CN108641649A - A kind of epoxy two-component hairbrush glue and preparation method thereof that bonding force is good - Google Patents
A kind of epoxy two-component hairbrush glue and preparation method thereof that bonding force is good Download PDFInfo
- Publication number
- CN108641649A CN108641649A CN201810373270.5A CN201810373270A CN108641649A CN 108641649 A CN108641649 A CN 108641649A CN 201810373270 A CN201810373270 A CN 201810373270A CN 108641649 A CN108641649 A CN 108641649A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- component
- weight
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of good epoxy two-component hairbrush glue of bonding force, the glue is made of A agent and B agent, and the weight ratio of wherein A agent and B agent is 5：1；The A agent is made of the component of following parts by weight：45 55 parts of bisphenol a resin；24 parts of benzyl alcohol；0.6 1.5 parts of auxiliary agent；41 51 parts of calcium carbonate；The B agent is made of the component of following parts by weight：54 66 parts of modified fatty amine curing agent；35 43 parts of polyamide curing agent；0.6 1.5 parts of adhesion promoter.Epoxy two-component hairbrush glue provided by the invention has many advantages, such as that bonding force is good, solvent resistance is good, can effectively improve the quality and service life of hairbrush.
Description
Technical field
The present invention relates to a kind of glue and preparation method thereof, and in particular to a kind of epoxy two-component hairbrush glue that bonding force is good
Water and preparation method thereof.
Background technology
Hairbrush in use, since it can frequently refer to different solvents（Such as ketone, alcohols, alkanes equal solvent）'s
Oil paint, therefore hairbrush is often corroded by all kinds of different solvents.Currently, due to the bonding force of existing hairbrush glue
It is poor with solvent resistance, therefore when hairbrush encounters above-mentioned class solvent, situations such as just will appear hair loss in very short time, or even
The case where hairbrush falls off from handle during use occurs, and the service life so as to cause existing hairbrush is shorter.
Invention content
In order to overcome the deficiencies of the prior art and there are the problem of, the present invention provides a kind of epoxy two-component hair that bonding force is good
Brush coating water.
The present invention is achieved by the following technical solutions：A kind of epoxy two-component hairbrush glue that bonding force is good, it is described
Glue is made of A agent and B agent, and the weight ratio of wherein A agent and B agent is 5：1；
The A agent is made of the component of following parts by weight：
45-55 parts of bisphenol a resin；
2-4 parts of benzyl alcohol；
0.6-1.5 parts of auxiliary agent；
41-51 parts of calcium carbonate；
The B agent is made of the component of following parts by weight：
54-66 parts of modified fatty amine curing agent；
35-43 parts of polyamide curing agent；
0.6-1.5 parts of adhesion promoter.
Preferably, the auxiliary agent is antifoaming agent, anti-settling agent mixes in any proportion.
Above-described epoxy two-component hairbrush glue, preparation method include the following steps：
Step S1, each component by the A agent is weighed according to parts by weight, by the bisphenol a resin after weighing, benzyl alcohol and
Calcium carbonate is positioned in production containers and is mixed, and the auxiliary agent weighed according to parts by weight, stirring are added in whipping process
After uniformly；
Step S2, each component by the B agent is weighed according to parts by weight, and each component after weighing is mixed
Uniformly；
Step S3, made from the step S1 and step 2, A agent and B agent are according to 5：1 weight ratio is weighed and is mixed
Uniformly；
Step S4, solution made from step S3 is cured, you can the glue is made.
Preferably, the solidification in the step S4 be included in the normal temperature cure carried out at 20-30 DEG C or at 50-60 DEG C into
Capable heating cure
Epoxy two-component hairbrush glue provided by the invention has many advantages, such as that bonding force is good, solvent resistance is good, can effectively improve
The quality and service life of hairbrush.
Specific implementation mode
For the ease of the understanding of those skilled in the art, present invention work is further retouched in detail below in conjunction with specific embodiment
It states.
Embodiment 1
The each component and parts by weight of the A agent：
45 parts of bisphenol a resin；
2 parts of benzyl alcohol；
0.6 part of auxiliary agent；
41 parts of calcium carbonate；
The each component and parts by weight of the B agent：
54 parts of modified fatty amine curing agent；
35 parts of polyamide curing agent；
0.6 part of adhesion promoter.
Wherein, the glue is made of A agent and B agent, and the weight ratio of wherein A agent and B agent is 5：1.The embodiment of the present invention
In, the epoxy two-component hairbrush glue, preparation method includes the following steps：
Step S1, each component by the A agent is weighed according to parts by weight, by the bisphenol a resin after weighing, benzyl alcohol and
Calcium carbonate is positioned in production containers and is mixed, and the auxiliary agent weighed according to parts by weight, stirring are added in whipping process
After uniformly；
Step S2, each component by the B agent is weighed according to parts by weight, and each component after weighing is mixed
Uniformly；
Step S3, made from the step S1 and step 2, A agent and B agent are according to 5：1 weight ratio is weighed and is mixed
Uniformly；
Step S4, solution made from step S3 is cured, you can the glue is made.
Wherein, the solidification in the step S4 is included in the normal temperature cure carried out at 20-30 DEG C or is carried out at 50-60 DEG C
Heating cure
It should be noted that in the present invention, the ratio of the A agent and B agent parts by weight is relatively independent, but works as A agent and B agent
When mixing, then the weight ratio of the two is 5：1.Such as in A agent, every portion of each component can be 5 kilograms, or 1
Kilogram, and in B agent, every portion of each component can be 1 kilogram or 2 kilograms；But when A agent and B agent are mixed to prepare
When the glue, then need according to weight ratio to be 5：1 ratio weighs the A agent and B agent.For example, in A agent, each component
Every portion when can be 5 kilograms, and in B agent, each component per it is a be 1 kilogram when, when preparing the glue, can claim
5 kilograms of A agent is taken, and weighs 1 kilogram of B agent and is prepared；And in A agent, when every portion of each component can be 1 kilogram, and
In B agent, when every portion of each component is 1 kilogram, when preparing the glue, equally it is to weigh 5 kilograms of A agent, weighs B agent 1
It kilogram is prepared；It is of course also possible to be weigh other weight A agent and B agent infiltrate capable preparation, as long as ensuring A agent and B agent
Weight ratio be 5：1.
Embodiment 2
The each component and parts by weight of the A agent：
55 parts of bisphenol a resin；
4 parts of benzyl alcohol；
1.5 parts of auxiliary agent；
51 parts of calcium carbonate；
The each component and parts by weight of the B agent：
66 parts of modified fatty amine curing agent；
43 parts of polyamide curing agent；
1.5 parts of adhesion promoter.
Method in the preparation method and embodiment 1 of the glue is same or like, and details are not described herein.
Embodiment 3
The each component and parts by weight of the A agent：
50 parts of bisphenol a resin；
3 parts of benzyl alcohol；
1 part of auxiliary agent；
46 parts of calcium carbonate；
The each component and parts by weight of the B agent：
60 parts of modified fatty amine curing agent；
39 parts of polyamide curing agent；
1 part of adhesion promoter.
Method in the preparation method and embodiment 1 of the glue is same or like, and details are not described herein.
Embodiment 4
The each component and parts by weight of the A agent：
48 parts of bisphenol a resin；
3.5 parts of benzyl alcohol；
1.2 parts of auxiliary agent；
48 parts of calcium carbonate；
The each component and parts by weight of the B agent：
63 parts of modified fatty amine curing agent；
41 parts of polyamide curing agent；
1.2 parts of adhesion promoter.
Method in the preparation method and embodiment 1 of the glue is same or like, and details are not described herein.
Embodiment 5
The each component and parts by weight of the A agent：
53 parts of bisphenol a resin；
2.5 parts of benzyl alcohol；
0.8 part of auxiliary agent；
43 parts of calcium carbonate；
The each component and parts by weight of the B agent：
58 parts of modified fatty amine curing agent；
37 parts of polyamide curing agent；
0.8 part of adhesion promoter.
Method in the preparation method and embodiment 1 of the glue is same or like, and details are not described herein.
Epoxy two-component hairbrush glue provided in an embodiment of the present invention has many advantages, such as that bonding force is good, solvent resistance is good,
So as to effectively improve the quality and service life of hairbrush.
Above-described embodiment is the preferable realization method of the present invention, is not limited to the present invention, is not departing from this hair
Under the premise of bright inventive concept, any obvious replacement is within protection scope of the present invention.
Claims (4)
1. a kind of good epoxy two-component hairbrush glue of bonding force, which is characterized in that the glue is made of A agent and B agent,
The weight ratio of middle A agent and B agent is 5：1；
The A agent is made of the component of following parts by weight：
45-55 parts of bisphenol a resin；
2-4 parts of benzyl alcohol；
0.6-1.5 parts of auxiliary agent；
41-51 parts of calcium carbonate；
The B agent is made of the component of following parts by weight：
54-66 parts of modified fatty amine curing agent；
35-43 parts of polyamide curing agent；
0.6-1.5 parts of adhesion promoter.
2. epoxy two-component hairbrush glue according to claim 1, it is characterised in that：The auxiliary agent is antifoaming agent, anti-settling
Agent mixes in any proportion.
3. a kind of preparation method of epoxy two-component hairbrush glue according to claim 1 or 2, which is characterized in that described
Preparation method include the following steps：
Step S1, each component by the A agent is weighed according to parts by weight, by the bisphenol a resin after weighing, benzyl alcohol and
Calcium carbonate is positioned in production containers and is mixed, and the auxiliary agent weighed according to parts by weight, stirring are added in whipping process
After uniformly；
Step S2, each component by the B agent is weighed according to parts by weight, and each component after weighing is mixed
Uniformly；
Step S3, made from the step S1 and step 2, A agent and B agent are according to 5：1 weight ratio is weighed and is mixed
Uniformly；
Step S4, solution made from step S3 is cured, you can the glue is made.
4. preparation method according to claim 3, it is characterised in that：Solidification in the step S4 is included in 20-30 DEG C
The normal temperature cure of lower progress or the heating cure carried out at 50-60 DEG C.