CN108611723A - A kind of highway barrier ribbon and its method of manufacturing technology - Google Patents
A kind of highway barrier ribbon and its method of manufacturing technology Download PDFInfo
- Publication number
- CN108611723A CN108611723A CN201611124949.8A CN201611124949A CN108611723A CN 108611723 A CN108611723 A CN 108611723A CN 201611124949 A CN201611124949 A CN 201611124949A CN 108611723 A CN108611723 A CN 108611723A
- Authority
- CN
- China
- Prior art keywords
- manufacturing technology
- highway barrier
- weft yarn
- ribbon
- band
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Include the band body formed by warp thread and weft yarns the invention discloses a kind of highway barrier ribbon and its method of manufacturing technology, the weft yarn is laterally extended from the side of band to side, the warp thread intermesh respectively with weft yarn along the longitudinal direction of weft yarn to be formed it is netted；The present invention has the characteristics that high intensity, low elongation; revolutionary flexible protective; mainly for the security performance of road guard-rail; the crashworthiness of guardrail, the steering capability of guardrail, the primary protections index such as maximum dynamic deformation amount are promoted; and entire production process environmental protection; low energy consumption, it is at low cost, it is suitble to promote the use of.
Description
Technical field
The present invention relates to a kind of highway barrier ribbon and its method of manufacturing technology.
Background technology
Existing flexibility highway barrier ribbon is to be in the market vacancy, low to extend (fracture since highway barrier desired strength is high
Elongation percentage≤10%).Only there are two types of polyester industrial yarn and nylon yarns in the world for the material of production high intensity ribbon.But nylon
Elongation percentage is more than 20% so can not be applied in highway barrier field.The elongation percentage of polyester industrial yarn compares and connects in 13%-14%
Nearly highway barrier technical indicator, but existing ribbon technical disadvantages can not reduce ribbon finished product and keep that polyester industrial yarn is original to be prolonged
The rate of stretching also is difficult to weave the thickness that highway barrier of the thickness more than 6.5mm needs.
Invention content
That technical problem to be solved by the invention is to provide a kind of intensity is high, elongation percentage is low, and rupture strength is high, production technology
Environmental protection, highway barrier ribbon at low cost and its method of manufacturing technology.
The present invention is achieved through the following technical solutions：A kind of highway barrier ribbon and its method of manufacturing technology, packet
The band body formed by warp thread and weft yarns is included, the weft yarn is laterally extended from the side of band to side, and the warp thread is along weft yarn
Longitudinal direction intermesh respectively with weft yarn to be formed it is netted.
Preferably, the weft yarn is combined by the first monofilament lines and multiply monofilament lines, combined by multiply monofilament lines
Around weft yarn is made, considerably increases the anti-intensity of ribbon and reduce the elongation percentage of ribbon.
Preferably, the with body surface is equipped with layer protecting film, the abrasionproof of ribbon can be increased by protective film effect,
Prolong the service life.
Preferably, its method of manufacturing technology includes the following steps：
(1) prepare pet material.
(2) plastic extrusion machine host is added in this material to be then shaped into secondly respectively by warping, upper guide frame, weaving
Band body.
(3) to proembryo ribbon carry out high temperature and pressure sizing, temperature can be 200 ° -210 ° between.
(4) it is reticulated by technologies braidings such as latitude needle, brown frames after the band body shaping after making, ensures thousands of lists
The width of the tension that silk is consistent, embryo ribbon is 120mm, thickness 6.5mm.
(5) again by tensile test, it is qualification that rupture strength, which is more than 370KN,.
(6) package test, manufacture sale.
Preferably, between a diameter of 0.05-0.30mm per one monofilament.
Preferably, the protective film is pvc material, its advantage is that being not easy by acid, caustic corrosion；It is more resistance to heat
By.
The beneficial effects of the invention are as follows：The present invention has the characteristics that high intensity, low elongation, revolutionary flexible protective,
Mainly for the security performance of road guard-rail, the crashworthiness of guardrail, the steering capability of guardrail, the master such as maximum dynamic deformation amount
Index is protected to be promoted, and entire production process environmental protection, low energy consumption is at low cost, is suitble to promote the use of.
Specific implementation mode
A kind of highway barrier ribbon and its method of manufacturing technology of the present invention includes the band formed by warp thread and weft yarns
Body, the weft yarn are laterally extended from the side of band to side, and the warp thread intermeshes with weft yarn shape respectively along the longitudinal direction of weft yarn
It reticulates.
Wherein, the weft yarn is combined by the first monofilament lines and multiply monofilament lines, is combined and is surrounded by multiply monofilament lines
Weft yarn is made, considerably increase the anti-intensity of ribbon and reduces the elongation percentage of ribbon；The with body surface is equipped with one layer of protection
Film can increase the abrasionproof of ribbon by protective film effect, prolong the service life.
Its method of manufacturing technology includes the following steps：
(1) prepare pet material.
(2) plastic extrusion machine host is added in this material to be then shaped into secondly respectively by warping, upper guide frame, weaving
Band body.
(3) to proembryo ribbon carry out high temperature and pressure sizing, temperature can be 200 ° -210 ° between.
(4) it is reticulated by technologies braidings such as latitude needle, brown frames after the band body shaping after making, ensures thousands of lists
The width of the tension that silk is consistent, embryo ribbon is 120mm, thickness 6.5mm.
(5) again by tensile test, it is qualification that rupture strength, which is more than 370KN,.
(6) package test, manufacture sale.
Between a diameter of 0.05-0.30mm per one monofilament.
The protective film is pvc material, its advantage is that being not easy by acid, caustic corrosion；Heat is relatively resistant to.
The beneficial effects of the invention are as follows：The present invention has the characteristics that high intensity, low elongation, revolutionary flexible protective,
Mainly for the security performance of road guard-rail, the crashworthiness of guardrail, the steering capability of guardrail, the master such as maximum dynamic deformation amount
Index is protected to be promoted, and entire production process environmental protection, low energy consumption is at low cost, is suitble to promote the use of.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
The change or replacement expected without creative work, should be covered by the protection scope of the present invention.Therefore, of the invention
Protection domain should be determined by the scope of protection defined in the claims.
Claims (6)
1. a kind of highway barrier ribbon and its method of manufacturing technology, it is characterised in that：Include being formed by warp thread and weft yarns
Band body, the weft yarn are laterally extended from the side of band to side, and the warp thread intermeshes with weft yarn respectively along the longitudinal direction of weft yarn
It is formed netted.
2. highway barrier ribbon according to claim 1 and its method of manufacturing technology, it is characterised in that：The weft yarn is by
One monofilament lines are combined into multiply monofilament lines.
3. highway barrier ribbon according to claim 1 and its method of manufacturing technology, it is characterised in that：The with body surface
Equipped with layer protecting film.
4. a kind of highway barrier ribbon and its method of manufacturing technology, method of manufacturing technology include the following steps：
(1) prepare pet material.
(2) plastic extrusion machine host is added in this material and is then shaped into band secondly respectively by warping, upper guide frame, weaving
Body.
(3) to proembryo ribbon carry out high temperature and pressure sizing, temperature can be 200 ° -210 ° between.
(4) it is reticulated by technologies braidings such as latitude needle, brown frames after the band body shaping after making, ensures that thousands of monofilament are protected
Consistent tension is held, the width of embryo ribbon is 120mm, thickness 6.5mm.
(5) again by tensile test, it is qualification that rupture strength, which is more than 370KN,.
(6) package test, manufacture sale.
5. highway barrier ribbon according to claim 1 or 2 and its method of manufacturing technology, it is characterised in that：It is described each
Between a diameter of 0.05-0.30mm of stock monofilament.
6. highway barrier ribbon according to claim 3 and its method of manufacturing technology, it is characterised in that：The protective film is
Pvc material.