CN108611645A - A kind of aluminium frame mould scavenger specially and preparation method thereof - Google Patents
A kind of aluminium frame mould scavenger specially and preparation method thereof Download PDFInfo
- Publication number
- CN108611645A CN108611645A CN201810349219.0A CN201810349219A CN108611645A CN 108611645 A CN108611645 A CN 108611645A CN 201810349219 A CN201810349219 A CN 201810349219A CN 108611645 A CN108611645 A CN 108611645A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium frame
- frame mould
- acid
- scavenger specially
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of aluminium frame mould scavenger speciallies, include the raw material of following parts by weight：15~25 parts of isopropanol, 8~14 parts of sodium metasilicate, 6~13 parts of Cocoamidopropyl betaine, 7~12 parts of alkylbenzene sulfonate, 10~20 parts of stearic acid triethanolamine ester quaternary, 15~30 parts of organic acid, 4~9 parts of aliphatic amine polyoxyethylene ether, 2~6 parts of silica, 7~11 parts of lauryl sodium sulfate, 3~5 parts of enuatrol, 8~14 parts of glycerine, 30~40 parts of softened water, 6~12 parts of modified meerschaum powder, 1~2 part of antifoaming agent, 2~4 parts of lubricant, 1~3 part of fungicide.Aluminium frame mould scavenger specially of the present invention can effectively remove impurity and greasy dirt on aluminium frame surface, substantially increase the cleannes of aluminium frame mould, to improve the quality of aluminium frame obtained.
Description
Technical field
The invention belongs to cleaning agent technical fields, and in particular to a kind of aluminium frame mould scavenger specially and preparation method thereof.
Background technology
Aluminium frame mould generally requires to touch many impurity during preparing aluminium frame, includes not only granule foreign,
Further include the impurity such as some greasy dirts, to bring certain influence to aluminium frame mould, not only influences its using effect, but also
The quality that can influence aluminium frame obtained, to bring certain influence to production.
Therefore it provides a kind of can effectively clean aluminium frame mould, impurity and greasy dirt on its surface are effectively removed, improves and is made
The aluminium frame mould detergent of quality of aluminium frame and preparation method thereof the problem of being urgent need to resolve of the present invention.
Invention content
The present invention provides a kind of aluminium frame mould scavenger speciallies and preparation method thereof, solve asking in background technology
Topic, the aluminium frame mould scavenger specially can effectively remove impurity and greasy dirt on aluminium frame surface, substantially increase aluminium frame mould
Cleannes, to improve the quality of aluminium frame obtained.
It is of the existing technology in order to solve the problems, such as, it adopts the following technical scheme that：
A kind of aluminium frame mould scavenger specially, includes the raw material of following parts by weight：15~25 parts of isopropanol, 8~14 parts of sodium metasilicate,
6~13 parts of Cocoamidopropyl betaine, 7~12 parts of alkylbenzene sulfonate, 10~20 parts of stearic acid triethanolamine ester quaternary,
15~30 parts of organic acid, 4~9 parts of aliphatic amine polyoxyethylene ether, 2~6 parts of silica, 7~11 parts of lauryl sodium sulfate, oil
3~5 parts of sour sodium, 8~14 parts of glycerine, 30~40 parts of softened water, 6~12 parts of modified meerschaum powder, 1~2 part of antifoaming agent, lubricant
2~4 parts, 1~3 part of fungicide.
Preferably, the aluminium frame mould scavenger specially, includes the raw material of following parts by weight：18~22 parts of isopropanol, silicon
9~13 parts of sour sodium, 7~10 parts of Cocoamidopropyl betaine, 9~11 parts of alkylbenzene sulfonate, Triethanolamine Esters of Stearic Acid season
12~16 parts of ammonium salt, 20~25 parts of organic acid, 5~7 parts of aliphatic amine polyoxyethylene ether, 3~5 parts of silica, dodecyl sulphur
8~10 parts of sour sodium, 3.5~4.2 parts of enuatrol, 9~13 parts of glycerine, 34~38 parts of softened water, 9~11 parts of modified meerschaum powder,
1.2~1.8 parts of antifoaming agent, 2.5~3.6 parts of lubricant, 1.4~2.2 parts of fungicide.
Preferably, the aluminium frame mould scavenger specially, includes the raw material of following parts by weight：20 parts of isopropanol, sodium metasilicate
11 parts, 8 parts of Cocoamidopropyl betaine, 10 parts of alkylbenzene sulfonate, 14 parts of stearic acid triethanolamine ester quaternary, organic acid
23 parts, 6 parts of aliphatic amine polyoxyethylene ether, 4 parts of silica, 9 parts of lauryl sodium sulfate, 3.8 parts of enuatrol, 12 parts of glycerine,
35 parts of softened water, 10 parts of modified meerschaum powder, 1.7 parts of antifoaming agent, 3.2 parts of lubricant, 1.9 parts of fungicide.
Preferably, the preparation method of the modified meerschaum powder is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 120~220 DEG C stir 1~3
Hour, it filters, dry, pulverize at 120 DEG C and obtain hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
Preferably, the organic acid is any one of citric acid, oxalic acid.
Preferably, it is Polyether Modified Polysiloxanes Defoaming Agent to state antifoaming agent.
A method of the aluminium frame mould scavenger specially is prepared, is included the following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 50~70 DEG C, then sequentially adds glycerine, isopropanol, coconut oleoyl amine third
Base glycine betaine, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether, side are added
Side is stirred, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 30~40 DEG C, then sequentially adds sodium metasilicate, silica, dodecane
Base sodium sulphate, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in the dispersion of high speed dispersor high speed
Processing, then it is placed in microwave treatment in microwave environment, 1~2 hour is stood to get the aluminium frame mould scavenger specially.
Preferably, the step（3）The time of high speed decentralized processing is 10~20 minutes, and the time of microwave treatment is 30
~60 seconds.
Compared with prior art, the present invention it has the advantages that：
Aluminium frame mould scavenger specially of the present invention can effectively remove impurity and greasy dirt on aluminium frame surface, substantially increase aluminium
The cleannes of frame mould, it is specific as follows to improve the quality of aluminium frame obtained：
（1）Aluminium frame mould scavenger specially of the present invention is using isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkyl
Benzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid, aliphatic amine polyoxyethylene ether, silica, dodecyl sulphate
Sodium, enuatrol, glycerine, softened water, modified meerschaum powder, antifoaming agent, lubricant, fungicide etc. are used as raw material, various components pair
It is environmental-friendly, it mutually acts synergistically between component, product obtained has stronger clean effect, and stability is strong, can make metal
It is bright；
（2）The modified meerschaum powder added in the present invention easily generates preferable hydrophily in cleaned body surface, and hydrophily carries
High soil release performance, grease proofing diffusion resistance and oiliness is removed, after having water droplet to body surface, due to the surface property of modified meerschaum
Cause to form water membrane on surface, when moisture film moves, since the effect of surface tension causes the pollutant of object plane to remove therewith
It goes, has good effect to the surface cleaning of aluminium frame；
（3）It is added to fungicide in the present invention, can inhibit the growth of bacterium, bactericidal effect is good, improves the work of staff
Environmental quality.
Specific implementation mode
Present invention will be further explained below with reference to specific examples.These embodiments are merely to illustrate the present invention and do not have to
In limiting the scope of the invention.
Embodiment 1
The present embodiment is related to a kind of aluminium frame mould scavenger specially, includes the raw material of following parts by weight：15 parts of isopropanol, sodium metasilicate
8 parts, 6 parts of Cocoamidopropyl betaine, 7 parts of alkylbenzene sulfonate, 10 parts of stearic acid triethanolamine ester quaternary, organic acid 15
Part, 4 parts of aliphatic amine polyoxyethylene ether, 2 parts of silica, 7 parts of lauryl sodium sulfate, 3 parts of enuatrol, 8 parts of glycerine, softened water
30 parts, 6 parts of modified meerschaum powder, 1 part of antifoaming agent, 2 parts of lubricant, 1 part of fungicide.
Wherein, the preparation method of the modified meerschaum powder is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 120 DEG C stir 1 hour, take out
Filter, dry, pulverize at 120 DEG C and obtains hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
Wherein, the organic acid is citric acid.
Wherein, it is Polyether Modified Polysiloxanes Defoaming Agent to state antifoaming agent.
A method of the aluminium frame mould scavenger specially is prepared, is included the following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 50 DEG C, then sequentially adds glycerine, isopropanol, cocamidopropyl propyl amide sweet tea
Dish alkali, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether are stirred when being added
It mixes, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 30 DEG C, then sequentially adds sodium metasilicate, silica, dodecyl sulphur
Sour sodium, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in high speed dispersor high speed decentralized processing,
It is placed in microwave treatment in microwave environment again, stands 1 hour to get the aluminium frame mould scavenger specially.
Wherein, the step（3）The time of high speed decentralized processing is 10 minutes, and the time of microwave treatment is 30 seconds.
Embodiment 2
The present embodiment is related to a kind of aluminium frame mould scavenger specially, includes the raw material of following parts by weight：25 parts of isopropanol, sodium metasilicate
14 parts, it is 13 parts of Cocoamidopropyl betaine, 12 parts of alkylbenzene sulfonate, 20 parts of stearic acid triethanolamine ester quaternary, organic
Acid 30 parts, 9 parts of aliphatic amine polyoxyethylene ether, 6 parts of silica, 11 parts of lauryl sodium sulfate, 5 parts of enuatrol, 14 parts of glycerine,
40 parts of softened water, 12 parts of modified meerschaum powder, 2 parts of antifoaming agent, 4 parts of lubricant, 3 parts of fungicide.
Wherein, the preparation method of the modified meerschaum powder is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 220 DEG C stir 3 hours, take out
Filter, dry, pulverize at 120 DEG C and obtains hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
Wherein, the organic acid is oxalic acid.
Wherein, it is Polyether Modified Polysiloxanes Defoaming Agent to state antifoaming agent.
A method of the aluminium frame mould scavenger specially is prepared, is included the following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 70 DEG C, then sequentially adds glycerine, isopropanol, cocamidopropyl propyl amide sweet tea
Dish alkali, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether are stirred when being added
It mixes, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 40 DEG C, then sequentially adds sodium metasilicate, silica, dodecyl sulphur
Sour sodium, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in high speed dispersor high speed decentralized processing,
It is placed in microwave treatment in microwave environment again, stands 2 hours to get the aluminium frame mould scavenger specially.
Wherein, the step（3）The time of high speed decentralized processing is 20 minutes, and the time of microwave treatment is 60 seconds.
Embodiment 3
The present embodiment is related to a kind of aluminium frame mould scavenger specially, includes the raw material of following parts by weight：18 parts of isopropanol, sodium metasilicate
9 parts, 7 parts of Cocoamidopropyl betaine, 9 parts of alkylbenzene sulfonate, 12 parts of stearic acid triethanolamine ester quaternary, organic acid 20
Part, 5 parts of aliphatic amine polyoxyethylene ether, 3 parts of silica, 8 parts of lauryl sodium sulfate, 3.5 parts of enuatrol, 9 parts of glycerine, softening
34 parts of water, 9 parts of modified meerschaum powder, 1.2 parts of antifoaming agent, 2.5 parts of lubricant, 1.4 parts of fungicide.
Wherein, the preparation method of the modified meerschaum powder is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 150 DEG C stir 1.5 hours,
It filters, dry, pulverize at 120 DEG C and obtain hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
Wherein, the organic acid is citric acid.
Wherein, it is Polyether Modified Polysiloxanes Defoaming Agent to state antifoaming agent.
A method of the aluminium frame mould scavenger specially is prepared, is included the following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 55 DEG C, then sequentially adds glycerine, isopropanol, cocamidopropyl propyl amide sweet tea
Dish alkali, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether are stirred when being added
It mixes, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 32 DEG C, then sequentially adds sodium metasilicate, silica, dodecyl sulphur
Sour sodium, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in high speed dispersor high speed decentralized processing,
It is placed in microwave treatment in microwave environment again, stands 1.2 hours to get the aluminium frame mould scavenger specially.
Wherein, the step（3）The time of high speed decentralized processing is 13 minutes, and the time of microwave treatment is 40 seconds.
Embodiment 4
The present embodiment is related to a kind of aluminium frame mould scavenger specially, includes the raw material of following parts by weight：22 parts of isopropanol, sodium metasilicate
13 parts, it is 10 parts of Cocoamidopropyl betaine, 11 parts of alkylbenzene sulfonate, 16 parts of stearic acid triethanolamine ester quaternary, organic
25 parts of acid, 7 parts of aliphatic amine polyoxyethylene ether, 5 parts of silica, 10 parts of lauryl sodium sulfate, 4.2 parts of enuatrol, glycerine 13
Part, 38 parts of softened water, 11 parts of modified meerschaum powder, 1.8 parts of antifoaming agent, 3.6 parts of lubricant, 2.2 parts of fungicide.
Wherein, the preparation method of the modified meerschaum powder is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 180 DEG C stir 2 hours, take out
Filter, dry, pulverize at 120 DEG C and obtains hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
Wherein, the organic acid is citric acid.
Wherein, it is Polyether Modified Polysiloxanes Defoaming Agent to state antifoaming agent.
A method of the aluminium frame mould scavenger specially is prepared, is included the following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 60 DEG C, then sequentially adds glycerine, isopropanol, cocamidopropyl propyl amide sweet tea
Dish alkali, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether are stirred when being added
It mixes, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 35 DEG C, then sequentially adds sodium metasilicate, silica, dodecyl sulphur
Sour sodium, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in high speed dispersor high speed decentralized processing,
It is placed in microwave treatment in microwave environment again, stands 1.5 hours to get the aluminium frame mould scavenger specially.
Wherein, the step（3）The time of high speed decentralized processing is 15 minutes, and the time of microwave treatment is 45 seconds.
Embodiment 5
The present embodiment is related to a kind of aluminium frame mould scavenger specially, includes the raw material of following parts by weight：20 parts of isopropanol, sodium metasilicate
11 parts, 8 parts of Cocoamidopropyl betaine, 10 parts of alkylbenzene sulfonate, 14 parts of stearic acid triethanolamine ester quaternary, organic acid
23 parts, 6 parts of aliphatic amine polyoxyethylene ether, 4 parts of silica, 9 parts of lauryl sodium sulfate, 3.8 parts of enuatrol, 12 parts of glycerine,
35 parts of softened water, 10 parts of modified meerschaum powder, 1.7 parts of antifoaming agent, 3.2 parts of lubricant, 1.9 parts of fungicide.
Wherein, the preparation method of the modified meerschaum powder is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 200 DEG C stir 2.5 hours, take out
Filter, dry, pulverize at 120 DEG C and obtains hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
Wherein, the organic acid is oxalic acid.
Wherein, it is Polyether Modified Polysiloxanes Defoaming Agent to state antifoaming agent.
A method of the aluminium frame mould scavenger specially is prepared, is included the following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 65 DEG C, then sequentially adds glycerine, isopropanol, cocamidopropyl propyl amide sweet tea
Dish alkali, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether are stirred when being added
It mixes, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 38 DEG C, then sequentially adds sodium metasilicate, silica, dodecyl sulphur
Sour sodium, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in high speed dispersor high speed decentralized processing,
It is placed in microwave treatment in microwave environment again, stands 1.7 hours to get the aluminium frame mould scavenger specially.
Wherein, the step（3）The time of high speed decentralized processing is 17 minutes, and the time of microwave treatment is 50 seconds.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of aluminium frame mould scavenger specially, which is characterized in that include the raw material of following parts by weight：15~25 parts of isopropanol,
8~14 parts of sodium metasilicate, 6~13 parts of Cocoamidopropyl betaine, 7~12 parts of alkylbenzene sulfonate, Triethanolamine Esters of Stearic Acid
10~20 parts of quaternary ammonium salt, 15~30 parts of organic acid, 4~9 parts of aliphatic amine polyoxyethylene ether, 2~6 parts of silica, dodecyl
7~11 parts of sodium sulphate, 8~14 parts of glycerine, 30~40 parts of softened water, 6~12 parts of modified meerschaum powder, disappears at 3~5 parts of enuatrol
1~2 part of infusion, 2~4 parts of lubricant, 1~3 part of fungicide.
2. aluminium frame mould scavenger specially according to claim 1, which is characterized in that include the raw material of following parts by weight：
It is 18~22 parts of isopropanol, 9~13 parts of sodium metasilicate, 7~10 parts of Cocoamidopropyl betaine, 9~11 parts of alkylbenzene sulfonate, hard
12~16 parts of resin acid triethanol amine ester quat, 20~25 parts of organic acid, 5~7 parts of aliphatic amine polyoxyethylene ether, silica 3
~5 parts, it is 8~10 parts of lauryl sodium sulfate, 3.5~4.2 parts of enuatrol, 9~13 parts of glycerine, 34~38 parts of softened water, modified
9~11 parts of sepiolite powder, 1.2~1.8 parts of antifoaming agent, 2.5~3.6 parts of lubricant, 1.4~2.2 parts of fungicide.
3. aluminium frame mould scavenger specially according to claim 1, which is characterized in that include the raw material of following parts by weight：
20 parts of isopropanol, 11 parts of sodium metasilicate, 8 parts of Cocoamidopropyl betaine, 10 parts of alkylbenzene sulfonate, Triethanolamine Esters of Stearic Acid
14 parts of quaternary ammonium salt, 23 parts of organic acid, 6 parts of aliphatic amine polyoxyethylene ether, 4 parts of silica, 9 parts of lauryl sodium sulfate, oleic acid
3.8 parts of sodium, 12 parts of glycerine, 35 parts of softened water, 10 parts of modified meerschaum powder, 1.7 parts of antifoaming agent, 3.2 parts of lubricant, fungicide
1.9 part.
4. aluminium frame mould scavenger specially according to claim 1, which is characterized in that the preparation of the modified meerschaum powder
Method is as follows：
（1）By sepiolite pulverize the last water with 10 times of quality mix be packed into autoclave, in 120~220 DEG C stir 1~3
Hour, it filters, dry, pulverize at 120 DEG C and obtain hydrothermal modification sepiolite；
（2）By step（1）The hydrothermal modification sepiolite of gained and a concentration of 8% hydrochloric acid（Percent by volume）It is added to reaction
Kettle, solid-liquid mass ratio 1: 10, stirring at normal temperature 7 hours filter, and are washed with distilled water in aqueous solution and are free of magnesium ion, gained
Solid matter obtains the modified meerschaum in 120 DEG C of dryings.
5. aluminium frame mould scavenger specially according to claim 1, which is characterized in that the organic acid is citric acid, grass
Any one of acid.
6. aluminium frame mould scavenger specially according to claim 1, which is characterized in that the antifoaming agent has to be polyether-modified
Machine silicon defoaming agent.
7. a kind of method preparing any one of claim 1~6 aluminium frame mould scavenger specially, which is characterized in that including
Following steps：
（1）Isopropanol, sodium metasilicate, Cocoamidopropyl betaine, alkylbenzene sulfonate, stearic triethylenetetraminehexaacetic acid are weighed by above-mentioned formula
Hydramine ester quat, organic acid, aliphatic amine polyoxyethylene ether, silica, lauryl sodium sulfate, enuatrol, glycerine, softening
Water, modified meerschaum powder, antifoaming agent, lubricant, fungicide, it is spare；
（2）Softened water is placed in reaction kettle and is heated to 50~70 DEG C, then sequentially adds glycerine, isopropanol, coconut oleoyl amine third
Base glycine betaine, alkylbenzene sulfonate, stearic acid triethanolamine ester quaternary, organic acid and aliphatic amine polyoxyethylene ether, side are added
Side is stirred, until all dissolution of raw material；
（3）By step（2）The mixed liquor of gained is cooled to 30~40 DEG C, then sequentially adds sodium metasilicate, silica, dodecane
Base sodium sulphate, enuatrol, modified meerschaum powder, antifoaming agent, lubricant, fungicide are first placed in the dispersion of high speed dispersor high speed
Processing, then it is placed in microwave treatment in microwave environment, 1~2 hour is stood to get the aluminium frame mould scavenger specially.
8. preparation method according to claim 7, which is characterized in that the step（3）The time of high speed decentralized processing
It it is 10~20 minutes, the time of microwave treatment is 30~60 seconds.