CN108643504A - A kind of transparent balance paper, laminated flooring and preparation method thereof - Google Patents
A kind of transparent balance paper, laminated flooring and preparation method thereof Download PDFInfo
- Publication number
- CN108643504A CN108643504A CN201810389513.4A CN201810389513A CN108643504A CN 108643504 A CN108643504 A CN 108643504A CN 201810389513 A CN201810389513 A CN 201810389513A CN 108643504 A CN108643504 A CN 108643504A
- Authority
- CN
- China
- Prior art keywords
- paper
- balance paper
- preparation
- transparent balance
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of transparent balance paper comprising following processing step：1) wood pulp carries out pulping, carries out defibrination afterwards, the average length of control gained wood pulp cellulose is within the scope of 2.5~3mm；2) it is 3 by parts by weight of raw materials ratio with acrylic resin by wood pulp cellulose obtained by step 1):7 manufacture paper with pulp after mixing, and transparent balance paper product is prepared by rewinding.The present invention by adjusting the raw material components of balance paper, with when preparation process, without adding inorganic mineral filler, reinforcing agent and the retention agent etc. that reduce transparency, greatly reduce heat transfer consumption when raw material input is overlayed with post-processing, it is with excellent transparency simultaneously, post-processing can really, clearly show the decorative pattern of substrate after overlaying, and enhance vision both visual sense and validity.The transparent balance paper that the present invention is prepared into has both excellent transparency and mechanical property.The invention also discloses a kind of laminated floorings and preparation method thereof with the transparent balance paper.
Description
Technical field
The present invention relates to decorative building material field, more particularly to a kind of dalle.
Background technology
Balance paper be balance body paper dipping process after high temperature and pressure effect push be affixed on substrate backside high quality it is special
With paper, main function is retentively board size stabilization and moistureproof and waterproof.Conventional balance body paper is a kind of plain color paper, in its production
A certain amount of inorganic mineral and dyestuff and the dispensings such as PAE reinforcing agents and PAM retention agents can be added in flow, to reduce original
Paper transparency, reinforcing fiber cross-link intensity and raising filler retention ratio, reach and cover base material crude fibre, improve flooring look quality
Decorative purpose.With the raising of material life quality, consumer more pursues a kind of ecosystem U.S. to get close to nature, conventional element
The color of colour balance paper is bionical artificial color, and vision distortion, effect are stiff and opacity is high, lacks natural activity.How
It is prepared into that a kind of transparency is high and the transparent balance paper of excellent combination property is of great significance.
Laminated flooring, i.e. impregnated-paper laminated wood floor are a kind of hot-forming composite floor boards.It is each in the prior art
The kind competing product of timber floor emerge one after another, and comprehensive performance is also poor secondary uneven.Therefore, structure and the simple comprehensive performance simultaneously of preparation method
Excellent laminated flooring is increasingly favored by manufacturer and consumer.
Invention content
It is an object of the invention in view of the above shortcomings of the prior art, provide a kind of transparent balance paper and be compounded with this thoroughly
The laminated flooring of bright balance paper, while the preparation method of the transparent balance paper and laminated flooring being provided.
The technical solution used in the present invention is：A kind of preparation method of transparent balance paper comprising following processing step：
1) wood pulp carries out pulping using intermittent mode, rear to carry out defibrination using free beating mode, and control gained wood pulp is fine
The average length of dimension is within the scope of 2.5~3mm；
2) it is 3 by parts by weight of raw materials ratio with acrylic resin by wood pulp cellulose obtained by step 1):7 are copied after mixing
It makes, controls the online a concentration of 1.2~1.6% for process of manufacturing paper with pulp, quantitative 50 ± 2g/m2, transparent balance paper is prepared by rewinding
Finished product.
Specifically, balance paper of the invention does not add the raw material components such as inorganic mineral filler, reinforcing agent and retention agent, greatly
It is big to reduce raw material input and heat transfer consumption when post-processing overlays, effectively save production cost, while it is with excellent
Transparency, post-processing overlay after can the decorative pattern of substrate is true, clearly show, enhance vision both visual senses and true
Solidity, to which enhancing overlays the surcharge of plank.The mixed proportion of wood fibre and acrylic resin in balance paper of the present invention
The comprehensive performance of its finished product is had a major impact, wherein particular determination to wood fibre and its suitably matching with acrylic resin
Than not only realizing the raising of balance paper transparency, while it ensure that it with good mechanical property and processability.
As being further improved for said program, a concentration of 4.2~5.5% are cracked during the step 1) pulping.
Specifically, the dispersibility for cracking concentration and can guarantee wood fibre.
As being further improved for said program, the beating consistency described in step 1) is 35~38 ° of SR.Specifically, described
Beating consistency can effectively improve the processability of balance paper during following process.
As being further improved for said program, regulation speed is 70~80m/min during manufacturing paper with pulp described in step 2).
As being further improved for said program, step 2) the lower machine moisture of control in the process of manufacturing paper with pulp is 4~4.5%.
Specifically, the restriction of lower machine moisture can effectively prevent the balance paper product moisture absorption.
A kind of laminated flooring, from top to bottom by wood grain spraying paper, E1 level high-densities fibre base plate and transparent balance paper
It presses, the transparent balance paper is the transparent balance paper that above-mentioned technical proposal is prepared into.
As being further improved for said program, the wood grain spraying paper is by graining impregnated paper and is coated on wood grain dress
Adorn the aluminum oxide coating composition of impregnated paper upper surface.Specifically, alundum (Al2O3) is coated directly onto graining dipping
On paper, the preparation of abrasion-proof paper in the prior art is omitted and overlays process, has saved the cost input of wood-fibred and adhesive, from
And improve can plank manufacture efficiency, reduce production cost.
As being further improved for said program, the E1 level high-densities fibre base plate burst size of methanal≤0.124mg/
m3。
A kind of preparation method of laminated flooring as described above comprising following processing step：
1) urea-formaldehyde resin adhesive for selecting the small diameter grade wood fibre of diameter d1≤13cm to be modified with MDI environment-friendlyadhesive adhesives or through MDI
It is uniformly mixed, through boiling, defibrator process plus glue, hot pressing, is prepared into E1 level high-density fibre base plates；
2) the transparent balance paper of above-mentioned gained is overlayed into the E1 level high-densities obtained by step 1) after melmac impregnates
Fibre base plate lower surface；
3) it is overlayed in step 1) after graining impregnated paper spraying alundum (Al2O3) solution being formed aluminum oxide coating
Gained E1 level high-density fibre base plates upper surface.
The beneficial effects of the invention are as follows：
The present invention by adjusting the raw material components of balance paper, with when preparation process, without adding the nothing for reducing transparency
Machine mineral filler, reinforcing agent and retention agent etc. greatly reduce heat transfer consumption when raw material input is overlayed with post-processing, effectively
Production cost is saved, while it with excellent transparency, post-processing can be by the decorative pattern of substrate really, clearly after overlaying
It shows, enhances vision both visual sense and validity, to which enhancing overlays the surcharge of plank.The present invention is prepared into saturating
Bright balance paper has both excellent transparency and mechanical property.
For the laminated flooring of the present invention using E1 level high-densities fiberboard as substrate, substrate backside overlays transparent balance paper,
Substrate surface overlays wood grain spraying paper, improve in the prior art traditional laminated flooring in appearance, vision, environmental protection and price etc.
Competitive disadvantages in aspect improve the market competitiveness of the laminated flooring.
Specific implementation mode
The present invention is specifically described with reference to embodiment, in order to technical field personnel to the present invention
Understand.It is necessary to it is emphasized that embodiment is only intended to, the present invention will be further described herein, should not be understood as to this
The limitation of invention protection domain, fields person skilled in the art, the non-intrinsically safe that the present invention is made according to foregoing invention content
The modifications and adaptations of property, should still fall within protection scope of the present invention.Mentioned raw materials following simultaneously are unspecified, are
Commercial product；The processing step or preparation method not referred in detail be processing step known to a person skilled in the art or
Preparation method.
Embodiment 1
A kind of preparation method of transparent balance paper comprising following processing step：
1) wood pulp carries out pulping using intermittent mode, and control is cracked a concentration of 4.2%, carried out afterwards using free beating mode
Defibrination, control beating consistency are 38 ° of SR, and the average length of control gained wood pulp cellulose is within the scope of 2.5~3mm；
2) it is 3 by parts by weight of raw materials ratio with acrylic resin by wood pulp cellulose obtained by step 1):7 are copied after mixing
It makes, controls the online a concentration of 1.2% for process of manufacturing paper with pulp, quantitative 50 ± 2g/m2, while regulation speed is 80m/min, lower machine moisture
It is 4%, 1 transparent balance paper product of embodiment is prepared by rewinding.
Prepare 1 laminated flooring of embodiment with the 1 transparent balance paper product of embodiment that is prepared into, the laminated flooring its from
It is pressed by wood grain spraying paper, E1 level high-densities fibre base plate and 1 transparent balance paper product of embodiment under above, wherein described
Wood grain sprays paper and is made of with the aluminum oxide coating for being coated on graining impregnated paper upper surface graining impregnated paper.
The preparation method of 1 laminated flooring of embodiment comprises the technical steps that：
1) urea-formaldehyde resin adhesive for selecting the small diameter grade wood fibre of diameter d1≤13cm to be modified with MDI environment-friendlyadhesive adhesives or through MDI
It is uniformly mixed, through boiling, defibrator process plus glue, hot pressing, is prepared into burst size of methanal≤0.124mg/m3E1 level high-density fiber bases
Plate；
2) 1 transparent balance paper of embodiment is overlayed into the E1 level high-densities fibre obtained by step 1) after melmac impregnates
Tie up base lower surface；
3) it is overlayed in step 1) after graining impregnated paper spraying alundum (Al2O3) solution being formed aluminum oxide coating
Gained E1 level high-density fibre base plates upper surface.
Embodiment 2
A kind of preparation method of transparent balance paper comprising following processing step：
1) wood pulp carries out pulping using intermittent mode, and control is cracked a concentration of 5.5%, carried out afterwards using free beating mode
Defibrination, control beating consistency are 35 ° of SR, and the average length of control gained wood pulp cellulose is within the scope of 2.5~3mm；
2) it is 3 by parts by weight of raw materials ratio with acrylic resin by wood pulp cellulose obtained by step 1):7 are copied after mixing
It makes, controls the online a concentration of 1.6% for process of manufacturing paper with pulp, quantitative 50 ± 2g/m2, while regulation speed is 70m/min, lower machine moisture
It is 4.5%, 2 transparent balance paper product of embodiment is prepared by rewinding.
Prepare 2 laminated flooring of embodiment with the 2 transparent balance paper product of embodiment that is prepared into, the laminated flooring its from
It is pressed by wood grain spraying paper, E1 level high-densities fibre base plate and 1 transparent balance paper product of embodiment under above, wherein described
Wood grain sprays paper and is made of with the aluminum oxide coating for being coated on graining impregnated paper upper surface graining impregnated paper.
The preparation method of 2 laminated flooring of embodiment comprises the technical steps that：
1) urea-formaldehyde resin adhesive for selecting the small diameter grade wood fibre of diameter d1≤13cm to be modified with MDI environment-friendlyadhesive adhesives or through MDI
It is uniformly mixed, through boiling, defibrator process plus glue, hot pressing, is prepared into burst size of methanal≤0.124mg/m3E1 level high-density fiber bases
Plate；
2) 2 transparent balance paper of embodiment is overlayed into the E1 level high-densities fibre obtained by step 1) after melmac impregnates
Tie up base lower surface；
3) it is overlayed in step 1) after graining impregnated paper spraying alundum (Al2O3) solution being formed aluminum oxide coating
Gained E1 level high-density fibre base plates upper surface.
Embodiment 3
A kind of preparation method of transparent balance paper comprising following processing step：
1) wood pulp carries out pulping using intermittent mode, and control is cracked a concentration of 5%, ground afterwards using free beating mode
Slurry, control beating consistency are 36 ° of SR, and the average length of control gained wood pulp cellulose is within the scope of 2.5~3mm；
2) it is 3 by parts by weight of raw materials ratio with acrylic resin by wood pulp cellulose obtained by step 1):7 are copied after mixing
It makes, controls the online a concentration of 1.4% for process of manufacturing paper with pulp, quantitative 50 ± 2g/m2, while regulation speed is 75m/min, lower machine moisture
It is 4.2%, 3 transparent balance paper product of embodiment is prepared by rewinding.
Prepare 3 laminated flooring of embodiment with the 3 transparent balance paper product of embodiment that is prepared into, the laminated flooring its from
It is pressed by wood grain spraying paper, E1 level high-densities fibre base plate and 3 transparent balance paper product of embodiment under above, wherein described
Wood grain sprays paper and is made of with the aluminum oxide coating for being coated on graining impregnated paper upper surface graining impregnated paper.
The preparation method of 3 laminated flooring of embodiment comprises the technical steps that：
1) urea-formaldehyde resin adhesive for selecting the small diameter grade wood fibre of diameter d1≤13cm to be modified with MDI environment-friendlyadhesive adhesives or through MDI
It is uniformly mixed, through boiling, defibrator process plus glue, hot pressing, is prepared into burst size of methanal≤0.124mg/m3E1 level high-density fiber bases
Plate；
2) 1 transparent balance paper of embodiment is overlayed into the E1 level high-densities fibre obtained by step 1) after melmac impregnates
Tie up base lower surface；
3) it is overlayed in step 1) after graining impregnated paper spraying alundum (Al2O3) solution being formed aluminum oxide coating
Gained E1 level high-density fibre base plates upper surface.
Above-described embodiment is the preferred embodiment of the present invention, it is all with similar technique of the invention and made by equivalence changes,
The protection category of the present invention should all be belonged to.
Claims (10)
1. a kind of preparation method of transparent balance paper, it is characterised in that comprise the technical steps that：
1) wood pulp carries out pulping using intermittent mode, rear to carry out defibrination using free beating mode, control gained wood pulp cellulose
Average length is within the scope of 2.5~3mm；
2) it is 3 by parts by weight of raw materials ratio with acrylic resin by wood pulp cellulose obtained by step 1):7 manufacture paper with pulp after mixing,
Control the online a concentration of 1.2~1.6% for process of manufacturing paper with pulp, quantitative 50 ± 2g/m2, by rewinding be prepared into transparent balance paper at
Product.
2. a kind of preparation method of transparent balance paper according to claim 1, it is characterised in that：Step 1) the pulping mistake
A concentration of 4.2~5.5% are cracked in journey.
3. a kind of preparation method of transparent balance paper according to claim 1, it is characterised in that：Mashing described in step 1)
A concentration of 35~38 ° of SR.
4. a kind of preparation method of transparent balance paper according to claim 1, it is characterised in that：Step 2) is described to manufacture paper with pulp
Regulation speed is 70~80m/min in journey.
5. a kind of preparation method of transparent balance paper according to claim 1, it is characterised in that：Step 2) is described to manufacture paper with pulp
It is 4~4.5% that lower machine moisture is controlled in journey.
6. a kind of transparent balance paper being prepared by Claims 1 to 5 any one of them preparation method.
7. a kind of laminated flooring, it is characterised in that：From top to bottom by wood grain spraying paper, E1 level high-densities fibre base plate and transparent
Balance paper presses, and the transparent balance paper is the transparent balance paper described in claim 6.
8. a kind of laminated flooring according to claim 7, it is characterised in that：The wood grain spraying paper is soaked by graining
Stain paper and the aluminum oxide coating composition for being coated on graining impregnated paper upper surface.
9. a kind of laminated flooring according to claim 7, it is characterised in that：The E1 level high-densities fibre base plate formaldehyde
Burst size≤0.124mg/m3。
10. a kind of preparation method of such as claim 7~9 any one of them laminated flooring, it is characterised in that including as follows
Processing step：
1) urea-formaldehyde resin adhesive that the small diameter grade wood fibre of diameter d1≤13cm is modified with MDI environment-friendlyadhesive adhesives or through MDI is selected to mix
Uniformly, through boiling, defibrator process plus glue, hot pressing, E1 level high-density fibre base plates are prepared into；
2) the transparent balance paper described in claim 6 is overlayed after melmac impregnates highly dense in E1 grades of step 1) gained
Spend fibre base plate lower surface；
3) graining impregnated paper spraying alundum (Al2O3) solution is formed after aluminum oxide coating and is overlayed obtained by step 1)
E1 level high-density fibre base plates upper surface.