CN207432901U - Air cushion foam material - Google Patents
Air cushion foam material Download PDFInfo
- Publication number
- CN207432901U CN207432901U CN201721288965.0U CN201721288965U CN207432901U CN 207432901 U CN207432901 U CN 207432901U CN 201721288965 U CN201721288965 U CN 201721288965U CN 207432901 U CN207432901 U CN 207432901U
- Authority
- CN
- China
- Prior art keywords
- layer
- cloth
- bubble
- air cushion
- foam material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of air cushion foam materials, including bubble film layer, the first layer of cloth is equipped with above bubble film layer, pearl cotton layer is equipped with above first layer of cloth, pearl cotton layer top is equipped with face mask layer, the second layer of cloth is equipped with below bubble film layer, the first aluminium plating membrane is arranged below in second layer of cloth, face mask layer has rough outer surface, first layer of cloth and the second layer of cloth are formed by warp thread and weft yarns, the grammes per square metre of first layer of cloth and the second layer of cloth is 30~40g/ ㎡, bubble film layer is two-layer composite, two layers of bubble film layer is bonded by adhesive layer, 3~5cm is spaced in the warp thread and weft yarn of first layer of cloth or/and the second layer of cloth and is provided with reinforcement yarn, reinforcement yarn is bundled yarn or nylon yarn.Two layers of aluminium plating membrane can be used citicall limited aluminium film, and bubble cushion is rational in infrastructure in the utility model, and the good barrier property of the bubble cushion, skid resistance is good, and high flame retardant, tear resistance be good and high resiliency etc., have well that comprehensive performance, using effect are good.
Description
Technical field
The utility model is related to a kind of air cushion foam materials, and in particular to a kind of air cushion foam material.
Background technology
Bubble chamber film is using polyethylene from high pressure process as primary raw material, then adds the auxiliary materials such as brightening agent, opening agent, through 230 degree or so
High temperature basis plastic uptake is the New Plastic Packing Materials that a kind of quality is light, the transparency is good, nontoxic into the product of bubble, can be right
Product plays the effects that damp proof, buffering and heat preservation.The prior art in above-mentioned polyethylene film raw material by adding in different add
Add agent that can manufacture the special bubble chamber film for possessing different performance, as antistatic plays vacuolar membrane, can play and prevents electrostatic again
It can play and buffer shockproof effect.However the synthesis performance of existing bubble chamber film still shows generally, therefore its structure is also
In the presence of can improvements.
Utility model content
In this regard, the utility model is intended to provide a kind of air cushion foam material rational in infrastructure, the tear-proof of the bubble cushion material
Intensity is high, and elastic buffer and excellent to light barriering effect, and use as packaging material has good using effect.
Realizing the technical solution of the utility model aim is:
A kind of air cushion foam material including bubble film layer, is equipped with the first layer of cloth, first layer of cloth above the bubble film layer
The upper surface of be equipped with pearl cotton layer, the pearl cotton layer top is equipped with face mask layer, and the second layer of cloth is equipped with below the bubble film layer,
The first aluminium plating membrane is equipped with below second layer of cloth, the face mask layer has rough outer surface, first cloth
Layer and second layer of cloth are formed by warp thread and weft yarns, the grammes per square metre of first layer of cloth and second layer of cloth for 30~
40g/ ㎡, the bubble film layer are two-layer composite, and two layers of bubble film layer is bonded by adhesive layer, and in two bubble film layers
Bubble is towards the adhesive layer, and 3~5cm of interval is set in the warp thread and weft yarn of first layer of cloth or/and second layer of cloth
It is equipped with reinforcement yarn.
In above-mentioned technical proposal, bubble height is 5-10mm, bubble diameter 8-15mm in the bubble film layer.
In above-mentioned technical proposal, the surface of first layer of cloth or/and second layer of cloth is equipped with anti-flaming dope layer.
In above-mentioned technical proposal, above the pearl cotton layer and the face mask layer forms latticed dent.
In above-mentioned technical proposal, the thickness ratio of each bubble film layer and the pearl cotton layer is 1~1.5:1.
In above-mentioned technical proposal, the face mask layer is structure of composite membrane, including the second aluminium plating membrane, arranged on described second
Ink layer outside aluminium plating membrane and the transparent film layer on the ink layer, second aluminium plating membrane connect with pearl cotton layer
It connects.
In above-mentioned technical proposal, first aluminium plating membrane and the second aluminium plating membrane are using BOPP aluminizers, the BOPP
The thickness of aluminizer is 15~25um.
In above-mentioned technical proposal, the reinforcement yarn is bundled yarn either nylon yarn or glass wire.
The utility model has positive effect:Bubble film layer in the utility model has two layers, and adds pearl cotton layer
It thereby may be ensured that the elasticity of material, while the setting of the first aluminium plating membrane, effectively enhance barriering effect of the product to light,
Add in first layer of cloth and the second layer of cloth on the basis of this in material again, so as to effectively enhance the tearing toughness of material,
There is good using effect when this air cushion foam material in the utility model is used as packaging material.
Description of the drawings
Fig. 1 is the sectional view of bubble cushion material in the utility model;
Fig. 2 is the top view of bubble cushion material in the utility model;
Fig. 3 is the sectional view of face mask layer in the utility model.
Reference numeral is shown in figure:1- bubble film layers;The first layer of cloths of 2-;3- pearl cotton layers;The second layer of cloths of 4-;5- first
Aluminium plating membrane;6- face mask layers;The second aluminium plating membranes of 61-;62- ink layers;63- transparent film layers;7- dents;8- adhesive layers.
Specific embodiment
The concrete structure in the utility model is done with explanation with reference to Figure of description:
A kind of air cushion foam material, as shown in Figure 1, including including bubble film layer 1, the bubble film layer 1 is equipped with first above
Layer of cloth 2, described first layer of cloth 2 the upper surface of are equipped with pearl cotton layer 3, and 3 top of pearl cotton layer is equipped with face mask layer 6, the bubble
The second layer of cloth 4 is equipped with below film layer 1, the first aluminium plating membrane 5, first aluminizer are equipped with below second layer of cloth 4
5 and second aluminium plating membrane of layer can be used BOPP aluminizers, and the thickness of the BOPP aluminizers is 15~25um, BOPP aluminizers with
BOPP film aluminizes to be formed by one or both sides for base material, the aluminizer have high tensile, impact strength, rigidity and by force
Toughness, therefore with good performance, the face mask layer 6 is with rough outer surface, first layer of cloth 2 and institute
It states the second layer of cloth 4 to be formed by warp thread and weft yarns, terylene or polypropylene fibre, first layer of cloth 2 can be used in the warp thread and weft yarn
And the grammes per square metre of second layer of cloth 4 is 30~40g/ ㎡, the bubble film layer 1 is two-layer composite, and two layers of bubble film layer 1 is logical
Cross adhesive layer bonding, and the bubble in two bubble film layers 1 is towards the adhesive layer 8, first layer of cloth 2 or/and described the
3~5cm is spaced in the warp thread and weft yarn of two layer of cloths 4 and is provided with reinforcement yarn, the reinforcement yarn is bundled yarn or nylon yarn
Line or glass wire, bubble film layer has two layers in the present embodiment, and adds the bullet that pearl cotton layer thereby may be ensured that material
Property, while the setting of the first aluminium plating membrane 5, barriering effect of the product to light is effectively enhanced, then is added on the basis of this in material
Enter first layer of cloth 2 and the second layer of cloth 4, so as to effectively enhance the tearing toughness of material, this in the utility model
Kind air cushion foam material has good using effect when being used as packaging material.
In the present embodiment, bubble height is 5~10mm in the bubble film layer 1, and bubble diameter is 8~15mm, further,
The height of the bubble may be configured as 8mm, a diameter of 15mm.
Further, a cloth layer surface in first layer of cloth 2 and second layer of cloth 4 sets anti-flaming dope layer,
Or anti-flaming dope layer is respectively provided on the surface of the first layer of cloth 2 and the second layer of cloth 4, it can be enhanced by the setting of anti-flaming dope layer
The flame retardant property of material.
In the present embodiment, referring to described in Fig. 2, the pearl cotton layer 3 above and the face mask layer 6 form it is latticed recessed
Trace 7, dent 7 formed after on face mask layer formed rectangular array arrangement protrusion, production when by grid roller squeeze so as to
The dent is generated, the presence of dent 7 makes the outer surface of face mask layer 6 become uneven, and then can reinforcing material when using
Antiskid effect.
Further, each bubble film layer 1 and the thickness ratio of the pearl cotton layer 3 are 1~1.5:1.
Referring to described in Fig. 3, the face mask layer 6 in the present embodiment is structure of composite membrane, including the second aluminium plating membrane 61,
Ink layer 62 arranged on 61 outside of the second aluminium plating membrane and the transparent film layer 63 on the ink layer 62, second aluminizes
Film layer 61 is connected with pearl cotton layer 3, and material can be improved by adding in the second aluminium plating membrane 61 in face mask layer in the present embodiment
Barrier property, further by transparent film layer by be used as pattern ink layer 62 covering can to ink layer formed protect, so as to
Largely playing prevents the phenomenon that fades.
Obviously, above-described embodiment of the utility model is only intended to clearly illustrate the utility model example, and
It is not the restriction to the embodiment of the utility model.For those of ordinary skill in the art, in above description
On the basis of can also make other variations or changes in different ways.There is no need and unable to give all embodiments
It is exhaustive.And the obvious changes or variations that these connotations for belonging to the utility model are extended out still falls within this practicality
New protection domain.
Claims (8)
1. a kind of air cushion foam material, which is characterized in that including bubble film layer (1), the bubble film layer (1) is equipped with the first cloth above
Layer (2), described first layer of cloth (2) the upper surface of are equipped with pearl cotton layer (3), and pearl cotton layer (3) top is equipped with face mask layer (6),
The second layer of cloth (4) is equipped with below the bubble film layer (1), the first aluminium plating membrane is equipped with below second layer of cloth (4)
(5), the face mask layer (6) has rough outer surface, and first layer of cloth (2) and second layer of cloth (4) are by warp thread
It is formed with weft yarns, the grammes per square metre of first layer of cloth (2) and second layer of cloth (4) is 30~40g/ ㎡, the bubble chamber film
Layer (1) is two-layer composite, and two layers of bubble film layer (1) is bonded by adhesive layer, and the equal court of bubble in two bubble film layers (1)
To the adhesive layer (8), the bubble on two layers of bubble film layer (1) is oppositely arranged, first layer of cloth (2) or/and described second
3~5cm is spaced in the warp thread and weft yarn of layer of cloth (4) and is provided with reinforcement yarn.
2. air cushion foam material according to claim 1, which is characterized in that bubble height is 5- on the bubble film layer (1)
10mm, bubble diameter 8-15mm.
3. air cushion foam material according to claim 2, which is characterized in that first layer of cloth (2) or/and second cloth
The surface of layer (4) is equipped with anti-flaming dope layer.
4. air cushion foam material according to any one of claim 1 to 3, which is characterized in that the pearl cotton layer (3) is above
And the face mask layer (6) forms latticed dent (7).
5. air cushion foam material according to claim 1, which is characterized in that each bubble film layer (1) and the pearl cotton layer (3)
Thickness ratio be 1~1.5:1.
6. air cushion foam material according to claim 1, which is characterized in that the face mask layer (6) is structure of composite membrane, is wrapped
Include the second aluminium plating membrane (61), the ink layer (62) outside second aluminium plating membrane (61) and arranged on the ink layer
(62) transparent film layer (63) on, the second aluminium plating membrane (61) are connected with pearl cotton layer (3).
7. air cushion foam material according to claim 6, which is characterized in that first aluminium plating membrane (5) and second is aluminized
Film layer (61) uses BOPP aluminizers, and the thickness of the BOPP aluminizers is 15~25um.
8. air cushion foam material according to claim 1, which is characterized in that the reinforcement yarn is bundled yarn or nylon yarn
Line or glass wire.