CN108649311A - A kind of production method of cavity coupler - Google Patents
A kind of production method of cavity coupler Download PDFInfo
- Publication number
- CN108649311A CN108649311A CN201810886508.4A CN201810886508A CN108649311A CN 108649311 A CN108649311 A CN 108649311A CN 201810886508 A CN201810886508 A CN 201810886508A CN 108649311 A CN108649311 A CN 108649311A
- Authority
- CN
- China
- Prior art keywords
- cavity
- initial
- intermediate bulkhead
- processing
- coupler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present embodiments relate to a kind of production methods of cavity coupler.This method includes:It is split treating process chambers coupler, after obtaining initial upper cavity, initial lower chamber and initial intermediate bulkhead, the flatness of initial upper cavity, initial lower chamber and initial intermediate bulkhead is handled respectively, obtain upper cavity, lower chamber and intermediate bulkhead, after carrying out clamping processing to upper cavity, lower chamber and intermediate bulkhead, clamping cavity coupler is obtained, to obtaining after clamping cavity coupler measures processing, obtaining cavity coupler.The technical solution provided through this embodiment, on the one hand, avoid in the prior art, welding times are on the high side, reduce the technology drawback of production efficiency, realize the technique effect for improving production efficiency;On the other hand, influence of the operating personnel to production itself is avoided, the stability of production and the technique effect of reliability are improved;In another aspect, realizing raising production precision, the technique effect of yield rate is improved.
Description
Technical field
The present embodiments relate to coupler technique manufacture technology field more particularly to a kind of making sides of cavity coupler
Method.
Background technology
The function of cavity coupler is to carry out power distribution in the ratio of design and direction and export, and general structure is complicated,
Interior step, partition are numerous, and when manufacture need to divide multistage processing again by multiple Welding at one integral piece.Manufacture difficulty is big, production
Period is long, yield rate and low production efficiency.How to improve yield rate and production efficiency is technical barrier urgently to be resolved hurrily.
In the prior art, cavity coupler designs the two-way waveguiding structure that is made of multiple discrete parts, in waveguide
Portion's step chamber is numerous, is welded together by aluminium soldering between each part, to waveguide air-tightness and three waveguides during use
The bulk of mouth requires stringent.
Technological difficulties present in production mainly have:
1. multiple parts need first to carry out vacuum Aluminum brazing in cavity coupler, re-segmenting carries out multiple Manual flame weldering
It connects, 30 many places of weld seam, postwelding accumulated deformation is big.When segmentation carries out Manual flame soldering, vacuum brazing solder early period two is easily caused
Secondary fusing leads to gas leakage, can only carry out leak stopping by multiple repair welding after welding, product quality is poor.And it is based on existing structure, hand
Weld seam can not be directly heated and be observed at the multiple steps being affected to electrical specifications when work flame welding, solder dissolve and pricker
Material heap product situation is difficult to observe.Simultaneously because two waveguide bend weld seams are up to 225mm, postwelding end stress concentration is serious, later stage dress
Timing easily causes waveguide bend end to be snapped.
2. the bulk between liang waveguide mouth only leans on end cavity in connection to ensure have between two waveguide bends super
The hanging of 200mm is crossed, post welding distortion is big, two waveguide mouth central space distances 25.05 0.1 of drawing requirement, 75 ° of space angle
± 10 ' extremely difficult guarantees, can only be by postwelding school shape, but school shape process easily leads to weld cracking.
3. step piece cavity is the vital part for influencing transmitting-receiving feed insertion loss, step piece thickness only 1mm therein, warp
After crossing processing and welding, the deformation of step piece is serious, it is difficult to ensure that symmetry ± 0.05mm.
4. the deeply narrow chamber of cavity part and step cavity configuration feature in cavity coupler are at present external coordination electrical discharge machining, add
Work efficiency rate is low, of high cost, and part process cycle is long, restricts model batch production progress.
Invention content
To solve at least one of above-mentioned background technology technical problem, an embodiment of the present invention provides a kind of couplings of cavity
The production method of device, the method includes:
It treats process chambers coupler and carries out deconsolidation process, obtain initial upper cavity, initial lower chamber and initial middle interval
Plate;
Respectively to the flatness of the initial upper cavity, the initial lower chamber and the initial intermediate bulkhead at
Reason, obtains upper cavity, lower chamber and intermediate bulkhead;
Clamping processing is carried out to the upper cavity, the lower chamber and the intermediate bulkhead, obtains clamping cavity coupler;
Processing is measured to the clamping cavity coupler, obtains cavity coupler.
It provides through this embodiment:Split treating process chambers coupler, obtain initial upper cavity, it is initial under
After cavity and initial intermediate bulkhead, respectively to the flatness of initial upper cavity, initial lower chamber and initial intermediate bulkhead at
Reason, obtains upper cavity, lower chamber and intermediate bulkhead, after carrying out clamping processing to upper cavity, lower chamber and intermediate bulkhead, obtains
Clamping cavity coupler obtains the technical solution of cavity coupler to obtaining after clamping cavity coupler measures processing, and one
Aspect avoids in the prior art, and welding times are on the high side, reduces the technology drawback of production efficiency, realizes raising production effect
The technique effect of rate;On the other hand, influence of the operating personnel to production itself is avoided, the stability of production and reliable is improved
The technique effect of property;In another aspect, realizing raising production precision, the technique effect of yield rate is improved.
Preferably, the flatness of the initial upper cavity and the initial lower chamber is handled, is specifically included:
Respectively to the initial upper cavity and the initial lower chamber carry out successively the processing of milling side, the processing of milling inner cavity,
Heat treatment, the again processing of milling inner cavity, deburring processing and back chipping processing.
It provides through this embodiment:Milling side's processing, primary is carried out successively to initial upper cavity and initial lower chamber respectively
The technical solution of the processing of milling inner cavity, heat treatment, the again processing of milling inner cavity, deburring processing and back chipping processing, realizes and moves back completely
The technique effect that residual stress influences is eliminated in fiery destressing, ensure that carry out flatness treated initial upper cavity and
The technique effect of the Pingdu degree accuracy of initial lower chamber.
Preferably, the flatness of the initial intermediate bulkhead is handled, is specifically included:
Assembly processing, hot smoothing process, milling processing and deburring is carried out to the initial intermediate bulkhead successively to handle.
It provides through this embodiment:Assembly processing, hot smoothing process, milling processing are carried out to initial intermediate bulkhead and gone
The technical solution of burr processing realizes the technology effect of the flatness of the high accuracy for the initial intermediate bulkhead that ensures that treated
Fruit.
Preferably, assembly processing is carried out to the initial intermediate bulkhead, specifically included:
The coating lubricating oil on working plate;
The initial intermediate bulkhead is pushed into the working plate so that the initial intermediate bulkhead is fastened on the working plate
Fixed baffle and the active block stop of the working plate between.
It provides through this embodiment:Working plate intermediate bulkhead being pushed into after coating lubricating oil so that intermediate bulkhead card
Technical solution between fixed baffle and active block stop is closed, realizes and easy, at low cost clamping is carried out to intermediate bulkhead
Technique effect, and avoid the technology drawback that deformation is easy tod produce in clamping process in the prior art, in realizing and ensuring
The technique effect of the flatness of spacing board.
Preferably, in the milling processing procedure, use the tool cutting edge angle of blade for 45 ° of wire rod quality.
It provides through this embodiment:The tool cutting edge angle of blade is used to be realized in milling for the technical solution of 45 ° of wire rod quality
It cuts in processing procedure, a component is provided always, intermediate bulkhead is pressed on working plate, reduced in milling processing procedure
Vibration ensure that milling treated the flatness and roughness of intermediate bulkhead.
Preferably, described that clamping processing is carried out to the upper cavity, the lower chamber and the intermediate bulkhead, it is specific to wrap
It includes:
Set the first SiC plates to lower plate;
Set the 2nd SiC plates to upper layer locating back;
The lower chamber, the intermediate bulkhead and described are set gradually between the lower plate and the upper layer locating back
Upper cavity, and placed between the lower chamber and the intermediate bulkhead and between the intermediate bulkhead and the upper cavity
Solder;
Wherein, the lower plate is bonded with the lower chamber, and the upper layer locating back is bonded with the upper cavity.
It provides through this embodiment:Set gradually between lower plate and upper layer locating back lower chamber, intermediate bulkhead, on
Cavity, and between lower chamber and intermediate bulkhead, the technical solution of solder is placed between intermediate bulkhead and upper cavity respectively, both really
Pressing force has been protected, has also ensured higher flatness and the coefficient of heat conduction, has also ensured the technology of lower linear expansion coefficient
Effect.
Preferably, the method further includes:
The fitting setting cast iron pressing plate on the upper layer locating back.
It provides through this embodiment:The technical solution of cast iron pressing plate is set on the locating back of upper layer, is further ensured
Pressing force.
Preferably, described that processing is measured to the clamping cavity coupler, cavity coupler is obtained, is specifically included:
Gap between the lower plate and the lower chamber measures, and obtains measurement result;
The measurement result is compared with preset measurement threshold value, if the measurement result, which is less than, measures threshold value,
The clamping cavity coupler is determined as the cavity coupler.
It provides through this embodiment:Measurement result is compared with threshold value is measured, measurement result is less than and measures threshold
The clamping cavity coupler of value is determined as the technical solution of cavity coupler, it is ensured that the accuracy of obtained cavity coupler,
Stability and reliability.
Wherein, the measurement threshold value is 0.05mm.
Preferably, the method further includes:
Vacuum brazing processing is carried out to the cavity coupler, obtains target cavity coupler.
It provides through this embodiment:Vacuum brazing processing is carried out to cavity coupler, obtains target cavity coupler
Technical solution realizes solder and melts flowing well, the excellent technique effect of weldquality.
Description of the drawings
Fig. 1 is a kind of flow diagram of the production method of cavity coupler provided in an embodiment of the present invention.
Specific implementation mode
In being described below, for illustration and not for limitation, it is proposed that such as specific system structure, interface, technology it
The detail of class, to understand thoroughly the present invention.However, it will be clear to one skilled in the art that there is no these specific
The present invention can also be realized in the other embodiments of details.In other situations, it omits to well-known and method detailed
Describe in detail it is bright, in order to avoid unnecessary details interfere description of the invention.
An embodiment of the present invention provides a kind of production methods of cavity coupler.
First embodiment:
Referring to Fig. 1, Fig. 1 is a kind of flow signal of production method of cavity coupler provided in an embodiment of the present invention
Figure.
As shown in Figure 1, this method includes:
S100:Treat process chambers coupler and carry out deconsolidation process, obtain initial upper cavity, initial lower chamber and it is initial in
Spacing board.
The threedimensional model of each discrete part can be built using ProE on the basis of two-dimentional drawing.That is, passing through ProE pairs
Pending cavity coupler is split, and discrete part (initial upper cavity, initial lower chamber and initial intermediate bulkhead) is obtained.
S200:The flatness of initial upper cavity, initial lower chamber and initial intermediate bulkhead is handled respectively, is obtained
Cavity, lower chamber and intermediate bulkhead.
The flatness of initial upper cavity, initial lower chamber and initial intermediate bulkhead is handled respectively, to ensure to handle
The accurately flatness of the upper cavity, lower chamber and the intermediate bulkhead that obtain afterwards.
S300:Clamping processing is carried out to upper cavity, lower chamber and intermediate bulkhead, obtains clamping cavity coupler;
S400:Processing is measured to clamping cavity coupler, obtains cavity coupler.
Wherein, the aluminum alloy blank that F states are replaced using the aluminum alloy blank of annealed condition (O), as pending cavity
The composition material of coupler.
It provides through this embodiment:Split treating process chambers coupler, obtain initial upper cavity, it is initial under
After cavity and initial intermediate bulkhead, respectively to the flatness of initial upper cavity, initial lower chamber and initial intermediate bulkhead at
Reason, obtains upper cavity, lower chamber and intermediate bulkhead, after carrying out clamping processing to upper cavity, lower chamber and intermediate bulkhead, obtains
Clamping cavity coupler obtains the technical solution of cavity coupler to obtaining after clamping cavity coupler measures processing, and one
Aspect avoids in the prior art, and welding times are on the high side, reduces the technology drawback of production efficiency, realizes raising production effect
The technique effect of rate;On the other hand, influence of the operating personnel to production itself is avoided, the stability of production and reliable is improved
The technique effect of property;In another aspect, realizing raising production precision, the technique effect of yield rate is improved.
Second embodiment:
The present embodiment is based on first embodiment.In the present embodiment, S200 is specifically included:
The processing of milling side is carried out successively to initial upper cavity and initial lower chamber respectively, a milling inner cavity processing, is heat-treated, again
Secondary milling inner cavity processing, deburring processing and back chipping processing.
To ensure the flatness of upper cavity and lower chamber, made allowance 1mm is handled a milling inner cavity, passes through heat together later
The process of processing eliminates the influence of residual stress as possible so as to full annealing destressing.It is carried out after heat treatment at milling inner cavity again
Reason, residual stress that treated to reduce milling inner cavity again to the greatest extent.
It provides through this embodiment:Milling side's processing, primary is carried out successively to initial upper cavity and initial lower chamber respectively
The technical solution of the processing of milling inner cavity, heat treatment, the again processing of milling inner cavity, deburring processing and back chipping processing, realizes and moves back completely
The technique effect that residual stress influences is eliminated in fiery destressing, ensure that carry out flatness treated initial upper cavity and
The technique effect of the Pingdu degree accuracy of initial lower chamber.
3rd embodiment:
The present embodiment is based on first or second embodiments.In the present embodiment, S200 is also specifically included:
Assembly processing, hot smoothing process, milling processing and deburring is carried out to initial intermediate bulkhead successively to handle.
Wherein, initial intermediate bulkhead is the thin plate of 400 200 (mm).
It provides through this embodiment:Assembly processing, hot smoothing process, milling processing are carried out to initial intermediate bulkhead and gone
The technical solution of burr processing realizes the technology effect of the flatness of the high accuracy for the initial intermediate bulkhead that ensures that treated
Fruit.
Fourth embodiment:
The present embodiment is based on 3rd embodiment.In the present embodiment, assembly processing is carried out to initial intermediate bulkhead, had
Body includes:
The coating lubricating oil on working plate;
Initial intermediate bulkhead is pushed into working plate so that initial intermediate bulkhead is fastened on the fixed baffle and tooling of working plate
Between the active block stop of plate.
In the prior art, assembly processing can be carried out to initial intermediate bulkhead by vacuum cup installation way.
Certainly, also initial intermediate bulkhead can be pressed in certain using screw by the surrounding milling counterbore in initial intermediate bulkhead
In fixed plate.Using this kind of mode, have it is simple, and it is opposite use vacuum cup installation way, have at low cost excellent
Gesture.
But due to the restriction of the quantity of the counterbore on initial intermediate bulkhead and position so that away from the region of counterbore farther out
Thin plate is not easy to be compacted.And housing screw limits the deformation that initial intermediate bulkhead is generated by cutting force, causes not by spiral shell
The region that nail compresses generates deformation of arching upward, or even will produce the technology drawback of tiny step.
In the present embodiment, using principle of negative pressure, multiple blind holes to oil storage are processed on working plate, working plate
Fixed baffle is arranged in one end, and the thickness of fixed baffle is 4.5mm, and active block stop is arranged in the other end of working plate.
When carrying out assembly processing to initial intermediate bulkhead, when screw is pushed, it can be ensured that active block stop is close to tooling
Plate presses to initial intermediate bulkhead, and initial intermediate bulkhead attaches working plate when ensureing to compress.
When assembling processing, first a facing cut of initial intermediate bulkhead is put down, after suitable lubricating oil is smeared on working plate,
It is required that oil mass there was not oil storage hole (i.e. blind hole), initial intermediate bulkhead is pushed into working plate from side, screws housing screw so that just
Beginning intermediate bulkhead is fastened between the fixed baffle of working plate and the active block stop of working plate.
It provides through this embodiment:Working plate intermediate bulkhead being pushed into after coating lubricating oil so that intermediate bulkhead card
Technical solution between fixed baffle and active block stop is closed, realizes and easy, at low cost clamping is carried out to intermediate bulkhead
Technique effect, and avoid the technology drawback that deformation is easy tod produce in clamping process in the prior art, in realizing and ensuring
The technique effect of the flatness of spacing board.
5th embodiment:
The present embodiment is based on third or four embodiments.In the present embodiment, in milling processing procedure, using blade
Tool cutting edge angle be 45 ° of wire rod quality.
To ensure that initial intermediate bulkhead is compacted on working plate always in milling processing procedure, is needed processed to milling
Cutting force direction in journey is planned, in order to obtain a point for pressing to working plate always in entire milling processing procedure
Power, it is 45 wire rod qualities to have selected the tool cutting edge angle of blade.In milling processing procedure, during a component general can be provided always initially
Spacing board is pressed on working plate, squeezes out the bubble between initial intermediate bulkhead and working plate, is formed negative pressure, is made initial intermediate bulkhead
It is fitted tightly on working plate, reduces the vibration in milling processing procedure, ensure that milling treated initial intermediate bulkhead
Flatness and surface roughness.
It provides through this embodiment:The tool cutting edge angle of blade is used to be realized in milling for the technical solution of 45 ° of wire rod quality
It cuts in processing procedure, a component is provided always, intermediate bulkhead is pressed on working plate, reduced in milling processing procedure
Vibration ensure that milling treated the flatness and roughness of intermediate bulkhead.
Sixth embodiment:
The present embodiment is based on any embodiment in the first to the 5th embodiment.In the present embodiment, S300 is specific
Including:
Set the first SiC plates to lower plate;
Set the 2nd SiC plates to upper layer locating back;
Set gradually lower chamber, intermediate bulkhead and upper cavity between lower plate and upper layer locating back, and in lower chamber and
Solder is placed between intermediate bulkhead and between intermediate bulkhead and upper cavity;
Wherein, lower plate is bonded with lower chamber, and upper layer locating back is bonded with upper cavity.
Ensureing enough pressing forces simultaneously, is needing to select suitable upper layer locating back, should ensure higher flatness
And the coefficient of heat conduction, also there is lower linear expansion coefficient, while stable chemical performance, cannot react with aluminium.Through
It screens, selects using SiC plates as lower plate and upper layer locating back, the SiC plate coefficients of heat conduction of use reach after layer by layer
120W/ (mK) is four times of alumina ceramic plate, while linear expansion coefficient is only 3 10-6/K, is shown in Table 1.
1 SiC plates of table and alumina plate performance comparison
Specifically installation way is:
Bottom places monoblock SiC bottom plates (lower plate), and lower chamber+solder+intermediate bulkhead+solder+upper cavity assembles postposition
In on bottom plate, then place the monoblock SiC plates (upper layer flat clamp) of same specification.
It provides through this embodiment:Set gradually between lower plate and upper layer locating back lower chamber, intermediate bulkhead, on
Cavity, and between lower chamber and intermediate bulkhead, the technical solution of solder is placed between intermediate bulkhead and upper cavity respectively, both really
Pressing force has been protected, has also ensured higher flatness and the coefficient of heat conduction, has also ensured the technology of lower linear expansion coefficient
Effect.
7th embodiment:
The present embodiment is based on any embodiment in sixth embodiment.In the present embodiment, this method further includes:
The fitting setting cast iron pressing plate on the locating back of upper layer.
Monoblock 20mm cast iron pressing plates are pressed on SiC plates (upper layer locating back).
It provides through this embodiment:The technical solution of cast iron pressing plate is set on the locating back of upper layer, is further ensured
Pressing force.
8th embodiment:
The present embodiment is based on the 6th or the 7th embodiment.In the present embodiment, clamping cavity coupler is surveyed
Amount processing, obtains cavity coupler, specifically includes:
Gap between lower plate and lower chamber measures, and obtains measurement result;
Measurement result is compared with preset measurement threshold value, if measurement result, which is less than, measures threshold value, by clamping chamber
Body coupler is determined as cavity coupler.
Wherein, it is 0.05mm to measure threshold value.
Specifically, using clearance gauge measurement gap size, the clearance gauge of 0.05mm can not be inserted into, meet the requirements, that is, be determined as chamber
Body coupler.
9th embodiment:
The present embodiment is based on any embodiment in the first to the 8th embodiment.In the present embodiment, this method is also
Including:
Vacuum brazing processing is carried out to cavity coupler, obtains target cavity coupler.
After carrying out vacuum brazing processing to cavity coupler, it is found that solder melts flowing well, weldquality is excellent.For
It more accurately monitors actual temperature in Process of Vacuum Brazing and rises situation, optimize three thermocouples in aluminium vacuum drying oven and be positioned over cavity
The position of coupler.Two thermocouples at rear portion are positioned over upper cavity top surface edge in vacuum drying oven, to monitor cavity
The temperature of the outside surrounding of coupler.A thermocouple in the middle part of vacuum drying oven passes through the venthole between upper cavity and intermediate bulkhead
It is inserted into the inside of cavity coupler, the temperature of the bosom of test chamber coupler.By optimizing the placement location of thermocouple,
It can be with the real time temperature of cavity coupler in accurate measurements Process of Vacuum Brazing.It is monitoring the result shows that:Upper cavity, lower chamber
The big surplus removal of large area solid area after temperature rise uneven problem and greatly improved.
Reader should be understood that in the description of this specification reference term " one embodiment ", " is shown " some embodiments "
The description of example ", " specific example " or " some examples " etc. means specific features described in conjunction with this embodiment or example, structure
Or feature is included at least one embodiment or example of the invention.In the present specification, to the schematic of above-mentioned term
Statement need not be directed to identical embodiment or example.Moreover, specific features, structure or the feature of description can be any
It can be combined in any suitable manner in a or multiple embodiments or example.In addition, without conflicting with each other, the technology of this field
The feature of different embodiments or examples described in this specification and different embodiments or examples can be combined by personnel
And combination.
It should also be understood that in various embodiments of the present invention, size of the sequence numbers of the above procedures is not meant to execute sequence
Priority, each process execution sequence should be determined by its function and internal logic, without cope with the embodiment of the present invention implementation
Journey constitutes any restriction.
More than, specific implementation mode only of the invention, but scope of protection of the present invention is not limited thereto, and it is any to be familiar with
Those skilled in the art in the technical scope disclosed by the present invention, can readily occur in various equivalent modifications or substitutions,
These modifications or substitutions should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be wanted with right
Subject to the protection domain asked.
Claims (10)
1. a kind of production method of cavity coupler, which is characterized in that the method includes:.
It treats process chambers coupler and carries out deconsolidation process, obtain initial upper cavity, initial lower chamber and initial intermediate bulkhead;
The flatness of the initial upper cavity, the initial lower chamber and the initial intermediate bulkhead is handled respectively, is obtained
To upper cavity, lower chamber and intermediate bulkhead;
Clamping processing is carried out to the upper cavity, the lower chamber and the intermediate bulkhead, obtains clamping cavity coupler;
Processing is measured to the clamping cavity coupler, obtains cavity coupler.
2. a kind of production method of cavity coupler according to claim 1, which is characterized in that the initial upper cavity
It is handled, is specifically included with the flatness of the initial lower chamber:
The processing of milling side is carried out successively to the initial upper cavity and the initial lower chamber respectively, a milling inner cavity is handled, at heat
Reason, the again processing of milling inner cavity, deburring processing and back chipping processing.
3. a kind of production method of cavity coupler according to claim 1, which is characterized in that the initial middle interval
The flatness of plate is handled, and is specifically included:
Assembly processing, hot smoothing process, milling processing and deburring is carried out to the initial intermediate bulkhead successively to handle.
4. a kind of production method of cavity coupler according to claim 3, which is characterized in that the initial middle interval
Plate carries out assembly processing, specifically includes:
The coating lubricating oil on working plate;
The initial intermediate bulkhead is pushed into the working plate so that the initial intermediate bulkhead is fastened on consolidating for the working plate
Determine between baffle and the active block stop of the working plate.
5. a kind of production method of cavity coupler according to claim 3, which is characterized in that
In the milling processing procedure, use the tool cutting edge angle of blade for 45 ° of wire rod quality.
6. a kind of production method of cavity coupler according to any one of claims 1-5, which is characterized in that described right
The upper cavity, the lower chamber and the intermediate bulkhead carry out clamping processing, specifically include:
Set the first SiC plates to lower plate;
Set the 2nd SiC plates to upper layer locating back;
The lower chamber, the intermediate bulkhead and the epicoele are set gradually between the lower plate and the upper layer locating back
Body, and place solder between the lower chamber and the intermediate bulkhead and between the intermediate bulkhead and the upper cavity;
Wherein, the lower plate is bonded with the lower chamber, and the upper layer locating back is bonded with the upper cavity.
7. a kind of production method of cavity coupler according to claim 6, which is characterized in that the method further includes:
The fitting setting cast iron pressing plate on the upper layer locating back.
8. a kind of production method of cavity coupler according to claim 6, which is characterized in that described to the clamping chamber
Body coupler measures processing, obtains cavity coupler, specifically includes:
Gap between the lower plate and the lower chamber measures, and obtains measurement result;
The measurement result is compared with preset measurement threshold value, if the measurement result, which is less than, measures threshold value, by institute
It states clamping cavity coupler and is determined as the cavity coupler.
9. a kind of production method of cavity coupler according to claim 8, which is characterized in that
The measurement threshold value is 0.05mm.
10. a kind of production method of cavity coupler according to any one of claim 1-5,7-9, which is characterized in that
The method further includes:
Vacuum brazing processing is carried out to the cavity coupler, obtains target cavity coupler.