CN108610850A - Cure liquor and curing to house wall - Google Patents

Cure liquor and curing to house wall Download PDF

Info

Publication number
CN108610850A
CN108610850A CN201810373499.9A CN201810373499A CN108610850A CN 108610850 A CN108610850 A CN 108610850A CN 201810373499 A CN201810373499 A CN 201810373499A CN 108610850 A CN108610850 A CN 108610850A
Authority
CN
China
Prior art keywords
parts
liquor
curing
water
barium sulfate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810373499.9A
Other languages
Chinese (zh)
Inventor
王震
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810373499.9A priority Critical patent/CN108610850A/en
Publication of CN108610850A publication Critical patent/CN108610850A/en
Pending legal-status Critical Current

Abstract

The present invention relates to building decoration area, cures liquor and curing with disclosing a kind of house wall, be characterized in that：Including acrylic resin, antifoaming agent, barium sulfate, acrylic elastic emulsion, binary polymer, hydrogen peroxide, water and modified kaolin, cures liquor with first configuring wall, cure liquor with being reconfigured wall；It covers, is stood in coating layer surface covering film again；It tears film open again and removes covering film after coat drying, solve the solidification liquor prepared in existing construction and there is the problem of higher formaldehyde and other other toxic residuals, need the long period to stand after finishing.

Description

Cure liquor and curing to house wall
Technical field
The present invention relates to building decoration areas, be concretely house wall cure liquor and curing.
Background technology
The house of user's purchase is mostly rough house, needs to carry out building decoration and fitment before normal use, be built for protection The use function and beautifying constructure built the agent structure of object, improve building, using decorating and renovating material or jewelry, to building The various processing that the surfaces externally and internally of object and space carry out.
In house decoration in order to achieve the purpose that good waterproof, counnter attack alkalinity, sealing, moisture-proof, need to metope and Solidification liquor is brushed on ground, then in other construction layers of solidification liquor applied atop, and the solidification liquor prepared in existing construction exists Higher formaldehyde and other toxic other remain, and need the long period to stand after finishing.
Accordingly, it is desirable to provide a kind of low formaldehyde content, it can achieve the purpose that good waterproof, counnter attack alkalinity, sealing, moisture-proof House wall cure liquor and curing.
Invention content
The present invention is directed to the solidification liquor prepared in existing construction and there is higher formaldehyde and other other toxic residuals, dress The problem of needing the long period to stand after repairing cures liquor and curing with providing house wall.
The present invention solves above-mentioned technical problem, the technical solution adopted is that, it includes propylene to cure liquor to a kind of house wall Acid resin, antifoaming agent, barium sulfate, acrylic elastic emulsion, binary polymer, hydrogen peroxide, water and modified kaolin.
Further, by weight, acrylic resin be 30~50 parts, 2~3 parts of antifoaming agent, 5~10 parts of barium sulfate, 20~40 parts of acrylic elastic emulsion, 4~10 parts of binary polymer, hydrogen peroxide 2~3,40~60 parts of water and modified kaolin 30 ~40 parts.
Further, by weight, acrylic resin be 32~38 parts, 2~3 parts of antifoaming agent, 6~9 parts of barium sulfate, third 25~35 parts of olefin(e) acid elastic emulsion, 5~9 parts of binary polymer, hydrogen peroxide 2~3,25~55 parts of water and modified kaolin 32~38 Part.
Further, by weight, acrylic resin be 34~36 parts, 2~3 parts of antifoaming agent, 7~8 parts of barium sulfate, third 28~32 parts of olefin(e) acid elastic emulsion, 6~8 parts of binary polymer, hydrogen peroxide 2~3,30~50 parts of water and modified kaolin 34~36 Part.
Further, by weight, acrylic resin be 35 parts, 3 parts of antifoaming agent, 7 parts of barium sulfate, acrylic acid elasticity breast 35 parts of 30 parts of liquid, 7 parts of binary polymer, hydrogen peroxide 3,40 parts of water and modified kaolin.
The purpose designed in this way is, is combined with binary polymer by acrylic resin so as to cure liquor final Wash-resistant property and ageing-resistant performance are significantly improved, while replacing existing bis-phenol using acrylic resin A formaldehyde epoxy resin, is greatly reduced whole content of formaldehyde so that can shorten time of repose after finishing, solve existing With the presence of the higher formaldehyde of solidification liquor prepared in construction and other other toxic residuals, the long period is needed to stand after finishing The problem of.
The curing for curing liquor the present invention also provides a kind of house wall, includes the following steps：
The first step cures liquor to configuration wall, acrylic resin, antifoaming agent, barium sulfate, acrylic elastic emulsion, binary is gathered It closes object, hydrogen peroxide, water and modified kaolin and is mixed with solidification liquor in proportion；
Second step is brushed, is brushed to metope and ground using the solidification liquor of preparation；
Third walks, covering, is stood in coating layer surface covering film；
4th step tears film open and removes covering film after coat drying.
Further, the first step, by acrylic resin, antifoaming agent, barium sulfate, acrylic elastic emulsion, binary polymer, After hydrogen peroxide, water and modified kaolin mix in proportion, it is stirred 20~40min.
Further, solidification liquor is fallen in ground and metope, is used in combination brush cutter painting to cover uniformly, brushing thickness is by second step 0.5mm~1mm is brushed using bilayer is crisscross.
The purpose designed in this way is, by that can improve solidification liquor entirety mixing uniformity after stirring so that Carrying out follow-up brush can reduce because solidification liquor unevenness leads to local seepage problem.
Moreover solidification liquor can be enable to be carried out with metope or ground tight using the double-deck crisscross brushing when brushing It is closely connected attached.
Finally, dust granules can be reduced by, which being covered on brush using covering film, influences construction in later period operation, rises To certain waterproof, counnter attack alkali, sealing, moisture-proof role, the race sand effect during subsequent construction, live neat and tidy, profit are prevented In cleaning.
Beneficial effects of the present invention are at least following one：
1. being combined by acrylic resin and binary polymer so that curing the final wash-resistant property of liquor and resistance to ag(e)ing It can significantly be improved, while existing bisphenol A formaldehyde epoxy resin is replaced using acrylic resin, substantially be dropped Low entirety content of formaldehyde so that time of repose can be shortened after finishing, solve the solidify liquid prepared in existing construction There is the problem of higher formaldehyde and other other toxic residuals, need the long period to stand after finishing in agent.
2. by the way that solidification liquor entirety mixing uniformity can be improved after stirring so that can carrying out follow-up brush It reduces because solidification liquor unevenness leads to local seepage problem.
3. solidification liquor can be enable to be carried out with metope or ground close using the double-deck crisscross brushing when brushing It attaches.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments to the present invention It is described in further detail.It should be appreciated that specific embodiment described herein is used only for explaining the present invention, it is not used to limit The fixed present invention.
Embodiment 1
Cure to house decoration wall solidification liquor by weight, including acrylic resin is 30 parts, 2 parts of antifoaming agent, barium sulfate 5 Part, 20 parts of acrylic elastic emulsion, 4 parts of binary polymer, hydrogen peroxide 2,40 parts of water and 30 parts of modified kaolin.
Embodiment 2
Cure to house decoration wall solidification liquor by weight, including acrylic resin is 50 parts, 3 parts of antifoaming agent, barium sulfate 40 parts of 10 parts, 40 parts of acrylic elastic emulsion, 10 parts of binary polymer, hydrogen peroxide 3,60 parts of water and modified kaolin.
Embodiment 3
Cure to house decoration wall solidification liquor by weight, including acrylic resin is 35 parts, 3 parts of antifoaming agent, barium sulfate 7 Part, 30 parts of acrylic elastic emulsion, 7 parts of binary polymer, hydrogen peroxide 3,40 parts of water and 35 parts of modified kaolin.
Embodiment 4
Based on embodiment 1, cures to house wall the curing of liquor, include the following steps：
The first step cures liquor to configuration wall, is 30 parts by acrylic resin, 2 parts of antifoaming agent, 5 parts of barium sulfate, acrylic acid elasticity 30 parts of 20 parts of lotion, 4 parts of binary polymer, hydrogen peroxide 2,40 parts of water and modified kaolin are mixed with solidification liquor in proportion；
Second step is brushed, is brushed to metope and ground using the solidification liquor of preparation；
Third walks, covering, is stood in coating layer surface covering film；
4th step tears film open and removes covering film after coat drying.
In use, acrylic resin and binary polymer be combined so that cure the final wash-resistant property of liquor and it is resistance to always Change performance significantly to be improved, while existing bisphenol A formaldehyde epoxy resin is replaced using acrylic resin, greatly Width reduces whole content of formaldehyde so that can shorten time of repose after finishing, solve consolidating of being prepared in existing construction Change liquor and there is the problem of higher formaldehyde and other other toxic residuals, need the long period to stand after finishing.
Embodiment 5
Based on embodiment 2, cures to house wall the curing of liquor, include the following steps：
The first step cures liquor to configuration wall, is 50 parts by acrylic resin, 3 parts of antifoaming agent, 10 parts of barium sulfate, acrylic acid bullet Property 40 parts of 40 parts of lotion, 10 parts of binary polymer, hydrogen peroxide 3,60 parts of water and modified kaolin are mixed with solidify liquid in proportion Agent；
Second step is brushed, is brushed to metope and ground using the solidification liquor of preparation；
Third walks, covering, is stood in coating layer surface covering film；
4th step tears film open and removes covering film after coat drying.
In use, after metope brushing solidification liquor, penetration is strong, cohesive force is high, can effectively close the pore of base, together Shi Zengqiang foundation base intensions and adhesive force.Its surface strength and bonding are can obviously improve especially for dusting base and loose base Power.
By the way that solidification liquor entirety mixing uniformity can be improved after stirring so that can be reduced carrying out follow-up brush Because solidification liquor unevenness leads to local seepage problem.
Embodiment 6
Based on embodiment 3, cures to house wall the curing of liquor, include the following steps：
The first step cures liquor to configuration wall, is 35 parts by acrylic resin, 3 parts of antifoaming agent, 7 parts of barium sulfate, acrylic acid elasticity 35 parts of 30 parts of lotion, 7 parts of binary polymer, hydrogen peroxide 3,40 parts of water and modified kaolin are mixed with solidification liquor in proportion；
Second step is brushed, is brushed to metope and ground using the solidification liquor of preparation；
Third walks, covering, is stood in coating layer surface covering film；
4th step tears film open and removes covering film after coat drying.
In use, after solidification liquor is brushed on ground, good penetrability, strong covering power, cohesive force are high, bright in luster, can be effective Enhance ground intensity, improve the adhesive strength of postorder material and base, and construction site environment can be improved completely, effectively solves Determined ground in construction rise it is husky, raise soil, difficult the problems such as cleaning, mitigate worker's cleaning significantly and keep the difficulty of ground health.
Using the double-deck crisscross brushing when brushing, solidification liquor can be enable closely to be pasted with metope or ground It is attached.

Claims (8)

1. curing liquor to house wall, it is characterised in that：Including acrylic resin, antifoaming agent, barium sulfate, acrylic acid elasticity breast Liquid, binary polymer, hydrogen peroxide, water and modified kaolin.
2. curing liquor to house wall according to claim 1, which is characterized in that by weight, acrylic resin is 30~50 parts, 2~3 parts of antifoaming agent, 5~10 parts of barium sulfate, 20~40 parts of acrylic elastic emulsion, 4~10 parts of binary polymer, 30~40 parts of hydrogen peroxide 2~3,40~60 parts of water and modified kaolin.
3. curing liquor to house wall according to claim 2, it is characterised in that：By weight, acrylic resin is 32~38 parts, it is 2~3 parts of antifoaming agent, 6~9 parts of barium sulfate, 25~35 parts of acrylic elastic emulsion, 5~9 parts of binary polymer, double 32~38 parts of oxygen water 2~3,25~55 parts of water and modified kaolin.
4. curing liquor to house wall according to claim 3, it is characterised in that：By weight, acrylic resin is 34~36 parts, it is 2~3 parts of antifoaming agent, 7~8 parts of barium sulfate, 28~32 parts of acrylic elastic emulsion, 6~8 parts of binary polymer, double 34~36 parts of oxygen water 2~3,30~50 parts of water and modified kaolin.
5. curing liquor to house wall according to claim 4, it is characterised in that：By weight, acrylic resin is 35 parts, 3 parts of antifoaming agent, 7 parts of barium sulfate, 30 parts of acrylic elastic emulsion, 7 parts of binary polymer, hydrogen peroxide 3,40 parts of water and change 35 parts of kaolin of property.
6. curing to house wall the curing of liquor, it is characterised in that：Include the following steps：
The first step cures liquor to configuration wall, acrylic resin, antifoaming agent, barium sulfate, acrylic elastic emulsion, binary is gathered It closes object, hydrogen peroxide, water and modified kaolin and is mixed with solidification liquor in proportion；
Second step is brushed, is brushed to metope and ground using the solidification liquor of preparation；
Third walks, covering, is stood in coating layer surface covering film；
4th step tears film open and removes covering film after coat drying.
7. curing to house wall according to claim 6 the curing of liquor, it is characterised in that：The first step, will Acrylic resin, antifoaming agent, barium sulfate, acrylic elastic emulsion, binary polymer, hydrogen peroxide, water and modified kaolin press than After example mixing, it is stirred 20~40min.
8. curing to house wall according to claim 7 the curing of liquor, it is characterised in that：The second step, will Cure liquor to fall in ground and metope, brush cutter painting is used in combination to cover uniformly, brushing thickness is 0.5mm~1mm, using double-deck crisscross It is brushed.
CN201810373499.9A 2018-04-24 2018-04-24 Cure liquor and curing to house wall Pending CN108610850A (en)