CN108587466A - A kind of superhard chromatic metallic plate of water-based paint - Google Patents

A kind of superhard chromatic metallic plate of water-based paint Download PDF

Info

Publication number
CN108587466A
CN108587466A CN201810400668.3A CN201810400668A CN108587466A CN 108587466 A CN108587466 A CN 108587466A CN 201810400668 A CN201810400668 A CN 201810400668A CN 108587466 A CN108587466 A CN 108587466A
Authority
CN
China
Prior art keywords
water
based paint
metallic plate
parts
chromatic metallic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810400668.3A
Other languages
Chinese (zh)
Inventor
王欣南
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xinying Special Material Technologies Co Ltd
Original Assignee
Suzhou Xinying Special Material Technologies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Xinying Special Material Technologies Co Ltd filed Critical Suzhou Xinying Special Material Technologies Co Ltd
Priority to CN201810400668.3A priority Critical patent/CN108587466A/en
Publication of CN108587466A publication Critical patent/CN108587466A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of preparation methods of the superhard chromatic metallic plate of water-based paint, include the following steps:Step 1, water-based paint is configured:According to the mass fraction, following component is configured to water-based paint:40 50 parts of water-base resin, 25 parts of hydramine, 6 12 parts of amino resins, 20 25 parts of titanium dioxide, 0.5 1 parts of dispersant, 0.5 1 parts of antifoaming agent, 0.1 0.5 parts of levelling agent, 15 20 parts of deionized water;Step 2, it is coated with:It is 70 seconds 60 seconds that the water-based paint that step 1 configuration obtains, which is diluted to viscosity, and two rollers are inversely coated on the one or both sides of chromatic metallic plate;Step 3, it toasts:The baking oven of the chromatic metallic plate of water-based paint by 30 meters 60 meters will be coated in step 2, steel billet temperature reaches 220 DEG C 230 DEG C after baking, toasts at least 1 minute, obtains the superhard chromatic metallic plate of water-based paint.The present invention prevents the pernicious gases such as benzene, dimethylbenzene in organic solvent, realizes the target for reducing VOC emission, and can enhance the hardness of painted surface.

Description

A kind of superhard chromatic metallic plate of water-based paint
Technical field
The present invention relates to colored precoating plate technical fields, particularly relate to a kind of superhard chromatic metallic plate of water-based paint.
Background technology
Chromatic metallic plate has good molding processibility, disclosure satisfy that the requirement of high speed, precise machining equipment, can batch Applied to household electrical appliances, building, ship and furnishing fields.The production of existing chromatic metallic plate mainly utilizes roll coating process, will be oily Property paint be uniformly coated on metal sheet surface and form, what is used in process of production is organic solvent, therefore can be discharged big The VOC of amount.VOC, that is, volatile organic compounds has tremendous influence to health, when the VOC in room reaches a certain concentration When, people can feel headache, Nausea and vomiting, weak etc. in the short time, twitch, stupor be will appear when serious, and can hurt people Liver, kidney, brain and nervous system, cause the serious consequences such as failure of memory, influence environment, therefore, country also by Step adds sternly to the management and control of VOC emission amount.
Invention content
The present invention is intended to provide a kind of superhard chromatic metallic plate of water-based paint.
In order to solve the above technical problems, the technical scheme is that:
A kind of preparation method of the superhard chromatic metallic plate of water-based paint, includes the following steps:
Step 1, water-based paint is configured:According to the mass fraction, following component is configured to water-based paint:
Step 2, it is coated with:It is -70 seconds 60 seconds that the water-based paint that step 1 configuration obtains, which is diluted to viscosity, and two rollers inversely apply Cloth is in the one or both sides of chromatic metallic plate;
Step 3, it toasts:By the chromatic metallic plate for being coated with water-based paint in step 2 by 30 meters -60 meters of baking oven, dry Steel billet temperature reaches 220 DEG C -230 DEG C after roasting, toasts at least 1 minute, obtains the superhard chromatic metallic plate of the water-based paint.
The superhard colour of water-based paint made from a kind of preparation method according to the above-mentioned superhard chromatic metallic plate of water-based paint Metallic plate.
Using above-mentioned technical proposal, the present invention includes at least following advantageous effect:A kind of water-based paint of the present invention is superhard Chromatic metallic plate substitutes oil-based paints by using water-based paint, prevents harmful gas such as benzene, the dimethylbenzene in organic solvent Body realizes the target for reducing VOC emission, and can enhance the hardness of painted surface, reaches the painted surface of hardness 2H or more Hardness (hardness of oil-based paints is 1H).
Specific implementation mode
The technical solution in the present invention is clearly and completely described below in conjunction with specific embodiment, it is clear that retouched The embodiment stated is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, originally The every other embodiment that field those of ordinary skill is obtained without making creative work, belongs to the present invention The range of protection.
Embodiment 1
A kind of preparation method of the superhard chromatic metallic plate of water-based paint of the present embodiment, includes the following steps:
Step 1, water-based paint is configured:According to the mass fraction, following component is configured to water-based paint:
Step 2, it is coated with:It is 60 seconds that the water-based paint that step 1 configuration obtains, which is diluted to viscosity, and two rollers are inversely coated on coloured silk The side of non-ferrous metal plate;
Step 3, it toasts:The chromatic metallic plate of water-based paint will be coated in step 2 by 30 meters of baking oven, steel after baking Plate temperature reaches 220 DEG C, toasts 1 minute, obtains the superhard chromatic metallic plate of the water-based paint.
Embodiment 2
A kind of preparation method of the superhard chromatic metallic plate of water-based paint of the present embodiment, includes the following steps:
Step 1, water-based paint is configured:According to the mass fraction, following component is configured to water-based paint:
Step 2, it is coated with:It is 70 seconds that the water-based paint that step 1 configuration obtains, which is diluted to viscosity, and two rollers are inversely coated on coloured silk The both sides of non-ferrous metal plate;
Step 3, it toasts:The chromatic metallic plate of water-based paint will be coated in step 2 by 60 meters of baking oven, steel after baking Plate temperature reaches 230 DEG C, toasts 2 minutes, obtains the superhard chromatic metallic plate of the water-based paint.
Embodiment 3
A kind of preparation method of the superhard chromatic metallic plate of water-based paint of the present embodiment, includes the following steps:
Step 1, water-based paint is configured:According to the mass fraction, following component is configured to water-based paint:
Step 2, it is coated with:It is 65 seconds that the water-based paint that step 1 configuration obtains, which is diluted to viscosity, and two rollers are inversely coated on coloured silk The both sides of non-ferrous metal plate;
Step 3, it toasts:The chromatic metallic plate of water-based paint will be coated in step 2 by 50 meters of baking oven, steel after baking Plate temperature reaches 225 DEG C, toasts 1 minute, obtains the superhard chromatic metallic plate of the water-based paint.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention. Various modifications to these embodiments will be apparent to those skilled in the art, as defined herein General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one The widest range caused.

Claims (2)

1. a kind of preparation method of the superhard chromatic metallic plate of water-based paint, it is characterised in that include the following steps:
Step 1, water-based paint is configured:According to the mass fraction, following component is configured to water-based paint:
Step 2, it is coated with:It is -70 seconds 60 seconds that the water-based paint that step 1 configuration obtains, which is diluted to viscosity, and two rollers are inversely coated on The one or both sides of chromatic metallic plate;
Step 3, it toasts:The baking oven of the chromatic metallic plate of water-based paint by 30 meters -60 meters will be coated in step 2, after baking Steel billet temperature reaches 220 DEG C -230 DEG C, toasts at least 1 minute, obtains the superhard chromatic metallic plate of the water-based paint.
2. water-based paint made from a kind of preparation method of the superhard chromatic metallic plate of water-based paint according to claim 1 is super Yingcai non-ferrous metal plate.
CN201810400668.3A 2018-04-28 2018-04-28 A kind of superhard chromatic metallic plate of water-based paint Pending CN108587466A (en)