, host agent 20kg, curing agent 10kg, Tianna solution 60kg;
2, it is operated according to colour table;
3, the time to be done is preferably 4H.
12, color mill is made
1, hand-manipulated;
2, with 1000# sand paper;
3, purpose:Keep surface smooth dustless.
13, first time finishing coat waits doing
1, it is formulated
Temperature (degree Celsius) Host agent Diluent Lan Shui Plain boiled water
36-40 100 40-45 0.8m 1.2m
26-35 100 40-45 1.2m 1.5m
21-25 100 40-45 1.5m 1.8m
15-20 100 40-45 1.5m 2.0m
10-15 100 40-45 1.8m 2.2m
2, when temperature >=85%, indigo plant water consumption suitably increases 0.1-0.2%;
3, the time to be done is preferably 24H.
14, face mill is made
1, with 800# sand paper machine sand;
2, with the manual feelings head of 800# sand paper.
15, it waits doing after spraying second time finishing coat
1, paint proportioning is identical as first time finishing coat;
2, finishing coat is complete is finished to most preferably after 48 hours dry.
16, wool ball polishes
1, the fine and smooth softness of wool ball will not just destroy painted surface;
2, after polishing paint face will without particle, can be more preferable without tangerine peel and glossiness.And it can keep in practical process just In cleaning.
The present invention provides a kind of spraying process that can clearly embody the original lines of wood skin, by repairing wooden model amendment, repairing Mend product defect, keep surface clean, by high-pressure oil pump even application background color, make its appear the grain of wood skin dodge shadow obtain it is original Then the intracutaneous natural components of wood are sealed using wash coats with oil, are cured, by being polished for a plurality of times, reach not delamination by effect Impulse- free robustness keeps filling effect more preferable, effectively reduces the generation of bubble, after first time oil abrasion, can be filled out convenient for second time priming paint Fill and control paint thickness, after second of primer spray, done by waiting for a long time, process wood skin to be done have contraction, paint can under It sinks, prolonged sagging and surface the freezing action of paint, the dirt and paint of second time oil abrasion processing primed surface can be handled Thickness, then so that it is cleaned to no wave, Wu Keng, as the flatness of glass type by hardboard sand removal print, the second last is all over finishing coat After after dry, polished by wool ball, painted after polishing face will without particle, can be more preferable without tangerine peel and glossiness, and can protect It holds convenient for cleaning in practical process, and the polishing of wool ball will not destroy painted surface.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace And deformation, the scope of the present invention are limited by appended claims extremely equivalent.

Claims (9)

1. a kind of clear spraying process for embodying the original lines of wood skin, which is characterized in that the technique passes sequentially through following steps reality It is existing:
(1) wood mill is made:According to wood skin effect color matched color ash, technique staple hole is mended, the polishing of machine sand is with 240# sand paper along wood Line is beaten, and so that it is scratched to jump without seep through, offset printing of paper and is lacked, then with 320# sand paper sand removal veneer surfaces;
(2) it waits doing after jet background:A is matched:Color essence 15g and Tianna solution 20kg is deployed into diluent, b:Allotment stirs evenly according to the ratio, sprays Two crosses are applied, colored paint is sprayed into veneer surface with high-pressure oil pump, it is allowed to drench, the grain for appearing wood skin dodges shadow, if seal coat 0.5H to be done to 1H, if open paint 2H to be done to 3H;
(3) it waits doing after spraying wash coats:A is matched:Host agent 0.6kg to 0.8kg is deployed into wash coats with curing agent 0.4 to 0.6, b:Two crosses are sprayed, equipment is sprayed using oil pump or pump rifle apart from veneer surface 40-50m, common wood skin 3H to be done to 4H;
(4) head is polished:Impulse- free robustness is polished smooth with 400# sand paper;
(5) first pass priming paint is sprayed:A is matched:Blue plain boiled water collocation, 5 ° to 40 ° of temperature, host agent 100g, plain boiled water 0.5g to 3g, Lan Shui 0.5g to 2.5g, diluent 35 to 40, b:Humidity between 50% to 70% plus 5% plain boiled water can normal construction, as humidity is super Crossing 70% must stop constructing, c:Two crosses of first pass primer spray, after 22H to be done to 26H;
(6) first pass oil abrasion:Platen surface crosses machine and sands flat platform, is locally beaten clearly with 180# hand mills and edge;
(7) second time priming paint is sprayed:A is matched:Blue plain boiled water collocation, 5 ° to 40 ° of temperature, host agent 100g, plain boiled water 0.5g to 3g, Lan Shui 0.5g to 2.5g, diluent 30 to 35, b:Humidity between 50% to 70% plus 5% plain boiled water can normal construction, as humidity is super Crossing 70% must stop constructing, c:Second time primer spray, two crosses;
(8) second times priming paint waits doing:72H to be done to 76H;
(9) second times oil abrasions:Platen surface crosses machine and sands flat platform, is locally beaten clearly with 180# hand mills and edge, handles priming paint table The dirt in face and the thickness of paint;
(10) hardboard sand removal prints:Using hardboard manual operations, which is rubber slab, and the platform sand removal abrasive bands 240#, machine mill is clearly Sand 320# sand paper, is cleaned to no wave, Wu Keng, reaches the flatness of Glabrous thorn;
(11) it has a shave and waits doing after color:A paint proportionings:Color essence 140g to 160g, host agent 18kg to 21kg, curing agent 8kg to 12kg, Tianna solution 58kg to 62kg, b:Color of having a shave, 4H to be done to 5H are carried out according to colour table;
(12) color mill is made:Manual operations makes color mill with 1000# sand paper, keeps its surface smooth dustless;
(13) it waits doing after spraying first pass finishing coat:A is formulated:8 ° to 38 ° of temperature, host agent 100g, diluent 40 to 45, Lan Shui 0.6m are extremely 2m, plain boiled water 1m to 2.4m, b:When temperature >=85%, indigo plant water consumption suitably increases 0.1-0.2%, c:The complete 22H to be done of finishing coat is extremely 26H;
(14) face mill is made:Face mill is made manually with 800# sand paper machines sand;
(15) it waits doing after spraying second time finishing coat:A is formulated:8 ° to 38 ° of temperature, host agent 100g, diluent 40 to 45, Lan Shui 0.6m are extremely 2m, plain boiled water 1m to 2.4m, b:When temperature >=85%, indigo plant water consumption suitably increases 0.1-0.2%, c:The complete 46H to be done of finishing coat is extremely 50H;
(16) wool ball polishes:It is processed by shot blasting using wool ball.
2. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (2), the seal coat time to be done is preferably 0.5H, if the open paint time to be done is preferably 2H.
3. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (3), the proportioning of wash coats is preferably that host agent 0.8kg is mixed with curing agent 0.5, and sprinkling is 50m apart from veneer surface, often It is preferably 4H with the wood skin time to be done.
4. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (5), when temperature is 10 ° to 15 °, host agent 100g, plain boiled water 2.6g, Lan Shui 2.0g, diluent 35 to 40, humidity is 50% Between to 70% plus 5% plain boiled water can normal construction, if humidity is more than that 70% must stop constructing, first pass primer spray two ten Word, after 24H to be done;When temperature is 15 ° to 20 °, plain boiled water is changed to 2.3g, Lan Shui and is changed to 1.8g, remaining proportioning is constant; When temperature is 20 ° to 25 °, plain boiled water is changed to 2.0g, Lan Shui and is changed to 1.6g, remaining proportioning is constant;It it is 25 ° to 30 ° in temperature When, plain boiled water is changed to 1.6g, Lan Shui and is changed to 1.2g, remaining proportioning is constant;When temperature is 30 ° to 35 °, plain boiled water is changed to 1.2g, Lan Shui are changed to 1.0g, remaining proportioning is constant;When temperature is 35 ° or more, plain boiled water is changed to 1.0g, Lan Shui and is changed to 0.8g, remaining proportioning are constant.
5. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (7), when temperature is 10 ° to 15 °, host agent 100g, plain boiled water 2.6g, Lan Shui 2.0g, diluent 30 to 35, humidity is 50% Between to 70% plus 5% plain boiled water can normal construction, if humidity is more than that 70% must stop constructing, first pass primer spray two ten Word, after 24H to be done;When temperature is 15 ° to 20 °, plain boiled water is changed to 2.3g, Lan Shui and is changed to 1.8g, remaining proportioning is constant; When temperature is 20 ° to 25 °, plain boiled water is changed to 2.0g, Lan Shui and is changed to 1.6g, remaining proportioning is constant;It it is 25 ° to 30 ° in temperature When, plain boiled water is changed to 1.6g, Lan Shui and is changed to 1.2g, remaining proportioning is constant;When temperature is 30 ° to 35 °, plain boiled water is changed to 1.2g, Lan Shui are changed to 1.0g, remaining proportioning is constant;When temperature is 35 ° or more, plain boiled water is changed to 1.0g, Lan Shui and is changed to 0.8g, remaining proportioning are constant.
6. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (8), second time priming paint time to be done is preferably 72H.
7. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (11), paint proportioning preferably color essence 150g, host agent 20kg, curing agent 10kg, Tianna solution 60kg, time to be done are preferably 4H。
8. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (13), in 36 ° to 40 ° of temperature, host agent 100g, diluent 40 to 45, Lan Shui 0.8m, plain boiled water 1.2m, when temperature >= Indigo plant water consumption suitably increases 0.1-0.2% when 85%, and the time to be done is preferably 24H;In 26 ° to 35 ° of temperature, Lan Shui is changed to 1.2m, plain boiled water are changed to 1.5m, remaining proportioning is constant;In 21 ° to 25 ° of temperature, Lan Shui is changed to 1.5m, and plain boiled water is changed to 1.8m, remaining proportioning are constant;In 15 ° to 20 ° of temperature, Lan Shui is changed to 1.5m, and plain boiled water is changed to 2.0m, remaining proportioning is not Become;In 10 ° to 15 ° of temperature, Lan Shui is changed to 1.8m, and plain boiled water is changed to 2.2m, remaining proportioning is constant.
9. a kind of clear spraying process for embodying the original lines of wood skin according to claim 1, it is characterised in that:The step Suddenly in (15), second time finishing coat proportioning is identical as the proportioning of first pass finishing coat in claim 8, and the time to be done is preferably 48H.
CN201810570866.4A 2018-06-05 2018-06-05 A kind of clear spraying process for embodying the original lines of wood skin Pending CN108672245A (en)