CN108660859A - Medical package dialyzing paper and its manufacturing method - Google Patents
Medical package dialyzing paper and its manufacturing method Download PDFInfo
- Publication number
- CN108660859A CN108660859A CN201810365160.4A CN201810365160A CN108660859A CN 108660859 A CN108660859 A CN 108660859A CN 201810365160 A CN201810365160 A CN 201810365160A CN 108660859 A CN108660859 A CN 108660859A
- Authority
- CN
- China
- Prior art keywords
- paper
- dialyzing
- medical package
- mass percent
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of medical package dialyzing paper and its manufacturing methods, belong to paper manufacturing technology, the prior art is coated processing on body paper surface and obtains dialyzing paper there are production costs high, low production efficiency, compared with prior art, the present invention only need to carry out top sizing on the basis of obtaining body paper and can be obtained dialysis paper product, production cost has been saved, production efficiency is improved.The high dialyzing paper of intensity can be obtained using plant fiber, adhesive and chemical addition agent, ideal resistance bacterium effect can be obtained additionally by the sizing material type and resin added of adjustment top sizing.
Description
Technical field
The invention belongs to paper manufacturing technologies, and in particular to a kind of medical package dialyzing paper and its manufacturing method.
Background technology
Dialyzing paper is chiefly used in the packaging of medical instrument, is made through coating, then with plastic film after usually obtaining dialysis body paper
Paper plastic bag.Dialyzing paper has certain intensity requirement as medical package paper, and has preferable resistance bacterium effect.Hindering bacterium effect is
One important indicator of dialyzing paper usually obtains preferable resistance bacterium effect, can be coated processing on body paper surface, this measure will
The production cost of dialyzing paper is improved, while reducing production efficiency.
Invention content
The technical problem to be solved in the present invention and the technical assignment of proposition are that the prior art is overcome to be applied on body paper surface
Cloth processing obtains dialyzing paper there are production costs high, low production efficiency defect, provide a kind of medical package dialyzing paper and its
Manufacturing method.
In order to achieve the above objectives, medical package dialyzing paper of the invention, it is characterized in that：At paper and it is attached to original by body paper
Paper is constituted at the glue application layer on paper surface, and the body paper is the plant fiber of 97-99%, 0.5-2% containing mass percent at paper bag
The chemical addition agent of adhesive, 0.5%-1%, the plant fiber, adhesive, chemical addition agent the sum of mass percent be
100%。
The optimization technique means of medical package dialyzing paper as the present invention：The ingredient of the glue application layer be starch,
At least one of polyvinyl alcohol, resin, neutral gum.
The optimization technique means of medical package dialyzing paper as the present invention：In the finished product dialyzing paper of unit area, apply
The quality of glue-line is 2-5% of the body paper at the quality of paper.
In order to achieve the above objectives, the manufacturing method of medical package dialyzing paper of the invention, it is characterized in that including following step
Suddenly：
1）Body paper is manufactured paper with pulp：Using plant fiber, adhesive, chemical addition agent, plant fiber, adhesive, chemical addition agent are in original
Paper is 100% at the sum of mass percent that the mass percent in paper is respectively 97-99%, 0.5-2%, 0.5%-1% and three；
2）Top sizing：Using at least one of starch, polyvinyl alcohol, resin, neutral gum be made rubber cement spread body paper at
On paper.
Optimization technique means as the manufacturing method of the present invention：In the finished product dialyzing paper of unit area, the matter of glue application layer
Amount is 2-5% of the body paper at the quality of paper.
Compared with prior art, the present invention only need to carry out top sizing on the basis of obtaining body paper and can be obtained dialyzing paper
Finished product has saved production cost, improves production efficiency.It can be obtained using plant fiber, adhesive and chemical addition agent
The high dialyzing paper of intensity can obtain ideal resistance bacterium effect additionally by the sizing material type and resin added of adjustment top sizing
Fruit.
Specific implementation mode
The present invention is illustrated by the following examples.
The manufacturing method of the medical package dialyzing paper of the present invention includes the following steps：
1）Body paper is manufactured paper with pulp：Using plant fiber, adhesive, chemical addition agent, plant fiber, adhesive, chemical addition agent are in original
Paper is 100% at the sum of mass percent that the mass percent in paper is respectively 97-99%, 0.5-2%, 0.5%-1% and three；
2）Top sizing：Using at least one of starch, polyvinyl alcohol, resin, neutral gum be made rubber cement spread body paper at
On paper；In the finished product dialyzing paper of unit area, the quality of glue application layer is 2-5% of the body paper at the quality of paper.
Thus the medical package dialyzing paper of gained, at paper and glue application layer structure of the body paper at paper surface is attached to by body paper
At body paper is at paper bag containing the chemistry addition that mass percent is the plant fiber of 97-99%, the adhesive of 0.5-2%, 0.5%-1%
Agent, plant fiber, adhesive, chemical addition agent the sum of mass percent be 100%.The ingredient of glue application layer is starch, polyethylene
At least one of alcohol, resin, neutral gum.In the finished product dialyzing paper of unit area, the quality of glue application layer is matter of the body paper at paper
The 2-5% of amount.
Embodiment one
The plant fiber mass percent used when body paper is manufactured paper with pulp is 98%, wherein hardwood pulp 50%, softwood pulp 48%；It uses
For wet strength agent as adhesive, the mass percent of wet strength agent is 1%；Using AKD as chemical addition agent, the mass percent of AKD
It is 1%.
Top sizing uses the mixed mortar of 25% starch and 75% polyvinyl alcohol, according to the sizing of every square metre of 2 g
Amount spreads rubber cement in body paper on paper.After measured, in the finished product dialyzing paper of unit area, the quality of glue application layer is body paper into paper
Quality 4%.According to resistance bacterium property testing result, the bacterial population through the finished product pattern is 0.
Embodiment two
The plant fiber mass percent used when body paper is manufactured paper with pulp is 98%, wherein hardwood pulp 53%, softwood pulp 45%；It uses
For wet strength agent as adhesive, the mass percent of wet strength agent is 1%；Using AKD as chemical addition agent, the mass percent of AKD
It is 1%.
Top sizing uses the mixed mortar of 30% starch and 70% polyvinyl alcohol, according to the sizing of every square metre of 3 g
Amount spreads rubber cement in body paper on paper.After measured, in the finished product dialyzing paper of unit area, the quality of glue application layer is body paper into paper
Quality 5%.According to resistance bacterium property testing result, the bacterial population through the finished product pattern is 0.
Embodiment three
The plant fiber mass percent used when body paper is manufactured paper with pulp is 98%, wherein hardwood pulp 49%, softwood pulp 49%；It uses
For wet strength agent as adhesive, the mass percent of wet strength agent is 1.5%；Using AKD as chemical addition agent, the quality percentage of AKD
Than being 0.5%.
Top sizing uses the mixed mortar of 25% starch and 75% polyvinyl alcohol, according to applying for every square metre of 3.5 g
Glue amount spreads rubber cement in body paper on paper.After measured, in the finished product dialyzing paper of unit area, the quality of glue application layer be body paper at
The 4.3% of the quality of paper.According to resistance bacterium property testing result, the bacterial population through the finished product pattern is 0.
Example IV
The plant fiber mass percent used when body paper is manufactured paper with pulp is 97%, wherein hardwood pulp 49%, softwood pulp 48%；It uses
For wet strength agent as adhesive, the mass percent of wet strength agent is 2%；Using AKD as chemical addition agent, the mass percent of AKD
It is 1%.
Top sizing uses the mixed mortar of 25% starch and 75% polyvinyl alcohol, according to the sizing of every square metre of 2 g
Amount spreads rubber cement in body paper on paper.After measured, in the finished product dialyzing paper of unit area, the quality of glue application layer is body paper into paper
Quality 2%.According to resistance bacterium property testing result, the bacterial population through the finished product pattern is 0.
Embodiment five
The plant fiber mass percent used when body paper is manufactured paper with pulp is 99%, wherein hardwood pulp 50%, softwood pulp 49%；It uses
For wet strength agent as adhesive, the mass percent of wet strength agent is 0.5%；Using AKD as chemical addition agent, the quality percentage of AKD
Than being 0.5%.
Top sizing uses the mixed mortar of 25% starch and 75% polyvinyl alcohol, according to the sizing of every square metre of 2 g
Amount spreads rubber cement in body paper on paper.After measured, in the finished product dialyzing paper of unit area, the quality of glue application layer is body paper into paper
Quality 4%.According to resistance bacterium property testing result, the bacterial population through the finished product pattern is 0.
Claims (5)
1. medical package dialyzing paper, it is characterized in that：It at paper and is attached to body paper by body paper and is constituted at the glue application layer on paper surface, institute
Body paper is stated into paper bag containing the chemistry addition that mass percent is the plant fiber of 97-99%, the adhesive of 0.5-2%, 0.5%-1%
Agent, the plant fiber, adhesive, chemical addition agent the sum of mass percent be 100%.
2. medical package dialyzing paper according to claim 1, it is characterized in that：The ingredient of the glue application layer be starch,
At least one of polyvinyl alcohol, resin, neutral gum.
3. medical package dialyzing paper according to claim 1, it is characterized in that：In the finished product dialyzing paper of unit area, apply
The quality of glue-line is 2-5% of the body paper at the quality of paper.
4. the manufacturing method of medical package dialyzing paper, it is characterized in that including the following steps：
1）Body paper is manufactured paper with pulp：Using plant fiber, adhesive, chemical addition agent, plant fiber, adhesive, chemical addition agent are in original
Paper is 100% at the sum of mass percent that the mass percent in paper is respectively 97-99%, 0.5-2%, 0.5%-1% and three；
2）Top sizing：Using at least one of starch, polyvinyl alcohol, resin, neutral gum be made rubber cement spread body paper at
On paper.
5. the manufacturing method of medical package dialyzing paper according to claim 4, it is characterized in that：The finished product of unit area is saturating
It analyses in paper, the quality of glue application layer is 2-5% of the body paper at the quality of paper.