CN108641612A - A kind of protection packaging material for controller switching equipment - Google Patents
A kind of protection packaging material for controller switching equipment Download PDFInfo
- Publication number
- CN108641612A CN108641612A CN201810517079.3A CN201810517079A CN108641612A CN 108641612 A CN108641612 A CN 108641612A CN 201810517079 A CN201810517079 A CN 201810517079A CN 108641612 A CN108641612 A CN 108641612A
- Authority
- CN
- China
- Prior art keywords
- switching equipment
- packaging material
- controller switching
- curing agent
- modified epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of protection packaging materials for controller switching equipment; including base material and the adhesive for being coated in the arbitrary one side of the base material; the base material is made of butyl rubber, modified epoxy and curing agent, the butyl rubber, modified epoxy, curing agent and adhesive weight percent dosage be：Butyl rubber 70 75%, modified epoxy 5 15%, curing agent 10 15%, adhesive 5% have many advantages, such as that sealed insulation, high voltage withstanding, high-low temperature resistant, waterproof fireproofing and anti-ultraviolet aging are had excellent performance.
Description
Technical field
The present invention relates to a kind of protection packaging materials for controller switching equipment.
Background technology
The tie point generated when needing the conducting wire to controller switching equipment to connect needs to carry out insulating processing to ensure
Controller switching equipment general safety is reliable, electric armour clamp, electric armour clamp would generally be used when connecting to be easy influent gas, wire clamp is as connecting
The conductor connection electric armour clamp of electric current is easier influent gas, aqueous vapor is in wire clamp due to its special structure and position than conducting wire
Portion's knot is poly-, and conducting wire and wire clamp is often caused to aoxidize, and conducting wire and wire clamp contact resistance is caused to increase, and strength reduction shortens conducting wire
Service life；Suspended insulated guide wire is connect by wire jumper with outdoor pole top switch or transformer, and tie point is exposed in air, this with
Wire clamp is similar, and contact site oxidation is be easy to cause after influent gas, and contact resistance increases, and causes security risk；Overhead bare conductor from
Newly-built building is too close, is security consideration when safe distance is inadequate, exhausted close to building or trees section work part in overhead bare conductor
Edgeization processing, insulated conductor is substituted for without whole section, more economically, and is operated relatively easier, it is ensured that the operation person and equipment
Safety；Existing packaging material is typically only capable to play insulation effect, can only realize the short-term insulating of tie point, under high and low temperature environment absolutely
Edge effect is poor, and water proof fire retardant ability is weak, and anti-ultraviolet property is poor easy to aging.
Invention content
It is an object of the invention to overcome the deficiency of the prior art, a kind of protection packaging material for controller switching equipment is provided.
The technical solution adopted by the present invention to solve the technical problems is：
A kind of protection packaging material for controller switching equipment, including base material and the adhesive for being coated in the arbitrary one side of the base material, institute
Base material is stated to be made of butyl rubber, modified epoxy and curing agent, the butyl rubber, modified epoxy, curing agent and
The weight percent dosage of adhesive is：Butyl rubber 70-75%, modified epoxy 5-15%, curing agent 10-15%, glue
Stick 5%.
In a further preferred embodiment, the thickness of the base material is 1.65mm.
In a further preferred embodiment, the controller switching equipment includes conducting wire and electric armour clamp.
In a further preferred embodiment, the electric armour clamp is the splicing fitting to be connected between conducting wire.
In a further preferred embodiment, the modified epoxy is elastomer-modified bisphenol A-type solid epoxy
Addition product.
In a further preferred embodiment, the curing agent is to stablize at 30 DEG C or less, in 120 DEG C or more energy and modified epoxy
Resin crosslinks the latent curing agent of reaction.
In a further preferred embodiment, the packaging material is in band-like.
The beneficial effects of the invention are as follows：Packet is made by using butyl rubber, modified epoxy, curing agent and adhesive
Material has the following advantages that：
1, sealed insulation, high voltage withstanding, high-low temperature resistant；
2, flexibility is excellent, high mechanical strength；
3, room temperature curing after constructing, initial stage adhesive performance and releasable energy are good, being bonded followability, good, hot setting can
It repairs；
4, strip of sheet material, construction are convenient；
5, waterproof fireproofing, fire-retardant rank is up to UL94-V1；
6, volatile substance is free of, on environment and human body without influence；
7, material is uniform, and insulation performance is small by man's activity；
8, anti-ultraviolet aging is had excellent performance, and energy prolonged application has certain machinery in outdoor environment, and after hardening and protects
Performance is protected, can not have to additionally plus protective coat, single material can meet application requirement；
9, reset condition is sufficiently flexible, fine from shape, and has good adhesion and adhesive force to metal, does not influence to dissipate
Heat and thermometric, apply and can be attached well in the irregular wire clamp position of shape, water proofing property is secure；
10, self-curing waterproof insulation protection packaging material can not influence resident's use with livewire work, without being laid with insulated conductor
Electricity, social influence are small.
Invention is further described in detail with reference to the accompanying drawings and embodiments；But one kind of the present invention is set for distribution
Standby protection packaging material is not limited to embodiment.
Description of the drawings
Fig. 1 is the structural schematic diagram of c-type wire clamp；
Fig. 2 is that the present invention applies the structural schematic diagram in c-type wire clamp scene；
Fig. 3 is the structural schematic diagram of parallel groove clamp；
Fig. 4 is that the present invention applies the structural schematic diagram on parallel groove clamp；
Fig. 5 is the structural schematic diagram of present invention application on the transformer；
Fig. 6 is that the present invention applies the structural schematic diagram on overhead bare conductor.
Specific implementation mode
A kind of protection packaging material for controller switching equipment, including base material and the adhesive for being coated in the arbitrary one side of the base material, institute
Base material is stated to be made of butyl rubber, modified epoxy and curing agent, the butyl rubber, modified epoxy, curing agent and
The weight percent dosage of adhesive is：Butyl rubber 70-75%, modified epoxy 5-15%, curing agent 10-15%, glue
Stick 5%, butyl rubber has the performances such as heat-resisting, resistance to ozone, ageing-resistant, chemical-resistant resistance, and has good shock-absorbing and electricity exhausted
Edge performance has good repellence to sunlight and ozone, can be exposed in animal or plant oil or oxidable chemicals；Change
Property epoxy resin the advantages of remaining epoxy resin, while the shortcomings that avoid epoxy resin, there is durability, ageing resistance, resistance to
The excellent performances such as fiery performance.The present invention has selected butyl rubber as main material, has ageing-resistant, heat-resisting, corrosion-resistant, insulating properties
The excellent excellent performance of energy；Include butyl rubber and modified epoxy in the base material of the present invention, two kinds of materials are by can be with
The latent curing agent that modified epoxy crosslinks reaction mutually merges, and forms integrated waterproof insulating layer.
Preferably, the thickness of the base material is 1.65mm.The packaging material is in band-like.
Preferably, the curing agent is to stablize at 30 DEG C or less, can be crosslinked with modified epoxy at 120 DEG C or more
The latent curing agent of reaction.
Preferably, the modified epoxy is the addition product of elastomer-modified bisphenol A-type solid epoxy, its viscosity
Low, intoxicated time property is good, excellent electrical property.
Butyl rubber in embodiment 1 to 3, modified epoxy, the weight percent dosage of curing agent and adhesive are as follows：
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| Butyl rubber | 70% | 71% | 72% |
| Modified epoxy | 10% | 9% | 8% |
| Curing agent | 15% | 15% | 15% |
| Adhesive | 5% | 5% | 5% |
Protection packaging material (including embodiment 1 to 3) attainable properties of product of the present invention for controller switching equipment, can
Referring to list 1：
1 properties of product list of table
Packaging material described in embodiment 1 to 3 can be applied once in scene：
Application scenarios 1：Shown in referring to Fig. 1 and Fig. 2, controller switching equipment includes electric armour clamp, and the electric armour clamp is to connect gold
C-type wire clamp 200 in tool, it is convenient that the sufficiently flexible package c-type wire clamp of band-like 100 reset condition of protection packaging material 200 is constructed, automatic solid
Have certain mechanical protection performance after change, can not have to additionally plus protective coat, initial stage adhesive performance and releasable energy are good
Good, fitting followability is good, and hot setting can be repaired, and single material can meet application requirement, is easy to use, imparted energy
Excellent, high-low temperature resistant is high voltage withstanding, waterproof fireproofing, adapts to outdoor environment, protection 100 material of packaging material is uniform, and insulation performance is by people
It is small to influence, volatile ingredient is free of, it is harmless to environment and human body, when carrying out insulating processing to c-type wire clamp 200, protection packet
Material 100 can not influence residential electricity consumption, social influence is small with livewire work without being laid with insulated conductor.
Application scenarios 2：Shown in Fig. 3 and Fig. 4, controller switching equipment includes electric armour clamp, and the electric armour clamp is to connect gold
Parallel groove clamp 300 in tool, 300 structure of the parallel groove clamp is more more irregular than c-type wire clamp 200, since protection packaging material 100 is former
Beginning state is sufficiently flexible, has good adhesion and adhesive force to metal, therefore applying can be well in 300 wire clamp of parallel groove clamp
It attaches.
Application scenarios 3：Shown in Figure 5, controller switching equipment includes transformer 400 and suspended insulated guide wire, and overhead insulating is led
Line is connect by wire jumper with transformer 400, and tie point is exposed in air, and protection packaging material 100 has good adhesion and attachment
Power, therefore realization insulating can be attached well in irregular metal connection point position by applying.
Application scenarios 4：Shown in Figure 6, controller switching equipment includes overhead bare conductor 500, and the overhead bare conductor 500 is from building
Room and trees are too close, and safe distance not enough has security risk, in overhead bare conductor 500 close to building and the wrapped guarantor of trees section
Packaging material 100 is protected, insulating protection is played.
A kind of protection packaging material for controller switching equipment that above-described embodiment only is used for further illustrating the present invention, but the present invention
It is not limited to embodiment, it is every according to the technical essence of the invention to any simple modification made by above example, equivalent
Variation and modification, each fall in the protection domain of technical solution of the present invention.
Claims (7)
1. a kind of protection packaging material for controller switching equipment, it is characterised in that：Including base material and it is coated in the arbitrary one side of the base material
Adhesive, the base material are made of butyl rubber, modified epoxy and curing agent, the butyl rubber, modified epoxy,
The weight percent dosage of curing agent and adhesive is：Butyl rubber 70-75%, modified epoxy 5-15%, curing agent 10-
15%, adhesive 5%.
2. a kind of protection packaging material for controller switching equipment according to claim 1, it is characterised in that：The thickness of the base material
It is 1.65mm.
3. a kind of protection packaging material for controller switching equipment according to claim 1, it is characterised in that：The controller switching equipment packet
Include conducting wire and electric armour clamp.
4. a kind of protection packaging material for controller switching equipment according to claim 3, it is characterised in that：The electric armour clamp is
To the splicing fitting connected between conducting wire.
5. according to a kind of protection packaging material for controller switching equipment described in claim 1, it is characterised in that：The modified epoxy
For the addition product of elastomer-modified bisphenol A-type solid epoxy.
6. according to a kind of protection packaging material for controller switching equipment described in claim 1, it is characterised in that：The curing agent is 30
DEG C or less stablize, at 120 DEG C or more can crosslink the latent curing agent reacted with modified epoxy.
7. according to a kind of protection packaging material for controller switching equipment described in claim 1, it is characterised in that：The packaging material is in band-like.