CN108642644A - A kind of two-component fabric and its processing method spinning style with color - Google Patents
A kind of two-component fabric and its processing method spinning style with color Download PDFInfo
- Publication number
- CN108642644A CN108642644A CN201810288153.9A CN201810288153A CN108642644A CN 108642644 A CN108642644 A CN 108642644A CN 201810288153 A CN201810288153 A CN 201810288153A CN 108642644 A CN108642644 A CN 108642644A
- Authority
- CN
- China
- Prior art keywords
- fiber
- color
- length
- spinning
- blowing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of two-component fabrics spinning style with color, the fabric is interwoven by warp thread and weft yarn according to institutional framework, the warp thread and weft yarn are mixed yarn, the mixed yarn is made of the first fiber and the second fiber, the content of first fiber is 75 90%, and the content of the second fiber is 10 25%；First fiber is the fiber that disperse dyes are not painted, and the second fiber is the fiber of disperse dyes colouring；Second fiber includes the fiber of two kinds of length, and the length of longer fibers is 50mm, and the length of relatively chopped fiber is 30mm；The fineness of two kinds of fibers is all 1.2D.Its processing method is that shredding blowing, cotton carding are distinguished after being pre-processed to two kinds of fibers, and then drafting carries out vortex spinning spinning, finally weaving and disperse dyeing.The present invention is axially distributed uneven after blended by using two-component scribbled, forms the color having a sense of hierarchy after dyeing and spins effect.
Description
Technical field
The invention belongs to household textiles fields, and in particular to a kind of two-component fabric and its processing for spinning style with color
Method.
Background technology
Color textile fabric is different from pure color or the unique look of printed fabric due to its color space vision melange effect, formation
Style is increasingly liked by consumer.General color textile fabric is by first having spun staple in bulk or sliver, according to certain color
Ratio mixes, and is made using techniques such as spinning process, weaving and final finishings.Fiber dyed yarn is suitble to be knitted fabric, weaving process
It is short, it is not required to starching.When for woven fabric, due to the high-temperature process of starching, colour-spun yarns color generates variation, be easy to cause color
Difference, influence finished fabric to color, and color fastness decreased influences the use of fabric.
The fabric that two-component or more component yarns are made into, if the dye type used in several components is different, single dye is wherein
A kind of composition can form the effect of Adjacent color spinning.But when using conventional spinning process, several fiber mixing are very uniform, dyeing
Gradation unobvious afterwards, it is undesirable that color spins effect.
Invention content
The technical issues of solution：The object of the present invention is to provide a kind of two-component and the uneven, layers of each component fiber mixing
Secondary abundant yarn, and spin style fabric with the color that two-component yarn is made into.
Technical solution：
A kind of two-component fabric spinning style with color, is interwoven by warp thread and weft yarn according to institutional framework, the warp
Yarn and weft yarn are mixed yarn, which is made of the first fiber and the second fiber, and the content of the first fiber is 75-90%,
The content of second fiber is 10-25%；
First fiber is the fiber that disperse dyes are not painted, and the second fiber is the fiber of disperse dyes colouring；
Second fiber includes the fiber of two kinds of length, and the length of longer fibers is 50mm, and the length of relatively chopped fiber is 30mm；
The fineness of two kinds of fibers is all 1.2D.
Further, the first fiber is natural fiber or regenerated celulose fibre, and natural fiber is selected from cotton fiber or fiber crops are fine
Dimension, regenerated celulose fibre are selected from viscose rayon, tencel fiber, Modal fibre or bamboo pulp fiber.
Further, when the first fiber is regenerated celulose fibre, length 38mm, fineness 1.2D.
Further, the second fiber is polyester fiber or Fypro.
The processing method of above-mentioned fabric includes following process successively：Fiber selection-the first fiber opening of pretreatment-is clear
Flower, the second fiber opening of cotton carding-blowing, cotton carding-pre-drawing-drafting-vortex spinning spinning-warping-starching-weaving-
Rayon gray fabric cold batching moves back and boils drift-pre-setting-disperse dyeing-softness sizing-preshrunk.
Further, the pretreatment process be by the regenerated celulose fibre of the first fiber cut into length be 38mm,
By the second fibre cutting at two kinds of length of 48-50mm and 30-32mm.
Further, when the second fiber is polyester fiber, sprinkling antistatic agent is also needed.
Further, the first fiber opening blowing, carding step and the second fiber opening blowing, carding step are past
Shredding blowing is carried out on compound griping cotton machine, sliver is combed on carding machine；The fiber of two kinds of length of the second fiber needs to distinguish
Shredding blowing, carding step are carried out, cotton roll obtained is separately stored.
Further, pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are the first fiber, 1
Root sliver is the longer fibers of the second fiber, and 1 sliver is the relatively chopped fiber of the second fiber；Adjust separately the first fiber simultaneously
Total draft multiplying power is 6-6.3, the total draft multiplying power of the second fiber longer fibers is 8-8.2, the second fiber relatively chopped fiber is always led
It is 4.5-5 to stretch multiplying power, and fiber axially does relative displacement along yarn when drawing-off.
Further, disperse dyeing process is to use high-temperature pressure dyeing.
Advantageous effect：
The present invention uses two-component scribbled, wherein the first fiber is cellulose fibre, accounting 75-90%, second is fine
Dimension is polyester fiber, accounting 10-25%.Second fiber cuts off mode using non-isometric spacing, forms two different cut-out length
Degree, longer fibers and relatively chopped fiber are respectively formed sliver, and when drafting separately feeds, and the effect of realization is that two kinds of component fibers are blended
Afterwards, along yarn, axially each fiber is unevenly distributed, and the dyed color having a sense of hierarchy that formed afterwards of fabric spins style.
Spinning uses 2 drawing processes, adjusts separately the first fiber and the second fiber longer fibers and the second fiber is shorter
The draft ratio of fiber increases fiber distribution randomness, wherein the shorter part of the second fiber is in scatterplot distribution, longer part
The gradation of distribution in a strip shape, manufactured dyeing fabric is abundant.
Specific implementation mode
Embodiment 1
Specification：106.5 "/32s*32s/133*72, fabric tissue are 3/1 left twill.
First fiber is viscose rayon, and the second fiber is polyester fiber.Blending rate through weft yarn is viscose glue/polyester
Fiber 80/20.
Production technology specifically includes following process：Fiber selection-pretreatment-viscose rayon shredding blowing, cotton carding-are poly-
Before ester fiber shredding blowing, cotton carding-pre-drawing-drafting-vortex spinning spinning-warping-starching-weaving-rayon gray fabric cold batching
Reason-pre-setting-disperse dyeing-softness sizing-preshrunk.
It is 38mm that viscose rayon, which is cut into length, in pretreatment process, and there are two types of the length after polyester fiber cut-out：Compared with
Long stapled length is 50mm, the length of relatively chopped fiber is 30mm, and polyester fiber is sprayed antistatic agent.
Viscose rayon shredding blowing, carding step and polyester fiber shredding blowing, carding step are to grab cotton reciprocating
Carry out shredding blowing on machine, be combed into sliver on carding machine, wherein the longer fibers and relatively chopped fiber of polyester fiber respectively into
Row shredding blowing, cotton carding, cotton roll obtained are separately stored and are marked.
Pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are viscose rayon, 1 sliver is poly-
The longer fibers of ester fiber, 1 sliver are the relatively chopped fiber of polyester fiber；Adjust separately the drawing-off of the first fiber and the second fiber
Multiplying power, wherein the total draft multiplying power of the first fiber is 6, the total draft multiplying powers of the second fiber longer fibers is 8.2, the second fiber compared with
The total draft multiplying power of staple fiber is 4.5, and fiber axially does relative displacement along yarn when drawing-off.
High-temperature pressure dyeing is carried out using disperse dyes, the second fibrous polyester fiber is made to paint, and the first viscose is not
Colouring.
Embodiment 2
Specification：106 "/40s*40s/144*75, fabric tissue are 2/2 left twill tissue.
First fiber is cotton fiber, and the second fiber is polyester fiber.Blending rate through weft yarn is cotton polyester fiber
80/20。
Production technology specifically includes following process：Fiber selection-pretreatment-cotton fiber shredding blowing, cotton carding-essence
Comb-polyester fiber shredding blowing, cotton carding-pre-drawing-drafting-vortex spinning spinning-warping-starching-weaving-fabric move back
Boil the light sanding-disperse dyeing-softness sizing-preshrunk of drift-pre-setting-.
There are two types of length after cutting off polyester fiber in pretreatment process：The length of longer fibers is 50mm, shorter fibre
The length of dimension is 30mm, and polyester fiber is sprayed antistatic agent.First fiber is cotton fiber, is natural fiber, is not required to cut off.
Cotton fiber shredding blowing, cotton carding and polyester fiber shredding blowing, carding step are enterprising in reciprocation bale plucker
Row shredding blowing is combed into sliver on carding machine, and the longer fibers and relatively chopped fiber of wherein polyester fiber carry out shredding respectively
Blowing, cotton carding, cotton roll obtained are separately stored and are marked.
Pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are cotton fiber, 1 sliver is polyester
The longer fibers of fiber, 1 sliver are the relatively chopped fiber of polyester fiber.
The draft ratio of the first fiber and the second fiber is adjusted separately, wherein the total draft multiplying power of the first fiber is 6.2, the
The total draft multiplying power of two fiber longer fibers is 8, and the total draft multiplying power of the second fiber relatively chopped fiber is 5, and fiber when drawing-off
Relative displacement is axially done along yarn.
Using disperse dyes carry out high-temperature pressure dyeing, make the second fibrous polyester fiber paint, and the first cellucotton not on
Color.
Reference examples 1
Specification：106.5 "/32s*32s/133*72, fabric tissue are 3/1 left twill.
First fiber is viscose rayon, and the second fiber is polyester fiber.
With being distinguished as embodiment 1, the blending rate through weft yarn is polyester fiber/viscose glue 80/20.
Production technology specifically includes following process：Fiber selection-pretreatment-viscose rayon shredding blowing, cotton carding-are poly-
Before ester fiber shredding blowing, cotton carding-pre-drawing-drafting-vortex spinning spinning-warping-starching-weaving-rayon gray fabric cold batching
Reason-pre-setting-disperse dyeing-softness sizing-preshrunk.
It is 38mm that viscose rayon, which is cut into length, in pretreatment process, and there are two types of the length after polyester fiber cut-out：Compared with
Long stapled length is 50mm, the length of relatively chopped fiber is 30mm, and polyester fiber is sprayed antistatic agent.
Viscose rayon shredding blowing, carding step and polyester fiber shredding blowing, carding step are to grab cotton reciprocating
Carry out shredding blowing on machine, be combed into sliver on carding machine, wherein the longer fibers and relatively chopped fiber of polyester fiber respectively into
Row shredding blowing, cotton carding, cotton roll obtained are separately stored and are marked.
Pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are viscose rayon, 1 sliver is poly-
The longer fibers of ester fiber, 1 sliver are the relatively chopped fiber of polyester fiber；Adjust separately the drawing-off of the first fiber and the second fiber
Multiplying power, wherein the total draft multiplying power of the first fiber is 6, the total draft multiplying powers of the second fiber longer fibers is 8.2, the second fiber compared with
The total draft multiplying power of staple fiber is 4.5, and fiber axially does relative displacement along yarn when drawing-off.
High-temperature pressure dyeing is carried out using disperse dyes, the second fibrous polyester fiber is made to paint, and the first viscose is not
Colouring.
Reference examples 2
With being distinguished as embodiment 1, it is 38mm that viscose rayon, which is cut into length, in pretreatment process, by polyester fiber
Also it is 38mm, polyester fiber length straight uniform to cut into length entirely.
Specification：106.5 "/32s*32s/133*72, fabric tissue are 3/1 left twill.
First fiber is viscose rayon, and the second fiber is polyester fiber.Blending rate through weft yarn is viscose glue/polyester
Fiber 80/20.
Production technology specifically includes following process：Fiber selection-pretreatment-viscose rayon shredding blowing, cotton carding-are poly-
Before ester fiber shredding blowing, cotton carding-pre-drawing-drafting-vortex spinning spinning-warping-starching-weaving-rayon gray fabric cold batching
Reason-pre-setting-disperse dyeing-softness sizing-preshrunk.
It is 38mm that viscose rayon, which is cut into length, in pretreatment process, and polyester fiber is also cut into length entirely is
38mm, polyester fiber length straight uniform, and polyester fiber is sprayed into antistatic agent.
Viscose rayon shredding blowing, carding step and polyester fiber shredding blowing, carding step are to grab cotton reciprocating
Carry out shredding blowing on machine, be combed into sliver on carding machine, wherein the longer fibers and relatively chopped fiber of polyester fiber respectively into
Row shredding blowing, cotton carding, cotton roll obtained are separately stored and are marked.
Pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are viscose rayon, 1 sliver is poly-
The longer fibers of ester fiber, 1 sliver are the relatively chopped fiber of polyester fiber；Adjust separately the drawing-off of the first fiber and the second fiber
Multiplying power, wherein the total draft multiplying power of the first fiber is 6, the total draft multiplying powers of the second fiber longer fibers is 8.2, the second fiber compared with
The total draft multiplying power of staple fiber is 4.5, and fiber axially does relative displacement along yarn when drawing-off.
High-temperature pressure dyeing is carried out using disperse dyes, the second fibrous polyester fiber is made to paint, and the first viscose is not
Colouring.
Reference examples 3
With being distinguished as embodiment 1：In pre-drawing process and mixing in doubling step, the drawing-off times of the first fiber and the second fiber
Rate is identical.
Specification：106.5 "/32s*32s/133*72, fabric tissue are 3/1 left twill.
First fiber is viscose rayon, and the second fiber is polyester fiber.Blending rate through weft yarn is viscose glue/polyester
Fiber 80/20.
Production technology includes the following steps：Fiber selection-pretreatment-viscose rayon shredding blowing, cotton carding-polyester are fine
Tie up shredding blowing, cotton carding-pre-drawing-drafting-vortex spinning spinning-warping-starching-weaving-rayon gray fabric cold batching pre-treatment-
Pre-setting-disperse dyeing-softness sizing-preshrunk.
It is 38mm that viscose rayon, which is cut into length, in pretreatment process, and there are two types of the length after polyester fiber cut-out：Compared with
Long stapled length is 50mm, the length of relatively chopped fiber is 30mm, and polyester fiber is sprayed antistatic agent.
It is 38mm that viscose rayon, which is cut into length, in pretreatment process, and there are two types of the length after polyester fiber cut-out：Compared with
Long stapled length is 50mm, the length of relatively chopped fiber is 30mm, and polyester fiber is sprayed antistatic agent.
Viscose rayon shredding blowing, carding step and polyester fiber shredding blowing, carding step are to grab cotton reciprocating
Carry out shredding blowing on machine, be combed into sliver on carding machine, wherein the longer fibers and relatively chopped fiber of polyester fiber respectively into
Row shredding blowing, cotton carding, cotton roll obtained are separately stored and are marked.
Pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are viscose rayon, 1 sliver is poly-
The longer fibers of ester fiber, 1 sliver are the relatively chopped fiber of polyester fiber；Adjust separately the drawing-off of the first fiber and the second fiber
The draft ratio of multiplying power, the first fiber and the second fiber is identical, draft ratio 6.2, and fiber is axial along yarn when drawing-off
Do relative displacement.
High-temperature pressure dyeing is carried out using disperse dyes, the second fibrous polyester fiber is made to paint, and the first viscose is not
Colouring.It is as follows with the comparing result of upper fabric：
It is axially distributed uneven after blended by above it is found that the fabric of the present invention is by using two-component scribbled,
The color having a sense of hierarchy is formed after dyeing spins effect.
Claims (8)
1. a kind of two-component fabric spinning style with color, is interwoven by warp thread and weft yarn according to institutional framework, feature exists
In：The warp thread and weft yarn are mixed yarn, which is made of the first fiber and the second fiber, and the content of the first fiber is
The content of 75-90%, the second fiber are 10-25%；
First fiber is the fiber that disperse dyes are not painted, and the second fiber is the fiber of disperse dyes colouring；
Second fiber includes the fiber of two kinds of length, and the length of longer fibers is 50mm, and the length of relatively chopped fiber is 30mm；Two kinds
The fineness of fiber is all 1.2D.
2. the two-component fabric according to claim 1 for spinning style with color, it is characterised in that：First fiber is natural fine
Dimension or regenerated celulose fibre, natural fiber are selected from cotton fiber or flaxen fiber, and regenerated celulose fibre is selected from viscose rayon, tencel
Fiber, Modal fibre or bamboo pulp fiber.
3. the two-component fabric according to claim 2 for spinning style with color, it is characterised in that：First fiber is that regeneration is fine
When cellulose fiber, length 38mm, fineness 1.2D.
4. the two-component fabric according to claim 1 for spinning style with color, it is characterised in that：Second fiber is that polyester is fine
Dimension or Fypro.
5. the processing method of the two-component fabric described in claim 1 for spinning style with color, it is characterised in that：Include successively with
Lower process：Fiber selection-the first fiber opening of pretreatment-blowing, the second fiber opening of cotton carding-blowing, cotton carding-are pre- simultaneously
Item-drafting-vortex spinning spinning-warping-starching-weaving-rayon gray fabric cold batching or move back boils drift-pre-setting-disperse dyes dye
Color-softness sizing-preshrunk；
The pretreatment process is that the regenerated celulose fibre of the first fiber is cut into length for 38mm, by the second fibre cutting
At two kinds of length of 48-50mm and 30-32mm；
Pre-drawing process and mixing in doubling step are 8 sliver feedings, wherein 6 slivers are the first fiber, 1 sliver is second fine
The longer fibers of dimension, 1 sliver are the relatively chopped fiber of the second fiber；The total draft multiplying power for adjusting separately the first fiber simultaneously is 6-
6.3, the total draft multiplying power of the second fiber longer fibers is 8-8.2, the total draft multiplying power of the second fiber relatively chopped fiber is 4.5-5,
And fiber axially does relative displacement along yarn when drawing-off.
6. the processing method of the two-component fabric according to claim 5 for spinning style with color, it is characterised in that：Second is fine
When dimension is polyester fiber, sprinkling antistatic agent is also needed.
7. the processing method of the two-component fabric according to claim 5 for spinning style with color, it is characterised in that：First is fine
Dimension shredding blowing, carding step and the second fiber opening blowing, carding step be on reciprocation bale plucker progress shredding it is clear
Flower is combed into sliver on carding machine；The fiber of two kinds of length of the second fiber need to carry out shredding blowing, carding step respectively,
Cotton roll obtained is separately stored.
8. the processing method of the two-component fabric according to claim 5 for spinning style with color, it is characterised in that：Dispersion dye
Material dyeing process is to use high-temperature pressure dyeing.