CN108659599A - A kind of antibacterial water-repellent paint - Google Patents
A kind of antibacterial water-repellent paint Download PDFInfo
- Publication number
- CN108659599A CN108659599A CN201810561309.6A CN201810561309A CN108659599A CN 108659599 A CN108659599 A CN 108659599A CN 201810561309 A CN201810561309 A CN 201810561309A CN 108659599 A CN108659599 A CN 108659599A
- Authority
- CN
- China
- Prior art keywords
- water
- asphalitine
- repellent paint
- essential oil
- hydrophobic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterial water-repellent paints, including following weight percentage components：Aqueous acrylic modified epoxy resin 20 30%, Petropols 10 15%, benzotriazole 5 10%, polysiloxane 5 10%, asphalitine 3 5%, osmanthus essential oil 3 5%, super hydrophobic material 1 3%, coalescents 0.5 1%, plasticizer 0.5 1%, emulsifier 0.5 1%, dispersant 0.5 1%, antifoaming agent 0.5 1%, levelling agent 0.5 1%, fire retardant 0.5 1%, remaining is water.The present invention is under asphalitine and the scientific compatibility of osmanthus essential oil and unclassified stores, under the action of asphalitine, has outstanding water resistance based on it, it can effectively ensure that the coating produced has excellent waterproof effect, under the action of osmanthus essential oil, have outstanding fungi-proofing performance based on it, can effectively ensure that the coating produced has excellent fungi-proofing effect.
Description
Technical field
The present invention relates to coating preparation, specifically a kind of antibacterial water-repellent paint.
Background technology
Coating is to be coated in the body surface protected or decorated, and can form the continuous of firm attachment with coated article
Film addition or does not add pigment, filler typically based on resin or oil or lotion, adds corresponding additive, with organic molten
The thick liquid that agent or water are formulated.Chinese coating circle is more authoritative《Coating process》The definition of one book is：" coating is one
Kind of material, this material can use different construction technologies to be coated in object surface, formed adherency securely, with some strength,
Continuous solid film.The film common name film formed in this way, also known as paint film or coating." coating early stage is mostly based on vegetable oil
Raw material is wanted, therefore is called " paint ".Whether traditional using natural materials as in the coating products of raw material or modern development
To synthesize coating products of the chemical products as raw material, organic chemical industry's macromolecular material is belonged to, film is formed by and belongs to high score
Sub- type of compounds.According to the classification of modern times current chemical products, coating belongs to fine chemical product.
Existing coating produce prepare when, main emphasis be its anticracking, antirust function, but existing painting
Material requires also improving for environment-friendly type, and current coating needs to pay close attention to its antibacterial ability when preparing, and reinforces coating
Effect.
Invention content
The purpose of the present invention is to provide a kind of antibacterial water-repellent paints, to solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides the following technical solutions：
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 20-
30%, Petropols 10-15%, benzotriazole 5-10%, polysiloxane 5-10%, asphalitine 3-5%, osmanthus essential oil
3-5%, super hydrophobic material 1-3%, coalescents 0.5-1%, plasticizer 0.5-1%, emulsifier 0.5-1%, dispersant 0.5-
1%, antifoaming agent 0.5-1%, levelling agent 0.5-1%, fire retardant 0.5-1%, remaining is water.
As a further solution of the present invention：Including following weight percentage components：Aqueous acrylic modified asphalt mixtures modified by epoxy resin
Fat 22-28%, Petropols 11-14%, benzotriazole 6-9%, polysiloxane 6-9%, asphalitine 3.2-4.8%,
Osmanthus essential oil 3.2-4.8%, super hydrophobic material 1.2-1.8%, coalescents 0.6-0.9%, plasticizer 0.6-0.9%, emulsification
Agent 0.6-0.9%, dispersant 0.6-0.9%, antifoaming agent 0.6-0.9%, levelling agent 0.6-0.9%, fire retardant 0.6-0.9%,
Remaining is water.
As a further solution of the present invention：Including following weight percentage components：Aqueous acrylic modified asphalt mixtures modified by epoxy resin
Fat 24-26%, Petropols 11-13%, benzotriazole 6-8%, polysiloxane 6-8%, asphalitine 3.5-4.5%,
Osmanthus essential oil 3.5-4.5%, super hydrophobic material 1.5-2.5%, coalescents 0.6-0.8%, plasticizer 0.6-0.8%, emulsification
Agent 0.6-0.8%, dispersant 0.6-0.8%, antifoaming agent 0.6-0.8%, levelling agent 0.6-0.8%, fire retardant 0.6-0.8%,
Remaining is water.
As a further solution of the present invention：Including following weight percentage components：Aqueous acrylic modified asphalt mixtures modified by epoxy resin
It is fat 25%, Petropols 12%, benzotriazole 7%, poly organo 7%, asphalitine 4%, osmanthus essential oil 4%, super-hydrophobic
Material 2%, coalescents 0.7%, plasticizer 0.7%, emulsifier 0.7%, dispersant 0.7%, antifoaming agent 0.7%, levelling agent
0.7%, fire retardant 0.7%, remaining is water.
It is a further object of the present invention to provide a kind of preparation methods of antibacterial water-repellent paint, which is characterized in that steps are as follows：
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Then material filters；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, and precursor powder is obtained after dry；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and the anticorrosive paint of suspension is obtained after stirring.
As a further solution of the present invention：In step 1, high-speed discrete 20-30min, low speed stirs in becoming after high-speed discrete
Mix 10min.
As a further solution of the present invention：In step 2, stirred 6~18 hours after super hydrophobic material is added.
As a further solution of the present invention：Precursor powder, which is obtained, in step 3, after dry crosses 100-200 mesh screens.
As a further solution of the present invention：In step 4, antifoaming agent uses nonylphenol polyoxyethylene ether.
It is yet another object of the invention to provide application of the antibacterial water-repellent paint in coating preparation.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention is in asphalitine and osmanthus essential oil and unclassified stores (aqueous acrylic modified epoxy resin, Petropols, benzene
And triazole, poly organo, super hydrophobic material, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent, resistance
Fire agent and water) scientific compatibility under, under the action of asphalitine, have outstanding water resistance based on it, can effectively ensure that
There is the coating produced excellent waterproof effect to be had outstanding fungi-proofing performance based on it under the action of osmanthus essential oil,
It can effectively ensure that the coating produced has excellent fungi-proofing effect.
Specific implementation mode
The technical solution of this patent is described in more detail With reference to embodiment.
Embodiment 1
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 20%,
Petropols 10%, benzotriazole 5%, polysiloxane 5%, asphalitine 3%, osmanthus essential oil 3%, super hydrophobic material
1%, coalescents 0.5%, plasticizer 0.5%, emulsifier 0.5%, dispersant 0.5%, antifoaming agent 0.5%, levelling agent
0.5%, fire retardant 0.5%, remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 20min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 6~18 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Precursor powder is obtained after dry sieves with 100 mesh sieve net；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
Embodiment 2
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 30%,
Petropols 15%, benzotriazole 10%, polysiloxane 10%, asphalitine 5%, osmanthus essential oil 5%, super hydrophobic material
3%, coalescents 1%, plasticizer 1%, emulsifier 1%, dispersant 1%, antifoaming agent 1%, levelling agent 1%, fire retardant 1%,
Remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 30min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 6~18 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Precursor powder is obtained after dry crosses 200 mesh screens；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
Embodiment 3
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 22%,
Petropols 11%, benzotriazole 6%, polysiloxane 6%, asphalitine 3.2%, osmanthus essential oil 3.2%, super-hydrophobic material
Material 1.2%, coalescents 0.6%, plasticizer 0.6%, emulsifier 0.6%, dispersant 0.6%, antifoaming agent 0.6%, levelling agent
0.6%, fire retardant 0.6%, remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 20min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 6~18 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Precursor powder is obtained after dry sieves with 100 mesh sieve net；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
Embodiment 4
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 28%,
Petropols 14%, benzotriazole 9%, polysiloxane 9%, asphalitine 4.8%, osmanthus essential oil 4.8%, super-hydrophobic material
Material 1.8%, coalescents 0.9%, plasticizer 0.9%, emulsifier 0.9%, dispersant 0.9%, antifoaming agent 0.9%, levelling agent
0.9%, fire retardant 0.9%, remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 30min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 6~18 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Precursor powder is obtained after dry crosses 200 mesh screens；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
Embodiment 5
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 24%,
Petropols 11%, benzotriazole 6%, polysiloxane 6%, asphalitine 3.5%, osmanthus essential oil 3.5%, super-hydrophobic material
Material 1.5%, coalescents 0.6%, plasticizer 0.6%, emulsifier 0.6%, dispersant 0.6%, antifoaming agent 0.6%, levelling agent
0.6%, fire retardant 0.6%, remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 20min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 6~18 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Precursor powder is obtained after dry sieves with 100 mesh sieve net；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
Embodiment 6
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous interior olefin(e) acid modified epoxy 26%,
Petropols 13%, benzotriazole 8%, polysiloxane 8%, asphalitine 4.5%, osmanthus essential oil 4.5%, super-hydrophobic material
Material 2.5%, coalescents 0.8%, plasticizer 0.8%, emulsifier 0.8%, dispersant 0.8%, antifoaming agent 0.8%, levelling agent
0.8%, fire retardant 0.8%, remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 30min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 6~18 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Presoma powder is obtained after dry crosses 200 mesh screens；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
Embodiment 7
A kind of antibacterial water-repellent paint, including following weight percentage components：Aqueous acrylic modified epoxy resin 25%,
Petropols 12%, benzotriazole 7%, poly organo 7%, asphalitine 4%, osmanthus essential oil 4%, super hydrophobic material 2%,
Coalescents 0.7%, plasticizer 0.7%, emulsifier 0.7%, dispersant 0.7%, antifoaming agent 0.7%, levelling agent 0.7%, resistance
Agent 0.7% is fired, remaining is water.
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution,
High-speed discrete 25min, stirring at low speed 10min in becoming after high-speed discrete；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, continuously add super-hydrophobic
Material is stirred 12 hours after super hydrophobic material is added, is then filtered；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, be obtained precursor powder after dry, be done
Precursor powder is obtained after dry crosses 150 mesh screens；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent,
Fire retardant and water are mixed to get slurry, and antifoaming agent uses nonylphenol polyoxyethylene ether, the anticorrosive paint of suspension is obtained after stirring.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, one skilled in the relevant art within the scope of knowledge, can also be under the premise of not departing from this patent objective
It makes a variety of changes.
Claims (10)
1. a kind of antibacterial water-repellent paint, which is characterized in that including following weight percentage components：Aqueous acrylic modified epoxy
Resin 20-30%, Petropols 10-15%, benzotriazole 5-10%, polysiloxane 5-10%, asphalitine 3-5%,
Osmanthus essential oil 3-5%, super hydrophobic material 1-3%, coalescents 0.5-1%, plasticizer 0.5-1%, emulsifier 0.5-1%, divide
Powder 0.5-1%, antifoaming agent 0.5-1%, levelling agent 0.5-1%, fire retardant 0.5-1%, remaining is water.
2. antibacterial water-repellent paint according to claim 1, which is characterized in that including following weight percentage components：Water
Property acrylic modified epoxy resin 22-28%, Petropols 11-14%, benzotriazole 6-9%, polysiloxane 6-
9%, asphalitine 3.2-4.8%, osmanthus essential oil 3.2-4.8%, super hydrophobic material 1.2-1.8%, coalescents 0.6-0.9%,
Plasticizer 0.6-0.9%, emulsifier 0.6-0.9%, dispersant 0.6-0.9%, antifoaming agent 0.6-0.9%, levelling agent 0.6-
0.9%, fire retardant 0.6-0.9%, remaining is water.
3. antibacterial water-repellent paint according to claim 1, which is characterized in that including following weight percentage components：Water
Property acrylic modified epoxy resin 24-26%, Petropols 11-13%, benzotriazole 6-8%, polysiloxane 6-
8%, asphalitine 3.5-4.5%, osmanthus essential oil 3.5-4.5%, super hydrophobic material 1.5-2.5%, coalescents 0.6-0.8%,
Plasticizer 0.6-0.8%, emulsifier 0.6-0.8%, dispersant 0.6-0.8%, antifoaming agent 0.6-0.8%, levelling agent 0.6-
0.8%, fire retardant 0.6-0.8%, remaining is water.
4. antibacterial water-repellent paint according to claim 1, which is characterized in that including following weight percentage components：Water
Property acrylic modified epoxy resin 25%, Petropols 12%, benzotriazole 7%, poly organo 7%, asphalitine 4%,
Osmanthus essential oil 4%, super hydrophobic material 2%, coalescents 0.7%, plasticizer 0.7%, emulsifier 0.7%, dispersant 0.7%,
Antifoaming agent 0.7%, levelling agent 0.7%, fire retardant 0.7%, remaining is water.
5. a kind of preparation method of antibacterial water-repellent paint as described in claim 1-4 is any, which is characterized in that steps are as follows：
Step 1: aqueous acrylic modified epoxy resin, benzotriazole and Petropols are discrete to having in aqueous solution；
Step 2: poly organo, asphalitine and osmanthus essential oil is then added, after stirring, ultrasound, super-hydrophobic material is continuously added
Material, then filters；
Step 3: will filter, product will be washed, alcohol is washed for several times to cleaning solution to be neutral, and precursor powder is obtained after dry；
Step 4: by the precursor powder, coalescents, plasticizer, emulsifier, dispersant, antifoaming agent, levelling agent, fire-retardant
Agent and water are mixed to get slurry, and the anticorrosive paint of suspension is obtained after stirring.
6. antibacterial water-repellent paint according to claim 5, which is characterized in that in step 1, high-speed discrete 20-30min is high
Stirring at low speed 10min in becoming after speed is discrete.
7. antibacterial water-repellent paint according to claim 5, which is characterized in that in step 2, stirred after super hydrophobic material is added
It mixes 6~18 hours.
8. antibacterial water-repellent paint according to claim 5, which is characterized in that in step 3, precursor is obtained after dry
100-200 mesh screens are crossed at end.
9. antibacterial water-repellent paint according to claim 5, which is characterized in that in step 4, antifoaming agent is poly- using nonyl phenol
Ethylene oxide ether.
10. a kind of application of antibacterial water-repellent paint as described in claim 1-4 is any in coating preparation.