CN108587105A - A kind of polycarbonate film and preparation method thereof - Google Patents
A kind of polycarbonate film and preparation method thereof Download PDFInfo
- Publication number
- CN108587105A CN108587105A CN201810440198.3A CN201810440198A CN108587105A CN 108587105 A CN108587105 A CN 108587105A CN 201810440198 A CN201810440198 A CN 201810440198A CN 108587105 A CN108587105 A CN 108587105A
- Authority
- CN
- China
- Prior art keywords
- parts
- polycarbonate film
- nano
- titanium dioxide
- prothioconazoles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of polymer materials, and in particular to a kind of polycarbonate film and preparation method thereof.Polycarbonate film is made of 35 parts of 75 95 parts of makrolon, 15 parts of nano-titanium dioxide, 5 15 parts of dimethyl silicone polymer, 5 15 parts of silane coupling agent, 29 parts of dispersant, 26 parts of sparteine and prothioconazoles.Makrolon, nano-titanium dioxide, dimethyl silicone polymer, silane coupling agent, dispersant, sparteine and prothioconazoles are uniformly mixed first, are granulated by extruder；Then polycarbonate film is made by casting technique.The present invention is improved by reasonable component and processing technology to make the safety of product obtain to a certain extent, especially the flame retardant property of product.Meanwhile by the addition of the substances such as nano-titanium dioxide, dimethyl silicone polymer, the wear-resisting property of product can be promoted.
Description
Technical field
The present invention relates to technical field of polymer materials, and in particular to a kind of polycarbonate film and preparation method thereof.
Background technology
Polycarbonate film, dimensionally stable, ultraviolet resistance, toughness is fabulous, and intensity is high, and it is damaged to be not easy tearing.Easily bonding, easily
Printing, good moldability are used for the silk-screen printing of various labels, adapt to the processing methods such as IMD, plastic uptake, fitting, lamination.With excellent
Different electric property, high resistance, low-dielectric loss, while having excellent anti-flammability are outstanding insulating materials, extremely suitable
The purposes such as electrical apparatus insulation shielding, power-supply battery shell.Various functions polycarbonate film purposes is more extensive, can be used as conduction
Carrier band, diffusion sheet, light guide plate, reflective membrane, visual window lens etc..
Invention content
In order to solve the technical problems existing in the prior art, the present invention proposes a kind of polycarbonate film and its preparation
Method has excellent flame retardant effect.
The technical scheme is that：A kind of polycarbonate film is made of the raw material of following parts by weight：
75-95 parts of makrolon, 1-5 parts of nano-titanium dioxide, 5-15 parts of dimethyl silicone polymer, silane coupling agent 5-15
Part, 2-9 parts of dispersant, 2-6 parts of sparteine and 3-5 parts of prothioconazoles.
As the preferred embodiment of the present invention, polycarbonate film is made of the raw material of following parts by weight：
80 parts of makrolon, 3 parts of nano-titanium dioxide, 10 parts of dimethyl silicone polymer, 10 parts of silane coupling agent, dispersant
4 parts of 7 parts, 3 parts of sparteine and prothioconazoles.
A method of polycarbonate film being prepared, first by makrolon, nano-titanium dioxide, polydimethylsiloxanes
Alkane, silane coupling agent, dispersant, sparteine and prothioconazoles are uniformly mixed, and are granulated by extruder；Then by being cast work
Polycarbonate film is made in skill.
Beneficial effects of the present invention are shown：
By reasonable component and processing technology, improved to a certain extent to make the safety of product obtain, especially product
Flame retardant property.Meanwhile by the addition of the substances such as nano-titanium dioxide, dimethyl silicone polymer, the wear-resisting of product can be promoted
Performance.
Specific implementation mode
Embodiment 1
A kind of polycarbonate film is made of the raw material of following parts by weight：
95 parts of makrolon, 1 part of nano-titanium dioxide, 15 parts of dimethyl silicone polymer, 5 parts of silane coupling agent, dispersant 9
5 parts of part, 2 parts of sparteine and prothioconazoles.
A method of polycarbonate film being prepared, first by makrolon, nano-titanium dioxide, polydimethylsiloxanes
Alkane, silane coupling agent, dispersant, sparteine and prothioconazoles are uniformly mixed, and are granulated by extruder；Then by being cast work
Polycarbonate film is made in skill.
Embodiment 2
A kind of polycarbonate film is made of the raw material of following parts by weight：
75 parts of makrolon, 5 parts of nano-titanium dioxide, 5 parts of dimethyl silicone polymer, 15 parts of silane coupling agent, dispersant 2
3 parts of part, 6 parts of sparteine and prothioconazoles.
A method of polycarbonate film being prepared, first by makrolon, nano-titanium dioxide, polydimethylsiloxanes
Alkane, silane coupling agent, dispersant, sparteine and prothioconazoles are uniformly mixed, and are granulated by extruder；Then by being cast work
Polycarbonate film is made in skill.
Embodiment 3
A kind of polycarbonate film is made of the raw material of following parts by weight：
80 parts of makrolon, 3 parts of nano-titanium dioxide, 10 parts of dimethyl silicone polymer, 10 parts of silane coupling agent, dispersant
4 parts of 7 parts, 3 parts of sparteine and prothioconazoles.
A method of polycarbonate film being prepared, first by makrolon, nano-titanium dioxide, polydimethylsiloxanes
Alkane, silane coupling agent, dispersant, sparteine and prothioconazoles are uniformly mixed, and are granulated by extruder；Then by being cast work
Polycarbonate film is made in skill.
The above content is just an example and description of the concept of the present invention, affiliated those skilled in the art
It makes various modifications or additions to the described embodiments or substitutes by a similar method, without departing from invention
Design or beyond the scope defined by this claim, be within the scope of protection of the invention.
Claims (3)
1. a kind of polycarbonate film, which is characterized in that be made of the raw material of following parts by weight：
75-95 parts of makrolon, 1-5 parts of nano-titanium dioxide, 5-15 parts of dimethyl silicone polymer, 5-15 parts of silane coupling agent,
3-5 parts of 2-9 parts of dispersant, 2-6 parts of sparteine and prothioconazoles.
2. polycarbonate film as described in claim 1, which is characterized in that be made of the raw material of following parts by weight：
80 parts of makrolon, 3 parts of nano-titanium dioxide, 10 parts of dimethyl silicone polymer, 10 parts of silane coupling agent, 7 parts of dispersant,
4 parts of 3 parts of sparteine and prothioconazoles.
3. a kind of method preparing polycarbonate film as claimed in claim 1 or 2, which is characterized in that first by makrolon,
Nano-titanium dioxide, dimethyl silicone polymer, silane coupling agent, dispersant, sparteine and prothioconazoles are uniformly mixed, and are passed through
Extruder is granulated；Then polycarbonate film is made by casting technique.