CN108559590A - A kind of wear-resistant lubricating oil - Google Patents
A kind of wear-resistant lubricating oil Download PDFInfo
- Publication number
- CN108559590A CN108559590A CN201810445182.1A CN201810445182A CN108559590A CN 108559590 A CN108559590 A CN 108559590A CN 201810445182 A CN201810445182 A CN 201810445182A CN 108559590 A CN108559590 A CN 108559590A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricating oil
- wear
- resistant lubricating
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of wear-resistant lubricating oil, are made of the raw material below according to parts by weight:2 14 parts of tertiary sodium phosphate, 5 15 parts of triethanolamine, 6 18 parts of boric acid, 4 18 parts of polyethylene glycol, 3 13 parts of tartaric acid, 4 18 parts of polyvinyl alcohol, 2 14 parts of sulfide isobutene, 3 13 parts of trimethylolpropane, 6 18 parts of oleic acid fourth diester, 3 13 parts of aluminum stearate, 2 18 parts of antirust agent, 1 11 parts of antioxidant, 28 parts of pour-point depressant, 2 18 parts of dispersant.The present invention has many advantages, such as high lubricating effect, cooling and anticorrosive.
Description
Technical field
The present invention relates to a kind of lubricating oil more particularly to a kind of wear-resistant lubricating oil.
Background technology
Lubricating oil is used in various types automobile, on mechanical equipment to reduce the liquid of friction, protection machinery and workpiece
Or semisolid lubricants, the effects that mainly playing lubrication, supplement heat rejecter, antirust, cleaning, sealing and buffer, and with science and technology
Development, robot field needs to coat lubrication to part portion also in rapid advances, and during the use of robot
The case where oil plays the role of lubrication, prevents part from wearing, but existing lubricating oil selects unreasonable etc. ask because of dispensing
Topic, can not play preferable lubricating action, be unfavorable for the use of people.
Invention content
In order to overcome the defect of the above-mentioned prior art, the object of the present invention is to provide a kind of wear-resistant lubricating oil.
The present invention takes following technical scheme to realize:A kind of wear-resistant lubricating oil, by below according to parts by weight
Raw material composition:2-14 parts of tertiary sodium phosphate, 5-15 parts of triethanolamine, 6-18 parts of boric acid, 4-18 parts of polyethylene glycol, tartaric acid 3-
13 parts, it is 4-18 parts of polyvinyl alcohol, 2-14 parts of sulfide isobutene, 3-13 parts of trimethylolpropane, 6-18 parts of oleic acid fourth diester, stearic
Sour aluminium 3-13 parts, 2-18 parts of antirust agent, 1-11 parts of antioxidant, 2-8 parts of pour-point depressant, 2-18 parts of dispersant.
A kind of above-mentioned wear-resistant lubricating oil, is made of the raw material below according to parts by weight:2-12 parts of tertiary sodium phosphate, three
5-13 parts of ethanol amine, 6-16 parts of boric acid, 4-16 parts of polyethylene glycol, 3-11 parts of tartaric acid, 4-16 parts of polyvinyl alcohol, vulcanization isobutyl
2-12 parts of alkene, 3-11 parts of trimethylolpropane, 6-16 parts of oleic acid fourth diester, 3-11 parts of aluminum stearate, 2-16 parts of antirust agent, antioxygen
1-9 parts of agent, 2-6 parts of pour-point depressant, 2-16 parts of dispersant.
A kind of above-mentioned wear-resistant lubricating oil, is made of the raw material below according to parts by weight:8 parts of tertiary sodium phosphate, three second
10 parts of hydramine, 12 parts of boric acid, 11 parts of polyethylene glycol, 8 parts of tartaric acid, 11 parts of polyvinyl alcohol, 8 parts of sulfide isobutene, trihydroxy methyl
8 parts of propane, 12 parts of oleic acid fourth diester, 8 parts of aluminum stearate, 10 parts of antirust agent, 6 parts of antioxidant, 5 parts of pour-point depressant, 10 parts of dispersant.
In summary the invention has the advantages that:The present invention has high lubricating effect, cooling and anticorrosive etc.
Advantage can effectively reduce the friction coefficient between each part, prevent the feelings of abrasion by the collective effect of each material
Condition extends the service life of part.
Specific implementation mode
Embodiment 1
A kind of wear-resistant lubricating oil, is made of the raw material below according to parts by weight:2 parts of tertiary sodium phosphate, 5 parts of triethanolamine, boron
6 parts of acid, 4 parts of polyethylene glycol, 3 parts of tartaric acid, 4 parts of polyvinyl alcohol, 2 parts of sulfide isobutene, 3 parts of trimethylolpropane, oleic acid fourth
6 parts of diester, 3 parts of aluminum stearate, 2 parts of antirust agent, 1 part of antioxidant, 2 parts of pour-point depressant, 2 parts of dispersant.
Embodiment 2
A kind of wear-resistant lubricating oil, is made of the raw material below according to parts by weight:8 parts of tertiary sodium phosphate, 10 parts of triethanolamine,
12 parts of boric acid, 11 parts of polyethylene glycol, 8 parts of tartaric acid, 11 parts of polyvinyl alcohol, 8 parts of sulfide isobutene, 8 parts of trimethylolpropane, oil
12 parts of sour fourth diester, 8 parts of aluminum stearate, 10 parts of antirust agent, 6 parts of antioxidant, 5 parts of pour-point depressant, 10 parts of dispersant.
Embodiment 3
A kind of wear-resistant lubricating oil, is made of the raw material below according to parts by weight:14 parts of tertiary sodium phosphate, 15 parts of triethanolamine,
18 parts of boric acid, 18 parts of polyethylene glycol, 13 parts of tartaric acid, 18 parts of polyvinyl alcohol, 14 parts of sulfide isobutene, trimethylolpropane 13
Part, 18 parts of oleic acid fourth diester, 13 parts of aluminum stearate, 18 parts of antirust agent, 11 parts of antioxidant, 8 parts of pour-point depressant, 18 parts of dispersant.
The present invention has many advantages, such as high lubricating effect, cooling and anticorrosive, passes through the collective effect of each material, Neng Gouyou
Friction coefficient between each part of reduction of effect, extends the service life of part at the case where preventing abrasion.
The above is the embodiment of the present invention, therefore all structure, feature and principles according to described in the present patent application range are done
Equivalent change or modification, be included within the scope of present patent application.
Claims (3)
1. a kind of wear-resistant lubricating oil, which is characterized in that be made of the raw material below according to parts by weight:Tertiary sodium phosphate 2-14
Part, 5-15 parts of triethanolamine, 6-18 parts of boric acid, 4-18 parts of polyethylene glycol, 3-13 parts of tartaric acid, 4-18 parts of polyvinyl alcohol, vulcanization
2-14 parts of isobutene, 3-13 parts of trimethylolpropane, 6-18 parts of oleic acid fourth diester, 3-13 parts of aluminum stearate, 2-18 parts of antirust agent,
1-11 parts of antioxidant, 2-8 parts of pour-point depressant, 2-18 parts of dispersant.
2. a kind of wear-resistant lubricating oil according to claim 1, which is characterized in that by below according to the raw material of parts by weight
Composition:2-12 parts of tertiary sodium phosphate, 6-16 parts of boric acid, 4-16 parts of polyethylene glycol, 3-11 parts of tartaric acid, gathers 5-13 parts of triethanolamine
4-16 parts of vinyl alcohol, 2-12 parts of sulfide isobutene, 3-11 parts of trimethylolpropane, 6-16 parts of oleic acid fourth diester, aluminum stearate 3-
11 parts, 2-16 parts of antirust agent, 1-9 parts of antioxidant, 2-6 parts of pour-point depressant, 2-16 parts of dispersant.
3. a kind of wear-resistant lubricating oil according to claim 1, which is characterized in that by below according to the raw material of parts by weight
Composition:8 parts of tertiary sodium phosphate, 10 parts of triethanolamine, 12 parts of boric acid, 11 parts of polyethylene glycol, 8 parts of tartaric acid, 11 parts of polyvinyl alcohol,
8 parts of sulfide isobutene, 8 parts of trimethylolpropane, 12 parts of oleic acid fourth diester, 8 parts of aluminum stearate, 10 parts of antirust agent, antioxidant 6
Part, 5 parts of pour-point depressant, 10 parts of dispersant.